为了解决Ti1300合金筒形件成形难题和提高铸造管坯的机械性能,开展Ti1300合金筒形件旋压成形工艺研究,分析了旋压工艺参数对旋压成形的影响规律.研究表明：Ti1300合金热旋压温度为800～900℃时可以避免旋压缺陷的产生;进给比在不同道次间有所不同,开坯旋压时采用小进给,为0.5～0.8mm/r,终旋道次采用大进给比,为1.2～2.0mm/r;Ti1300合金的极限减薄率可以达到85％左右,单道次减薄率可以实现45％,在开坯旋压时不易采用超过30％的道次减薄率,随着材料旋压加工硬化,能够实现大减薄率.     

优化无焊缝钛内衬内表面质量的旋压工艺

针对复合材料压力容器用无焊缝TA1钛内衬,利用收口旋压实验和有限元模拟分析研究了两种典型收口旋压旋轮轨迹(水平直线和斜线轨迹)对旋压封头内表面缺陷的影响。结果表明:较斜线旋压,水平旋压后内表面褶皱等缺陷明显减少,说明水平旋压是一种优化无焊缝钛封头内表面质量的有效方式。有限元模拟分析表明:较斜线旋压,水平旋压每道次内表面的等效应变增量分布更均匀,并且多道次旋压后内表面的累积等效应变更小,说明水平旋压具有更均匀的变形特点和更少的应变累积,是内表面具有较弱褶皱趋势的主要原因。     

带底部法兰筒形件切旋成形工艺研究

旋压成形工艺是一种少/无切削、成形力小的渐进成形技术,广泛应用于现代制造业。针对带底部法兰的筒形件提出一种切旋两步成形工艺,采用有限元方法对不同参数条件下的旋压成形过程进行数值模拟,得到旋轮倾角、旋轮圆角半径以及进给比等因素对成形过程中成形力大小和坯料的筒壁厚度分布以及应变分布的影响,并通过试验验证了工艺的可行性。     

GH625高温合金管缩径旋压成形数值模拟及试验研究

基于ABAQUS/Explicit平台建立了高温合金管缩径旋压三维弹塑性有限元模型,对GH625高温合金管缩径旋压成形过程进行了模拟分析,研究了轴向进给速度、旋轮圆角半径、旋轮安装角度对高温合金管缩径旋压成形质量的影响规律。研究结果表明,高温合金变径管在旋压过程中,随旋轮的轴向进给,不同的区域截面变化趋势不同。对工艺参数进行分析,发现轴向进给速度及旋轮圆角半径增大时,壁厚增大;旋轮安装角度对零件壁厚无明显影响;进给速度越大或圆角半径越大,截面椭圆度越大;距自由端较远时,旋轮安装角度越小,截面椭圆度越大;随着旋轮的进给,距自由端越近,椭圆度波动越严重。最后,根据数值模拟结果确定最终工艺参数为轴向进给速度0.25mm/r,圆角半径取值2~4mm,旋轮安装角度为90o,并进行了高温合金管缩径旋压试验,得到了较好的成形件。     

铝合金旋压塑性成形的有限元模拟分析及其应用

以某铝合金旋压塑性成形工艺为应用研究对象,结合旋压成形工艺的关键技术,采用基于Msc.Marc的非线性有限元分析软件平台,对平板旋压和锥形件收口剪切旋压进行了模拟,模拟分析结果对产品旋压方案设计、模具设计、旋压工艺参数的制定有较好的实用价值.     

筒形旋压件内径尺寸精度预测

筒形件强力旋压中各工艺参数在生产中常用试旋的方法确定。本文用数值模拟方法给出了筒形件强力旋压时减薄率、进给比、旋轮工作角等对旋压件内径尺寸精度的影响规律，计算与试验结果一致。     

Ti55531钛合金筒形件的旋压成形

分析了成形参数对Ti55531钛合金筒形件旋压成形的影响规律。结果表明:采用880℃+保温30min/空冷的热处理可获得较好的强塑性匹配;当旋压温度为750~800℃时,金属流动性好,筒形件表观质量好,且随着旋压道次增加,旋压温度可适当降低,但不应低于650℃,旋压极限减薄率可达80%左右;进给比在0.45~0.78 mm/r取值,在开始道次中采用大点的进给比,使工件较好贴模,在最后道次中采用相对小的进给比便于工件脱模;道次减薄率在30%~45%时较为合适,有利于旋压成形。     

