连续碳纤维增强聚醚醚酮预浸带成型工艺及性能

利用浸渍法制备连续碳纤维增强聚醚醚酮(CF/PEEK)预浸带,对其成型温度、行进线速度进行研究,并测试了CF/PEEK预浸带的热胀系数、拉伸性能,利用SEM扫描电镜观察CF/PEEK预浸带内部界面结合状态。结果显示,预热区、熔融热压区温度分别控制在110~130℃和220~370℃,预浸带行进线速度控制在2 m/min时,制备的预浸带性能较好;在-150~+150℃范围内,CF/PEEK预浸带线胀系数为0.5×10-6/K,并随着纤维体积分数增大而减小;CF/PEEK预浸带最大拉伸强度达到1.81 GPa;SEM扫描电镜显示碳纤维与PEEK界面结合良好。研究显示,CF/PEEK预浸带制备工艺参数可行,CF/PEEK预浸带性能较好,具有工程应用价值。     

T700/PEEK热塑性自动铺放预浸纱制备质量控制及性能研究

为满足高性能热塑性复合材料自动铺丝（AFP）成型工艺的原材料需求,研究了粉末悬浮法浸渍制备T700/PEEK预浸纱关键工艺参数及预浸料性能,分析聚醚醚酮PEEK浸渍连续碳纤维过程中不同工艺参数（悬浊液浓度、超声功率、张力、牵引速率、浸渍温度、辊压温度及压辊间隙）对预浸纱质量的影响规律,利用扫描电子显微镜（SEM）观察T700/PEEK预浸纱内部孔隙率及界面结合状态,将粉末悬浮法制备的T700/PEEK预浸纱模压制备了热塑性复合材料单向层合板试样,并测试了其热塑性复合材料层间剪切强度和拉伸强度。研究结果表明：预浸纱含胶量与粉末悬浮液浓度变化线性正相关,且随超声功率的增大而升高;浸渍过程中伴随温度的升高以及牵引速率的减小,预浸纱宽度变小、孔隙率降低,随着张力的增大,预浸纱宽度增大、孔隙率降低;辊压成型过程中随着温度的提高以及压辊间隙的减小,预浸纱宽度增大、孔隙率降低。综合考虑各工艺参数的影响规律,获得优化的热塑性预浸纱制备工艺参数：浸渍温度为360~370℃,辊压温度为330℃,压辊间隙为0.1 mm,牵引速率为15~20 mm/s,张力为7 N。扫描电镜结果显示树脂与纤维界面结合紧密,复合材料的孔隙率可降低至1.8%,复合材料层间剪切强度为73.43 MPa,纵向拉伸强度达1.71 GPa。     

碳纤维/聚苯硫醚复合材料复合工艺及力学性能的研究

 对连续碳纤维增强聚苯硫醚复合材料进行了复合工艺及力学性能的研究。研制出了制备碳纤维/聚苯硫醚复合材料预浸带的悬浮-熔融法、并优化了模压工艺条件;测定了力学性能,观察了断口形貌。结果表明:聚苯硫醚树脂与碳纤维之间有很好的粘接性、纤维得到了充分的浸润。     

制备预浸料的JFY—1静电粉末预浸机及其制备工艺

本文介绍了一种静电粉末预浸机及其制备工艺。这是一种将增强体通过树脂粉末带电的流化床，使树脂粉末沉积在纤维上而制备预浸料的新方法，该设备装有β射线仪，用微机闭环控制预浸料树脂含量，制备的碳纤维帘子布／ＰＥＥＫ预浸料控制精度可达±３％最大工作宽度３００ｍｍ。     

一种混合织物增强复合材料的性能

使用碳纤维平纹布、玻璃纤维平纹布/环氧树脂预浸料制备了一种混合织物增强复合材料,并对其拉伸、弯曲、层间剪切性能以及导电性能进行了测试表征。结果表明,在-50~200℃,制备的混合织物增强复合材料的拉伸、弯曲强度相对纯玻璃纤维布增强复合材料下降,拉伸、弯曲模量均提高,两种复合材料的层剪强度保持不变;此外,碳纤维布预浸料的加入,降低了复合材料的密度,增加了导电性能,拓宽了玻璃布增强复合材料的应用范围。     

适用自动铺丝工艺的中模高强碳纤维预浸料研究

目前,自动铺丝技术是航天航空大型结构件制备工艺的发展方向,而中模高强碳纤维预浸料适用于航天航空主承力结构件的制备,达到减重的需求,因此,自动铺丝工艺用中模高强碳纤维预浸料的研究至关重要。采用HF40A中模高强碳纤维匹配EH918树脂体系,开展了预浸料的自动铺丝工艺适用性研究。通过与满足自动铺丝工艺的某预浸料对比分析,确定了满足自动铺丝工艺要求的EH918/HF40A;对比手工铺放与自动铺丝制备的板材的力学性能,数据表明,自动铺丝板材的力学性能与手工铺放板材性能相当,无明显差异;采用该材料和自动铺丝工艺制备了典型部件,并进行了无损测试,其质量满足指标要求。     

