船用钢需钠弧菌附着腐蚀电化学噪声特征分析

选取船用钢板DH34为研究对象 ，将试验钢板浸泡于需钠弧菌培养液中和无菌培养液中进行腐蚀试验，对比分析了该材料在需钠弧菌培养液中的腐蚀特征。采用扫描电镜观察腐蚀形貌，结果表明在需钠弧菌培养液中试样发生局部点蚀，而在无菌培养液中则为全面腐蚀。对腐蚀过程进行了噪声电压和噪声电流的采集，时域和频域分析表明:在有需钠弧菌的培养液中，电压噪声功率谱的高频斜率高于-20 dB/dec，截止频率大于0.2 Hz，起始两天噪声的点蚀指数接近于1;而在无菌的培养液中，电压噪声功率谱的高频斜率小于-20 dB/dec，截止频率低于0.2 Hz。需钠弧菌的培养液中噪声电阻值高于无菌培养液中噪声电阻值。点蚀指数、噪声功率谱密度的高频斜率和截止频 率可用于判断需钠弧菌附着时船用钢板DH34的腐蚀行为。     

LC4铝合金服役环境下点蚀形貌特征及其演变规律

为获取飞机LC4铝合金在服役环境下典型点蚀形貌特征,采用模拟服役环境的加速腐蚀实验环境谱对材料试件进行加速腐蚀实验,定义3个参数蚀坑深度H、蚀坑表面长度L、蚀坑表面宽度W为表征蚀坑形貌特征参量,跟踪测量典型蚀坑不同腐蚀年限下此3个特征参量数值,获取典型蚀坑形貌特征参量数据检测结果。在此基础上,对检测结果分别采用统计分析和分形理论方法进行数据分析,获取LC4铝合金同一腐蚀年限下和不同腐蚀年限下典型点蚀蚀坑的形貌特征及其演变规律。结果表明:同一腐蚀年限下,点蚀蚀坑形貌特征参量符合对数正态分布;随着腐蚀年限的增加,点蚀蚀坑形貌特征参量逐渐体现出明显的分形特征,蚀坑形貌逐渐趋向坑深度较浅、坑表面长度较长、坑表面宽适中的特征。     

多孔NiCr在750℃ NaCl沉积盐中的热腐蚀机理研究

针对飞机发动机高压压气机NiCr系可磨耗封严涂层发生的NaCl热沉积盐高温腐蚀现象,采用粉末烧结法制备了多孔80Ni20Cr合金,研究了其在750℃空气气氛中的NaCl热腐蚀行为。采用X射线衍射和能谱分析等技术对腐蚀产物进行了分析。结果表明,NaCl固体盐通过阻碍合金表面生成连续致密的Cr_2O_3,加速多孔NiCr的腐蚀和氧化。研究发现,在样品外表面形成的Cr_2O_3、NiO、NiCr_2O_4混合氧化物膜易开裂剥落,是合金加速腐蚀的主要方式。此外,通过同步热分析并结合热力学模拟计算发现,NiCr合金的热腐蚀由氯化-氧化协同控制,初始依靠NaCl与Cr元素反应引发合金的循环腐蚀,并推动整个腐蚀过程不断进行。     

电化学辅助沉积KH-570硅烷对AZ31B镁合金耐蚀性能的影响

采用电化学辅助沉积方法对AZ31B镁合金进行硅烷化处理,借助于动电位极化曲线和电化学阻抗谱等电化学测试手段研究了γ-(甲基丙烯酰氧基)丙基三甲氧基硅烷(KH-570)添加量对膜层质量及耐蚀性能的影响,并比较了利用羟基磷灰石(HA)颗粒、铈盐离子(Ce3+)两种改性物质改良硅烷溶液后所制得膜层的质量及耐蚀性能.结果表明:AZ31B镁合金经电化学辅助沉积硅烷处理后,表面生成一层均匀而致密的硅烷透明膜层,有效地减缓了镁合金的腐蚀行为,促使其自腐蚀电流密度大大降低;在硅烷电化学辅助沉积处理过程中,KH-570存在最佳添加量,当其添加体积约为8 mL时所制备出的硅烷膜层质量最好、耐蚀性能最佳;通过改良硅烷溶液,电化学辅助沉积制备的硅烷膜层质量进一步提高,Ce3+改良效果更佳.     

