7075铝合金在超塑处理和拉伸过程中的显微组织变化

 研究了 70 75铝合金在超塑性预处理和拉伸过程。结果表明 ,合金经过固溶处理炉冷→轧制预处理后 ,形成 1～ 2 μm的胞块组织。在超塑拉伸过程中胞块发生回复和再结晶 ,形成细晶组织 ,使合金获得优异的超塑性性能     

Study on the Microstructure and Dielectric Properties of Barium Strontium Titanate Thin Films Prepared by Sol-gel Method

Sr05Ba0.5-xBixTiO3 （BST） thin films were fabricated on a Pt/SiO2/Si substrate by the sol-gel method. Then follows an investigation of the influeoces of bismuth （Bi） on the microstructures and the dielectric properties of Sr0.5Ba0.5-xBixTiO3 （BST） thin films. The microstructures of the BST thin films were examined by the XRD and the TEM techniques. Tetragonal perovskite crystal grains were observed in BST thin films. Increasing Bi^3＋ doping ration in BST will lead to decrease of the grain size. It is found that Bi^3＋ doping decreases the dielectric loss and improves the frequency dispersion of the BST thin films. Not only is compressed the peak of temperature-dependence of dielectric constant of Bi^3＋-doped BST thin films but also moves into the low-temperature region. Moreover, the average Curie tem- perature decreases gradually with the Bi^3＋ contents increasing.     

热处理对二次锻造高Nb-TiAl基合金组织的影响

研究了热处理对二次锻造高Nb-TiAl基合金组织的影响。通过对Ti-45Al-9(Nb,W,B,Y)金属间化合物进行不同的热处理,得到不同的显微组织。结果表明,经1310℃/20min+1250℃/2h/AC热处理后,β相被有效地消除,得到细小均匀的双态组织。此后直接加热到α单相区,得到条带状的全片层组织。增加在两相区的停留,得到相对比较均匀细小的全片层组织。将锻造组织先转变为近γ组织再进行全片层组织处理,得到最均匀细小的全片层组织。     

Microstructure and Optical Characterization of Magnetron Sputtered NbN Thin Films

Some fundamental studies on the preparation, structure and optical properties of NbN films were carried out. NbN thin films were deposited by DC reactive magnetron sputtering at different N2 partial pressures and different substrate temperatures ranging from –50 ℃ to 600 ℃. X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM) were employed to characterize their phase com- ponents, microstructures, grain sizes and surface morphology. Optical properties inclusive of refractive indexes, extinction coefficients and transmittance of the NbN films under different sputtering conditions were measured. With the increase in the N2 partial pressure, δ-NbN phase structure gets forming and the grain size and lattice constant of the cubic NbN increasing. The deposited NbN film has relatively high values of refractive index and extinction coefficient in the wavelength ranging from 240 nm to 830 nm. Substrate tem- perature exerts notable influences on the microstructure and optical transmittance of the NbN films. The grain sizes of the δ-NbN film remarkably increase with the rise of the substrate temperature, while the transmittance of the films with the same thickness decreases. Ultra-fine granular film with particle size of several nanometers forms when the substrate is cooled to –50 ℃, and a remarkable aug- mentation of transmittance could be noticed under so low a temperature.     

喷射沉积过程中显微组织的形成机制

通过对沉积还纵剖面的组织分析，发现沉积坯在进缘、上下表面及中心部位的显微组织明显不同。边缘及上下表面区试样的退火试验研究表明，细小的枝晶碎块在高温退火过程中发生凝共和粗化，并导致近球状晶粒组织的形成。试验确定其生长服从：D2-D02=6.37×1020e(-70036.1/T)·τ，晶界迁移激活能Qg=582KJ／mol。并依赖于两种机制：（1）在喷射沉积过程中无强烈变形枝晶的均匀化；（2）变形及断裂枝晶的生长和粗化。     

热处理对Nb-10Si合金显微组织的影响

采用真空电弧熔炼法制备了 Nb-1 0 Si ( at% )合金 ,并在 1 85 0℃和 1 5 5 0℃温度氩气保护下进行了 2～ 1 0 0 h的热处理。综合通过 X射线衍射、透射电子显微术、扫描电子显微术及 X射线能谱对合金的显微组织进行了研究。结果表明 ,铸态 Nb-1 0 Si合金由连续的 Nb3 Si基体与均匀分布的 Nb相组成 ,1 85 0℃温度下热处理 2 h后 ,Nb晶粒明显长大 ;而在 1 5 5 0℃热处理后 ,Nb晶粒尺寸基本不变 ,Nb3 Si逐渐转变为 Nb和 Nb5Si3 相 ,且它们之间存在着一定的取向关系。1 5 5 0℃热处理 1 0 0 h后可以获得稳定的 Nb+ Nb5Si3 双相显微组织 ,是合适的热处理制度     

电场均匀化对 2091Al-Li 合金的显微组织及力学性能的影响

 应用扫描电镜（SEM）及电子探针（EPMA）研究了强电场作用下Al-Li合金的均匀化过程。实验结果表明，强电场加速了2091Al-Li合金的均匀化过程，但是随着电场作用时间的增加，发生了镁、铜原子的上坡扩散，导致镁、铜原子的非平衡偏聚。因此，电场及非电场的联合处理方法是一个有效的均匀化处理制度。同时，还研究了强电场均匀化对显微组织及力学性能的影响，发现强电场均匀化促进T1相的形核，抑制δ‘和S’相析出，提高了Al-Li合金的屈强比。     

扫描隧道显微镜对粘胶基碳纤维表面微观结构的研究

用扫描隧道显微镜（STM）对粘胶基碳纤维（RCF）表面的微观结构进行了研究，首次获得了原子级的RCF图像，对其原子间距作了精确地量化，并且尝试着将所得到的图像与高定向降解石墨（HOPG）相比较，以期对RCF的微观结构有更深入的了解，在原子级尺度上，发现了原子排列并不规则的石墨状结构，二维视图量化结果表明：相邻原子间距为0．142nm，最近六圆环中心的距离是0．253nm。     

GH169合金细晶锻造工艺研究

为了提高涡轮盘的强度和低周疲劳性能,要求锻件具有ASTM10级以上的细晶组织国外在大型压力机上采用低温大变形锻造和直接时效热处理以获得性能良好的细晶锻件,而我国则试图采用锻锤生产GH169合金涡轮盘锻件,因此,需要探索适合国情的GH169合金细晶锻造工艺。根据以往的研究,δ相对GH169合金的显微组织有明显影响,因而可     

SCR技术制备A2017半固态材料及其触变性能的研究

单辊搅拌技术 (SCRShearing/CoolingRollProcess)技术制备的A2 0 17半固态材料比常规铸造坯组织优良 ;SCR技术制备的A2 0 17半固态材料在 5 30～ 5 70℃范围内 ,可以进行触变成形 ;半固态成形平均屈服强度比热加工时的屈服强度低 10MPa ;A2 0 17半固态材料触变过程分为四个阶段 ,稳定触变阶段A2 0 17半固态材料的触变性能稳定 ,半固态加工时容许的最大加工变形范围为 6 4 %～ 72 %。