三种钻头钻削CFRP的制孔损伤对比

采用二刃双锋角钻头、三刃双锋角钻头和圆弧形钻头在不同加工参数下钻削CFRP,对比分析了孔入出口质量(入口损伤、毛刺和出口撕裂),并采用毛刺存在角度来衡量毛刺的多少。结果表明:随着进给量的增大毛刺存在的角度(范围)α先减小后增大;综合考虑孔入口和出口质量(毛刺和撕裂因子),三刃双锋角钻头最适合钻CFRP。     

双锋角钻头钻削碳纤维增强树脂基复合材料研究

采用双锋角钻头和普通麻花钻对T700碳纤维复合材料(CFRP)进行钻削试验,从钻削轴向力、制孔出口质量和表面粗糙度等方面分析双锋角钻头在不同加工参数下制孔特点,并与普通麻花钻进行对比。试验结果表明:与普通麻花钻对比,双锋角钻头钻削CFRP时钻削轴向力减小约20%,制孔出口质量更好,孔壁的表面粗糙度值减小,体现优异的切削性能更适合CFRP的制孔加工。     

麻花钻几何参数对碳纤维复合材料钻削性能的影响

采用不同几何参数硬质合金麻花钻对碳纤维复合材料(CFRP)进行钻削试验,研究了麻花钻几何参数对钻削轴向力、钻削温度、孔出口撕裂因子L_d及形貌的影响。结果表明:对CFRP进行钻削加工时,钻削轴向力随钻尖角的增大、螺旋角的减小及横刃长度的增大而增大。钻尖角和螺旋角对钻削温度无明显影响,随横刃长度的减小,钻削温度有所降低。小钻尖角和大螺旋角麻花钻制孔的出口撕裂因子L_d较小且形貌较好。综合考虑,钻尖角2θ选在90°~115°,螺旋角卢选用30°甚至更大,横刃长度b_ψ磨到0.2~0.6 mm比较合适。     

三种钻头钻削CFRP轴向力的时变曲线及预测

采用二刃、三刃双锋角钻头和圆弧形钻头钻削CFRP单向板,研究钻削过程中轴向力时变曲线的特征,并探索用预测轴向力时变曲线上的关键拐点的方法来构建预测轴向力时变曲线模型。结果表明:三刃双锋角钻头的轴向力时变曲线最为稳定,钻削过程最为稳定;轴向力最大的是三刃双锋角钻头,其次是圆弧形钻头,最小的是二刃双锋角钻头,说明二刃双锋角钻头适合钻削CFRP;用预测轴向力时变曲线上的关键拐点的方法构建的轴向力时变曲线可以很好地预测双锋角钻头轴向力时变曲线。     

阶梯钻钻削碳纤维复合材料的钻削力及孔质量

根据碳纤维复合材料制孔过程中产生的缺陷,自主磨制专用钻头——阶梯钻对碳纤维复合材料进行钻削实验,研究了在不同加工参数下阶梯钻钻削碳纤维复合材料的钻削力、孔出口质量、孔壁表面粗糙度,并与普通麻花钻头进行对比。结果表明:阶梯钻产生的钻削轴向力是麻花钻的一半,孔壁表面粗糙度值更小,孔出口没有明显的缺陷,阶梯钻适合钻削碳纤维复合材料。     

镁基碳纤维增强复合材料超声辅助切削试验研究

为研究镁基碳纤维增强复合材料(C_f/Mg)的切削力与已加工表面质量,开展了硬质合金铣刀与硬质合金钻头超声辅助切削试验研究。通过正交试验得到,超声辅助铣削C_f/Mg复合材料时铣削力随每齿进给量及铣削深度的增加而明显增大,随主轴转速的增加而减小;试验中,在超声辅助铣削时每齿进给量0.025mm、铣削深度0.2mm、转速6000r/min加工参数下铣削力最小,每齿进给量0.025mm、铣削深度0.2mm、转速4000r/min加工参数下表面质量较好;采用硬质合金钻头进行单因素钻削试验时,轴向钻削力随主轴转速的升高而减小;与传统钻削相比,超声辅助钻削能减小轴向钻削力,在机床转速6000r/min、机床进给速度100mm/min加工参数下超声辅助钻削相比传统钻削可减小约36%的轴向钻削力;超声辅助钻削相比传统钻削能改善钻孔出口的毛刺、分层等缺陷。     

