高温处理对中密度针刺C/C复合材料性能的影响

针对C/C复合材料脆性问题,对密度为1.60 g/cm3的碳布叠层针刺C/C复合材料进行了1800、2 000、2 200和2 500℃的高温处理,研究了不同热处理温度对C/C复合材料微晶结构、力学和抗热震等性能的影响.结果表明,高温处理使针刺C/C复合材料的层间剪切和面内拉伸强度出现不同程度的降低,但材料的断裂伸长率和抗热震性能得到大幅度提高.其中,1 800℃高温处理后的C/C复合材料具有优异的力学和抗热震性能.     

先驱体转化法制备2D C/SiC-ZrC复合材料中ZrC含量对材料结构性能影响研究

针对高超音速飞行器、可重复使用运载器和下一代火箭发动机等超高温使用环境的工况要求,提出在2D C/SiC复合材料中引入耐超高温ZrC填料.采用先驱体转化法制备了不同ZrC含量的2D C/SiC-ZrC新型复合材料,考察了ZrC含量对材料力学性能、抗烧蚀性能和组成结构的影响.结果表明,材料的弯曲强度和弯曲模量随着ZrC含量的增加有一定程度的下降,材料的抗烧蚀性能明显提高,其中ZrC含量最高(33.3vol%)的试样S-50弯曲强度和弯曲模量均最低,分别为192.1MPa和27.5GPa;经氧乙炔焰烧蚀考核60s后,表面温度达到2123℃,试样表现出最低的烧蚀率,线烧蚀率为0.004mm/s,质量烧蚀率为0.006g/s.     

2D C/SiC-ZrB2复合材料的烧蚀性能

用ZrB2微粉对2D C/SiC基体进行改性,研究了化学气相渗透结合浆料浸渍及先驱体浸渍裂解工艺制备2DC/SiC-ZrB2复合材料在氧-乙炔焰和1800℃甲烷风洞环境中的烧蚀行为.结果表明:在氧-乙炔环境中,2D C/SiC-ZrB2的线烧蚀率和质量烧蚀率分别为6.1×10-2 mm/s和1.0×10 -2g/s,相对2D C/SiC复合材料而言,ZrB2微粉并没有提高C/SiC复合材料的抗烧蚀性能.在1800℃甲烷风洞环境中,涂层致密度起主要作用,涂层致密度相同时,复合材料的开气孔率越大,质量烧蚀率越大,ZrB2微粉的渗入对C/SiC复合材料的烧蚀性能影响不大.     

C/ C-Cu 复合材料的烧蚀性能

以聚丙烯腈预氧化纤维针刺毡为预制体,经碳化后采用CVI和树脂浸渍(IR)工艺制备出不同密度的多孔C/C预制件,然后采用气体压力浸渗方法制备了C/C-Cu复合材料.采用氢氧(H2-O2)焰对C/C-Cu的烧蚀性能进行测试考核.结果表明:以密度为0.99 g/cm3的C/C预制件制备出的C/C-Cu复合材料的线烧蚀率和质量烧蚀率均小于密度为1.9 g/cm3的C/C复合材料,其烧蚀性能良好;在烧蚀过程中C/C-Cu的铜基体的熔化吸收了大量的热量,降低了材料的表面温度,提高了材料的抗烧蚀性能;烧蚀机制主要是热氧化烧蚀和机械冲刷的综合作用.     

先驱体转化2DCf/SiC-Cu复合材料热处理工艺

针对固体火箭发动机喉衬的使用工况,在Cf/SiC中引入Cu,通过Cu发汗降低材料表面温度,提高其烧蚀性能.采用先驱体转化法制备了2D Cf/SiC-Cu,考察了裂解温度为1 000、1 100、1 200、1 350℃时,对材料力学、烧蚀性能及微观结构的影响.结果表明,随着裂解温度的提高,试样的弯曲强度和断裂韧度均逐渐下降,分别为:280.0、225.7、193.2、163.0 MPa和18.0、13.6、13.4、13.2 MPa·m1/2.经氧乙炔焰烧蚀30 s后试样的弯曲强度随着裂解温度的提高基本不变,分别为121.2、115.5、124.2和117.5 MPa,其中1 200℃裂解制得的试样具有较低的线烧蚀率(0.025 5mm/s)和质量烧蚀率(0.028 g/s).烧蚀后试样中的Cu大量流失,基体中有少量铜硅化合物(Cu3Si,Cu5Si)出现.     

