碳纳米管改性对碳/ 环氧复合材料层间性能的影响

研究了在碳纤维织物上生长碳纳米管的改性对环氧树脂基复合材料层间性能的影响,对比了有无碳纳米管的碳纤维复合材料的层间剪切和弯曲性能,并采用碳纤维表面结合碳纳米管膜的方法研究了碳纳米管对碳/环氧复合材料层间性能的影响。结果表明,由于生长的碳纳米管长度过长(10μm)、末端无序排列为笼状,树脂无法进入碳纳米管内部,碳纳米管无法发挥增强作用,同时由于碳纳米管过长,复合材料内部缺陷增多,使得四种生长碳纳米管的碳纤维复合材料层间性能均有下降;而碳纳米管膜与碳纤维和树脂基体结合较好,使得复合材料层间剪切强度提高12%。     

微纳粒子对高硅氧/酚醛烧蚀性能的影响

利用TalyScan150型表面粗糙度测试仪及其分析软件,对含有纳米碳粉、碳纳米管、复合碳纳米管、微米级磁性铁粉和不含微纳粒子的高硅氧纤维增强酚醛树脂复合材料的烧蚀表面进行了测试和分析,研究了材料的烧蚀特性与所引入的微粒子高温结构性能的对应关系.结果表明,微纳粒子自身的高温结构稳定性直接影响材料的烧蚀性能,含有高温结构稳定的纳米碳粉、碳纳米管、复合碳纳米管的试样,其烧蚀性能较不合微纳粒子的试样有明显提高,烧蚀表面粗糙度也有显著改善;含有高温结构稳定性差的微米级磁性铁粉试样的烧蚀性能较不含微纳粒子的试样明显恶化,烧蚀表面的粗糙程度明显增大.其机理是高温结构稳定的微纳粒子通过自身的耐高温特性及其对材料结构的增强作用提高了材料抵抗了高温气流冲刷的能力.     

热处理前后包覆Co及Co/Fe碳纳米管电磁性能的研究

表面包覆金属Co及Co-Fe多壁碳纳米管是一种比重较轻的电磁吸收剂,通过对包覆金属Co及Co/Fe的多壁碳纳米管进行700℃下的热处理,研究了对其电磁性能的影响。分别采用场发射扫描电子显微镜(FE-SEM)、X射线能谱仪(EDX)和X-射线衍射仪(XRD)对包覆Co和Co/Fe碳纳米管表面组成和结构进行了表征;用网络矢量分析仪和振动样品磁强计(VSM)对Co和Co/Fe包覆的碳纳米管的电磁性能进行了测试,并通过计算分析了其微波吸收性能。结果表明热处理能改善包覆Co和Co/Fe的碳管在高频范围的微波吸收性能,并提高其饱和磁化强度,降低矫顽力。     

镀钴碳纳米管/环氧树脂基复合材料的制备及其微波吸收特性研究

采用化学镀法制备了表面镀钴的多壁碳纳米管，并将其均匀分散在环氧树脂基体中固化成膜，形成镀钴碳纳米管／环氧树脂基复合材料。采用透射电镜、X射线衍射及振动样品磁强计等对镀钴碳纳米管的形貌、微结构与磁性能进行了表征，还采用数字化网络分析仪对该复合材料在0．5～40GHz频段内的微波吸收特性进行了研究。结果表明：在相同的碳管质量分数(1％)和吸波介质层厚度(2．0mm)等条件下，与纯碳纳米管相比，表面镀钴碳纳米管的吸收峰往高频方向移动，吸收强度略有增加，但吸收频带并没有宽化趋势。     

碳纳米管的表面功能化研究:接枝环氧基聚合物

通过共价键修饰将酸化的多壁碳纳米管(MWNTs)与环氧树脂进行接枝反应,并通过傅立叶变换红外光谱(FTIR)、X射线衍射(XRD),拉曼光谱(Raman spectra),热失重分析(TGA)和透射电镜(TEM)对其进行表征.研究发现,酸化处理在多壁碳纳米管管壁产生羧基、羟基,并检测到环氧树脂是通过共价键接枝到多壁碳纳米管管壁上,其接枝率达到39%.差示扫描晕热仪(DSC)显示改性的多壁碳纳米管对环氧树脂的固化反应有显著的影响.     

镀镍碳纳米管的制备及电磁性能

将碳纳米管经过纯化、敏化、活化处理后,采用化学镀方法制备镀镍碳纳米管,利用DSC分析出合适的热处理温度,然后在惰性气体保护下进行退火处理.利用TEM、EDS、XRD对退火前后镀镍碳纳米管的形貌、元素组成、结构进行表征.结果表明:碳纳米管表面被成功镀上了一层镍磷合金,热处理后镀层更光滑,并发生晶化反应得到晶态镍,使得电磁性能得到较大提升.电性能测试表明,镀镍碳纳米管的电导率为450 S/m,热处理后提高到1400 S/m.磁性能测试表明,镀镍碳纳米管热处理前后均表现为软磁性,热处理前饱和磁化强度为2.753 emu/g,热处理后提高到11.254 emu/g.     

