激光冲击对TC11钛合金组织和力学性能的影响

对TC11钛合金进行激光冲击强化处理,通过透射电子显微镜观察不同参数下TC11钛合金的微观组织变化,用显微硬度计和X射线应力测试仪分别测试材料表层硬度和残余应力,并通过TC11钛合金标准疲劳试片高周振动疲劳试验验证激光冲击对其疲劳性能的影响.试验结果表明:激光冲击波作用后表面组织结构发生明显变化,当冲击次数增加,先后出现了高密度位错、位错胞和纳米级晶粒等微观组织特征.冲击10次后,表面残余应力最高达到-632.5MPa,相应的塑性变形层深度达到1500μm左右;同时表面硬度在冲击1次即可提高19%,硬度影响深度为700μm,随着次数增加而提高,但幅度不大.经3次冲击处理的TC11钛合金标准疲劳试片的疲劳极限由原始483MPa提高到593MPa.      

激光喷丸强化TC6钛合金的振动疲劳寿命及断口形貌分析

为了研究TC6钛合金激光喷丸强化(Laser Shocking Peening,LSP)处理后对振动疲劳寿命的影响,采用不同喷丸次数的方法对TC6钛合金进行LSP处理,采用振动疲劳测试系统对振动试样进行振动疲劳测试,用X射线衍射仪和显微硬度计测试LSP前后试样的残余应力和硬度,研究LSP对TC6钛合金振动疲劳性能的影响...     

激光冲击强化对钛合金高温微动疲劳寿命的影响

为了解高温工作环境下激光冲击强化工艺(LSP)对钛合金材料微动疲劳寿命的影响,开展了强化前后TC11钛合金在室温、300°C和500°C下的微动疲劳试验并测试了试验件表层的残余应力及硬度。结果表明:随着温度的升高,激光冲击强化对TC11钛合金微动疲劳寿命的提高倍数逐渐减小。在轴向载荷为400MPa,法向载荷为65.5MPa时,经激光冲击强化后TC11钛合金试验件在室温、300°C和500°C下的微动疲劳寿命分别为强化前的5.5倍、3.5倍和1.7倍;强化后试验件表层的残余应力会在高温下发生松弛,且松弛程度会随温度的升高而增大,这是激光冲击强化效果随温度升高而逐渐弱化的主要原因。     

Laser Shock Peening of Aluminum Alloy 7050 for Fatigue Life Improvement

The effects of laser shock peening (LSP) on improving fatigue life of aluminum alloy 7050 are investigated.Surface hardness is increased corresponding to a high dislocation density induced by LSP.The X-ray diffraction stress measurement shows that LSP results in prominent increase of surface compressive stress,quasi-symmetrically distributed in the laser peened region.The fatigue life of the alloy 7050 in rivet fastener hole structure is notably improved owing to LSP.The sequence of LSP and fastener hole preparation also influence the fatigue cycle life of the alloy.     

超声喷丸与传统喷丸对TC4 钛合金残余应力影响的仿真分析

为了预测喷丸TC4钛合金试件的残余压应力层深度及值的分布和冲击面凹坑的直径、深度特征曲线及表面形貌的变化,采用ABAQUS/Explicit软件建立2个3D模型。通过超声喷丸与传统喷丸2种工艺过程数值仿真对比了表面残余应力场差异,分析了TC4钛合金弹丸直径、速度和冲击次数等喷丸参数对残余应力分布的影响。结果表明:当动能相同时,2种强化过程表面所产生的残余压应力是可比较的,超声喷丸模型亚表层残余应力深度为0.16 mm,约为传统喷丸模型深度的2倍;传统喷丸产生的残余压应力最大值约-800 MPa,约为超声喷丸的1.6倍。与传统喷丸相比,超声喷丸具有较低的表面粗糙度以及较深的残余压应力层。残余压应力层深度与弹丸直径呈正相关,但过大的弹丸尺寸会引起薄壁件另一侧残余拉应力区域的增大。     

