氟塑料-阀芯黏结工艺

为了解决液体火箭发动机主阀阀芯氟塑料与金属黏结不良问题,对其成因与黏结工艺进行研究。采用阀芯压制氟塑料前涂覆自制聚全氟乙丙烯胶黏剂的黏结工艺方法,通过扫描电镜观察黏结面微观结构形貌并进行能谱分析,进而对涂聚全氟乙丙烯胶黏剂的黏结工艺方法进行机理分析,最后开展菌状物试样黏结工艺验证、阀芯工艺验证、工作性能试验验证。试验表明:采用涂聚2遍全氟乙丙烯胶黏剂黏结的工艺方法,可提高氟塑料和金属黏结强度,黏结强度可提高到19 MPa以上,达到未涂胶氟塑料与金属黏结强度的3倍,阀芯黏结合格率达到100%,使用性能满足使用要求,有效解决液体火箭发动机主阀阀芯黏结不良问题。     

Effect of curing condition on bonding quality of scarf-repaired composite laminates

Both single-face vacuum bag curing (SVC) and double-face vacuum bag curing (DVC) can be used in scarf repair of composite structures. But different curing conditions caused by the sealing state may affect the bonding quality of scarf-repaired structures. In this paper, the effect of curing condition on bonding quality of scarf-repaired laminates was experimentally investigated in terms of surface profiles, moisture absorption curves and section profiles. In order to further explore the moisture absorption mechanism, finite element model of the repaired laminates using DVC was established with moisture diffusion of both the adhesive and composite laminates considered. This model was verified by experimental results. Based on the model of DVC case, the model of SVC case was built by changing moisture absorption parameters of the adhesive. Results show that SVC reduces the bonding quality, mainly reflecting in more adhesive inner voids and patch-to-parent dislocation. And SVC increases moisture absorption rate and moisture equilibrium content of the adhesive, and its effect on the former is far greater than that on the latter.     

影响胶粘剂剪切强度因素的探讨

分析了在胶粘剂剪切强度检测过程中,胶接材料表面处理方法、胶层的厚度、测试时加的垫片厚度和试样的夹距距离、涂胶时的晾置时间等因素对检测结果影响。研究结果表明,上述因素不仅直接影响了胶粘剂粘接强度的大小,而且关系到胶粘剂剪切强度检测试验的测试结果。     

新型结构粘接材料对航空有机玻璃性能的影响

选用新型结构粘接材料中低温固化环氧结构胶膜J-351和改性丙烯酸酯液体胶胶黏剂SY-50s,表征胶黏剂对有机玻璃的粘接性能以及应力-溶剂银纹性能,并研究胶黏剂对有机玻璃力学性能的影响。结果表明:两种胶黏剂对有机玻璃具有良好的粘接性能,J-351抗应力溶剂银纹性能优于SY-50s;有机玻璃表面施胶后力学性能下降,与定向有机玻璃相比,浇注有机玻璃力学性能下降更为明显。通过对拉伸试样断口形貌分析发现,拉伸试样带有胶黏剂的一侧首先发生破坏。因SY-50s与有机玻璃界面结合紧密,导致带有SY-50s胶黏剂的有机玻璃力学性能下降程度较大;而J-351环氧胶膜与有机玻璃界面清晰,对有机玻璃力学性能影响相对较小。因胶黏剂对有机玻璃性能的影响,导致采用SY-50s胶黏剂粘接的试样边缘连接强度低于J-351胶黏剂粘接的试样,新型结构粘接材料J-351环氧胶膜在有机玻璃粘接中应用性能良好。     

胶粘剂拉伸剪切强度不合格原因分析

针对X牌号环氧胶粘剂在试验过程中出现拉伸剪切强度不合格的现象,通过大量的试验查找原因,最终确定了影响胶粘剂拉伸剪切强度的因素。同时,提高了对试片的制备、处理、粘接、固化的理论认识和实际操作水平。     

Fatigue crack propagation of new aluminum lithium alloy bonded with titanium alloy strap

A new type of aluminum lithium alloy (Al-Li alloy) Al-Li-S-4 was investigated by test in this paper. Alloy plate of 400 mm · 140 mm · 6 mm with single edge notch was made into samples bonded with Ti-6Al-4V alloy (Ti alloy) strap by FM 94 film adhesive after the surface was treated. Fatigue crack growth of samples was investigated under cyclic loading with stress ratio (R) of 0.1 and load amplitude constant. The results show that Al-Li alloy plate bonded with Ti alloy strap could retard fatigue crack propagation. Retardation effect is related with width and thickness of strap. Flaws have an observable effect on crack propagation direction.     

