等离子体处理对T700/环氧复合材料湿热性能的影响

研究了等离子体处理对T700/环氧复合材料湿热性能的影响。考察了该复合材料在50℃和80℃的3.5%NaCl水溶液中的吸湿特性和层间剪切强度的变化,并用SEM观察了层间剪切试样断口形貌。结果表明,该复合材料的吸湿行为符合Fick第二定律;随着温度升高平衡吸湿率和扩散系数均增大;经过等离子体处理的复合材料平衡吸湿率比未经处理的平衡吸湿率明显降低;等离子体处理能够提高界面结合强度,吸湿后其层间剪切强度保持率显著提高;SEM结果表明,复合材料的性能变化是由基体破坏和界面脱粘引起的。     

湿热老化对T700/3234复合材料力学性能影响研究

在室温及70℃条件下对单向T700/3234复合材料进行了湿热老化试验,分别测试了经历不同吸湿时间后材料的吸湿率、层间剪切强度和弯曲强度,并且利用扫描电镜(SEM)对力学性能试样的断口形貌进行了分析.结果表明,吸湿温度越高,饱和吸湿率越高.T700/3234复合材料具有良好的耐湿热性能,其层间剪切强度、弯曲强度保持率分别为69.33％和76.06％.吸湿使界面出现一定程度的脱粘是导致其力学性能下降的主要原因.     

GFRP 层压板挖补修理后的吸湿行为

对采用不同台阶比率挖补修理的玻璃纤维增强树脂基复合材料层合板进行了吸湿实验,获得了 各种台阶比率试样的吸湿规律以及损伤行为。通过面内剪切强度测试以及形貌观察,研究分析了导致吸湿试 件强度降低以及层间开裂的主要因素。实验发现:玻璃纤维增强树脂基复合材料的孔隙率是影响层合板吸湿 率和层间开裂的重要影响因素,孔隙率越高,吸湿率越高,但层间开裂倾向却降低;台阶比率对长时间吸湿试件 的强度保持率有较大的影响,恰当选择台阶比率不但有助于提高强度恢复率,还可减小因吸湿而产生的强度降 低幅度;吸湿会导致玻璃纤维增强树脂基复合材料层合板的面内剪切强度大幅度下降,导致这种结果主要原因 之一是吸湿会严重劣化纤维/ 树脂界面粘结状态。     

HS40碳纤维/氰酸酯树脂复合材料的湿热行为

通过对低温固化HS40碳纤维/氰酸酯树脂复合材料进行不同湿热环境处理以及3次循环吸湿-脱湿处理,研究其湿热行为。结果表明:复合材料在70℃水浸以及70℃/95%RH两种环境吸湿31 d饱和吸湿率分别为0.71%和0.11%,说明该低温固化氰酸酯树脂基复合材料有很好的耐湿热性;研究复合材料的循环吸湿-脱湿行为,发现复合材料在70℃水浴锅中第1次水浸10 d的吸湿率为0.69%,尚未达到饱和,而第2、3次水浸10 d后的吸湿率分别提高到0.72%和0.74%;复合材料的层间剪切强度随着循环次数的增加,降低更为明显,经过3次循环吸湿-脱湿之后试样的层间剪切强度较干态试样降低了50.77%,连续吸水60 d的试样层间剪切强度较干态试样降低了58.98%。     

纤维增强基于α-BPDA 聚酰亚胺复合材料性能

为了考察基于α-BPDA聚酰亚胺复合材料的高温性能,制备了纤维增强复合材料,进行了高温力学和热物理性能的测试。研究结果表明纤维增强复合材料的T5d分解温度为565℃;Tg超过471℃;在450℃下的弯曲强度保持率大于42%,弯曲模量保持率大于55%,短梁剪切强度保持率超过44%;400℃空气热老化50 h后碳纤维复合材料的弯曲强度保持率66%,弯曲模量保持率为95%;300、500℃的石英增强复合材料的热导率分别为0.503和0.657 W/(m.K)。     