ZrB2 改性C/ C-SiC 复合材料性能研究

采用碳纤维复合网胎针刺预制体,通过溶液浸渍工艺制备了碳纤维增强C/C-SiC和C/C-SiC-ZrB2陶瓷基复合材料,并对材料的力学、热物理和烧蚀性能进行了分析对比。结果表明:针刺C/C-SiC-ZrB2复合材料的面内弯曲强度、厚度方向的压缩强度、层间剪切强度分别为199、274和19.3 MPa,各性能均低于对应的针刺C/C-SiC复合材料。针刺C/C-SiC-ZrB2材料与针刺C/C-SiC材料相比,热导率得到大幅度提高,而线胀系数略微有所降低。2 500 K、600 s风洞试验后,针刺C/C-SiC-ZrB2复合材料表现出良好的抗氧化烧蚀性能,质量烧蚀率约0.4×10-4g/s。     

Cf / ZrB2 -SiC 复合材料的制备及抗热冲击性能

采用前驱体转化法制备Cf / ZrB2 -SiC 复合材料,对材料的热物理和热震性能进行了研究。采用 扫描电镜和X 射线衍射分析材料的微观结构及物相变化。结果表明:复合材料在1 700℃热震循环10 次材料 保持完整,表现出了良好的抗热震性能。通过微观结构分析,高温氧化后生成的多孔SiO2 氧化层能够吸收热 应力,缓解因热震带来的巨大温度差,ZrB2 组元的加入有效地提高了材料抗热震性。     

C/C-Cu复合材料的烧蚀形貌和烧蚀机理

以PAN预氧化纤维整体毡为增强体,经碳化、等温CVI致密化后制备多孔的C/C复合材料预制体,利用气体压力浸渗法将Cu引入C/C预制体中制备C/C-Cu复合材料。采用氢氧(H2-O2)焰考核C/C-Cu复合材料的烧蚀性能,经扫描电镜和电子能谱对不同烧蚀区域的微观结构和成分进行分析,结果表明:预制体密度为0.96 g/cm3的C/C-Cu复合材料的线烧蚀率和质量烧蚀率分别为4.75μm/s、0.223 mg/s,烧蚀性能优良;其烧蚀表面具有不同的宏观形貌,在烧蚀中心区产生了明显的凹坑,主要烧蚀机制为C/C预制体的氧化和铜基体的机械冲刷;烧蚀过渡区聚集了大量的铜基体,其烧蚀机制为Cu的热氧化和机械冲刷;烧蚀边缘区材料表面变黑,主要因为C/C的氧化。为了提高C/C-Cu的烧蚀性能,需要发挥C/C预制体的"钉扎"作用,阻止Cu在高温下被气流冲刷而发生流动。     

酚醛树脂基泡沫碳材料的烧蚀与隔热性能

为考察纳米孔径的酚醛树脂基泡沫碳材料的烧蚀与隔热性能,以酚醛树脂为碳源,环戊烷为发泡剂,吐温80为表面活性剂,对甲苯磺酸为固化剂,采用发泡固化碳化工艺制备了低密度泡沫碳材料。所制备的泡沫碳材料密度为0. 3 g/cm^3,压缩强度达到了11. 7 MPa。采用LFA457激光导热仪考察了泡沫碳材料在不同温度下(25、200、400、600℃)的导热性能,25℃下热导率为0. 141 W/(m·K),600℃下热导率为0. 344 W/(m·K);通过氧乙炔试验(30 s/60 s)对泡沫碳材料与C/C复合材料在同样的气流条件下隔热性能进行了比较,在材料正面烧蚀峰值温度泡沫碳材料比C/C复合材料高出约400℃的情况下,背面峰值温度比C/C复合材料仍低出150℃;通过氧乙炔试验考察泡沫碳材料的抗烧蚀性能,氧乙炔烧蚀60 s的线烧蚀率为0. 031 mm/s。试验结果证明低密度的泡沫碳材料同时具备优异的隔热与高温抗烧蚀性能。     