TC4钛合金激光冲击强化数值模拟

采用连续显式动态冲击策略对航空用TC4钛合金进行激光冲击强化数值模拟研究。根据冲击波能量变化曲线确定单次冲击求解时间为3 000 ns,并分析了应力波传播过程。在此基础上开展多点冲击模拟,分析了功率密度、冲击次数和光斑搭接率对残余应力、应变场的影响。得出增加功率密度对增大表面残余压应力的效果更好;增加冲击次数对增大残余压应力影响深度的效果更好;50%光斑搭接率有效地避免了冲击不均匀和搭接空隙现象。实验和仿真所得的试件表面残余压应力变化趋势相同,数值大小基本吻合。冲击1、3次时,两者的误差分别为4.1%、2.6%,说明仿真结果具有一定的参考意义。      

激光冲击强化对加力燃烧室火焰探测器焊缝的影响

为了研究激光冲击强化(LSP)后加力燃烧室火焰探测器焊缝位置异常开裂原因,采用X射线衍射方法和金相方法对激光冲击强化效果进行分析,并利用扫描电子显微镜对断口进行了观察。在Abaqus有限元分析软件中建立了与观察到的焊缝缺陷相似的有限元模型,对焊缝缺陷的LSP处理及冲击波传播过程进行了模拟分析。试验结果表明:具有较好材料完整性的区域经LSP处理后,表面会预置较大残余压应力,同时表面金属晶粒得到细化,疲劳裂纹会在焊缝缺陷位置萌生和扩展。有限元分析结果表明:存在分层缺陷的焊缝经LSP强化后,冲击波会在分层缺陷处产生反射,造成分层位置发生开裂,形成裂纹源造成疲劳开裂。根据试验和仿真分析结果,为提升火焰探测器焊缝激光冲击抗疲劳效果,建议优化焊接工艺,提高焊接质量。     

激光冲击强化7075铝合金熔焊接头的疲劳性能

激光冲击强化（LSP）技术具有残余压应力场深、冷作硬化程度低和强化区域可控等优点,在焊接结构表面改性方面应用前景广阔。对2 mm厚度的7075-T6铝合金激光-电弧复合焊接接头实施了激光冲击强化处理,对比分析了强化前后接头的硬度、残余应力、疲劳寿命以及疲劳裂纹形核机制。结果表明,焊缝中心的最高硬度由强化前的152 HV提高到强化后的175 HV,有效强化层深度约为100 μm;经激光冲击强化后,焊缝区呈现残余压缩应力,最大残余压应力为-200 MPa;9组焊接接头试样的平均疲劳寿命为675 937周,约为强化前疲劳寿命（262 297周）的2.6倍;疲劳裂纹萌生位置从具有高度应力集中的表面缺陷转移至强化层以下的亚表面,进而有效地提高了疲劳裂纹的形核寿命。     

激光冲击强化提高压气机叶片疲劳性能研究

根据1Cr11Ni2W2MoV不锈钢材料性能,确定了激光冲击强化参数;并通过标准试片疲劳试验,验证了该参数条件下激光冲击强化提高不锈钢材料振动疲劳寿命的有效性.设计了不锈钢叶片振动疲劳试验,确定了叶片冲击强化部位和方式,对强化叶片进行了型面检查、一阶弯曲振动疲劳试验和强化机理研究.结果表明:激光冲击强化后的叶片各个截面尺寸在设计范围之内,强化后叶片的应力-循环次数(S-N)曲线往上移动,提高了叶片的疲劳强度,在660MPa应力水平下,叶片的振动中值疲劳寿命提高70%;激光冲击强化引起的残余应力和表层微观组织变化是疲劳强度提高的主要原因.      

