涂层厚度对AZ91D镁合金WC涂层性能影响研究

采用JP-5000超音速火焰喷涂技术在AZ91D镁合金表面喷涂WC-10Co4Cr涂层。利用扫描电子显微镜、X射线衍射仪、显微硬度计等设备和浸泡腐蚀实验来分析WC涂层的组织结构和性能。结果表明：WC涂层均匀、致密,孔隙较少,涂层与基体结合紧密,无裂纹,无剥离;WC发生分解形成W2C,分解率与火焰作用时间有关;随涂层厚度的增加,涂层的显微硬度有增大的趋势;WC涂层提高了镁合金的耐腐蚀性。     

镁合金表面冷喷涂420不锈钢/WC-17Co涂层及其耐磨耐蚀性能

采用冷喷涂工艺在AZ80镁合金表面制备420/WC-17Co涂层。利用SEM分析喷涂粉末形貌及涂层显微结构;通过显微硬度计和万能材料试验机测定涂层的显微硬度和结合强度;采用球盘式摩擦磨损试验机考察涂层的摩擦磨损性能;通过电化学实验测定涂层和镁合金基材的耐腐蚀性能。结果表明:采用冷喷涂工艺可在AZ80镁合金基体上制备出高质量的420/WC-17Co涂层,冷喷涂420/WC-17Co涂层的显微硬度为(615±62)HV,结合强度为(57±11)MPa,涂层的磨损率为3.3×10~(–6) mm~3·N·m,其耐磨性较镁合金基材提高了2个数量级,涂层自腐蚀电流较镁合金基材降低了1个数量级。因此,冷喷涂420/WC-17Co涂层在不产生明显热影响的情况下,可以显著提高镁合金表面的耐磨耐蚀性能,是一种较为理想的镁合金表面强化工艺。     

不同工艺粉末对超音速火焰喷涂WC-10Co-4Cr涂层性能的影响

对比分析了采用烧结破碎和团聚烧结工艺制备的两种WC-10Co-4Cr粉末的物理性能和物相组成。采用超音速火焰喷涂技术对两种粉末进行了涂层制备,并对两种涂层的性能进行对比评价,结果表明:团聚烧结粉末制备涂层的硬度、孔隙率和抗冲蚀磨损性能均优于烧结破碎粉末制备涂层,但其结合强度略低于烧结破碎粉末制备涂层。     

三种热喷涂工艺制备NiCr/Cr_3C_2-BaF_2·CaF_2涂层的结构与性能

采用大气等离子喷涂、爆炸喷涂和超音速火焰喷涂三种热喷涂技术制备了NiCr／Cr3C2-BaF2·CaF2涂层,分析比较了涂层的显微组织、物相组成、孔隙率、硬度、结合强度及其摩擦学性能。结果表明,与大气等离子喷涂相比,超音速火焰喷涂和爆炸喷涂技术制备的涂层具有更高的致密度、硬度和结合强度。采用包覆法制备的粉末进行喷涂,碳化物失碳明显减少,涂层中氧化物含量低。三种NiCr／Cr3C2-BaF2·CaF2热喷涂涂层的摩擦系数都随着温度的升高而减小,爆炸喷涂和超音速火焰喷涂涂层的摩擦系数比等离子喷涂涂层的摩擦系数更低,耐磨性得到提高。高温下BaF2·CaF2润滑膜的形成均可有效降低三种涂层的摩擦系数,从而降低涂层和对磨球Si3N4的磨损率。     

HVOF制备CuNiIn涂层对TC4-DT钛合金抗微动磨损的改善

研究超音速火焰喷涂CuNiIn涂层对TC21钛合金疲劳性能的影响和TC4-DT钛合金微动磨损的防护行为.结果表明,超音速火焰喷涂制备的CuNiIn涂层致密均匀、与TC21基体结合良好,且对基体的疲劳极限影响不大;涂层防护前后,TC4-DT的微动磨损机理不同,使用前为切削磨损和磨粒磨损,使用后为粘着磨损和磨粒磨损;CuNiIn涂层可以有效改善TC4-DT的抗微动磨损性能,在本试验条件下,涂层使用前后磨损体积降低62％.     

TiC-TiB2复合相钛基稀土激光熔覆层组织与性能

采用通快同轴送粉4002光纤激光器,在TC4表面熔覆制备了不同含量Y₂O₃的TC4+Ni45+Co-WC+Y₂O₃钛基复合耐磨涂层。采用XRD、SEM、EDS、EPMA测试研究了涂层微观组织,利用显微硬度计、摩擦磨损实验机和白光轮廓仪分析评价了涂层的显微硬度和摩擦学性能。结果表明,涂层生成相不随Y₂O₃含量变化而改变,主要包括Ti₂Ni、TiC、TiB₂以及α-Ti;未添加Y₂O₃涂层,生成相尺寸粗大,方向性明显;随着Y₂O₃的加入,涂层组织逐步细化,生成相方向性减弱;当Y₂O₃为3wt%时,涂层析出相以颗粒和短棒状相为主,合成了大量TiC-TiB₂依附生长复合相,经二维点阵错配度计算,TiB₂（0001）与TiC （111）错配度δ为0.912%,TiC与TiB₂形成了共格界面,可有效增加涂层组织分布均匀性;Y₂O₃含量为0wt%、1wt%和3wt%时,涂层显微硬度逐渐减小,磨损体积先增大后减小,摩擦系数逐渐降低;在TiC-TiB₂复合相的作用下,3wt% Y₂O₃涂层的耐磨、减摩性最优,涂层磨损机理为磨粒磨损。     

