通过添加含卤-锑的阻燃剂、芳纶纤维和增塑剂,研制了一种耐低温无石棉的丁腈绝热层配方 (TI506)。研究了芳纶纤维和增塑剂对绝热层静态烧蚀性能和Tg 的影响,对绝热层材料力学性能、比热容、热 导率等性能进行了测试。结果表明:芳纶纤维浆粕用量为10 ~15 份、芳纶短纤维用量为4 ~6 份时,绝热层烧 蚀性能最佳,线烧蚀率达到45 μm/ s,所选增塑剂DOS 用量为10 份、DBP 或ATBC 用量为20 份时,Tg 可达- 40℃,芳纶纤维制备的丁腈绝热层力学性能及烧蚀性能优良,并满足固体火箭发动机耐-40 ~60℃的环境。     

三元乙丙橡胶内绝热层与纤维织物复合技术研究

研究了三元乙丙橡胶内绝热层分别与高硅氧纤维、芳纶纤维及碳纤维织物复合后绝热层的烧蚀性能.结果表明:绝热层与纤维织物复合可以提高绝热层的烧蚀性能;在这三种复合方法中,前两种织物分别铺设在绝热层表面的烧蚀性能优于将织物铺设在绝热层内部,后一种织物铺设在绝热层内部的烧蚀性能优于将织物铺设在绝热层表面;相比较而言,加入芳纶纤维织物绝热层的烧蚀性能最好,碳纤维织物绝热层的次之.高硅氧纤维织物绝热层的最差.     

固体火箭冲压发动机补燃室绝热层烧蚀试验方法

基于自主研发的氧-煤油烧蚀试验系统,发展了一种用于固体火箭冲压发动机补燃室热结构及材料烧蚀研究的试验方法。采用该方法开展了某型室温硫化硅橡胶基绝热材料的烧蚀试验,试验分别在含氧化铝粒子侵蚀和无粒子侵蚀条件下进行,并根据SEM图对比分析了粒子对材料表面微观形貌的侵蚀效应。结果表明:无粒子侵蚀条件下的试样经烧蚀后膨胀并分层,其平均线烧蚀率为-0.025mm/s;而粒子侵蚀条件下的试样平均线烧蚀率为1.901mm/s,试样中心区域的陶瓷层被粒子完全破坏,只留下极薄的热解层和裸露的碳纤维端部,碳纤维周围的基体主胶、颗粒填料及芳纶纤维均被高速焰流氧化剥离,充分说明粒子对绝热层材料的强剥蚀破坏效应;同时也验证了该方法能较好地模拟固冲发动机补燃室内的烧蚀热环境,可用于材料配方的筛选和耐烧蚀性能测试。      

耐烧蚀、低密度三元乙丙橡胶绝热层的研制

采用过氧化物硫化体系，芳纶纤维和耐烧蚀树脂作为耐烧蚀填料，阻燃剂为无卤的含磷阻燃剂，并通过L9(3^3)正交实验确定了含磷阻燃剂、耐烧蚀树脂、气相二氧化硅的最佳用量分别为25份、15份、15份。确定最佳配方和工艺生产出的三元乙丙橡胶绝热层密度为1．06—1．07g／cm^3，线烧蚀率为0.099mm／s，质量烧蚀率为0．043g／s，满足了某固体火箭发动机燃烧室内壁绝热层的技术要求。     

稠密粒子流作用下三元乙丙绝热材料烧蚀性能分析

为研究稠密粒子流作用下三元乙丙绝热层材料TI117的烧蚀性能,采用基于地面模拟试验发动机完成了18发烧蚀试验。通过分析试验数据,认为针对TI117绝热材料存在一个粒子冲刷速度临界值vcri=28m/s,当粒子流速度小于vcri时,粒子流状态参数对绝热层炭化烧蚀影响较小,当粒子流速度大于vcri时绝热层烧蚀率随粒子冲刷速度的增加增幅较快,粒子冲刷角度的影响也显著。通过分析颗粒浓度、冲刷速度和角度等随烧蚀试验状态的变化规律,结合试验数据进行回归分析,给出了三元乙丙绝热材料TI117在两种冲刷状态下的烧蚀率工程预示模型。通过分析芳纶纤维铺设方向对TI117绝热层烧蚀的影响,认为两种铺设方向下烧蚀结果基本一致,严酷条件下芳纶纤维垂直铺设优于平行铺设。     

