环氧／纳米SiO2杂化浆料的制备及其对碳纤维复合材料性能的影响

采用溶胶-凝胶技术制备了环氧/纳米SiO2杂化浆料,对杂化浆料膜的结构和性能进行了表征分析,同时研究了该浆料对碳纤维复合材料性能的影响.首先制备了(γ-异氰酸酯基)丙基三乙氧基硅烷接枝的环氧树脂,利用该树脂对纳米SiO2先驱体进行原位改性,制备碳纤维表面环氧/纳米SiO2杂化浆料.采用FT-IR,AFM和综合热分析仪对纳米SiO2先驱体的原位改性结构、浆料膜的显微形态和相态及其热性能进行分析,成功制备了环氧/纳米SiO2杂化浆料,SiO2以纳米尺度均匀地分布于杂化浆料膜中,纳米SiO2的引入使杂化浆料膜的热性能得到了提高.采用该杂化浆料对碳纤维表面进行改性,复合材料力学性能研究表明,杂化浆料可同时提高复合材料的层间剪切强度和冲击性能.     

溶胶-凝胶法制备SiO2 -TiO2 / 聚酰亚胺杂化材料及其性能

采用溶胶-凝胶法制备了纳米SiO2-TiO2溶胶,然后通过共混法制得SiO2-TiO2/聚酰亚胺杂化材料,SEM、DMTA和TGA等方法研究了无机组分的含量对聚酰亚胺性能的影响。结果表明:SiO2-TiO2/聚酰亚胺杂化材料的冲击强度和弯曲强度随无机粒子含量变化而变化,当无机粒子含量为3%(质量分数)时二者出现最大值,其冲击强度较纯树脂提高了177%,弯曲强度提高了54.6%。另外,随着SiO2-TiO2无机材料的增加,杂化材料热稳定性亦有所提高。     

玄武岩纤维表面涂层改性研究

采用溶胶-凝胶技术制备有机/无机纳米杂化涂层材料,通过红外光谱和原子力显微镜技术对该材料进行表征分析,结果表明合成了环氧/SiO2纳米杂化材料.采用合成的纳米杂化浆料对玄武岩纤维进行表面改性,通过纤维表面形貌、纤维复丝拉伸强度和复合材料层间剪切强度分析,研究玄武岩纤维表面涂层改性效果.试验结果表明:采用适当浓度的涂层溶液对玄武岩纤维进行表面改性可以有效的增加纤维表面粗糙度,提高纤维复丝拉伸强度,改善复合材料界面粘接强度,说明玄武岩纤维表面涂敷有机/无机纳米杂化涂层的改性方法是确实有效的.     

TiO2-有机硅热控涂层对空间聚合材料的防护

在原子氧 (AO)地面模拟设备中对空间材料Kapton及TiO2 有机硅热控涂层进行原子氧剥蚀效应试验。用LAMBDA 9分光度计、光电子能谱 (XPS)、红外光谱 (FTIR)和扫描电镜 (SEM )研究了原子氧 (AO)对Kapton侵蚀机理及对其表面涂覆的TiO2 有机硅热控涂层的防护作用进行了表征。AO对Kapton表现了较严重的侵蚀作用 ,而所施用的TiO2 有机硅热控涂层的表面形貌则变化甚少 ,实验表明 ,该涂层对AO辐照有较强的防护效果、较好的空间稳定性和热控性能。     

C/ C 复合材料SiC/ SiO2 涂层的制备及其抗氧化性能

为提高C/C复合材料的抗氧化性能,采用包埋法和低压化学气相法制备了SiC/SiO2涂层.借助XRD、SEM和EDS等测试手段分析了复合涂层的微观结构,并研究了其在l273、1773 K静态空气中的抗氧化性能.结果表明,包埋法制备的SiC涂层具有一定的浓度梯度.低压化学气相法制备的非晶Si02外涂层则有效地封堵了SiC内涂层的的裂纹和孔洞,并解决了SiC涂层在中温区(1073～1473 K)无法形成完整SiO2膜的问题.在l 273、1 773 K静态空气中经10h氧化后,涂层试样的质量损失率分别仅有4.97和0.36 mg/cm2,表现出良好的抗氧化性能.     

