纤维C涂层对SiC_f/Ti6Al4V界面及拉伸性能的影响

通过对SiC纤维增强Ti6Al4V复合材料的拉伸试件断口与界面观察,研究了SiC纤维C涂层对基体与纤维元素扩散、界面反应层厚度与成分、拉伸断口的影响。结果表明,与纤维无C涂层的SiCf/Ti6Al4V相比较,有纤维C涂层的SiCf/Ti6Al4V界面结合强度较弱、反应层厚度较厚,涂层能有效防止纤维性能在复合过程中下降,提高了复合材料拉伸强度。     

基体曲率对热障涂层结合强度影响的无损检测研究

 针对复杂型面航空发动机涡轮叶片表面热障涂层(TBCs)的失效问题,采用交流阻抗谱(IS)法和洛氏硬度(RH)压痕法对比研究了制备在平板基体和曲率基体上,热障涂层在热循环过程中微观结构和界面结合强度的演变规律。交流阻抗谱法的结果表明:两种涂层试样的热生长氧化(TGO)层厚度及陶瓷层内裂纹数量均随着热循环时间增加而增长,但曲率试样的微观结构恶化速度更快;洛氏硬度压痕法的结果验证了经热循环后,曲率基体上热障涂层界面结合强度低于平板样品。     

C／C复合材料抗烧蚀HfC涂层的制备

采用液相先驱体转化法在C/C复合材料表面制备了抗烧蚀HfC涂层.用红外光谱分析先驱体溶液的结构,用XRD、SEM和EDS对涂层进行了分析和表征.结果表明:先驱体溶液中主要存在Hf-O-Hf结构和Hf-O-C链式结构,有利于HfC涂层的形成;经过1800℃热处理后多层膜被转变为HfC涂层,形成的涂层中主要为HfC和HfO2;单次涂覆不能有效的覆盖C/C复合材料,多次涂覆能够生成致密的HfC涂层;涂层的厚度约为几十微米,涂层界面不明显,在涂层和基体间有较大过渡层能够缓解界面应力和提高与基体间的结合强度,有效延长寿命.     

离子辅助电弧沉积ZrN梯度涂层抗固体粒子冲蚀行为研究

为有效提高2Cr13不锈钢表面大攻角固体粒子冲蚀(SPE)抗力,利用离子辅助电弧沉积技术在氮化预处理的2Cr13钢表面制备了不同结构、不同厚度的ZrN梯度涂层,研究了涂层结构和厚度对膜基结合强度、涂层显微硬度、韧性、动静态承载能力以及抗固体粒子冲蚀行为的影响。结果表明:将合理结构的ZrN梯度涂层与离子氮化有机复合,能够获得承载能力高、界面应力应变协调性好、结合强度高、强韧性配合合理,抗多冲疲劳和抗塑性流变性能优的复合改性层,其90°大攻角SPE抗力显著高于2Cr13不锈钢基材。ZrN梯度涂层的SPE抗力同时与涂层厚度密切相关,当ZrN梯度涂层较薄时,其协调变形能力及承载能力较低,在冲击载荷作用下容易出现脱层失效,因而SPE抗力较低;当ZrN梯度涂层太厚时,涂层韧性和内聚强度降低,内部残余应力较大,受外界冲击载荷作用时容易出现局部脱层,因此SPE抗力亦不高。     

表面处理对热障涂层界面微结构的影响

采用真空电弧离子镀技术在单晶高温合金DD32上制备HY5金属粘结层,通过振动光饰、吹砂2种不同的表面处理方法改变粘结层表面状态,再在粘结层表面利用电子束物理气相沉积技术制备陶瓷层。研究了不同处理方法对粘结层表面状态的影响;测试了不同表面处理方法下制备的热障涂层的高温氧化性能并对比分析了它们的变化规律。此外,探讨了不同表面处理方法对界面元素成分及失效特征的影响。研究结果表明,通过表面处理可以去除粘结层表面较大的凸起,提高表面平整度,提高热障涂层抗氧化性能。与粗糙界面相比,光滑界面形成的TGO层均匀致密,Al含量高。经长时间的高温氧化后,粗糙界面的TGO层出现明显皱曲现象,陶瓷层开裂剥落。     