双脉冲固体发动机燃烧室EPDM绝热层烧蚀性能实验研究

双脉冲发动机工作时燃烧室内部热环境复杂,对内绝热层设计提出很高要求,但对双脉冲发动机燃烧室内EPDM绝热层的烧蚀性能研究较少。为此,本文提出了工作时间为15s和两次点火工作时间为7.5s+7.5s的发动机实验方案,以研究双脉冲固体发动机燃烧室内EPDM绝热层的烧蚀性能。采用SEM电镜扫描、微米CT测试分析获得了烧蚀试件的表面宏观形貌、炭化层表面和断面微观形貌以及炭化层三维构型;利用测厚仪测量结果计算了试件的烧蚀率。结果表明,在总工作时间相等的情况下,双脉冲发动机中EPDM绝热层的烧蚀率比传统发动机大;与传统发动机中单次热冲击下烧蚀后试件相比,双脉冲发动机二次热冲击下烧蚀后试件的炭化层厚度减小约50%,总体孔隙率增大约13%;烧蚀表面致密层的致密程度也有所减小。双脉冲发动机工作时,EPDM绝热层的烧蚀性能在二次热冲击下发生较大变化,需在燃烧室内绝热层的设计过程中予以重视。     

过载条件下不同配方体系绝热材料筛选及烧蚀特性

以国内某发动机在飞行过载下绝热层的异常烧蚀为研究背景,基于地面过载模拟装置,模拟了飞行过载条件下的颗粒冲刷状态参数,针对不同配方体系的绝热材料开展了筛选试验以及烧蚀特性研究,实验获得了三种材料的最大炭化烧蚀率和质量烧蚀率,筛选出了实验条件下抗颗粒冲刷能力较强的绝热材料,并针对实验后绝热材料的炭化层进行了电镜扫描分析,结合绝热材料配方开展了抗烧蚀特性分析。研究结果表明：（1）在实验条件下,材料B的炭化烧蚀率和质量烧蚀率均最大,材料A的居中,材料A1的最小,材料A1的抗颗粒冲刷性能最佳;（2）由于芳纶纤维的原位成炭特性,决定了三元乙丙/芳纶纤维体系绝热材料的炭化层具有一定结构强度,而恰当的纤维和SiO2含量将会增强绝热材料的抗烧蚀性能;（3）根据研究结果,建议在工艺允许的情况下,可以考虑研制同时采用芳纶纤维和石棉纤维的绝热材料体系,在针对颗粒冲刷条件时,炭化层内即有可以形成骨架结构的芳纶纤维,又可以利用石棉纤维在受热分解时SiO2和MgO熔融后和纤维以及基体之间的粘结交联效应。     

固体火箭冲压发动机补燃室硅基绝热层烧蚀模型

为了评估固冲发动机硅基绝热层的烧蚀性能,对硅基绝热层的烧蚀形成机制进行了分析并建立了数值模型。硅基绝热层烧蚀由气动冲蚀,化学烧蚀,颗粒剥蚀三个部分构成。数值结果表明,硅基绝热层失效的主要原因是气动冲蚀,化学烧蚀与颗粒剥蚀影响较小。理论计算同试验获得的烧蚀形态基本吻合,冲压发动机严重烧蚀部位在进气道两侧的下游区域。从结构设计上看,冲压发动机防隔热设计的重点应是降低冲压发动机气流冲蚀影响。     

