TiO2基紫外探测器的制备及退火工艺对光电性能的影响

采用磁控溅射方法,通过不同工艺的退火处理,制备了光电性能优良的TiO2基紫外探测器.通过紫外光电性能测试、扫描电子显微镜( SEM)观察及X射线衍射(XRD)分析,研究了退火工艺对探测器光电性能的影响规律.结果表明:随着退火温度的增加,TiO2晶粒尺寸显著增大,晶界和缺陷数量的变化是导致TiO2基紫外探测器的光电性能随退火工艺变化的根本原因.经500℃/2h退火后,紫外探测器的光电流高出暗电流近2.5个数量级,紫外波段的光响应高出可见光波段近2个数量级,所制备紫外探测器达到了高辐射灵敏度和可见盲特性的要求.     

2D C/SiC-ZrB2复合材料的烧蚀性能

用ZrB2微粉对2D C/SiC基体进行改性,研究了化学气相渗透结合浆料浸渍及先驱体浸渍裂解工艺制备2DC/SiC-ZrB2复合材料在氧-乙炔焰和1800℃甲烷风洞环境中的烧蚀行为.结果表明:在氧-乙炔环境中,2D C/SiC-ZrB2的线烧蚀率和质量烧蚀率分别为6.1×10-2 mm/s和1.0×10 -2g/s,相对2D C/SiC复合材料而言,ZrB2微粉并没有提高C/SiC复合材料的抗烧蚀性能.在1800℃甲烷风洞环境中,涂层致密度起主要作用,涂层致密度相同时,复合材料的开气孔率越大,质量烧蚀率越大,ZrB2微粉的渗入对C/SiC复合材料的烧蚀性能影响不大.     

星载单频GPS数据的电离层延迟改正方法分析

利用C/A码单点定位对LEO(Low Earth Orbit)卫星上的电离层延迟改正方法——"电离层比例因子法"进行了分析研究.计算的CHAMP卫星的轨道结果表明:采用电子密度峰值高度(hmF2,F2 region maximum electron density height)平均值和瞬时值计算的电离层比例因子α变化范围分别为0.3~0.4和0.2~0.65之间,两者最大差异可达0.3,相比较而言,hmF2瞬时值的结果更加合理,并且相应的大地高H方向的系统偏差要降低0.05~0.3m左右;与双频无电离层组合的普通单点定位结果相比表明该方法能较好地消除电离层一阶项所引入的H方向上的系统偏差;该方法适用的LEO卫星轨道高度范围大致在200~ 600km之间,当轨道高度超过700km时,该方法并不适用.     

Ionospheric disturbances on 8 September, 2010: Was it connected with the incoming moderate Chongqing earthquake?

Earthquake prediction stimulates the searches for a correlation between seismic activity and ionospheric anomalies. Contrary to common focuses on strong earthquakes, we report the ionospheric disturbances, 2 days before a moderate Ms = 4.7 Chongqing earthquake (29.4°N, 105.5°E, depth = 7.0 km, occurred at 21:21 LT, 10 September, 2010) with the data of ground-based ionosondes and IGS receivers. The data covering the period under the quiet geomagnetic conditions and a geomagnetic storm was analyzed with upper and lower bounds. It is found that there were significant enhancements of foF2 and total electron content (TEC) on the afternoon of 8 September, 2010, with a limited area close to the epicentre, which was different from the feature of ionospheric perturbations triggered by the geomagnetic storm on 15 September. Taking into account the heliogeomagnetical condition, we conclude that the observed ionospheric enhancements were very likely associated with the forthcoming moderate Chongqing earthquake, which implies that the relationship between the amplitudes of ionospheric disturbances and earthquakes is very complicated.     

A demonstration of the potential of Cryosat-2 to contribute to mesoscale observation

Cryosat-2 was designed for its primary scientific objectives, i.e. for cryosphere science. As far as oceanography is concerned, various mission design choices make it less accurate than missions designed to comply with ocean surface topography requirements such as Jason-2 or ENVISAT. Cryosat-2-specific errors are equivalent to more than 50% of the sea surface height variability over 40% of the oceans. Cryosat-2’s sampling pattern is also suboptimal for mesoscale observation because the satellite tracks from any consecutive period of 2 to 20 days (e.g. the most recent and most valuable data for near real time mesoscale observation) are aggregated in 500 km wide bands which are interleaved with 500 km wide observation gaps.     