湿热环境下复合材料孔板压缩性能的研究

采用压缩试验的方法,对含孔机织碳纤维环氧复合材料层板进行了湿热环境下的压缩试验,研究了湿热环境对其压缩性能的影响。分析了复合材料孔板的吸湿特性、压缩强度、破坏模式及动态力学性能。结果表明:机织碳纤维环氧复合材料吸湿率较低,其饱和吸湿率仅为0.88%左右。湿热环境会降低由基体性能主导的压缩强度,130℃下湿态试样的开孔压缩强度保持率约为70%。含孔复合材料层合板的破坏模式均为过孔破坏,破坏均发生在应力集中的区域,并且断裂都是沿着应力集中最大的方向扩展。侧面断口主要为剪切失效,有分层和屈曲的特征。吸湿后复合材料的DMA Tg为125℃,比干态时下降了16℃。     

树脂基复合材料T300/5405的吸湿性能及湿热环境对力学性能的影响

研究了单向铺层的T300/5405复合材料在六种湿热环境中的吸湿行为,并利用扫描电镜研究了材料吸湿过程中的形貌变化。同时计算了在不同湿热条件下的水分扩散系数。结果表明在较高的温度和湿度下会使水分的扩散速率增加。老化后试样的剪切强度、弯曲强度和压缩强度随着老化时间的延长均有所下降,同时在相同的温度条件下,提高湿度会使材料的力学性能下降更快。     

聚乙烯基吡咯烷酮改性氰酸酯树脂耐湿热性能研究

对聚乙烯基吡咯烷酮(PVP)/氰酸酯树脂体系的耐湿热性能进行系统研究.选取湿热老化环境为100h/100℃沸水老化.结果表明,随着体系中PVP用量的增大,固化改性树脂的吸湿率逐渐增大.湿热老化使固化树脂的力学性能急剧下降,但PVP的加入能够有效改善下降趋势.当PVP用量为5wt%时,湿热老化后固化树脂的弯曲强度和冲击强度的强度保持率从原始氰酸酯的38.8%和35.5%提高到86.8%和66.1%.湿热老化对体系力学性能的损伤可从固化树脂老化前后断口形貌得到合理解释.湿热老化过程中,PVP的加入对体系的热性能、电性能及尺寸稳定性的不利影响较小.综合考虑体系的各项性能指标,以PVP用量为5%时体系耐湿热性能最佳.     

国产T800级碳纤维/环氧树脂复合材料湿热性能

采用扫描电镜、红外图谱分析三种国产T800级碳纤维的物理形貌以及表面上浆剂的化学结构。针对三种国产T800级碳纤维(CCF800)/环氧树脂复合材料在湿热环境下的吸湿行为,研究经不同时间湿热和高温环境下处理后的层间剪切性能,并通过扫描电镜观察湿热处理后的复合材料界面结合状态。结果表明:三种国产T800级碳纤维表面物理形貌相同,而表面化学结构存在一定差异;三种碳纤维环氧复合材料的"饱和"吸湿周期相同,约为54 d,95%饱和吸湿周期也相同,约为30 d;而饱和吸湿量存在明显差异,其中3号纤维上浆剂中由于羟基含量最高,导致其环氧树脂基复合材料吸湿率最高,在高温高湿作用下,层间剪切强度下降最为明显。     

RTM 用耐高温R802 树脂工艺及性能

研究了RTM用耐高温R802邻苯二甲腈树脂黏度随温度、时间的变化,不同升温速率下的DSC特性,常、高温复合材料弯曲、层间剪切强度、树脂与纤维的界面等。黏度随时间变化曲线表明,其140℃下RTM工艺窗口不少于180 min;DSC曲线表明,在180℃时开始凝胶,固化温度203℃,后处理温度256℃;力学性能测试结果表明,R802/MT300复合材料200℃下弯曲强度保持率为103.8%,500℃下弯曲强度保持率为41.1%,300℃下层间剪切强度较常温提高18%,500℃下层间剪切强度保持率为44%,其树脂与纤维结合良好。     