Influence of laser shock peening on surface integrity and tensile property of high strength low alloy steel

Laser Shock Peening (LSP) is a well-established surface treatment commonly used to improve mechanical properties of material's surfaces. To further understand the relationship between tensile property and fatigue life improvement of high strength low alloy steel in the LSP process, LSP treatment of 32CrNi high strength low alloy steel was carried out by YAG laser with pulse energy of 15 J, and tensile property was tested by electronic universal material testing machine. Surface morphology, residual stress and tensile fracture of the specimens before and after LSP were observed by white light interferometer (WLI), X-ray measuring apparatus and scanning electron microscope (SEM). Result shows that LSP did not change tensile strength of 32CrNi steel but cause yield characteristic transform from obvious yield point to no yield phenomenon which is the only factor benefiting fatigue life, indicating that the increment of fatigue life was probably related to the disappearance of yield phenomenon. Formation mechanisms of tensile fractures and yield phenomenon induced by LSP at room temperature were also discussed and completely revealed. Deeper compressive residual stress and flat grains contributed to the transition of yield characteristic and lower elongation rate of 32CrNi steel subjected to LSP.     

激光冲击残余应力场的有限元分析

建立模拟激光冲击残余应力场的非线性弹塑性有限元模型,预测AISI 304奥氏体不锈钢厚、薄靶材经激光冲击后表面以及内部的残余应力场分布.模拟过程中,考虑材料高应变率(106s-1)下的力学性能和激光诱导冲击波的精确加载,分析激光功率密度、激光光斑尺寸、激光脉宽、激光冲击次数、激光单面与双面冲击等激光冲击参数以及初始残余应力等因素对不锈钢靶材残余应力分布的影响.数值模拟结果与X射线衍射法测量值吻合较好.在有初始残余拉应力(250MPa)存在的情况下,激光冲击仍能使304奥氏体不锈钢靶材形成残余压应力层,说明激光冲击工艺可提高奥氏体不锈钢焊接构件的抗应力腐蚀开裂能力.     

航空发动机风扇叶片两种表面处理方法对比

在对激光冲击强化技术与喷丸表面强化技术比较分析之后,表明航空发动机叶片经过激光冲击强化后,能显著增加叶片表面残余压应力,提高疲劳性能,并且其效果优于喷丸表面强化技术。     

激光冲击强化铝合金小孔构件的疲劳寿命研究

研究了激光冲击强化对7050-T7451铝合金小孔件疲劳寿命和断口形貌的影响。采用ABAQUS对峰值压力2.7GPa下小孔构件孔壁与表面上的应力分布进行了研究,并基于仿真结果对试样进行激光冲击强化试验和疲劳拉伸试验。结果显示,激光双面冲击强化在板料两侧形成一定深度的残余压应力影响层,而在中心形成一定范围的残余拉应力层,这也是导致疲劳源由孔角向孔壁中心转移的主要原因;在应力水平165.8MPa、195.0MPa和275.4MPa下,试样的疲劳寿命分别平均可增大451%、216%、116%;经激光冲击强化后,试样的疲劳源位置由孔角转移至孔壁内部,且疲劳裂纹扩展区面积明显增大。研究表明,激光冲击强化能明显改善铝合金小孔构件的疲劳性能,但强化效果随外加载荷的增加逐渐减小。     

TC17钛合金激光喷丸应力场及支持向量机应力热松弛模型

对TC17钛合金进行了不同功率密度下激光喷丸强化,使用X射线衍射仪测试了激光喷丸冲击波诱导的残余压应力场的分布,测试了不同温度真空保温下残余压应力的热松弛规律,最后基于支持向量机理论建立了残余压应力热松弛预测模型,并用试验结果对模型进行验证.研究表明:TC17钛合金在功率密度为4GW/cm2时表层残余压应力场最佳;残余压应力在280℃和450℃真空保温150min后分别有11.24%和27.11%的松弛;在280℃和450℃交替保温160min后应力松弛33.9%;残余压应力在试验温度保温160min后有大部分剩余,可以有效提高TC17钛合金抗疲劳性能、基于支持向量机的预测模型能够较精确的表征TC17钛合金的应力松弛规律,满足工程使用要求,对其他材料表层残余压应力热松弛分析具有借鉴意义.      