钛合金轮圈旋压的有限元模拟与试验

应用ANSYS/LS-DYNA软件对钛合金轮圈的旋压过程进行了有限元数值模拟,并开展了TC4钛合金热旋翻边的试验研究,基于此确定了钛合金轮圈合理的热旋成形方案。     

φ880mm发动机封头室温强力旋压研究

本文对φ880mm固体火箭发动机壳体的两种规格封头的首批试旋工作进行了总结。用D6AC钢室温强力旋压φ880mm的带法兰封头的过程中,在旋压坯的设计和加工、旋压芯模的设计和制造、工艺参数的选择、热处理制度的确定等方面,都获得了一些经验。 在封头壁厚一定的情况下,旋压坯的壁厚按其所处的半锥角的正弦规律变化;旋坯用型面必须与芯模很好贴合;每道次芯模确定的旋压减薄率取决于芯模的半锥角。文中给出的多道次旋压时道次减薄率与每道次芯模半锥角的关系式ε_1=1—sina_1/sina_(1-1),可用于制订旋压工艺及设计旋压芯模。     

TC4钛合金旋压成形工艺

通过对TC4钛合金旋压成形工艺技术的试验研究,分析了影响旋压成形和旋压件精度的因素,同时分析了旋压件的组织性能.试验结果表明,采用合理的旋压工艺及工艺参数,可以旋制较高精度的TC4钛合金零件,且旋压件材料组织性能提高,非金属成分含量仍满足标准要求.     

铝镁钪合金舱体内旋成形有限元分析

采用有限元法对带内环向加强筋铝镁钪合金筒形件旋压成形进行了数值模拟,分析了坯料应力应变分布状态和工艺参数对成形的影响.结果表明,轴截面坯料主要处于轴向伸长、径向压缩状态,内表面坯料处于轴向伸长状态;减薄率和进给比对成形影响显著,模拟分析减薄率不宜大于50％,进给比为0.5～2.0mm/r较佳.     

Ti-1023合金桨毂锻件变形过程有限元法模拟和分析

对三种不同毛坯的Ti-1023合金桨毂锻件的变形过程进行了有限元法模拟计算,分析和讨论了变形体流动充填模具的过程和等效应变、温度场分布、载荷变化及模具的表面应力等模拟计算结果,讨论了产生航空锻件有限元法模拟计算误差的原因,提出我国航空锻件变形过程模拟研究的主要方向包括集中在复杂形状的锻件变形过程模拟和晶粒生长、性能的预测上.     

Convex shaping process simulation during counter-rotating electrochemical machining by using the finite element method

In counter-rotating electrochemical machining(CRECM), a revolving cathode tool with hollow windows of various shapes is used to fabricate convex structures on a revolving part. During this process, the anode workpiece and the cathode tool rotate relative to each other at the same rotation speed. In contrast to the conventional schemes of ECM machining with linear motion of a block tool electrode, this scheme of ECM is unique, and has not been adequately studied yet. In this paper, the finite element method(FEM) is used to simulate the anode shaping process during CRECM, and the simulation process which involves a meshing model, a moving boundary,and a simulation algorithm is described. The simulated anode profiles of the convex structure at different processing times show that the CRECM process can be used to fabricate convex structures of various shapes with different heights. Besides, the variation of the inter-electrode gap indicates that this process can also reach a relative equilibrium state like that in conventional ECM. A rectangular convex and a circular convex are successfully fabricated on revolving parts. The experimental results indicate relatively good agreement with the simulation results. The proposed simulation process is valid for convex shaping prediction and feasibility studies as well.     

