CF/PEEK超声原位固结铺放及其复合材料力学性能

热塑性复合材料自动铺放（ATP）原位固结成型是未来航空复合材料结构件的发展趋势,缩小其制件与热压制件性能的差距具有工程实践意义。基于超声原位固结成型工艺,制备碳纤维增强聚醚醚酮树脂基复合材料（CF/PEEK）层合板,并与铺放后热压和直接平板热压试样比较力学性能差异,为热塑性复合材料的自动铺放提供参考。结果表明,超声热源能够满足CF/PEEK铺放的能量要求,功率的增加和铺放速度的降低有利于铺层结合;与平板热压试样相比,铺放成型试样的孔隙率高,纤维存在部分损伤;在节省了平板热压后固化周期的情况下,超声铺放单向层合板试样拉伸强度、拉伸模量和层间剪切强度分别为1.32、113.8 GPa和39.2 MPa,达到了直接热压试样的80.4%、84.8%和65.1%,在经过热压后固化后,分别提高到直接热压的92.1%、92.6%和82.5%。超声原位固结成型试样的简支梁摆锤冲击失效形式为分层,其经过热压后,孔隙率下降,铺层结合强度提高,试样的冲击失效形式为断裂,与直接热压的相同。     

碳纳米管改性对碳/ 环氧复合材料层间性能的影响

研究了在碳纤维织物上生长碳纳米管的改性对环氧树脂基复合材料层间性能的影响,对比了有无碳纳米管的碳纤维复合材料的层间剪切和弯曲性能,并采用碳纤维表面结合碳纳米管膜的方法研究了碳纳米管对碳/环氧复合材料层间性能的影响。结果表明,由于生长的碳纳米管长度过长(10μm)、末端无序排列为笼状,树脂无法进入碳纳米管内部,碳纳米管无法发挥增强作用,同时由于碳纳米管过长,复合材料内部缺陷增多,使得四种生长碳纳米管的碳纤维复合材料层间性能均有下降;而碳纳米管膜与碳纤维和树脂基体结合较好,使得复合材料层间剪切强度提高12%。     

复合材料制件成形用模具材料研究

复合材料以其优良的性能而在航天、航空领域得到日趋广泛的应用。为满足复合材料成形工艺的特定要求，一些新型模具材料及其制模工艺相继出现。本文对复合材料制件成形模具的特点及国外使用的新型模具材料进行了综述，并对其中的可喷镀的低熔点合金－锌基合金的组分及其热膨胀性能作了初步探讨性研究，以期找出一种可喷镀的低熔点、低热膨胀合金用于复合材料制件成形用模具。     

碳纤维增强复合材料结构阻尼性能研究

碳纤维增强复合材料的阻尼性能对所应用结构的动态承载能力、可靠性和安全性有重要影响。复合材料阻尼机理复杂,很难采用理论方法研究。本文基于瞬态激励法原理,设计了悬臂梁振动试验,利用有理分式多项式法提取试样的模态频率和模态损耗因子。分别对603和603A两种树脂基体,各三种T300纤维铺层方向的复合材料试样进行了振动测试,获得了材料1 kHz以内的动刚度和阻尼特性。结果表明,基体材料组分和纤维铺层方向对碳纤维增强复合材料的结构刚度和阻尼性能有重要影响;603A基体的碳纤维增强复合材料具有较603基体材料更好的损耗因子。铺层方向对结构阻尼的影响主要是通过对结构刚度的影响而体现出来的,不同纤维铺层方向的复合材料试样刚度差别很大。     

轻型电动飞机用碳纤维预浸料力学性能研究

飞机结构强度设计的过程需要基于有关材料的力学性能数据。为了避免因材料偏差而引起的结构破坏,应尽可能的排除可避免的影响因素,以保证产品质量稳定性。本文以多批次、不同厂家生产的UNI23100/9314碳纤维预浸料作为研究对象,对采用热压罐工艺和真空袋工艺制备的碳纤维复合材料开展了性能验证及评价分析。对试样进行拉伸及压缩试验,测出其单层(0°)拉伸强度、压缩强度、拉伸模量、压缩模量,并统计得出数据的离散系数和标准差。通过试验结果的比对,总结得到试样的制件厂家、材料批次、试验厂家、数据处理厂家及操作误差等因素对产品力学性能造成的影响,对其未来的设计标准、生产规范等提供了依据。     