非连续湿热作用对T700/TR1219B复合材料宏细观性能的影响

为研究非连续湿热作用对碳纤维环氧树脂基复合材料性能的影响,对T700/TR1219B试样进行了吸湿-脱湿试验,测试了其拉神性能,并采用SEM观察试样侧面;通过原子力显微镜的峰值力纳米力学成像技术(PF-QNM)对树脂进行纳米压痕测试。结果表明:吸湿率从0变化到1.2%,T700/TR1219B复合材料的一次及二次吸湿行为均满足Fick定律;经吸湿-脱湿-再吸湿,试样的拉伸强度、弹性模量及树脂的硬度及弹性模量均呈现先上升后下降的变化趋势。     

碳纤维环氧预浸料前热处理及储放老化对复材力学性能的影响

基于DSC测试数据,采用非模型拟合动力学方法 Flynn-Wall-Ozawa(FWO)对碳纤维环氧预浸料的固化过程进行研究,并将试验结果与模型预测进行对比。结果表明,采用FWO法能很好地预测预浸料的固化行为。同时,结合热隔膜成型工艺特点,将预浸料分别置于80℃和室温中进行分段处理,将经不同预处理的预浸料采用相同的固化工艺制作成复合材料板并进行力学测试。结果显示,随着80℃预加热时间的延长,层合板剪切强度逐渐降低,试样厚度增加,弯曲模量略微低,弯曲强度出现小幅度波动。室温老化结果表明,随着老化时间的延长,层合板的层间剪切性能和弯曲性能都存在小的波动,但无明显规律。     

Study on Compressive Properties of Z-pinned Laminates in RTD and Hygrothermal Environment

Compressive tests of [0] 12 and [90] 12 unidirectional laminates and [45/0/-45/90] 2S quasi-isotropic laminates are accomplished in both room-temperature and dry (RTD) and hygrothermal environment. And simulation studies on the compressive strength of Z-pinned laminates of [0] 12 and [45/0/-45/90] 2S are conducted by using finite element analysis (FEA). A microstructural unit cell for FEA is created to simulate a representative laminates unit with one pin. Within the unit cell, the first directions of the elements’ material coordinate systems are changed to simulate the fibres’ deflecting around the pin. The hygrothermal effect is simulated by the material properties’ adjustments which are determined by the compressive tests of non-pined laminates. The experimental results indicate that the percentage of reduction in the compressive modulus of Z-pinned laminates caused by Z-pin becomes smaller with the percentage of 0° fibres decreasing in the laminates; the compressive strength of quasi-isotropic laminates reduces and the percentage of the reduction in the compressive strength declines with Z-pin volume content increasing, and the moisture absorption ratio of the Z-pinned specimens is greater than that of the non-pinned specimens, because the cracks around Z-pin increase the moisture absorption. In addition, the simulations show that the deflection of fibres around Z-pin is the main factor for the reduction in the compressive strength of Z-pinned unidirectional laminates, the dilution of fibre volume content caused by resin-rich pocket is the principal factor for the decline in the compressive strength of Z-pinned quasi-istropic laminates, and the compressive strength of Z-pinned specimens in hygrothermal environment reduces as the result of superimposition of some factors, including the changes in material properties caused by hygrothermal environment, the deflection of fibres and the resin-rich pocket caused by Z-pin.     

纤维表面处理对PBO/ 环氧界面性能的影响

为提高PBO纤维/环氧树脂的剪切强度,采用聚合物涂层法对PBO纤维进行表面改性。通过NOL环复合材料层间剪切强度测试,研究不同浓度的表面涂层处理液、不同浸渍工艺对复合材料层间剪切强度的影响。结果表明:PBO纤维表面经不同涂层处理液处理后,层间剪切强度均高于未经表面处理的;当PBO纤维经过以涂层A为一浴浸渍液、涂层B为二浴浸渍液的两次浸渍工艺处理后,层间剪切强度最高,比未经表面处理的提高了61%。     