基于碳纳米管薄膜的复合材料层间增韧

通过浮动催化化学气相沉积法制备连续碳纳米管薄膜，并将其原位沉积到单向碳纤维织物表面，手工铺层后借助真空辅助树脂传递模塑成型（VARTM）工艺制备碳纳米管-碳纤维/环氧树脂复合材料层压板，研究不同面密度的碳纳米管薄膜对层压板Ⅱ型层间断裂韧性的影响。结果表明，随着碳纳米管薄膜面密度的增加，层压板Ⅱ型层间断裂韧性先逐渐提高，当碳纳米管薄膜面密度为9.64 g/m²时，层压板Ⅱ型层间断裂韧性最佳，与原始层压板相比提高了94%。碳纳米管通过桥接树脂裂纹、从树脂中拔出等方式提高层间断裂韧性。当碳纳米管面密度超过临界值时，会引起树脂浸润困难，导致增韧效果降低。     

电子束固化PVP 非共价功能化碳纳米管/ 环氧树脂

先制得PVP非共价功能化的多壁碳纳米管(MWNTs),而后利用电子束辐射固化制备PVP功能化的MWNTs(PVP-MWNTs)/环氧树脂复合材料。对PVP-MWNTs进行FTIR光谱表征及热重分析,表明碳纳米管表面有PVP包覆,PVP功能化的MWNTs的碳纳米管在环氧树脂中有良好的分散性。对电子束固化的复合材料进行拉伸性能测试,1.0wt%PVP-MWNTs/环氧树脂复合材料的拉伸模量较纯环氧树脂提高25%。动态力学性能分析表明添加PVP-MWNTs提高了环氧基体的储能模量。     

电化学合成法修饰高模碳纤维表面

采用电化学合成法,分别以对氨基苯甲酸/双酚A(PABA/BPA)、对氨基苯甲酸/聚乙二醇600(PABA/PEG600)为反应体系,修饰高模碳纤维(HMCF)表面;研究了这两种体系下的连续电化学合成工艺,以及反应电位对HMCF性能的影响.通过SEM照片可见,HMCF经PABA/BPA体系修饰后表面存在化合物涂层;由红外光谱分析证实,表面化合物的红外谱图中存在明显的酯基峰.层间剪切强度(ILSS)结果表明,经PABA/BPA体系修饰过的HMCF复合材料的ILSS可达到73.1 MPa,表明PABA/BPA体系对HMCF具有较好的修饰效果.     

对苯二胺功能化多壁碳纳米管的制备与表征

通过将浓硫酸和浓硝酸处理过的多壁碳纳米管（MWNTs）与SOCl2回流进而与对苯二胺（p-PDA）反应,得到了p-PDA功能化的多壁碳纳米管（p-MWNTs）。首次采用Raman光谱、X-射线光电子能谱（XPS）、透射电子显微镜（TEM）、热重分析（TGA）对p-MWNTs的结构和性能进行研究。结果表明：化学修饰过程没有过多地降低p-MWNTs表面石墨片层的结构规整度,苯胺基团以3.7%的表面含量通过酰胺键连接到p-MWNTs表面;p-MWNTs在200-500℃范围内热失重9.47%,间接地证明了苯胺基团通过化学键连接在p-MWNTs的表面;经化学修饰反应后,有较多的缺陷和不导电的有机官能团分布在p-MWNTs表面,但p-MWNTs仍具有71.69 S/cm的室温电导率。     

KH550修饰碳纳米管增韧环氧树脂的研究

利用偶联剂KH550对多壁碳纳米管(MWCNTs)进行化学修饰,并制备了MWCNTs/环氧树脂纳米复合材料.研究了不同含量的MWCNTs对纳米复合材料力学性能的影响.研究结果表明,MWCNTs表面成功接枝上了一定量的KH550,将其加入环氧树脂基体可大幅提高复合材料的力学性能.当添加量达到0.5%时,复合材料的力学性能最好,冲击韧度和弯曲强度较纯环氧树脂分别提高了85.3%和21.6%.扫描电镜结果显示,复合材料由脆性断裂转变为韧性断裂.     

碳纳米管增强复合材料研究进展

介绍了碳纳米管的结构、性能等特点，综述了碳纳米管在金属基复合材料、聚合物基复合材料和陶瓷基复合材料中的应用研究情况，并对今后碳纳米管复合材料的发展趋势进行了展望。     

Carbon nanotube protected composite laminate subjected to lightning strike: Interlaminar film distribution investigation

A kind of interlaminar film with carbon nanotubes inserted into polyether ketone with cardo was used for lightning strike protection of composite laminates. The distribution of the interlaminar film was investigated by experimental and numerical methods. Artificial lightning strike tests were conducted for 12-film carbon nanotube and traditional surface silver coating protected specimens. Then corresponding finite element models (FEMs) were established to analyze the lightning strike effect and validated by the experimental results. Based on the FEMs, the number, distribution and thickness of interlaminar film were investigated in order to obtain equivalent protection effect with the traditional surface silver coating. The results show that only the first two layers were damaged for the surface silver coating protected specimen, while 5 layers were ablated for the 12-film protected specimen. Lightning strike damage area of the laminate protected with 5-film carbon nanotube is almost the same as that of the laminate protected with 12-film carbon nanotube. Compared with traditional surface silver coating protection, one film protection with thickness of 360 μm can make the laminate to obtain equivalent damage depth, 54.8% smaller damage area and 58% less additional weight. And reparability of the laminate is better than that of the laminate protected with 5 interlaminar films.     