表面改性C/C复合材料与LAS玻璃陶瓷的连接

采用MgOAl₂O₃SiO₂(MAS)玻璃作为中间层,对SiCMoSi₂表面改性的C/C复合材料与Li₂CO₃Al₂O₃SiO₂(LAS)玻璃陶瓷进行热压连接。通过正交实验,研究了连接温度、连接压力和保温时间对试样连接强度的影响,确定最佳工艺参数为：1 200 ℃,20 MPa,15 min,所得到连接接头的最高剪切强度可达30 MPa。利用扫描电子显微镜（SEM）、能谱仪（EDS）和背散射电子像（BEI)对SiCMoSi₂涂层、连接界面的形貌以及组成进行了分析。研究结果表明,SiCMoSi₂涂层与基体结合紧密,Si,C元素在界面处呈梯度状分布,形成厚度约为15 μm的过渡层。MAS玻璃中的组分与LAS玻璃陶瓷和SiCMoSi₂涂层存在相互渗透现象,形成紧密的C/C(SiCMoSi₂)/MAS/LAS结构,界面间的结合良好。     

热压压力对B/Al复合材料组织结构及力学性能的影响

使用表面覆有B4C涂层的硼纤维，采用大气等离子喷涂法制备连续硼纤维增强铝基复合材料预制片，结合真空热压扩散焊制备了纤维均匀分布的B／Al复合材料。探讨在接近铝基体熔点温度的条件下热压压力对复合材料力学性能与B／Al界面结合的影响，分析了B／Al界面结合状态与断口形貌及力学性能之间的关系。研究表明：热压压力对制备的B／Al复合材料的纤维体积分数、B纤维与Al基体的界面结合状态和拉伸强度有显著的影响；纤维表面的B4c涂层有效地防止了B纤维与Al基体间的界面反应，在温度6500C、压力10MPa的条件下，制备的纤维体积分数为42％的B／Al复合材料拉伸强度达到968MPa，达到了纤维理想强度的77％。     

基体预热温度对ZrO2 涂层结合强度的影响

用等离子喷涂的方法在不同温度的45#钢基体上制备ZrO2涂层,通过涂层的结合实验、X射线衍射分析了基体温度与涂层结合强度之间的关系,发现当基体预热温度为250℃时涂层的结合强度最高,可达13.4 MPa;当预热温度高于350℃时,粘结层中的热生长氧化物明显增加,导致涂层的结合强度降低。     

TC4钛合金表面激光原位反应制备TiN涂层及性能研究

利用激光原位反应技术在TC4钛合金表面制备了无裂纹、组织均匀致密的TiN涂层,并分析了激光氮化层的显微组织、成分和物相,测试了涂层横截面显微硬度、涂层耐磨性能及抗SiO_2颗粒高速冲蚀的能力。结果表明:在适当的激光参数下制备的氮化钛涂层与TC4基体之间呈现良好的冶金结合,其界面结合强度为240～270MPa;涂层主要为硬质TiN相,涂层硬度高达1550HV_(0.1),约为基材的4.5倍;涂层磨损失重量是TC4钛合金的14.7%;在60o冲蚀角度下,基材的冲蚀质量损失为涂层的2倍。     

铂铝黏结层体系EB-PVD热障涂层的热循环行为

在镍基单晶高温合金基体上采用化学气相沉积法制备铂铝金属黏结层,并采用电子束物理气相沉积制备氧化钇部分稳定化的氧化锆(YSZ)陶瓷面层。研究了黏结层相组成对热障涂层循环氧化行为的影响,借助扫描电子显微镜(SEM)、X射线能谱分析(EDS)和X-射线衍射分析(XRD)等方法分析涂层的相结构、显微组织和化学成分。结果表明：黏结层主要成分包括Ni、Al、Pt、Co和Cr元素并由β-(Ni,Pt)Al相和PtAl₂相组成;经热循环测试后,涂层在热生长氧化物(TGO)和黏结层内部及其界面可能出现剥离;随着热暴露时间的延长,TGO层处的残余应力总体上呈现出逐渐减小的演变趋势;控制铂铝黏结层前驱体活性、Pt/Al元素含量、抑制脆性PtAl₂相生成、改善TGO层/黏结层界面韧性和降低TGO层应力应变水平可有效延长铂铝黏结层体系热障涂层的热循环寿命。     

