This paper deals with three-point flexure tests on hybrid I-and P-beams,made out of multi-layer carbon fiber/epoxy resin(including twill woven fabric CF3031/5284 and unidirectional cord fabric U3160/5284)reinforced composites,processed using the RTM(resin transfer molding)technique.Static bending properties were determined and failure initiation mechanism was deduced from experimental observations.Failure mode of the tested hybrid RTM-made I-beams can be reckoned to be characteristic of the delamination from the cutout edge within the web and the debonding propagation along the interface between the inverted triangular resin-rich zone and the adjacent curved web until local buckling within the curved webs around the conjunction fillet region.In contrast,as distinct from hybrid RTM I-beams subjected to three-point bending loading,hybrid RTM-made P-beams in three-point flexure tests experienced the resin debonding in the inverted triangular resin-rich zones and the debonding propagation along the interface between the inverted triangular resin-rich zone and the adjacent curved web until complete separation of the curved web from the flange.Progressive damage models(PDMs)were presented to predict failure loads and process of hybrid RTM-made I-and P-beams under three-point flexure.Good correlation was achieved between experimental and numerical results.     

复合材料十字型接头力学性能实验研究与数值模拟(英文)

通过拉伸和剪切试验,研究了3种不同的树脂转型模型(RTM)成型工艺(即RTM、引入缝纫的RTM和共胶接)对复合材料十字型接头力学性能的影响。根据实验现象,分析和讨论了其破坏机理。实验结果表明,3种工艺中,RTM成型的十字型接头力学性能最优,胶接和缝纫工艺都会对接头的强度产生不同程度的影响。通过有限元分析,数值模拟了RTM十字型接头的破坏过程,与实验现象吻合良好。     

固体火箭发动机壳体复合裙RTM成型技术

树脂传递模塑工艺(RTM)可实现复合材料承力构件高表面质量净尺寸成型。以A配方为树脂基体、3K缎纹碳布为增强材料,采用RTM工艺制备了固体火箭发动机壳体复合裙。分析了A配方的RTM工艺特性及树脂浇铸体性能,介绍了复合裙注射模具和注射设备,讨论了RTM工艺参数及复合裙材料性能。结果表明:RTM复合裙纤维体积分数达54. 5%,联合载荷(轴压+弯矩)条件下轴压达748 kN,弯矩达94 N·m;纯轴压载荷达1 062 kN,纯弯矩载荷达143. 1 N·m,壳体复合裙整体强度高,满足设计和使用要求。     

固体火箭发动机喷管用树脂基烧蚀防热材料研究进展

从材料和成型两个方面介绍了树脂基烧蚀防热材料的研究进展情况。主要包括基体材料、增强材料,以及模压、缠绕、铺放与RTM成型工艺的研究情况。     

复合材料帽型筋条脱粘的失效机理分析

复合材料加筋结构承受后屈曲载荷时,蒙皮局部屈曲会导致筋条承受面外弯曲载荷,极易引起蒙皮与筋条的界面脱粘,最终导致结构破坏.通过四点弯曲试验模拟加筋结构受后屈曲载荷时的蒙皮/筋条界面性能,建立渐进损伤模型,分别考虑筋条与蒙皮胶接界面以及复合材料层板的失效,并引入材料刚度退化模型,详细分析蒙皮/筋条界面的脱粘机理和失效过程.分析结果与试验结果一致,表明加载跨距对于结构的失效形式影响较大,90 mm加载时,胶层均首先失效于筋条与蒙皮内角处的胶接界面,且主要受Ⅱ型剪切模式影响;而150 mm加载情况下胶层均首先失效于翼缘自由端与蒙皮交界处.正向加载时胶层失效主要受Ⅰ型和Ⅱ型混合模式影响,反向加载胶层主要受Ⅱ型剪切模式影响.界面脱粘以后,随着载荷增加,筋条腹板与缘条转角外侧出现分层破坏,损伤模型预测结果与超声扫描检测结果一致.     

三维浅交弯联机织复合材料弯曲性能的有限元分析

借助Pro/Engineer绘图软件,建立三维浅交弯联机织复合材料及弯曲压头的结构模型,进行弯曲性能研究。借助ANSYS Workbench有限元软件,探究复合材料在5 mm弯曲位移载荷作用下纤维、树脂和复合材料的应力、应变分布,并对复合材料的破坏模式进行预测。结果表明:三维浅交弯联机织复合材料在弯曲载荷的作用下,试样与上、下压头接触处最容易发生弯曲破坏;三维浅交弯联机织复合材料在承载弯曲载荷时,增强体纤维起到主要承载作用,树脂基体起次要承载作用;在5 mm的弯曲载荷作用下,复合材料的破坏模式主要是树脂的破碎。     