三维编织与层合复合材料力学性能对比试验

对比研究利用相同碳纤维、基体和相同制备工艺(RTM)加工的三维多向编织和层合板复合材料的力学性能。四种三维多向编织结构分别利用三维四向、三维五向、三维六向和三维七向编织工艺制备;三种层合复合材料利用帘子布制成,分别为0°单向板、90°单向板和层合板[0/(±45)2/90]2s。采用相同的拉伸、压缩和剪切试验方法对各类试样进行试验。结果表明:与三维编织试样相比,0°单向板的拉伸和压缩性能最高,而其他层合试样的各项性能均较低;对于编织试样,编织角越小,纵向拉伸和压缩性能越高,剪切性能越低;编织结构也是影响编织试样力学性能的重要因素。同时,对试样的破坏模式也进行了讨论,发现编织结构和编织角是影响材料破坏模式的重要因素。     

聚醚醚酮/多壁碳纳米管复合材料的凝聚态结构与交流电性能

利用同体合金化方法,制备了不同质量比的聚醚醚酮(PEEK)/多壁碳纳米管(MwNT)复合材料,通过场发射扫描电镜观察了凝聚态结构;对比研究了缓冷和速冷模压成型复合材料的熔融吸热峰和热焓的变化、交流电性能参数.结果表明:固体合金化方法能实现MWNT在PEEK基体中的短切与良好分散,有利于导电网络的形成:添加MWNT可促使低温晶相的形成;随MWNT含量的增加,PEEK/MWNT复合材料低温结晶相的熔融峰更加明显;速冷成型能降低复合材料的结晶度,增大晶粒尺寸分布,促进不同尺度晶粒晶界处形成不同长度MWNT的导电网络,有效降低材料的电阻和体系的逾渗阈值;PEEK/MWNT复合材料的交流电性能参数随频率和MWNT含量的变化而变化,但缓冷成型和速冷成型具有不同的临界频率和逾渗阈值.     

T700/PEEK热塑性自动铺放预浸纱制备质量控制及性能研究

为满足高性能热塑性复合材料自动铺丝（AFP）成型工艺的原材料需求,研究了粉末悬浮法浸渍制备T700/PEEK预浸纱关键工艺参数及预浸料性能,分析聚醚醚酮PEEK浸渍连续碳纤维过程中不同工艺参数（悬浊液浓度、超声功率、张力、牵引速率、浸渍温度、辊压温度及压辊间隙）对预浸纱质量的影响规律,利用扫描电子显微镜（SEM）观察T700/PEEK预浸纱内部孔隙率及界面结合状态,将粉末悬浮法制备的T700/PEEK预浸纱模压制备了热塑性复合材料单向层合板试样,并测试了其热塑性复合材料层间剪切强度和拉伸强度。研究结果表明：预浸纱含胶量与粉末悬浮液浓度变化线性正相关,且随超声功率的增大而升高;浸渍过程中伴随温度的升高以及牵引速率的减小,预浸纱宽度变小、孔隙率降低,随着张力的增大,预浸纱宽度增大、孔隙率降低;辊压成型过程中随着温度的提高以及压辊间隙的减小,预浸纱宽度增大、孔隙率降低。综合考虑各工艺参数的影响规律,获得优化的热塑性预浸纱制备工艺参数：浸渍温度为360~370℃,辊压温度为330℃,压辊间隙为0.1 mm,牵引速率为15~20 mm/s,张力为7 N。扫描电镜结果显示树脂与纤维界面结合紧密,复合材料的孔隙率可降低至1.8%,复合材料层间剪切强度为73.43 MPa,纵向拉伸强度达1.71 GPa。     