复合材料修复铝合金薄板的湿热特性

采用真空袋压技术将T300/CYD128复合材料补片胶接修复于含中心裂纹的铝合金1.76 mm薄板。研究了实验室模拟湿热环境对复合材料修复铝合金薄板的力学性能影响,修复用复合材料的吸湿特性,以及修复用复合材料拉伸试样及其基体树脂浇铸体的湿热性能。结果显示,浇铸体饱和吸水率为0.9%,复合材料吸湿动力学曲线则出现台阶;随湿热老化时间延长,浇铸体与复合材料拉伸性能先升后降,其性能峰值出现时间分别为500 h(73.9 MPa)和300 h(1 531 MPa);随湿热老化时间延长,铝合金裂纹板拉伸性能基本呈线性下降,断裂载荷下降速率ΔN=0.12 kN/100 h,修复板性能出现波动。     

增黏成型RFI层合板复合材料性能的实验研究

通过测试PT500粉末状环氧树脂型增黏剂的动态黏度特性，确定了在增强织物表面涂覆定量增黏剂的固态粉末涂布工艺及增黏层合预制件真空袋成型工艺。以M18型环氧树脂膜为基体，利用RFI成型工艺制备了增黏成型RFI层合板制件。实验结果表明：当增黏剂涂覆量≥10%时，随着增黏剂涂覆量的增加，RFI制件的厚度和孔隙含量逐渐增加，从而使RFI制件的弯曲强度和层间剪切强度亦相应降低，即增黏剂涂覆量的多少直接影响到RFI制件弯曲强度和层间剪切强度的高低。     

硼酸铝晶须增强氰酸酯树脂/玻璃布复合材料的研究

为了改善氰酸酯树脂基复合材料的层间性能,加入硼酸铝(AlBw)晶须制得晶须/氰酸酯树脂/玻璃布复合材料。研究了晶须对氰酸酯树脂的反应活性、工艺性的影响以及对复合材料力学性能的改善效果,并分析了复合材料断裂的SEM照片。凝胶时间和差示扫描量热(DSC)分析表明,晶须的加入对树脂体系反应性影响较小。晶须的加入增大了氰酸酯树脂的粘度,但增加幅度不大,当晶须加入质量为20%时树脂粘度仍小于8Pa·s,具有良好的工艺性。随晶须加入量的增加,复合材料的层间剪切强度(ILSS)和弯曲强度增大,晶须质量占10%时,4%硼酸酯处理的晶须使ILSS和弯曲强度分别提高45%和32%。晶须的加入使复合材料耐湿热性提高,水煮100h后,吸水率降为1.09%,力学强度保持率高于85%。     

碳纤维/环氧树脂复合材料微波固化试验

采用微波固化技术,对碳纤维/环氧树脂复合材料NOL环试样进行固化试验研究。通过开展力学性能测试、电镜扫描及CT扫描,对比分析了热固化与微波固化试样宏观力学性能及微细观形态。结果表明:微波固化与热固化的固化机理不同,微波固化提高了固化反应速率,固化周期缩短了57%;微波固化试样的拉伸强度和层间剪切强度与热固化试样基本相当,但微波固化试样力学性能离散系数更小,碳纤维表面有更多的树脂基体粘附,这是由于微波固化的选择性加热造成的;微波固化试样孔隙率为0.78%～1.05%,稍低于热固化试样。     

海洋环境下G814/3233复合材料的老化机理及加速老化与自然老化的相关性

为探索航空用碳纤维增强树脂基复合材料（CFRP）的老化机理及实验室加速老化环境与真实服役环境间的相关性,以飞机常用的G814/3233复合材料为研究对象,以海洋环境为服役背景开展了实验室加速老化试验和随舰自然暴露试验,观测了老化前后CFRP试件的力学性能、微观结构、组织成分等;改进了传统的大样本统计方法,提出了确定自然老化方程的小子样方法,有效扩大了数据样本;提出了以纵横剪切强度保持率为基准的当量折算系数计算方法并开展了验证试验。结果表明：在加速老化1个月后,G814/3233复合材料的表面树脂及碳纤维/树脂界面遭到破坏,剩余强度、纵横剪切强度、玻璃化转变温度分别下降6.93%、7.30%、0.87%,室温条件下的储能模量升高约5 GPa;获得了该型CFRP在南海环境下的老化机理和纵横剪切强度中值曲线;确定了自然老化环境与加速老化环境之间的当量折算系数为7.25;所建立的实验室加速老化方法对自然老化方具有较好的加速性和重现性。