Electrochemical machining of a convex strips structure on a revolving part by using site directed power interruption

Revolving parts with complex surface structures are widely used in machinery and mechanical equipment. The ECM process provides its adequacy to cut hard materials with different shapes, and its applications are widely increased, due to its outstanding advantages. In this paper, a new method for machining a convex strips structure on a cylinder by using site directed power interruption(SDPI) in the ECM process is presented. A variable correction value of the power-off time was defined and optimized to obtain the ideal interval for better machining accuracy and stability.The electric field distribution and the simulated convex profiles show that the stray current density can be reduced effectively by using the proposed method. The correction value has an important influence on the machining accuracy. A suitable correction value in the range of 0.6–1.2 s can effectively improve the machining accuracy of the convex strips structure. Experiments were also conducted to verify the proposed method. Results have confirmed that the stray corrosion on the convex strips surface is significantly reduced and the machining accuracy of convex strips structure is remarkably improved by using the proposed method with a suitable correction value in the ECM process. Finally, a convex strip with a height of 2 mm on a thin-wall revolving part was also produced successfully using a correction value of 0.9.     

基于远场涡流技术的油气集输管道缺陷检测研究

由于石油和天然气在集输过程中含有大量腐蚀成分，会对集输管道造成腐蚀形成穿孔、凹槽等缺陷，为了保证集输管道的安全，需要对腐蚀缺陷进行检测。本文运用远场涡流检测原理，建立了基于集输管道的远场涡流仿真模型，通过管道缺陷对磁感应强度轴向分量幅值和相位的影响进行分析，得出了管道内壁缺陷的深度与对应检测信号的关系，解决了对缺陷深度的定量测量问题。     

1420 铝锂合金锻件开裂原因分析与控制

某产品用1420 铝锂合金锻件在存放过程中发生开裂。本文通过对失效锻件进行形貌观察以及

断口、金相和力学性能分析,结合此锻件的制造工艺,分析认为:此锻件的开裂属于延迟开裂;锻件小端转角区

(R 区)存在较大的应力,淬火水冷阶段在R 区内表面形成微小表层裂纹;长期的存放过程中,锻件表面受到腐

蚀,发生应力腐蚀;微裂纹在残余应力及应力腐蚀的作用下缓慢扩展直至发生失稳扩展形成宏观贯穿裂纹,致

使锻件开裂。通过车光锻件内外表面及车光后的荧光检查,有效地预防了此类开裂故障的发生。

     

大气腐蚀电化学测定研究

介绍了自行研制的环境试验中大气腐蚀电化学测定装置,包括Kelvin 大气腐蚀测定仪的工作原理,功能用途,软硬件结构及初步测试结果.自行研制的Kelvin大气腐蚀测定仪采用振动电容法技术,不需与被测量试样及电解液相接触,用Kelvin探针作参比电极,即可测得液膜下金属电极电位及极化曲线,为研究大气环境下的材料腐蚀行为提供了先进的技术和方法.     

海南万宁大气腐蚀环境特点的研究

通过利用大气腐蚀监测仪(ACM)对海南万宁地区的大气腐蚀进行长期电化学监测的结果,与该地区同期的主要大气腐蚀环境因素对比分析,初步找出海南万宁大气腐蚀的主要环境因子及其腐蚀环境特点.海南万宁长期处于高温高湿条件下,大气腐蚀处于连续不断过程之中,但这一地区大气污染少,加速因素较小,因而大气腐蚀不严重.     

某型教练机油门操纵系统支座裂纹分析与研究

针对某型教练机发动机油门操纵系统支座裂纹现象,对其进行了材料特性、安装位置及形式、载荷、强度校核、装配应力和理化分析,结果表明,铆钉孔周向干涉配合或强迫装配使其上壁板与背板交界拐角处弯曲产生的拉应力,使表面防护层被破坏,随后在拉应力和腐蚀环境的共同作用下导致支座开裂.