SiO2溶胶在电沉积法制备CuInS2薄膜中的作用

 针对目前电沉积法制备的CuInS2(CIS)薄膜存在S元素含量不足以及微观形貌差的问题,通过在普通镀液中加入SiO2溶胶,采用一步电沉积技术在ITO导电玻璃上制备Cu In S预制薄膜,镀液的主要组成为金属盐、硫代硫酸钠和不同浓度SiO2溶胶。在空气气氛中对Cu In S预制薄膜进行退火处理以获得多晶的CIS薄膜,并通过X射线衍射（XRD）、扫描电镜（SEM）、能量色散谱仪（EDS）及开路电位对CIS薄膜的结构、形貌、成分组成及光响应性能进行研究。结果表明：SiO2溶胶浓度为4 mL/L时,得到的CIS薄膜的结晶度提高,同时,SiO2溶胶作用下得到的CIS薄膜的表面形貌、成分组成和光响应性能都得到改善。因此,镀液中加入SiO2溶胶有利于提高CIS薄膜的性能,尤其是浓度为4 mL/L时,性能提高得最为明显。     

溶胶-凝胶法制备纳米SiO2／CE复合材料的研究

采用溶胶-凝胶法,利用正硅酸乙酯(TEOS)在有机溶剂中的水解-缩合制备纳米SiO2.将所制备的纳米SiO2用于改性双酚A型氰酸酯树脂(BADCy),制备纳米SiO2/BADCy浇铸体.采用透射电镜(TEM)分析SiO2在BADCy基体中的分散性,同时测试了复合材料的力学性能.结果表明,粒径为20～50 nm的SiO2在基体中以纳米量级均匀分散,与BADCy结合界面模糊,两者具有较好粘结性;添加纳米SiO2可以明显提高复合材料的冲击强度和弯曲强度,当纳米SiO2的含量为4%时,力学性能改性效果最佳.     

不同介孔结构的SiO2 对PMMA 性能的影响

分别采用二维六方孔结构SiO2(SBA-15) 和蠕虫状孔结构SiO2(MSU-J) 与MMA 原位聚合制备

介孔SiO2 / PMMA 杂化材料。采用XRD、N2 吸附-脱附、SEM、DSC 和TGA 等方法研究了材料的微观结构、力学

性能、热性能和介电性能。结果表明:介孔SiO2 对PMMA 有增强增韧作用,同时也有利于杂化材料热性能和介

电性能的提高。杂化材料的热稳定性和耐热性均高于PMMA,含4wt% 的SBA-15/ PMMA 和7wt% 的MSU-J/

PMMA 杂化材料的介电常数由2. 91 分别降至最低2. 73 和2. 64。

     

飞机透明件用光固化有机-无机杂化耐磨涂层的研究

采用溶胶-凝胶法通过控制催化剂添加量制备了不同纳米粒径的纳米二氧化硅粒子,用偶联剂MEMO对其表面进行改性处理后制备了有机玻璃用光固化有机-无机杂化涂层。结果表明,经过MEMO处理的纳米二氧化硅粒子与光固化聚氨酯丙烯酸酯树脂有很好的相容性,PMMA涂覆光固化PUA/SiO2涂层后,其硬度由原来的HB提高到3H,体积收缩率降低52%,耐磨性能比未添加的纳米SiO2涂层提高了70%以上。     

2DCf／SiC-Si复合材料的制备和性能研究

针对短时高温抗氧化的具体环境,采用先驱体转化工艺制备2D Cf/SiC-Si复合材料.首先考察首周期裂解温度对2D Cf/SiC-Si材料力学性能的影响,结果表明,首周期采用1200℃裂解,所制备的2D Cf/SiC-Si复合材料界面结合较好,弯曲强度和断裂韧性分别达到305.4MPa和15.7 MPa·m1/2.在此基础上研究了Si粉含量对材料性能的影响.结果表明,随着Si含量的增加,2D Cf/SiC-Si材料的力学性能稍有降低,而抗氧化性能明显提高,主要原因在于材料中游离碳含量的降低和Si氧化后生成的具有封填裂纹和隔氧作用的SiO2膜.     

First-principle Calculations of V/Fe Doped Anatase TiO_2

The electronic structures of the titanium dioxide(TiO2) doped with V and Fe were analyzed by using first-principle calculations based on the density functional theory(DFT) with the full potential linearized augmented plane wave method (FP-LAPW). The fully optimized structure and the relaxation introduced by impurity were obtained by minimizing the total energy and atomic forces. The unit cell of the V-doped anatase TiO2 is smaller than that of the non-doped one, but for the Fe-doped one, the case is just the opposite. It is found that the apical Ti-O and impurity-O bond lengths of the V/Fe-doped anatase TiO2 are greater than those of the non-doped structure, but smaller for the equatorial bond length. Through the band structures and the density of states, the V-doped TiO2 is shown to be a kind of half-metal, while the Fe-doped TiO2 a kind of metal. The magnetic moments of the V/Fe-doped system are mainly generated by the dopants. The results may be helpful for us to understand the experimental outcome of this system.     