三维全五向编织耳片接头力学性能试验研究

通过单向静力拉伸试验研究了三维全五向编织复合材料耳片接头的力学性能。试件选用T700-12K碳纤维采用四步法编织预制件,以TDE-85环氧树脂为基体,经树脂传递模塑（RTM）工艺固化成型。对两种几何尺寸、两种孔加工方式（编织预留孔和机械制孔）的三维全五向编织复合材料耳片接头试件的力学性能进行了试验研究。试验结果表明,同尺寸三维全五向编织预留孔接头的承载力是机械制孔接头承载力的6倍;对相同孔径及厚度的耳片,增大耳片宽度能大幅提升耳片承载力,但并不能显著提高其初始破坏载荷。     

复合材料编织接头承载能力的试验研究

 试验研究了用于航空结构的三维整体编织复合材料单耳承力接头在静载条件下的承载能力与破坏模式。单耳接头试样采用RTM(Resin Transfer Molding 树脂传递模塑)工艺制成，重点研究了由3种编织工艺（三维四向、三维五向和三维六向）、2种连接孔加工方式（机械钻孔和编织孔）、2种几何外形所组成的10组三维编织复合材料单耳承力接头的破坏机理与破坏载荷。对其在航空结构中的可应用性做出了评估。     

不同纤维预制体结构对SiC_f/PyC/SiBCN复合材料力学性能的影响

使用不同织造方式(二维机织,法向增强2.5维机织和三维五向编织)制备了3种SiC纤维预制体,采用树脂转移模塑(RTM)和聚合物浸渍裂解(PIP)工艺制备了SiC_f/PyC/SiBCN复合材料。观察复合材料的显微组织,测试弯曲强度、拉伸强度、压缩强度等力学性能,探究不同预制体结构对复合材料力学性能的影响行为。结果表明:同一预制体结构在不同方向的纤维分布不同导致材料力学性能的各向异性;不同预制体结构对材料力学性能有着显著的影响。     

Thermo-mechanical properties of RTM-made carbon fibre/polyimide composite attaching collar under transient heating

This study focuses on the thermo-mechanical properties of Carbon Fibre/Polyimide Composite (CFPC) attaching collars under transient heating. The CFPC attaching collars were fabricated by a high-temperature resin transfer moulding process, and their thermo-mechanical properties under the conditions of simultaneous transient heating and bending load were investigated. The results show that the attaching collar tends to fail at 118% of the limit load. The failure mode includes the fracture of the connecting screws, local extrusion damage of the hole edges, and slight ablation damage at the outer plies. And there is no observable residual deformation in the composite attaching collar. Furthermore, considering that the material properties vary with temperature, a progressive damage model based on the sequential thermo-mechanical coupling method was established to study the failure mechanism of the attaching collar. Finally, the damage factor of the CFPC was calculated to assess the safety status of the attaching collar. The results show that the primary damage modes of the composite attaching collar are intralaminar failure, which mainly occurs at the heat insulation layer and the hole edges, and these slightly affect the structural bearing capacity. A good correlation between the experiment and FEA is obtained. The test methods and analysis models proposed contribute to the safety assessment of composite structures under transient heating.     

RTM成型聚酰亚胺复合材料的热氧老化特性

采用树脂传递模塑(RTM)工艺制备了U-3160碳纤维增强HT-350RTM聚酰亚胺树脂基复合材料(U-3160/HT-350RTM),研究了不同老化温度、老化时间下U-3160/HT-350RTM复合材料的失重率的变化规律,建立聚酰亚胺复合材料老化失效特征与老化时间/老化温度的关系,并通过微观形貌分析阐述了其在热氧老化过程中的失效机理。结果表明:在一定温度下复合材料的失重率变化符合三次多项式的变化规律,复合材料的老化在材料近表面尤为明显,由于氧分子作用,聚酰亚胺树脂发生降解导致孔隙率增加,因此温度越高、老化时间越长老化加速现象越明显。     

复合材料结构长桁端头设计

现代民用飞机结构中大量采用复合材料长桁,而其材料性能和工艺特殊性会导致在使用过程中经常出现长桁和蒙皮分离现象。为了提高脱胶起始载荷,通过有限元方法分别对长桁末端腹板斜削设计和增加长桁末端附近缘条面积设计进行研究分析,总结出了复合材料结构长桁端头细节设计诸多有意义的结论。     