颗粒冲刷条件下三元乙丙绝热材料烧蚀特性实验

为了研究三元乙丙基础配方、抗过载配方、无SiO2配方和无纤维配方等不同配方绝热材料在颗粒冲刷条件下的烧蚀特性和机理,基于高过载地面模拟试验发动机,开展了烧蚀试验研究。分析了实验后绝热材料的表面以及断面形貌特征和宏观烧蚀率结果,探讨了三元乙丙基础配方和抗过载配方绝热材料炭化层中致密结构形成的机理,进行了不同配方材料的烧蚀模式和机理的分析。研究结果表明:相同颗粒冲刷条件下,不同配方三元乙丙材料烧蚀模式和破坏机理不同,烧蚀率从小到大依次为抗过载配方基础配方无SiO2配方无纤维配方;其中基础配方和抗过载配方三元乙丙材料在烧蚀过程中炭化层形成"致密/疏松"结构,表面形成的致密结构可以提高材料的抗烧蚀性能,无SiO2和无纤维三元乙丙材料以基体的粒状和块状剥落破坏为主;不同配方绝热层炭化层的形貌和结构与纤维、SiO2含量以及烧蚀环境密切相关。     

硅橡胶涂覆织物的性能优化研究

为优化硅橡胶涂覆织物的防隔热效率,在硅橡胶基体中添加新型耐烧蚀填料,采用新型骨架材料,制备出耐烧蚀硅橡胶涂覆织物;分别研究了纤维织物、耐烧蚀填料对硅橡胶涂覆织物的柔性、拉伸性能和烧蚀性能的影响。试验结果表明:硅橡胶涂覆织物的柔性和拉伸性能主要由纤维织物决定;M40J碳纤维织物作为骨架材料的硅橡胶涂覆织物烧蚀性能更优;当添加短切黏胶基碳纤维作为耐烧蚀填料时,硅橡胶涂覆织物在较高热流条件下(480 kW/m~2、120 s)的防隔热效率更高。     

基于飞机油箱模型形状特征油量测量切片步长选择方法研究

 在分析飞机数字式油量测量过程中目前广泛使用的切片法油量测量原理的基础上,针对现有的定步长切片法无法得到准确、可靠的燃油质量特性数据库的缺陷,结合对飞机油箱模型形状特征的分析,提出了基于飞机油箱模型形状特征的油量测量切片步长选择方法。此方法包括切片步长整体和局部选择两个过程,整体选择以实现相邻两切片平面所夹油箱模型体积近似相等为目的来确定切片步长,以体现油箱模型截面整体变化规律;局部选择以设计切片平面与截面突变平面重合或尽可能接近的方式,突出油箱截面的局部变化特征。实验结果表明：该切片步长选择方法较定步长方法能够建立更为合理、可靠的燃油质量特性数据库,从而提高了油量测量精度。     

二维翼段颤振的μ控制

 采用超声电机作为作动器来实现含控制面的翼段颤振鲁棒抑制。针对作者设计的二维翼段颤振主动抑制系统，通过理论与实验相结合的方法，建立了考虑沉浮方向阻尼和作动器模型参数不确定性的控制系统模型，设计了μ控制器，并对控制器做了降阶处理。数值仿真和风洞试验表明，μ控制器可有效地抑制颤振的发生，将颤振临界速度提高23.4%。相对于H_∞控制器，μ控制器的控制效果和鲁棒性更好。     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

Abnormal Shape Mould Winding

为解决网格化芯模的缠绕问题,本文提出了复合材料面片缠绕机理;接着详细分析了面片缠绕过程中的芯模凹曲面上纤维滑线和架空现象,应用微分几何曲面理论和空间几何理论,提出判据及其解决方案;最后,针对飞机发动机进气道的缠绕成型,编制缠绕控制程序并进行相应的实验,验证了面片缠绕方法的可行性。     