Preliminary characterization of carbon dioxide transfer in a hollow fiber membrane module as a possible solution for gas–liquid transfer in microgravity conditions

In microgravity, one of the major challenge encountered in biological life support systems (BLSS) is the gas–liquid transfer with, for instance, the necessity to provide CO₂ (carbon source, pH control) and to recover the evolved O₂ in photobioreactors used as atmosphere bioregenerative systems.     

地-月L2点中继星月球近旁转移轨道设计

位于地月L2点周期轨道的中继星将首次为"嫦娥4号"月球背面着陆探测任务提供通信中继服务。中继星转移轨道设计是中继任务实施的关键环节。针对中继星转移轨道存在转移时间、近月点高度和halo轨道振幅等约束条件,系统研究了基于月球近旁的地月L2点转移轨道设计方法。首先基于限制性三体模型,分析了halo轨道族与着陆点可见性关系;然后将月球近旁转移轨道分为地月直接转移段和地月动平衡点附近周期轨道拟流形入轨转移段,采用带有状态约束的微分修正算法对这两段轨道进行拼接,得到了从地球附近至目标轨道族的月球近旁转移轨道;最后,针对南族halo轨道分析了halo轨道振幅和月球飞越高度对转移轨道设计的影响,以及转移轨道的入轨相位分布。仿真结果表明:月球近旁转移轨道设计方案具备工程上的可行性与优越性。该方案可以为实际工程任务和应用提供参考。     

TA2/Ni+Nb中间层/1Cr18Ni9Ti扩散焊接头的组织与性能

采用50μm纯Ni箔+10μm纯Nb箔复合中间层,在焊接温度840℃,880℃和920℃,压力4MPa以及保温时间60min的工艺下,对工业纯钛TA2和1Cr18Ni9Ti不锈钢进行了真空扩散焊实验,测试了接头的抗拉强度,并利用光学显微镜(OM)、扫描电镜(SEM)、能谱(EDS)和X射线衍射(XRD)对接头的组织结构、元素分布以及断口形貌和相组成进行了分析。结果表明:Ni+Nb复合中间层的存在成功阻止了Fe,Ti互扩散,实现了TA2与1Cr18Ni9Ti的可靠连接,接头的拉伸强度达到261MPa,该强度主要受剩余Ni箔控制,且焊接温度的变化对其影响不大。接头所生成反应层自不锈钢一侧起分别为FeCrNi固溶体、剩余Ni,Ni3Nb,剩余Nb以及TiNb魏氏体。     

均匀化处理对TiAl 合金铸造组织的影响

研究了均匀化处理对两种含B的铸造TiAl合金铸造组织的影响。研究发现1 370℃/5 min/OQ+1150℃/6 h/AC均匀化热处理能有效消除B2相,将b稳定化元素固溶到基体中,实现成分均匀化;1 370℃/5 min/OQ+1 150℃/24 h/AC均匀化热处理后可使粗大的铸造片层组织分解转变为细晶近g组织,平均晶粒直径50mm。     

氧化钇稳定氧化锆多孔陶瓷的制备与性能

以叔丁醇为溶剂,采用凝胶注模成型方法,制备出防/隔热的摩尔分数为8%Y_2O_3-ZrO_2(8YSZ)多孔陶瓷.在浆料中初始固相含量固定为10%体积分数的基础上,研究了烧结温度对8ySZ陶瓷材料的气孔率、开气孔率、孔径尺寸分布及显微结构的影响,分析了压缩强度、热导率与结构之间的关系.通过改变烧结温度,所制备的8YSZ多孔陶瓷的气孔率为65%～74%,孔隙分布均匀,平均孔径为0.68～1.82μm,压缩强度为7.92～13.15 MPa,室温热导率[最低可达0.053 W/(m·K)],比相应的致密陶瓷[～2.2 W/(m·K)]低一个数量级,且随着气孔率的增加而降低.