SiCp／Al电子封装复合材料预制坯的制备

文章研究了粘结剂的含量、成型压力和烧结工艺对SiCp预制坯性能的影响规律,结果表明:随着粘结剂含量的增加,预制坯中SiC颗粒的体积分数越来越小,抗压强度在粘结剂含量为30%时达到最大,随后缓慢下降;成形压力在10-25MPa之间时,随着成型压力的增大,预制坯中SiC颗粒的体积分数越来越大,其抗压强度也越来越大;在800℃以下烧结时,随着烧结温度的提高,预制坯中SiC颗粒的体积分数变得越来越小,但在800℃以后没有明显的变化,预制坯的抗压强度随着烧结温度的提高而增大,在1100℃时,效果最好。     

亚微米晶NiAl-Al2O3复合材料的制备及其烧结-锻造短流程成形

以Ni粉和Al粉为原料,通过机械合金化和真空热压烧结制备了高致密的NiAl-5％Al2O3(体积分数,下同)复合材料,并利用烧结-锻造技术制成了该材料的前缘模拟件.机械球磨后,粉末颗粒充分细化,Ni和Al发生原位反应,并最终生成NiAl-5％Al2O3复合材料粉末.经1300℃真空热压烧结,获得致密的NiAl-Al2O...     

复杂陶瓷件烧结过程温度场数值模拟及仿真

随着陶瓷应用领域的不断扩展,对其品质要求也越来越高.而传统的设计工艺与制造过程是相分离的,到最终生产工艺的定型需要大量的反复修改.为解决传统陶瓷设计工艺只能依靠经验的现状,节约成本,缩短生产周期,故开发了复杂陶瓷零构件烧结过程计算机仿真软件.首先借助传热学原理来建立温度场模型,其次借助有限差分法处理温度场模型,编写出此仿真模拟软件的核心计算代码,从而实现了复杂陶瓷零件和组合构件烧结过程中温度场的模拟仿真.      

La2Mo2O9粉体的制备及表征

本文采用溶胶-凝胶法和固相反应法制备La2Mo2O9粉体。采用XRD对不同方法制备的粉体的相组成进行了表征,结合TG-DTA结果确定了粉体烧结温度为600℃。SEM分析表明用柠檬酸盐法和固相反应法制备的粉体按1∶1混合制成的样品的高温烧结性能得到改善。     

STUDIES ON SINTERING TECHNOLOGY OF HAMMERS OF FOOD HAMMER MILL

提出了粉碎机锤片的烧结新工艺，并且系统研究了烧结配方、工艺参数。通过单因素试验和正交试验获得最佳参数。实验结果为锤片的进一步应用提供了理论指导和实验数据。     

激光选区烧结金属粉末的研究(英文)

采用激光选区烧结的方法 ,对铜、镍 -铜混合粉末进行了一系列激光烧结试验。分析了烧结过程中出现的现象 ,讨论了工艺参数对金属粉末烧结成形的影响 ,用带能谱的扫描电镜、X光衍射等手段分析了多层烧结体不同区域的成分、组织形貌和相结构特征。初步探讨了金属粉末直接烧结成形的基本机理 ,为金属粉末的激光快速成形提供了依据。     

W-Re合金构件气氛保护等离子喷涂成形技术

采用包覆法制备W-5％(质量分数)Re复合粉末,采用气氛保护等离子喷涂成形技术制备某实验型固体火箭发动机喷管(Solid Rocket Motor,SRM),研究2300 ℃真空烧结时喷管致密度、组织结构及显微硬度、抗拉强度、压缩强度等性能随烧结时间的变化规律.研究表明:喷涂成形件为典型的柱状晶层片结构,粒子层片结合部位存在较多孔隙及微观缝隙,成形件致密度为87.5％,其显微硬度、抗拉强度、压缩强度分别为321.8 HV0.025,57.9 MPa及390.2MPa.随着真空烧结时间由2h延长至6h及8h,W-Re合金逐渐由定向凝固柱状晶层片结构转化为颗粒状结构,致密度及力学性能均随之提高.其中经8h烧结处理后,W-Re合金致密度、显微硬度、抗拉强度、压缩强度及屈服强度分别增加至98.6％,529.7 HV0.025,384.7 MPa,1466.5 MPa及879.6 MPa.由于Re元素可提高W-Re合金的再结晶温度,有效细化晶粒,显著提高合金的程度及塑性,等离子喷涂成形W-Re合金经真空烧结后可观察到明显的Re效应.     

Preparation of bimodal grain size 7075 aviation aluminum alloys and their corrosion properties

The bimodal grain size metals show improved strength and ductility compared to traditional metals; however, their corrosion properties are unknown. In order to evaluate the corrosion properties of these metals, the bimodal grain size 7075 aviation aluminum alloys containing different ratios of coarse(100 μm in diameter) and fine(10 μm in diameter) grains were prepared by spark plasma sintering(SPS). The effects of grain size as well as the mixture degree of coarse and fine grains on general corrosion were estimated by immersion tests, electrochemical measurements and complementary techniques such as scanning electron microscope(SEM) and transmission electron microscope-energy disperse spectroscopy(TEM-EDS). The results show that, compared to fine grains, the coarse grains have a faster dissolution rate in acidic NaCl solution due to the bigger size,higher alloying elements content and larger area fraction of second phases in them. In coarse grains,the hydrogen ions have a faster reduction rate on cathodic second phases, therefore promoting the corrosion propagation. The mixture of coarse and fine grains also increases the electrochemical heterogeneity of alloys in micro-scale, and thus the increased mixture degree of these grains in metal matrix accelerates the corrosion rate of alloys in acidic NaCl solution.     

热压烧结型石油射孔弹药形罩的配方优化

介绍了一种制备石油射孔弹药形罩的新方法，采用粉末冶金热压烧结工艺制备石油射孔弹药形罩，并对药形罩的配方进行优化。试验结果表明采用该工艺制备的石油射孔弹药形罩品质较好。     

非金属电热膜材料及工艺分析

本文论述了制作电热膜的工艺过程.对电热膜的材料、烧结工艺及使用寿命进行了试验,获得了有价值的结论.并论述了提高电热膜产品寿命应注意的问题.