轴棒法编织C/C复合材料的超声速火焰烧蚀性能

为了研究轴棒法编织、高压浸渍-碳化致密工艺(HPIC)及高温处理工艺制成的高密度的碳/碳(C/C)复合材料在火箭发动机中的烧蚀性能,使用气氧和煤油超声速(HVO)火焰对复合材料进行含铝工况烧蚀/侵蚀实验,烧蚀时间为30s;对比研究了复合材料在有、无含铝粒子侵蚀时烧蚀性能的差别;分别用扫描电镜、微CT和表面能谱分析了不同工况烧蚀表面的形貌和成分。结果表明,在不同的烧蚀工况下,材料的表面粗糙度不同,微观形貌和烧蚀率也有很大差异;复合材料在无粒子侵蚀工况下的线烧蚀率和质量烧蚀率的平均值分别是0.0318mm/s和0.0319g/s,烧蚀表面呈竹笋状和毛絮状,热化学烧蚀起主导作用;有粒子侵蚀时的线烧蚀率和质量烧蚀率的平均值分别是0.0516mm/s和0.0353g/s,烧蚀表面呈钝竹笋状,纤维从根部断裂,热化学烧蚀和机械剥蚀同时起作用;在纤维和基体表面有Al2O3粒子沉积;含铝烧蚀/侵蚀的线烧蚀率是不含铝烧蚀的1.6倍,质量烧蚀率的1.1倍。在烧蚀区的内部,基体碳受热后开裂,而碳纤维与基体碳间的界面相受热后无明显变化。     

ZrB2/C复合材料抗烧蚀性能及微观结构的研究

采用热压法制备ZrB2／C复合材料，利用氧乙炔火焰烧蚀法测试材料的质量烧蚀率和线烧蚀率，采用扫描电镜和X射线衍射分析材料的微观结构及物相变化。研究结果表明：和相同工艺制备的纯石墨材料相比，ZrB2的引入降低了炭材料的质量和线烧蚀率，ZrB2的加入量越大，烧蚀率降低幅度越大，ZrB2引入明显提高了炭材料的抗烧蚀性能；通过微观结构分析，探讨了ZrB2形态和含量对复合材料抗烧蚀性能影响的机理，研究结果展示了此材料作为高温烧蚀材料的良好应用前景。     

Microstructure,thermophysical property and ablation behavior of high thermal conductivity carbon/carbon composites after heat-treatment

Uni-directional carbon/carbon composites with high thermal conductivity are suitable to supply continuous thermal protection for future reentry vehicles since they could reduce surface temperature and ablation rates simultaneously in harsh environments. In this work, the high thermal conductivity carbon/carbon composites were prepared by chemical vapor infiltration. After heat-treatment, both their open porosity and internal friction increase due to the fiber/matrix thermal expansion mismatch; while their thermal conductive performance become better due to more complete carbon structure. With raising heat-treatment temperature from 1800 °C to 2450 °C, the mass and linear ablation rates of C/C composites with fibers vertical to the oxyacetylene torch for 60 s decrease from 0.66 mg/s and 2.95 μm/s to 0.51 mg/s and 2.05 μm/s respectively. The improved ablation resistance is resulted from the increased thermal conductivity from 282 to 508 W/(m·K) and more carbon fibers exposed to the flame during ablation, which have better oxidation resistance than those of carbon matrix. While such ablation rates become larger for composites with fibers parallel to the flame, from 1.02 mg/s and 3.73 μm/s to 1.28 mg/s and 5.01 μm/s respectively since the ablation occurred more easily through gaps at the fiber/matrix interfaces, which become larger and are always exposed to the flame for this case.     

高超声速飞行器TPS破损修复涂料

分别采用环氧树脂和呋喃树脂作为基体混合碳化硅粉末与晶须制备了耐高温修复涂料.以氧-乙炔烧蚀试验测试涂料的耐高温烧蚀性能,用扫描电子显微镜分析烧蚀后涂料表面的微观形貌,用X射线衍射、表面能谱分析对涂料烧蚀后成分进行分析表征.结果表明:碳化硅粉末与晶须的质量分数比为8/4的呋喃树脂/碳化硅体系涂料具有良好的耐高温烧蚀性能,...     