加载速率对层间断裂韧性的影响

虽然加载速率对层间断裂的影响已经被广泛的研究,但是现有的研究结果还未能给出加载速率对层间断裂韧性影响的明确趋势。研究人员发展了许多测量层合板复合材料以及胶接层断裂韧性的实验方法。本文的主要目的是对层间断裂韧性测量的实验方法进行综述,尤其是准静态和动态加载条件下层间起裂韧性的测量。首先介绍了准静态下Ⅰ型、Ⅱ型以及Ⅰ/Ⅱ复合型层间断裂韧性的测量方法,然后综述动态加载下层间断裂韧性的实验方法。前两部分着重介绍断裂实验中断裂参数(载荷、位移、起裂时间以及裂纹长度)的测量以及断裂韧性的计算。之后又综述了两种光学测量方法在层间断裂实验中的应用。最后将文献中加载速率对层间断裂韧性影响的实验研究结果进行了总结。     

应用于陶瓷试件的胶粘剂粘贴强度研究

陶瓷试验件在800℃以上快速升温过程中,对粘贴温度传感器的胶粘剂剥离试件现象进行研究。首先从接触角入手,阐述试验用高温胶粘剂在陶瓷试件表面进行粘贴的前提条件是胶粘剂与被粘贴物表面的接触角θ范围为0°≤θ90°;对实际中陶瓷试件表面的粗糙化处理影响胶粘剂粘贴强度进行了理论和试验分析,说明对试件表面适当粗糙化处理提高了粘贴强度并减小了接触角;最后对高温胶粘剂在高温固化过程中的加压工艺改进进行说明,并进行了试验,试验结果表明工艺改进改善了试验过程中的胶粘剂剥离问题。     

定应变贮存条件下HTPB推进剂填料/黏合剂界面性能

为研究定应变贮存条件下HTPB推进剂的主要失效原因,基于单轴拉伸实验,得到HTPB推进剂的宏观力学性能。基于扫描电镜观察和测试探测液在填料AP,黏合剂基体上的接触角方法,表征了微观界面性能。实验结果显示,随老化时间的延长,最大延伸率显著降低,填料与黏合剂基体黏结变差,黏附功Wa减小,界面张力γsl增大。HTPB推进剂填料与黏合剂基体的界面黏结情况可由填料与黏合剂基体的黏附功、界面张力来表征。定应变作用下推进剂老化后黏附功的值远低于无应变热老化的值,界面张力的值远高于无应变热老化的值,定应变的存在严重影响了推进剂填料/基体界面的黏结。宏观-微观性能的相关性研究表明,最大延伸率和黏附功存在线性相关关系,最大延伸率的降低主要由界面黏结的劣化引起的。     

经验模态分解火箭发动机多界面粘结检测特征信号提取技术

针对固体火箭发动机在存放期间粘结界面易出现脱粘的情况,采用超声纵波对其一二界面粘结质量进行检测,得到的二界面脱粘缺陷回波信号通常混叠了一界面多次反射透射的信号,无法与一界面粘结信号区分。为了区分不同界面回波信号,选用EMD(经验模态分解)对回波信号分解,并根据相关性系数得到信号主导作用模态分量,提取其检测信号幅度特征,得到界面粘结情况,再根据时间确定粘结位置是一界面还是二界面。结果表明:通过EMD对超声回波信号的特征提取可以实现固体火箭发动机界面最小直径为4 mm的脱粘缺陷检测,同时有效地降低分析计算的数据量,为固体火箭发动机粘结检测提供一定基础。