激光冲击叶片榫头变形控制与疲劳试验

针对某航空发动机涡轮叶片榫头部位疲劳断裂故障,利用激光诱导高压冲击波对榫头部位进行冲击强化,提高其抗疲劳性能。在试验测试激光冲击GH4133B镍基高温合金材料残余应力场的基础上,确定了叶片材料激光冲击工艺参数;根据榫齿面转接R区结构特征,设计了不等强度分布冲击方式,保证强化区域残余应力均匀、过渡分布,防止出现应力突变。由于榫头结构不均匀,高压冲击波引起的塑性流动使叶片发生宏观变形,采用数值仿真方法分析了激光冲击后叶片榫头宏观变形规律和机理。在此基础上提出了激光冲击叶片榫头变形控制的方法,并设计了榫头结合面冲击区域和方式,保证叶片榫头两侧对应区域的激光能量输入基本相当,通过结合面的塑性流动来减小叶片榫头宏观变形。冲击处理后的叶片榫头表面粗糙度、滚棒尺寸和平面度等均满足技术要求。并分析了激光冲击强化提高叶片高温疲劳寿命的原因。疲劳试验结果表明：激光冲击强化可提高叶片榫头部位的高温高低周复合疲劳寿命提高了279%。     

大规格损伤容限钛合金TC4-DT的研制及应用

为了满足新一代战斗机对大规格损伤容限钛合金的需求，开展了TC4-DT钛合金大规格棒材与锻坯的成分与组织控制、大型锻件热处理过程中的显微组织控制、材料与锻件的制造过程控制、零件的疲劳强化等研究。经过大型铸锭熔炼、大规格棒材和锻坯试制、大厚度锻件试制、结构设计与制造，结果表明：损伤容限钛合金TC4-DT大型铸锭的成分均匀、大型锻坯和大厚度锻件的抗拉强度变异系数降至约2%，激光冲击、喷丸和冷挤压等对该合金的寿命增益效果显著。损伤容限钛合金TC4-DT在新一代战斗机上获得了广泛应用。     

Development and Application of Laser Peening in Japan

Recent advances in laser technology have yielded amultitude of innovative processes and applications invarious industries. Laser peening without protectivecoating (LPPC) is a typical example and blazes a trail inthe field of preventive maintenance of operating nuclearfacilities, taking full advantage of inertia-less processover mechanical treatment[1]. LPPC introduces a compres-sive residual stress on metal surface by simply irradiat-ing laser pulses under water environment[2] . A remotepro…     

喷丸对激光辅助成形铝合金样件拉-拉疲劳性能的影响

为了研究激光辅助成形样件的疲劳性能及喷丸处理的作用规律,以2024铝合金板材为对象,对原始、激光辅助成形以及激光辅助成形后再喷丸等样件的微观组织、显微硬度、残余应力和拉-拉疲劳性能进行了对比分析研究.结果表明:激光辅助成形后,样件的组织和微结构未发现明显变化,但其硬度和残余拉应力水平有所下降;喷丸处理的激光辅助成形样件...     

航空钛合金抗疲劳表面改性技术研究进展

重点介绍了提高钛合金疲劳性能的表面改性技术的最新研究进展。主要从喷丸强化、激光冲击强化、挤压、滚压、离子注入、滚磨光整加工、水射流喷丸等典型方式对钛合金的加工能力、作用机理,以及加工后零件的残余应力水平和疲劳性能等方面进行了阐述,以期为航空钛合金零件的表面改性提供借鉴。     

LY2铝合金的激光冲击强化区硬度和残余应力测试分析

为了研究激光冲击处理对LY2航空铝合金力学性能的影响,采用Nd:YAG激光器对航空铝合金LY2进行了激光冲击强化处理,测定其显微硬度和残余应力.结果表明,经过激光冲击处理后,试样表面没有受强脉冲激光和冲击波的破坏,而显微硬度和残余压应力明显提高,激光冲击处理后的强化区与光斑相当,深度约为1.2mm.