助力器活塞杆表面裂纹的喷涂修复

采用爆炸喷涂WC-17Co工艺对助力器活塞杆表面出现的裂纹进行修复。爆炸喷涂WC涂层组织均匀、结合强度大于70MPa,显微硬度大于900Hv;活塞杆修复后裂纹消除,尺寸公差和密封性均满足要求,并已通过装配测试。     

NbC含量对激光熔覆不锈钢涂层组织和性能影响

本文采用激光熔覆技术在EA1T车轴钢表面制备了添加不同碳化铌（Nb C）含量的不锈钢涂层。利用X射线衍射仪（XRD）、扫描电镜（SEM）和能量色散光谱（EDS）分析了复合涂层的相结构和显微组织演变,并测定了涂层的硬度和摩擦学性能。结果表明,Nb C的加入起到了细化晶粒的作用,同时在晶间析出Fe(Nb,C)类硬质相。但Nb C的加入会导致涂层中树枝晶的方向性被破坏,但涂层性能增强,且随着Nb C质量分数的增加而提高。特别是当Nb C质量分数为20%时,添加的Nb C全部熔解,然后在晶间析出岛状硬质相。由于Nb C的添加引起细晶强化和弥散强化,显著提高了涂层的硬度和耐磨性。与未加Nb C涂层相比,加入质量分数20%NbC,硬度提高了15%,最高硬度为60HRC。磨损系数显著降低,强化效果最好。20%NbC的复合涂层磨损表面犁沟较浅,磨损机制为磨粒磨损。     

两种不同成分NiAl涂层性能的对比研究

采用双丝电弧喷涂在6061-T6铝合金基底上制备NiAl-95/05和NiAl-80/20涂层,利用标准测试方法测量涂层的机械性能,并提出了NiAl涂层摩擦磨损机理的新理论。结果表明：NiAl-80/20涂层具有较高的结合强度和显微硬度。随磨损进行,NiAl-80/20涂层的静摩擦系数随磨损的继续一直单调下降,直至最后进入稳态阶段;NiAl-95/05涂层的静摩擦系数先缓慢下降,200个循环之后由于磨损形貌的进一步恶化,静摩擦系数呈缓慢上升的趋势。NiAl-95/05涂层的磨损机制主要为磨粒磨损,并且在磨损过程中伴随有犁削效应;NiAl-80/20涂层主要为粘着磨损机制,并且具有更好的耐磨性。     

FeAlCrBSiNb非晶涂层形成机理和摩擦磨损行为

研发了一种FeAlCrBSiNb粉芯丝材,采用高速电弧喷涂技术在45钢基体上制备相应涂层.通过SEM,TEM和XRD表征涂层微观组织和相成分,阐述FeAlCrBSiNb非晶涂层的形成机理,利用显微硬度计,万能拉伸试验机和环-块式摩擦磨损试验机,分析涂层力学性能和摩擦磨损行为.结果表明:涂层主要由非晶相和弥散分布其中的α-(Fe),(Fe,Cr),CrB和Fe3Al微晶纳米晶相组成,非晶相体积含量大于91.3％;涂层呈层状结构,结构致密,总体孔隙率约为2％;平均显微硬度值为850 HV0.1,是基体45钢的4倍;优良的磨损抗力使其相对耐磨性是45钢的5倍,其磨损机制主要为剥落引起的剥落磨损.     

基于飞机油箱模型形状特征油量测量切片步长选择方法研究

 在分析飞机数字式油量测量过程中目前广泛使用的切片法油量测量原理的基础上,针对现有的定步长切片法无法得到准确、可靠的燃油质量特性数据库的缺陷,结合对飞机油箱模型形状特征的分析,提出了基于飞机油箱模型形状特征的油量测量切片步长选择方法。此方法包括切片步长整体和局部选择两个过程,整体选择以实现相邻两切片平面所夹油箱模型体积近似相等为目的来确定切片步长,以体现油箱模型截面整体变化规律;局部选择以设计切片平面与截面突变平面重合或尽可能接近的方式,突出油箱截面的局部变化特征。实验结果表明：该切片步长选择方法较定步长方法能够建立更为合理、可靠的燃油质量特性数据库,从而提高了油量测量精度。     