碳纳米管对环氧树脂力学性能的影响

用浇铸成型法制备了碳纳米管／环氧树脂复合材料，研究了其力学性能，并探讨了该材料的微观结构与性能之间的关系。结果表明，碳纳米管对环氧树脂具有明显增强增韧作用。在碳纳米管加入量为3.0％(质量分数)时，复合材料的综合性能较好，拉伸强度、拉伸模量及断裂伸长率较纯树脂分别提高了90％-100％、60％-70％、150％-200％。     

Studies of Electromagnetic Properties of MWCNTs after Electroless Plating with Co-Fe Alloy

A method of electroless plating is utilized to deposit Co-Fe alloy on the surface of multi-walled carbon nanotubes (MWCNTs), and electromagnetic parameters of MWCNTs with and without electroless plating are discussed. The MWCNTs covered by Co-Fe is a desirable light absorbent in wide wave band by utilizing electroless plating process in experiments. Field-emission scanning electron microscope (FESEM) and field-emission transmission electron microscope (FETEM) images as well as energy dispersive spectroscopy (EDS) results are presented to show the morphology, components and electromagnetic parameters of MWCNTs. Electromagnetic properties of MWCNTs are enhanced after electroless plating observed from contrast of results between MWCNTs with and without plating. In conclusion, the covering Co-Fe on the surface of MWCNTs in 2-18 GHz frequency range has better electromagnetic properties. When the material is in the 6.5 GHz electromagnetic waves, the reflection loss is up to ?10 dB, and the bandwidth more than ?4 dB is 5 GHz. The excellent electromagnetic properties make it probable for MWCNTs to be utilized as absorbent in electromagnetic shielding materials.     

MWCNT/ E 复合材料的制备及性能

利用三辊研磨分散技术制备了MWCNT/ E 复合材料。通过调节三辊研磨机入料辊和中辊的间
距,使MWCNT 在环氧树脂中均匀分散。所制备的MWCNT/ E 复合材料与纯环氧树脂相比,拉伸强度提高了
22%,弯曲强度提高了15%,导电性和导热性都得到明显改善。     

冷等离子体处理对碳纤维缝编织物/环氧复合材料界面性能的影响

采用冷等离子体对碳纤维缝编织物进行表面处理 ,并采用XRD对处理前后的碳纤维表面结构进行了分析 ,研究了冷等离子体处理对浸润性以及碳纤维缝编织物 /环氧复合材料的层间剪切强度的影响。实验结果表明 ,冷等离子体处理提高了碳纤维表面活性、浸润性 ,从而改善了碳纤维缝编织物 /环氧复合材料的界面粘结性能 ,进而改善了复合材料的界面性能。     

冷等离子体接枝处理对碳纤维织物／环氧复合材料界面性能的影响

采用冷等离子体接枝法对碳纤维织物进行表面处理,在纤维表面产生活性官能团,研究了冷等离子体接枝处理对碳纤维织物/环氧复合材料的层间剪切强度的影响。实验结果表明,冷等离子体接枝处理提高了碳纤维表面活性,从而改善了碳纤维织物/环氧复合材料的界面粘结性能,进而改善了复合材料的界面性能。     

纤维表面状态对C/C-SiC复合材料微观组织和相成分的影响

为了研究纤维表面状态对C/C-SiC复合材料微观组织和相成分的影响,将T300碳纤维在氮气氛围中进行不同温度的热处理后,采用液硅熔渗法制备了C/C-SiC复合材料。采用光电子能谱(XPS)对纤维表面成分进行了分析。结果表明:未处理纤维表面具有较高的氧含量,随着热处理温度的升高,纤维表面氧含量逐渐降低,导致纤维表面含氧官能团数目减少。扫描电镜(SEM)观察发现:未处理纤维增强的C/C预制体,孔隙尺寸较大且孔隙率低;而经1 500℃热处理纤维增强的预制体,孔隙尺寸较小但孔隙率高。随后对C/C预制体进行液硅熔渗处理,并对熔渗反应过程分析发现:由未处理纤维增强的预制体,液硅熔渗反应主要受溶解-沉淀和界面限制的扩散反应过程控制,获得的C/C-SiC复合材料中SiC基体相分布规则且含量较低,同时含有较高的残留Si;而经1 500℃热处理纤维增强的预制体,熔渗反应则主要受溶解-沉淀过程控制,获得的C/C-SiC复合材料中SiC基体含量多且分布较均匀,残留Si含量较少。