真空成型与热压罐成型复合材料的性能对比

针对一种碳纤维单向预浸料ZT7G/LT-03A及碳纤维平纹织物预浸料ZT7G3198P/LT-03A,采用热压罐成型工艺和真空成型工艺各制备了3批次复合材料,测试预浸料的物理性能以及复合材料层合板的力学性能,通过对两种制备工艺得到的复合材料力学性能、纤维体积含量及孔隙率的对比分析发现,该体系真空成型复合材料性能的保持率均在75%以上,有的甚至超过100%。对于碳纤维单向预浸料来说,层间剪切的保持率最低,0°拉伸强度的保持率最高;对于织物复合材料来说,0°压缩强度的保持率最低,0°拉伸的保持率最高。同时真空成型复合材料纤维体积含量较低,孔隙率较高,是影响其性能的主要原因。     

碳纤维复合材料面板—Nomex蜂窝夹层结构方向舵的研制

本文介绍某型飞机碳纤维复合材料面板－Ｎｏｍｅｘ蜂窝夹层结构方向舵的制造工艺，包括方向舵的结构特点及制造要求、成形模具结构的选择、预浸料的制备、预固化和二次胶接共固化工艺参数的确定等。     

民机内饰用阻燃环氧树脂及复合材料性能研究

合成一种无卤阻燃环氧树脂，并采用热熔法预浸工艺制备出玻璃纤维织物增强环氧树脂预浸料。通过DSC、流变仪等手段对树脂性能进行表征分析。将树脂与玻璃纤维织物进行复合制备预浸料并通过热压罐成型工艺制备复合材料，对复合材料的力学性能和阻燃性能进行表征分析。结果表明：该无卤阻燃环氧树脂及预浸料具有良好的工艺加工性，用其制备的复合材料试验件具有良好的力学性能和阻燃性能，垂直燃烧/水平燃烧、热释放速率、烟密度、烟毒性各项性能均可满足CCAR等适航标准的要求。     

热熔法制备连续纤维增强热塑性预浸料的浸渍模型和研究进展

力学性能优异、使用温度区间广、可二次加工等独特性能使得连续纤维增强热塑性预浸料得到长足发展。热熔法是一种精确高效的热塑性预浸料成型方法,而如何实现PPS、PEEK等高黏度树脂熔体对连续纤维束的均匀、充分浸渍是亟待解决的工程难题。首先,基于Darcy定律提出了4个浸渍理论模型,充分考虑了工艺温度、压力、加工阶段及纤维束形状对浸渍程度的影响,为连续纤维增强热塑性预浸料生产线的搭建和工艺参数的制定提供了理论指导。然后,对国内外连续纤维强热塑性预浸料的研究及产业化现状进行对比:国外相关产业发展成熟,预浸料种类繁多且在军机、民机等领域广泛应用,但对国内实行严厉的限购政策;国内,高性能连续纤维增强热塑性预浸料具有广阔的应用空间和急切的需求,介绍了北航热塑团队自主研发的热熔法制备连续纤维增强高性能热塑性预浸料的中试生产线,其从一定程度上缓解了国内的需求。     

Effects of FDM-3D printing parameters on mechanical properties and microstructure of CF/PEEK and GF/PEEK

Fused deposition modeling (FDM) has unique advantages in the rapid prototyping of thermoplastics which have been developed in diverse fields. However, although great efforts have been made to optimize FDM process, the mechanical properties of printed parts are limited by the weak interlamination bonding as well as the poor performance of raw filaments used, such as acrylonitrile butadiene styrene (ABS), polylactic acid (PLA). Adding fibers into thermoplastic matrix and preparing high-performance filaments have been indicated to enhance the properties of fabricated parts. Recently, heat-resistant polyetheretherketone (PEEK) and its fiber reinforced composites were proposed for FDM process due to overcoming the limitation of equipment and process. However, few researches have been reported on the effects of FDM-3D printing parameters on the mechanical properties of fiber reinforced PEEK composites. Therefore, 5wt% carbon fiber (CF) and glass fiber (GF) reinforced PEEK composite filaments were prepared respectively in this study. The effects of various printing parameters including nozzle temperature, platform temperature, printing speed and layer thickness on the mechanical properties (including tensile strength, flexural strength and impact strength) were surveyed. To analyze the microstructure and failure reasons of printed CF/PEEK and GF/PEEK samples, the tensile fractured surfaces were investigated via scanning electron microscope (SEM).     