二维翼段颤振的μ控制

 采用超声电机作为作动器来实现含控制面的翼段颤振鲁棒抑制。针对作者设计的二维翼段颤振主动抑制系统，通过理论与实验相结合的方法，建立了考虑沉浮方向阻尼和作动器模型参数不确定性的控制系统模型，设计了μ控制器，并对控制器做了降阶处理。数值仿真和风洞试验表明，μ控制器可有效地抑制颤振的发生，将颤振临界速度提高23.4%。相对于H_∞控制器，μ控制器的控制效果和鲁棒性更好。     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

Abnormal Shape Mould Winding

为解决网格化芯模的缠绕问题,本文提出了复合材料面片缠绕机理;接着详细分析了面片缠绕过程中的芯模凹曲面上纤维滑线和架空现象,应用微分几何曲面理论和空间几何理论,提出判据及其解决方案;最后,针对飞机发动机进气道的缠绕成型,编制缠绕控制程序并进行相应的实验,验证了面片缠绕方法的可行性。     

基于H∞性能指标的质量矩拦截弹鲁棒控制

 以所建立的质量矩拦截弹数学模型为基础，利用微分几何的反馈线性化理论，得到一个解耦线性系统，考虑到拦截弹的鲁棒性要求和3个滑块的协调控制问题，提出采用双回路的设计方法，内回路采用线性二次调节器（LQR），外回路采用考虑混合灵敏度问题的H_∞控制设计。仿真结果证明了该方法动态性能满足设计要求，同时对系统参数的不确定性具有较强的鲁棒性。     

航天器返回地球的气动特性综述

航天器返回地球的飞行过程中,气动特性是实现将宇宙飞行速度减到落地前速度、保证再入飞行得到有效控制以及再入防热安全可靠的关键因素。针对简单旋成体气动外形、半弹道式再入控制、烧蚀防热类返回航天器,综述了返回地球过程中变化的空气流域特性、航天器周围的气体绕流环境、空气与航天器作用产生的动力学与热效应等。系统地给出了该类航天器的再入气动特性参数与飞行性能的共性规律,包括:气动阻力与再入减速、气动升力与再入轨迹控制、配平攻角与飞行稳定性、气动加热与防热,以及再入过程中不同气动特性航天器、气象条件变化等对再入飞行性能的影响规律。为航天器开展返回飞行过程的跨流域气动性能工程研制提供设计参考。     

基于马赫数分布可控曲面外/内锥形基准流场的前体/进气道一体化设计

提出了一种高超声速飞行器乘波前体的外锥形基准流场设计方法,在锥面马赫数分布规律给定的条件下,通过有旋特征线法实现反设计,提高了基准流场设计的灵活性。该基准流场通过锥形"下凹"弯曲激波和波后等熵压缩波系压缩气流,可以在较短的长度内完成高效压缩。基于反正切马赫数分布外锥形基准流场设计的乘波前体具有较高的容积率,乘波特性良好且出口均匀,设计点时有黏升阻比为1.89。另外,基于该乘波前体和马赫数分布可控的内收缩进气道给出了一种双乘波的前体与进气道一体化设计方案,实现了内外流分别独立乘波,充分发挥了乘波前体和内收缩进气道的各自优势。     

Potentials of manufacture and repair of nickel base turbine components used in aero engines and power plants by laser metal deposition and laser drilling

IntroductionExpensive turbine parts like HPT(HighPressure Turine)blades or vanes are replaced bynew parts in case of damage.For example theburn through of the inner side of a blade or vane(Figure 1)is a frequently appearing damage,which cannot be repaired…     

Enhancing the efectiveness of film cooling

Advanced gas turbine stages are designed to operate at increasingly higher inlet temperatures to increase thermal efficiency and specific power output.To maintain durability and reasonable life,film cooling is needed in addition to internal cooling,especially for the first stage.Film cooling lowers material temperature by forced convection inside film-cooling holes and by forming a layer of coolant about component surfaces to insulate them from the hot gases.Unfortunately,each cooling jet forms a pair of counter-rotating vortices that entrains hot gas and causes the film-cooling jet to lift off from the surface that it is intended to protect.This paper gives an overview of efforts to enhance the effectiveness of film-cooling.This paper also describes two new design concepts.One design concept seeks to minimize the entrainment of hot gases underneath of film-cooling jets by using flow-aligned blockers.The other design concept shifts the interaction between the approaching hot gas and the cooling jet to occur further above the surface by using an upstream ramp.For both design concepts,computational fluid dynamics results are presented to examine their usefulness in enhancing film-cooling effectiveness.      

Guide for Authors

<正>About Journal Chinese Journal of Aeronautics(CJA)is a comprehensive academic journal dealing with the fields of aeronautics and astronautics.It reports researches concerning the two fields in China and abroad to promote the academic exchange.Founded in 1988 and sponsored by the Chinese Society of Aeronautics and Astronautics and Beihang University,CJA publishes papers bimonthly,with issues released in February,April,June,August,October and December.