薄壁件周铣切削力建模与表面误差预测方法研究

薄壁件加工变形是影响加工精度与质量的关键因素,而切削力建模则是预测表面加工误差的基础。针对两种典型的切削力模型,系统地研究了薄壁件周铣加工过程中切削力变化及表面变形误差分布的有限元计算方法,提出了基于三维非规则网格的刀具/工件变形的耦合迭代格式以及恒定网格下材料去除效应的变刚度处理方法等关键技术,仿真过程充分考虑了切屑厚度变化及不同切削参数对预测结果的影响。以典型钛合金航空材料构件为例,数值计算结果与实验参考数据比较表明,两种切削力模型对同一切削过程的预测均具有很好的一致性。     

有间隙涡轮叶栅壁面流谱实验与数值模拟研究

对具有 3 .6 %相对叶顶间隙的涡轮叶栅进行了壁面流动显示和三维流场数值模拟 ,分析了大叶顶间隙涡轮叶栅的壁面流动特点 ,从数值模拟上特别对尾缘附近的壁面流动结构进行了详细讨论。实验与计算结果表明叶栅尾缘附近的流动是非常复杂的 ,同时由于叶顶间隙的存在 ,上下尾缘附近的壁面流谱明显不同     

基于ANN的FGH96合金热变形行为的模拟电路模型

在锻造领域,多采用数字模型进行工艺设计和过程控制,但数字模型无法完成材料成形过程的实时控制。因此,有必要建立一种适合于实时控制的材料动态流动行为模型,以提高生产效率和锻件质量。通过热模拟试验,对细晶态FGH96合金的高温流动特性进行了研究,用BP（Back Propagation）网络建立了FGH96合金热变形行为的人工神经网络模型,根据电模拟理论,利用模拟电路的快速反应与易于控制等特点,建立了基于ANN的FGH96合金的模拟电路模型。测试结果表明,所建立的ANN模型和模拟电路模型均具有较高的预测精度,能很好地反映材料热成形过程的动态流动行为,可用于材料热成形过程的实时控制。     

Formability enhancement in hot spinning of titanium alloy thin-walled tube via prediction and control of ductile fracture

The damage and fracture in hot spinning of titanium alloy is a very complex process under the combined effects of microstructure evolution and stress state. In this study, their dependences on processing parameters were investigated by an integrated FE model considering microstructure and damage evolution, and revealing the effects of microstructure and stress states on damage evolution. The results show that the inner surface of workpiece with the largest voids volume fraction is the place with...     

叶尖间隙对涡轮性能影响的计算与试验研究

采用电容型叶尖间隙测量系统,在国内首次对单级涡轮级性能试验状态下的转子叶尖间隙进行了实时测量,并利用获得的叶尖间隙热态试验数据,完善了涡轮转子叶尖间隙计算方法。同时,开展了变叶尖间隙的涡轮级性能试验,总结了叶尖间隙对涡轮性能的影响规律。另外,还对试验方案进行了数值模拟,并与试验结果进行对比分析,进一步研究了叶尖间隙对涡轮性能的影响。结果表明,电容型叶尖间隙测量系统具有较高的准确性,利用该系统有助于掌握叶尖间隙真实变化规律,提高试验安全;通过对叶尖间隙实时测量,可正确评估涡轮性能随叶尖间隙的变化规律,具有较高的工程应用价值。     

转速对高速旋转冲压增程弹用进气道影响数值模拟

结合分区对接网格技术以及二阶精度区域分解算法，对高速旋转、含侧向支柱冲压增程弹丸进气道内外复杂流场进行了数值模拟。得到了高速旋转工况下对应于不同来流攻角和旋转角速度，临界工况时，超声速进气道内外流场复杂的波系结构。随着旋转角速度的提高，进气道总压恢复系数和动能效率均有所降低，而流场畸变指数则显著增大。特别是当转速达到20kr／min，进气道总压恢复系数和动能效率下降趋势以及流场畸变指数增大趋势更明显。攻角的存在对冲压发动机进气道的总体性能产生了负面影响。     

材料参数对超塑性恒压充模胀形过程影响的数值分析

 采用大变形刚粘塑性有限元法模拟了超塑性恒压充模胀形过程，分析了应变速率敏感性指数m、应变硬化指数n和厚向异性指数R等材料参数对胀形件厚度分布、成形时间、等效应变场及胀形成形能力的影响；通过对铝合金LY12CZ板料的相应实验对模拟结果进行了验证。