化学气相渗透法制备碳化硅陶瓷复合材料

综述了化学气相渗透法制备连续纤维增强碳化硅陶瓷复合材料的过程，以及碳化硅陶瓷复合材料的性能及应用。     

"神舟二号"大气密度探测器的探测结果Ⅱ.在太阳和地磁扰动期间高层大气密度的变化

选用了Sz—2大气密度探测器在2001年2—4月间的探测数据,进行日照和阴影区域热层大气密度对太阳和地磁活动程度的响应变化的探讨．结果表明,日照区大气密度峰值主要随F10.7值而变,在地磁扰动期间,阴影区大气密度对扰动的响应更明显,通常响应变化开始于高纬度地区,然后向低纬度地区推移．     

SOME RESULTS OF UPPER ATMOSPHERIC COMPOSITION MEASUREMENTS BY A MASS-SPECTROMETER ON BOARD "SZ-2":CHANGE OF COMPOSITIONS DURING SOLAR AND GEOMAGNETIC DISTURBANCES

Upper atmosphere composition data were obtained for the last half year with a quadruple mass spectrometer on board spacecraft "SZ-2" launched on 10 Jan uary 2001. Based on the analysis of these data, the variations of atmospheric compositions in solar and geomagnetic quiet conditions are reported first, then a detailed discussion on the atmospheric composition variations under the so lar and geomagnetic disturbed conditions is given. The results show that near the altitude of 400 km the variations of main atmospheric compositions corre sponding to solar disturbances are more remarkable in the sunlit area than in the shade area. On the contrary, in geomagnetic disturbance events the corre sponding variations are more obvious in the shade area, an evident increase of N2 density at relatively higher latitudes was observed.     

大气湍流光学长曝光像的数值计算

在介绍大气湍流光学长曝光像的两个模型——高斯模型(空间域模型)和统计平均光学传递函数模型(空间频率域模型)的基础上，推导两模型之间的关系与差别，并应用两模型数值计算了扩展目标通过大气的长曝光成像结果。此外，还应用高斯模型给出了自适应光学系统校正后的远场光斑。     

Effects of the Fabrication Processes of NC-Si:H Films on Their Mechanical Properties

Studies of nanoindentation were performed on nc-Si:H films to evaluate the effects of the fabrication processes on their mechani-cal properties. It is observed that with the decrease of the SiH4 contents, the grain size of the films increases gradually, and as does the crystalline volume fraction. The smaller the grains become, the more homogeneous the films, and the more even the hardness as well as the modulus will be. The hardness and the modulus will increase with the substrate’s temperature rising. The hardness and the modulus of the nc-Si:H films on the Si substrate prove to be higher than those on the glass substrate given the same technology parameters. How-ever, the films on the glass substrate appear to be more homogeneous.     

喷射沉积过程中显微组织的形成机制

通过对沉积还纵剖面的组织分析，发现沉积坯在进缘、上下表面及中心部位的显微组织明显不同。边缘及上下表面区试样的退火试验研究表明，细小的枝晶碎块在高温退火过程中发生凝共和粗化，并导致近球状晶粒组织的形成。试验确定其生长服从：D2-D02=6.37×1020e(-70036.1/T)·τ，晶界迁移激活能Qg=582KJ／mol。并依赖于两种机制：（1）在喷射沉积过程中无强烈变形枝晶的均匀化；（2）变形及断裂枝晶的生长和粗化。     

Parylene真空涂覆新工艺研究

简述了Parylene真空沉积的机理,并对采用Parylene真空涂覆的涂层样件进行了全面的性能摸底试验。     

离子镀Ti(N,C)耐磨镀层成分与性能研究

 用空心阴极离子镀技术,在常用的不锈钢(1Cr18Ni9Ti)基材上,镀制Ti(N,C)耐磨镀层。对镀层的成分进行了分析,讨论了镀层成分的耐磨性,显微硬度和附着力的影响。通过对Ti(N,C)镀层与TiN和TiC镀层性能的对比,肯定了Ti(N,C)复合化合物镀层具有更优越的耐磨性和附着力。     

多层喷射沉积制备大尺寸耐热铝合金管坯的研究

采用多层喷射沉积工艺制备出了尺寸为Ф630 mm×250 mm×800 mm且质量较好的FVS0812耐热铝合金管坯,通过挤压获得了性能优良的大直径管材,并对管坯和挤压后管材的力学性能和微观结构进行了检测和分析.分析结果表明,多层喷射沉积制坯过程中,熔滴在沉积面的冷却速度约3.2×104 K@s-1～106K@s-1,熔滴凝固后在沉积坯中形成微细晶粒结构(200 nm～500 nm)和弥散分布的纳米析出相Al12(Fe,V)3Si(20nm～60 nm),使得沉积坯挤压致密后具有优异的性能.     

AB型聚酰亚胺单体的合成及气相沉积聚合研究

合成了三种AB型聚酰亚胺单体:4-(4-氨基苯氧基)邻苯二甲酸(单体4),4-(3-氨基苯氧基)邻苯二甲酸(单体7)和对(间)乙基4-(3-氨基苯氧基)邻苯二甲酸酯(单体8或9)。利用热失重分析(TGA)对比研究了这三种AB型聚酰亚胺单体的热行为。结果表明,单体4、单体7和单体8(9)在升温的过程中能发生热聚合生成聚酰亚胺。将单体4用于气相沉积聚合设备,得到了均匀透明的聚酰亚胺薄膜。对分子结构的修饰使单体8(9)较之单体7有更好的挥发性。