复合材料梁腹板不同开孔形式稳定性研究

由于工艺性、维护性等要求,复合材料结构梁腹板中不可避免需开孔,不同形式的开孔有着不同承载能力。通过对梁腹板结构不同形式的开孔进行剪切载荷下屈曲试验研究,得到屈曲载荷和破坏载荷,对比不同开孔对结构承载的影响,并通过有限元进行数值模拟分析,屈曲载荷和试验基本吻合。同时试验得到复合材料结构有较强的后屈曲承载能力。     

RTM工艺用耐高温树脂研制

以某飞行器透波结构件对材料的要求为背景，研制了可用于RTM成形工艺的耐高温树脂SH。SH树脂100℃下8h后粘度仅200mPa.s，适于RTM工艺成形；该树脂耐热性良好，玻璃化转变温度Tg为269℃，430℃热失重仅为10％；石英纤维／SH树脂腹合材料300℃时的弯曲强度σb＝139MPa，弯曲模量Eb＝9．5GPa，可在300℃以上短时使用。     

RTM 成型工艺及其派生工艺

简述了传统RTM工艺的成型原理和树脂工艺参数,详细介绍了两种常见的RTM派生工艺:真空导入模塑工艺、柔性辅助RTM工艺。展望了通过降低树脂黏度和成型工艺改进的两种方法,使RTM工艺更广泛的应用于航空航天等领域。     

航空发动机用复合材料支架成型工艺探索

针对航空发动机的特殊使用要求,通过树脂体系选择、增强体编织设计与制造、模具设计与制造、零件试验件的制造及性能试验等工作,对航空发动机用复合材料支架的制造工艺进行探索,为进一步推广复合材料在我国航空发动机上的应用进行技术储备.     

Temperature effect on buckling properties of ultra-thin-walled lenticular collapsible composite tube subjected to axial compression

This paper seeks to outline the temperature effect on the buckling properties of ultra-thin-walled lenticular collapsible composite tube(LCCT) subjected to axial compression.The buckling tests of the LCCT specimens subjected to axial compression were carried out on INSTRON-500 N servo-hydraulic machine in dry state and at the temperatures of 25 C, 100 C and 80 C. The load–displacement curves and buckling initiation loads were measured and the buckling initiation mechanism was discussed from experimental observations. Experiments show that the buckling initiation load, on average, is only about 2.2% greater at the low temperature of 80 C than at the room temperature of 25 C due to the material hardening, demonstrating an insignificant increase in the buckling initiation load, whereas it is about 19.5% lower at the high temperature of 100 C than at the room temperature owing to the material softening, implying a significant decrease in the buckling initiation load. The failure mode of the LCCT in axial compression tests at three different temperatures can be reckoned to be characteristic of the buckling initiation and propagation around the central region until rupture. The finite element(FE) model is presented to simulate the buckling initiation mechanism based on the eigenvalue-based methodology. Good correlation between experimental and numerical results is achieved.     

不同筋条刚度下复材加筋板剪切稳定性分析

在面内纯剪切载荷作用下,复合材料加筋壁板易丧失稳定性。通过试验与有限元仿真方法研究不同筋条刚度配比对复合材料加筋壁板屈曲及后屈曲行为的影响。试验中采用莫尔云纹观测法对试验件的屈曲模态进行定性观测,根据试验数据对试验件屈曲承载能力进行评估。研究结果表明:在保持筋条横截面积不变,只改变下缘条宽度和腹板高度的情况下,随着腹板高度的增加(下缘条宽度减小),筋条相对蒙皮的惯性矩增大,屈曲载荷逐渐减小;筋条刚度对屈曲载荷影响较大,对破坏载荷影响很小。有限元模拟结果与试验结果吻合较好。     

碳纤维复合材料在发射装置上的应用研究

机载弹射发射装置轻量化设计是现阶段机载武器系统重要的研究课题和难题,碳纤维复合材料应用于制造具有复杂外形的承力结构件,对于航空武器的轻量化设计具有重要意义。选取机载弹射发射装置的典型结构作为研究对象,首先通过结构优化设计和RTM成型工艺获得复合材料结构件;然后,经过各项结构件的试验和整机试验验证,结合应变测量数据,证明其强度满足设计要求,且获得了显著的减重效果。通过对复合材料典型结构件的研究,为其在发射装置领域的应用提供理论指导和依据。     

碳纤维复合材料短梁剪切疲劳特性

研究了碳纤维增强双马来酰亚胺复合材料的层间剪切静态与疲劳加载性质,分析了不同基体、不同铺层界面对层剪性质的影响。给出了层剪疲劳加载的S-N曲线;讨论了层间剪切损伤和增强机理,观察了微观特征。与碳/环氧复合材料相比,双马来酰亚胺基体复合材料在碳纤维和基体之间粘接良好,从而改进了纤维抗疲劳裂纹扩展的能力。