TC4钛合金钻削加工工艺参数研究

针对典型TC4钛合金材料进行了钻孔试验,分析了切削钻头材质、钻头锋角对钻孔质量的影响,并采用正交试验对钻削加工工艺参数进行选择,结果表明采用适当的钻头材质及相关工艺参数可降低钻削孔径毛刺,提高制孔质量。     

碳纤维复合材料高质量孔的钻削

探讨了获得钻削碳纤维复合材料高质量孔的两个关键因素:保持钻头切削刃的良好锋利性和采用高的钻削速度。指出了采用厚膜CVD金刚石钻头进行高速钻削加工是获得高质量孔的良好方法。     

八面钻超声振动钻削钛合金出口毛刺形成机理

钛合金在传统麻花钻常规钻孔后,会产生较大的孔出口毛刺,这将导致孔出口去毛刺困难且影响紧固件装配质量。本文引入一种八面钻新刃型刀具,并利用超声振动钻削技术,进行了八面钻超声振动钻削钛合金出口毛刺形成的基础理论和试验研究。理论分析了普通钻削和超声振动钻削的出口毛刺形成过程以及超声振动钻削的出口毛刺降低机理,同时试验验证了超声振动钻削的出口毛刺降低效果。结果表明:相比于钛合金普通钻削,超声振动钻削极大地提高了钻头刀具的切削能力,分别降低了钻削力16%~20%、切削温度18%~21%和出口毛刺高度82%~89%,有效降低了装配过程的去毛刺困难和生产成本。     

镗削碳纤维复合材料时切削用量对切削力及孔出口撕裂的影响

采用PCD刀具对碳纤维复合材料(CFRP)进行了镗削加工试验,分析了切削用量对切削力、孔出口撕裂因子(撕裂值与孔直径的比值)的影响规律.试验结果表明,三向切削力随背吃刀量、进给量、切削速率的增大而增大.经分析认为,切削速率的增大引起待加工材料的屈服应力增大.由于刀尖圆弧半径较大,试验中出现背向力大于主切削力的现象;撕裂因子与背吃刀量基本无关;进给量与撕裂因子呈线性正相关;当切削速率增大时撕裂因子呈减小趋势,并且减小到一定程度后基本不变;采用PCD刀具镗削加工该材料能够有效地减小孔出口撕裂程度.     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

基于飞机油箱模型形状特征油量测量切片步长选择方法研究

 在分析飞机数字式油量测量过程中目前广泛使用的切片法油量测量原理的基础上,针对现有的定步长切片法无法得到准确、可靠的燃油质量特性数据库的缺陷,结合对飞机油箱模型形状特征的分析,提出了基于飞机油箱模型形状特征的油量测量切片步长选择方法。此方法包括切片步长整体和局部选择两个过程,整体选择以实现相邻两切片平面所夹油箱模型体积近似相等为目的来确定切片步长,以体现油箱模型截面整体变化规律;局部选择以设计切片平面与截面突变平面重合或尽可能接近的方式,突出油箱截面的局部变化特征。实验结果表明：该切片步长选择方法较定步长方法能够建立更为合理、可靠的燃油质量特性数据库,从而提高了油量测量精度。     

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

二维翼段颤振的μ控制

 采用超声电机作为作动器来实现含控制面的翼段颤振鲁棒抑制。针对作者设计的二维翼段颤振主动抑制系统，通过理论与实验相结合的方法，建立了考虑沉浮方向阻尼和作动器模型参数不确定性的控制系统模型，设计了μ控制器，并对控制器做了降阶处理。数值仿真和风洞试验表明，μ控制器可有效地抑制颤振的发生，将颤振临界速度提高23.4%。相对于H_∞控制器，μ控制器的控制效果和鲁棒性更好。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

Abnormal Shape Mould Winding

为解决网格化芯模的缠绕问题,本文提出了复合材料面片缠绕机理;接着详细分析了面片缠绕过程中的芯模凹曲面上纤维滑线和架空现象,应用微分几何曲面理论和空间几何理论,提出判据及其解决方案;最后,针对飞机发动机进气道的缠绕成型,编制缠绕控制程序并进行相应的实验,验证了面片缠绕方法的可行性。