M40/4211 复合材料层合板铣削加工试验

通过分析碳纤维复合材料的性能特点及对切削加工性能的影响,提出了铣削刀具材料和几何结构形式的选用原则,介绍了几种适于碳纤维复合材料铣削的加工刀具。针对碳纤维复合材料中常用的M40/4211复合材料层合板进行加工缺陷试验和切削试验,总结出影响M40/4211复合材料层合板加工质量的因素及规律,得到每种刀具加工M40/4211复合材料层合板的最佳加工参数,较高的切削速度配合恰当的进给速度可以有效提高M40/4211复合材料层合板的加工质量和加工效率。     

微重力环境下碳纤维-铝合金复合材料的制造

本研究目的是在微重力环境下制造超低密度、高刚度的复合材料。制得的复合材料结构是通过涂覆在纤维上的铝合金,使高模、短碳纤维在接触处连接,而形成任意三维结构。此材料多孔,因此具有很低的密度。文中介绍了本研究的推动因素、模拟实验、组分材料的选择及国家空间研制局(NASDA)的火箭弹道飞行实验。基础实验表明,碳纤维和铝合金之间的结合良好,因此,要获得具有理想性能的复合材料,看来是可能的。     

Effects of FDM-3D printing parameters on mechanical properties and microstructure of CF/PEEK and GF/PEEK

Fused deposition modeling (FDM) has unique advantages in the rapid prototyping of thermoplastics which have been developed in diverse fields. However, although great efforts have been made to optimize FDM process, the mechanical properties of printed parts are limited by the weak interlamination bonding as well as the poor performance of raw filaments used, such as acrylonitrile butadiene styrene (ABS), polylactic acid (PLA). Adding fibers into thermoplastic matrix and preparing high-performance filaments have been indicated to enhance the properties of fabricated parts. Recently, heat-resistant polyetheretherketone (PEEK) and its fiber reinforced composites were proposed for FDM process due to overcoming the limitation of equipment and process. However, few researches have been reported on the effects of FDM-3D printing parameters on the mechanical properties of fiber reinforced PEEK composites. Therefore, 5wt% carbon fiber (CF) and glass fiber (GF) reinforced PEEK composite filaments were prepared respectively in this study. The effects of various printing parameters including nozzle temperature, platform temperature, printing speed and layer thickness on the mechanical properties (including tensile strength, flexural strength and impact strength) were surveyed. To analyze the microstructure and failure reasons of printed CF/PEEK and GF/PEEK samples, the tensile fractured surfaces were investigated via scanning electron microscope (SEM).     

Φ10 mm 碳纤维复合材料管成型工艺及性能研究

对外径为Φ10 mm碳纤维复合材料管成型工艺及性能进行了研究。结果表明,采用热缩工艺成型的碳纤维复合材料管工艺简单、质量可靠,Φ10 mm碳纤维复合材料管件弯曲刚度与不锈钢管相当,弯曲强度为不锈钢的3倍以上,质量仅为不锈钢的50%,尺寸精度满足设计要求。     

碳纳米管-碳纤维多尺度增强体研究进展

连续碳纤维增强树脂基复合材料在航空航天领域是一种关键的结构材料,将性能优异的纳米材料引入复合材料中将有可能提高材料的机械性能.文章介绍了化学气相沉积、化学接枝、电泳沉积等技术在制备碳纳米管-碳纤维多尺度增强体方面的研究进展,并阐述了碳纳米管的引入对复合材料界面性能的影响,提出电泳沉积作为一种经济、有效的技术而具有规模化生产的工业潜力.     