短切玻璃纤维增强聚醚醚酮承力支架研制

为加工某航天器高性能承力支架零件,本文对不同玻璃纤维含量的短切玻璃纤维增强聚醚醚酮(SGF/PEEK)的力学性能进行了分析,利用Moldflow分析软件对承力支架注塑模具、注塑工艺参数进行了优化。结果表明,30wt%的SGF/PEEK作为承力支架材料时力学性能最优,模流分析有效预测注塑过程,改善主流道及二级流道尺寸可有效提升保压效果,保压压力和模具温度对承力支架翘曲变形的影响最为显著,得出一组优化的工艺参数,采用该参数成型的零件已成功应用于某航天器燃料贮箱中并通过了飞行考核。     

长玻纤增强注塑聚醚醚酮复合材料加工工艺与力学性能的研究

以含30％的长玻璃纤维增强聚醚醚酮为原材料,采用注塑成型的方法研究了聚醚醚酮复合材料的加工工艺参数包括冷却速率、成型压力、成型温度及模具温度与力学性能的关系,并对模具温度为180℃时PEEK复合材料的微观形貌进行分析,研究结果表明：采用中速冷却速率,成型压力为120MPa,成型温度为后段375℃、中段425℃、前段425℃,模具温度保持为180℃时,复合材料的抗拉强度达81MPa、剪切强度为62．7MPa,制品表面光滑,其综合力学性能最佳。     

几种碳纤维/双马树脂复合材料湿热特性实验研究

 针对碳纤维/双马树脂体系,研究了不同湿热条件、不同碳纤维种类和预浸料制备方法下复合材料层板的湿热特性,通过考察吸湿量、动态力学性能、弯曲性能及其断口形貌等方面分析了各因素对复合材料吸湿特性的影响规律。结果表明,在实验范围内不同湿热条件下水分主要引起复合材料发生了物理变化,而没有发生明显的化学变化;国产T300级碳纤维复合材料湿热性能偏低,这与其界面粘结性能较弱有一致性;与干法预浸料相比,湿法预浸料制备的复合材料层板湿热性能明显偏低,说明溶剂对双马树脂复合材料的界面性能和吸湿性有重要影响。     

柔性混编预浸料制造热塑性复合材料加筋结构

PEEK树脂基复合材料具有突出的韧性和高损伤容限,但因成型工艺条件较为苛刻,且铺覆性能差,影响了曲面成型能力.利用柔性混编预浸料技术则可解决这一难题,高质量、高效率地实现复杂曲面结构件的制备.分别带有"L"型加强筋和帽型材的加筋口盖的制造,对此进行了充分的验证.     

可自展开碳纤维增强复合材料杆的制备与性能

采用T300碳纤维/环氧树脂预浸料制备了具有双凸透镜状构型的柔性铰链和圆管,通过金属法兰将铰链和圆管胶接组装得到可自展开碳纤维增强复合材料杆。研究了复合材料铰链的展开力矩和复合材料杆的固有频率及重复展开性能。结果表明:复合材料铰链的初始展开力矩为372.8 N·mm,功重比为13.3 W/kg,可自展开复合材料杆的一阶固有频率为4.25 Hz,重复指向精度为0.08°。     

熔融沉积制造材料的空间应用实验

为了解决熔融沉积制造(FDM)技术的空间应用问题,开展了不同材料的地面成形工艺实验研究。选取了聚乳酸(PLA)、聚碳酸酯(PC)、聚醚醚酮(PEEK)三种纯树脂材料以及碳纤维增强的PLA材料为研究对象,利用自主研发的空间微重力原理样机成功打印了标准试样,并进行了力学性能、阻燃特性、燃烧后毒气浓度、质量损失、可凝挥发等数据的测试,对比分析了PLA、PC、PEEK材料FDM成形件和传统注塑件的性能差别及不同纤维方向的碳纤维PLA复合材料试样的拉伸性能。结果表明:材料间结合能力是影响FDM成形制件性能的主要因素,异种材料间结合强度是影响复合材料样件性能的主要因素,结合能力越强的材料其FDM成形的质量越高,结晶材料的成形质量同时还受结晶度的影响,结晶度越高,制件性能越好。     

Influence and optimization of parameters of prepreg viscosity during placement

This paper tested the viscosity of prepreg in the automatic placement process, and conducted the probe and placement-90° peel tests through the test systems. The law of variation of prepreg viscosity during the laying process was studied through these tests under different conditions by taking the peel force to intuitively and quantitatively characterise the viscosity of the prepreg.The results show that this viscosity is inversely proportional to the laying rate, proportional to the laying pres...