基于H∞性能指标的质量矩拦截弹鲁棒控制

 以所建立的质量矩拦截弹数学模型为基础，利用微分几何的反馈线性化理论，得到一个解耦线性系统，考虑到拦截弹的鲁棒性要求和3个滑块的协调控制问题，提出采用双回路的设计方法，内回路采用线性二次调节器（LQR），外回路采用考虑混合灵敏度问题的H_∞控制设计。仿真结果证明了该方法动态性能满足设计要求，同时对系统参数的不确定性具有较强的鲁棒性。     

航天器返回地球的气动特性综述

航天器返回地球的飞行过程中,气动特性是实现将宇宙飞行速度减到落地前速度、保证再入飞行得到有效控制以及再入防热安全可靠的关键因素。针对简单旋成体气动外形、半弹道式再入控制、烧蚀防热类返回航天器,综述了返回地球过程中变化的空气流域特性、航天器周围的气体绕流环境、空气与航天器作用产生的动力学与热效应等。系统地给出了该类航天器的再入气动特性参数与飞行性能的共性规律,包括:气动阻力与再入减速、气动升力与再入轨迹控制、配平攻角与飞行稳定性、气动加热与防热,以及再入过程中不同气动特性航天器、气象条件变化等对再入飞行性能的影响规律。为航天器开展返回飞行过程的跨流域气动性能工程研制提供设计参考。     

基于马赫数分布可控曲面外/内锥形基准流场的前体/进气道一体化设计

提出了一种高超声速飞行器乘波前体的外锥形基准流场设计方法,在锥面马赫数分布规律给定的条件下,通过有旋特征线法实现反设计,提高了基准流场设计的灵活性。该基准流场通过锥形"下凹"弯曲激波和波后等熵压缩波系压缩气流,可以在较短的长度内完成高效压缩。基于反正切马赫数分布外锥形基准流场设计的乘波前体具有较高的容积率,乘波特性良好且出口均匀,设计点时有黏升阻比为1.89。另外,基于该乘波前体和马赫数分布可控的内收缩进气道给出了一种双乘波的前体与进气道一体化设计方案,实现了内外流分别独立乘波,充分发挥了乘波前体和内收缩进气道的各自优势。     

Potentials of manufacture and repair of nickel base turbine components used in aero engines and power plants by laser metal deposition and laser drilling

IntroductionExpensive turbine parts like HPT(HighPressure Turine)blades or vanes are replaced bynew parts in case of damage.For example theburn through of the inner side of a blade or vane(Figure 1)is a frequently appearing damage,which cannot be repaired…     

Enhancing the efectiveness of film cooling

Advanced gas turbine stages are designed to operate at increasingly higher inlet temperatures to increase thermal efficiency and specific power output.To maintain durability and reasonable life,film cooling is needed in addition to internal cooling,especially for the first stage.Film cooling lowers material temperature by forced convection inside film-cooling holes and by forming a layer of coolant about component surfaces to insulate them from the hot gases.Unfortunately,each cooling jet forms a pair of counter-rotating vortices that entrains hot gas and causes the film-cooling jet to lift off from the surface that it is intended to protect.This paper gives an overview of efforts to enhance the effectiveness of film-cooling.This paper also describes two new design concepts.One design concept seeks to minimize the entrainment of hot gases underneath of film-cooling jets by using flow-aligned blockers.The other design concept shifts the interaction between the approaching hot gas and the cooling jet to occur further above the surface by using an upstream ramp.For both design concepts,computational fluid dynamics results are presented to examine their usefulness in enhancing film-cooling effectiveness.      

Guide for Authors

<正>About Journal Chinese Journal of Aeronautics(CJA)is a comprehensive academic journal dealing with the fields of aeronautics and astronautics.It reports researches concerning the two fields in China and abroad to promote the academic exchange.Founded in 1988 and sponsored by the Chinese Society of Aeronautics and Astronautics and Beihang University,CJA publishes papers bimonthly,with issues released in February,April,June,August,October and December.