First-principle Calculations of V/Fe Doped Anatase TiO2

The electronic structures of the titanium dioxide（TiO2） doped with V and Fe were analyzed by using first-principle calculations based on the density functional theory（DFT） with the full potential linearized augmented plane wave method （FP-LAPW）. The fully optimized structure and the relaxation introduced by impurity were obtained by minimizing the total energy and atomic forces. The unit cell of the V-doped anatase TiO2 is smaller than that of the non-doped one, but for the Fe-doped one, the case is just the opposite. It is found that the apical Ti-O and impurity-O bond lengths of the V/Fe-doped anatase TiO2 are greater than those of the non-doped structure, but smaller for the equatorial bond length. Through the band structures and the density of states, the V-doped TiO2 is shown to be a kind of half-metal, while the Fe-doped TiO2 a kind of metal. The magnetic moments of the V/Fe-doped system are mainly generated by the dopants. The results may be helpful for us to understand the experimental outcome of this system.     

Ag/TiO2/ITO紫外探测器的制备及其光电性能

采用胶体晶体模板技术,结合磁控溅射工艺,制备出光电性能较为优异的 Ag反点阵列/TiO2/ITO三明治结构紫外探测器。通过扫描电子显微镜( SEM)、XRD、四探针测试仪及半导体参数测试仪对探测器的微观结构和光电性能进行了测试与表征。结果表明：反点阵列孔径对探测器光电性能影响较为显著;随着孔径增大,探测器的暗电流逐渐增大,光电流先增大后减小,响应时间逐渐延长;孔径为4.2μm时,探测器的光电性能达到最佳;孔径较大的反点阵列电极,具有较高的电导率、较低的紫外光透过率以及较大的光生电子-空穴的复合概率。     

纳米TiO2/Fe2O3复合材料的制备及其红外吸收性能研究

用溶胶-凝胶法制备了纳米TiO2／Fe2O3复合材料，并用XRD、TEM等方法对其进行了表征，给出了相关的工艺参数。研究了不同组分的纳米TiO2／Fe2O3的红外吸收特性。结果表明，纳米TiO2／Fe2O3复合材料在400cm^-1～1000cm^-1内随Fe2O3含量的增加，吸收峰明显宽化。     

TiO2-SiO2复合薄膜亲水性能研究

采用溶胶一凝胶法,钛酸丁酯和正硅酸乙酯为前驱体,在玻璃载体上制备了具有光致亲水性能的复合型TiO2-S iO2薄膜。研究了试剂配比、试剂加入方式、凝胶时间、镀膜速度、焙烧升温速度等对薄膜性能的影响。通过对试剂配比和工艺参数的优化,提高了复合薄膜的亲水性能。     

纳米TiO2光催化材料的研究现状及展望

评述了纳米TiO2光催化材料的发展概况、光催化降解原理及特点，纳米二氧化钛光催化材料粉末及薄膜的一些主要制备方法。介绍了TiO2光催化材料的几种应用研究以及所要克服的技术难点，并对今后的发展方向作了展望。     

Sol—GelTiO2薄膜的氮化研究

探讨了一种制备多孔性氮化钛薄膜的新方法。以钛酸正丁酯ＴＩＲ为前驱物,通过溶胶－凝胶（ｓｏｌ＿ｇｅｌ）过程可在不锈钢等基体材料表面涂覆一定厚度的ＴｉＯ２凝胶膜。Ｘ－射线衍射分析（ＸＲＤ）表明,以ＮＨ３气作为氮化气氛,能完成在ＴｉＯ２薄膜到ＴｉＮ薄膜的转变。     

Magnetic and Optical Properties of the TiO2-Co-TiO2 Composite Films Grown by Magnetron Sputtering

The TiO2-Co-TiO2 sandwich films were successfully grown on glass and silicon substrata making alternate use of radio frequency reactive magnetron sputtering and direct current magnetron sputtering. The structures and properties of these films were identified with X-ray diffraction (XRD), Raman spectra and X-ray photoemission spectra (XPS). It is shown that the sandwich film consists of two anatase TiO2 films with an embedded Co nano-film. The fact that, when the Co nano-film thickens, varied red shifts appear in optical absorption spectra may well be explained by the quantum confinement and tunnel effects. As for magnetic properties, the saturation magnetization, remnant magnetic induction and coercivity vary with the thickness of the Co nano-films. Moreover, the Co nano-film has a critical thickness of about 8.6 nm, which makes the coercivity of the composite film reach the maximum of about 1413 Oe.     

激光重熔Al_2O_3-13% TiO_2复合陶瓷涂层抗冲蚀性能

为了进一步提高TiAl合金表面等离子喷涂Al2O3-13%TiO2(质量分数,下同)复合陶瓷涂层的抗冲蚀性能,采用激光重熔工艺对涂层进行处理,研究了激光重熔对涂层微观组织和抗冲蚀性能的影响,并讨论了陶瓷涂层的冲蚀机理。结果表明,激光重熔处理会形成致密细小的等轴晶重熔区,导致涂层有更好的抗冲蚀性能。激光重熔试样仍表现为典型的脆性冲蚀特性,以近表面的裂纹萌生和扩展,最终导致重熔层破碎、晶粒剥离为主。