PIP法制备C/ZrC-SiC复合材料工艺与性能研究

为了提高超高温陶瓷基复合材料的力学性能和耐烧蚀性能,本文采用前驱体浸渍裂解(PIP)工艺制备了C/ZrC-SiC复合材料,研究了锆硅一体化陶瓷前驱体(ZS)的固化-裂解工艺对C/ZrC-SiC复合材料性能的影响。结果表明:前驱体的裂解温度对复合材料的力学性能影响较大。较高的裂解温度会损坏碳纤维,导致力学性能降低;较低的裂解温度会使碳热还原反应不充分,基体氧含量较高,结构疏松,导致力学性能下降;制备的C/ZrC-SiC复合材料通过了2 850 K的电弧风洞试验考核后线烧蚀率为8.75×10~(-4)mm/s,呈现出优异的耐烧蚀性能。     

硅橡胶/双酚A-苯胺型苯并噁嗪树脂耐烧蚀复合材料的制备与烧蚀结构的研究

苯并噁嗪树脂具有优异的成炭和抗高温氧化性能,是新一代的耐烧蚀树脂。以双酚A-苯胺型苯并噁嗪树脂为耐烧蚀树脂,采用1H-NMR、DSC和转矩流变仪研究其成环率和加工性能;以硅橡胶为耐烧蚀基体,采用熔融共混方法制备了硅橡胶苯并噁嗪树脂耐烧蚀复合材料。进行力学和氧乙炔焰烧蚀检测,利用FT-IR、Raman和SEM研究复合材料综合性能和烧蚀结构。结果表明:苯并噁嗪树脂能够明显提高硅橡胶复合材料的耐烧蚀性能,当树脂添加量为20份时,复合材料具有较好的耐烧蚀和力学性能;该复合材料经过氧乙炔焰烧蚀后,烧蚀层形成表面陶瓷层、裂解炭化层和基体层。表面陶瓷层主要由SiO_2,SiC和C组成,裂解炭化层的主要组由C,SiO_2,SiC以及炭化彻底的碳和炭化不完全的有机结构组成。     

C/SiC材料主动氧化烧蚀计算研究

建立了C/SiC材料的热化学平衡烧蚀模型,进行了C/SiC材料烧蚀机理的计算研究和试验验证,理论计算结果和试验数据符合良好。计算结果表明,在高温空气环境下,C/SiC材料的无因次质量烧蚀率B与材料中C元素、Si元素的质量分数及温度、压力有关。在同样条件下,C/SiC材料主动氧化烧蚀速率大于C/C复合材料烧蚀速率。     

基于热解过程的EPDM变热物性数值传热

针对三元乙丙橡胶(EPDM)类绝热材料热载荷作用下的热解炭化过程,基于热解动力学和多孔介质传质传热理论,建立了芳纶/EPDM绝热材料热物性参数随温度和时间变化的变热物性模型,并通过与实验的对比,验证了模型的准确性与可靠性。随后对热载荷作用下的烧蚀热响应开展了数值计算,结果表明:热载荷作用初期,材料表面升温迅速,随着能量不断传递,温度推进速率明显降低,炭化层厚度增长减慢,部分材料仍为原始状态；温度对热解反应速率的影响呈指数级,距表面越近反应速率越快,反之则慢。所提出的变热物性模型对绝热材料的烧蚀研究具有一定的参考价值。      

Microstructure, Mechanical Properties and Oxidation Resistance of Nb-22Ti-14Si-2Hf-2Al-xCr Alloys

Nb-22Ti-14Si-2Hf-2Al-xCr (x=2, 6, 10, 14, 17 at%) alloys are prepared by arc-melting under argon atmosphere. Microstructural characteristics, mechanical properties and oxidation resistance of the arc-melted alloys are investigated. At 2 at% Cr content, the microstructure is composed of Nbss, Nb3Si and a small quantity of Nb5Si3, when the Cr contents increase, Nb3Si disappears. For the high Cr content (x ≥ 10 at%) alloys, besides the Nbss and Nb5Si3, Cr2Nb is also detected. With the increase of Cr content, the volume fractions of Cr2Nb and Nb5Si3 increase, while that of Nbss increases firstly and then begins to degrade when the Cr content is higher than 6 at%. For the alloy with 2 at% Cr, the room temperature fracture toughness is about 14.5 MPa·m1/2, but badly decreases to about 8.5 MPa·m1/2, when the Cr contents increase. Vickers hardness of Nbss tends to increase linearly from about 400 to 500, while that of silicides is not sensitive to Cr contents, about 950. The appearance of Cr2Nb phase significantly improves the high temperature oxidation resistance of the alloys with high Cr contents. The isothermal oxidation tests show that the oxidation kinetics of the alloys with various Cr contents follows parabolic oxidation kinetics.