碳纤维增强树脂基摩擦材料摩擦磨损性能

为提高树脂基摩擦材料摩擦因数稳定性,改善其抗热衰退性能。以碳纤维作为增强纤维,采用热压成型工艺制备碳纤维增强树脂基摩擦材料;用XD-MSM型定速摩擦试验机测定摩擦磨损性能,研究了不同含量碳纤维增强对树脂基摩擦材料摩擦磨损性能的影响;利用VK-X200三维激光扫描显微镜观察了摩擦材料磨损后表面的微观形貌并探讨其磨损机理。结果表明,碳纤维增强树脂基摩擦材料的硬度、压缩强度和剪切强度均得到提高,并随碳纤维含量的增加而逐渐增大;碳纤维增强作用提高了树脂基摩擦材料的耐磨性和摩擦因数的稳定性,改变了树脂基摩擦材料的摩擦磨损形式;碳纤维含量为4wt%的增强树脂基摩擦材料摩擦因数稳定性较高,抗热衰退性能较好,磨损机制主要为疲劳磨损。     

CF3052/5284RTM 复合材料湿热性能

通过对CF3052/5284RTM复合材料进行试验研究,测定其在不同湿热条件下的基本力学性能,分析湿热条件对基本力学性能的影响。结果表明:湿热环境对该复合材料力学性能的影响程度不一,其中湿度的作用较温度更加明显;该复合材料在高温湿态条件下保持了较高的拉伸和纵横剪切强度,具有综合力学性能好、耐湿热性能好等优点。     

三维碳/碳化硅复合材料的显微结构与力学性能

 利用三维碳纤维预制体，采用等温CVI法制备连续碳纤维增韧碳化硅陶瓷基复合材料。无热解碳界面层的复合材料，其力学性能随密度的增加而提高，但密度较高时却表现出脆性断裂特征。热解碳界面层的存在，有利于纤维的拔出，但由于其结晶程度较低，仍然存在纤维束内部的脆性断裂。     

石墨纤维/改性氰酸酯复合材料的应用研究

采用环氧树脂对4,4-二氰酸酯基二苯基丙烷(BADCy)进行共聚改性,通过DSC分析,确定了固化工艺参数,并与石墨纤维(UHMCF)复合制成单向板,测试了不同后处理温度制得的单向板力学性能,并与现用UHMCF/树脂基复合材料单向板的力学性能进行了比较,测试了UHMCF/改性氰酸酯的空间环境性能;制备了UHMCF/改性氰酸酯结构件,测试其性能,并与现用UHMCF/树脂基复合材料同类结构件的性能进行了比较。结果表明:UHMCF/改性氰酸酯不论是单向板还是结构件的性能均优于现用UHMCF/树脂基复合材料的性能,且满足空间环境对航天器结构材料性能的要求。     

纤维增强基于α-BPDA 聚酰亚胺复合材料性能

为了考察基于α-BPDA聚酰亚胺复合材料的高温性能,制备了纤维增强复合材料,进行了高温力学和热物理性能的测试。研究结果表明纤维增强复合材料的T5d分解温度为565℃;Tg超过471℃;在450℃下的弯曲强度保持率大于42%,弯曲模量保持率大于55%,短梁剪切强度保持率超过44%;400℃空气热老化50 h后碳纤维复合材料的弯曲强度保持率66%,弯曲模量保持率为95%;300、500℃的石英增强复合材料的热导率分别为0.503和0.657 W/(m.K)。     

碳纤维增强复合材料与高强度金属的接触腐蚀

碳纤维/环氧树脂复合材料(CFRM)与高强度钛合金、铝合金、1Cr18Ni9Ti不锈钢等结构材料连接时,在界面形成了电偶腐蚀和缝隙腐蚀,这首先决定于材料本身的电化学性能;同时,也与相互的配偶情况、处理工艺和环境条件有关。电偶腐蚀受配偶材料各自的静态自腐电位(E_(corr))和电偶电位、电偶电流等闭路动态性能的影响。在3.5％NaCl溶液中,材料电化学特性和处理工艺对电偶腐蚀及缝隙腐蚀影响的趋势相同。用浸泡失重法、盐雾试验法及缝隙腐蚀法检验CFRM与阳极化钛合金,以及热水封和铬酸盐封闭的铝合金偶接时,稳定性较好,可满足工程应用的需要。