Effect of laser-discrete-quenching on bonding properties of electroplated grinding wheel with AISI 1045 steel substrate and nickel bond

To improve the bonding strength between the nickel bond and the hub of the electroplated diamond grinding wheel, a hybrid technique was proposed to combine laser pre-quenching steel substrate and post-electroplating nickel. To validate the effectiveness of the proposed technique, AISI 1045 substrate was nickel-coated. The bonding properties between the electroplated nickel coating and substrate with or without laser-discrete-quenching were discussed comparatively by scratch, indentation, and thermal shock tests. The results show that the pre-quenching treatment leads to phase transformation of AISI 1045 microstructure from the mixed pearlite and ferrite phases into the martensitic phase. Since the martensitic phase is characterized as a high corrosion resistance, the interface of substrate/coating is smooth and flat in the pre-quenched zone, and the coating is bonded well with the steel substrate. In contrast to the steel substrate without pre-quenching treatment, the proposed technique significantly enhanced the bonding strengths of the electroplated nickel-coating. On one hand, the average hardness of electroplated nickel-coating on the laser pre-quenched zone is increased by 18.7%, and the scratch depth with the same load become narrower and shallower. On the other hand, the coefficient of friction (CoF) and the vibration amplitude are reduced, and the coating is bonded effectively with the substrate to inhibit the crack initialization at the interface. This prevents effectively the coating from peeling off and improves significantly the thermal shock resistance property.     

热障涂层结合强度及失效模式研究

采用实验方法研究了热障涂层的结合强度,并探讨了温度、氧化时间、涂层厚度以及基体等因素对结合强度的影响。涂层采用了等离子和EB-PVD两种喷涂工艺,采用双向测试法,分析了粘结层氧化对涂层法向和切向结合强度的影响,研究结果表明同一种喷涂工艺方法,尽管涂层厚度不同,但其结合强度是非常接近的,为带涂层航空发动机部件的强度设计和分析以及涂层失效模型的建立提供的参考。      

聚甲基苯基硅氧烷涂层对高硅氧纤维/磷酸盐性能的影响

采用涂覆有机-无机杂化涂层的方法对高硅氧纤维(HSGF)进行表面改性.涂覆前后的纤维表面特性采用XPS和AFM进行表征;采用浸泡法腐蚀实验研究了涂层对HSGF耐酸腐蚀能力的影响;通过测试界面剪切强度(IFSS)评价了复合材料的界面粘结性能,并测试了涂层前后HSGF及其增强磷酸盐基复合材料力学性能.结果表明,聚甲基苯基硅氧烷(PSI)涂层可有效地保护高硅氧纤维,阻碍磷酸盐基体/高硅氧纤维之间的界面反应,降低磷酸对其的腐蚀速率,调节界面结合程度,使复合材料弯曲强度比未处理试样提高32%.     

含稀土TiCx增强钛基激光熔覆层组织与耐磨性

采用同轴送粉激光熔覆技术在Ti6Al4V合金表面成功制备了含稀土CeO₂的碳化钛增强钛基激光熔覆层。运用渗透探伤、光学显微镜、X射线衍射仪、扫描电镜、能谱分析仪、电子探针、显微硬度计、摩擦磨损试验机等分析和测试方法研究了碳化钛增强钛基激光熔覆层的成形质量、微观组织、元素分布、硬度和摩擦磨损性能。结果表明,涂层内无裂纹缺陷,仅在层间过渡区分布有少量气孔（孔隙率为1.65%）。涂层中物相主要包括富Ti、Cr元素的β固溶体（CrTi₄）、缺位型碳化钛（TiC_x）和稀土氧化物（CeO₂）。熔覆层各微区的碳化钛形貌存在显著差异,熔覆层顶部和中部区域呈发达树枝晶状和针状,而结合区由针状和小尺寸不发达枝晶组成。碳化钛枝晶中碳元素分布不均匀,一次枝晶含碳量高于二次枝晶。基体相中Ni和Cr元素呈现明显偏析,而Al和V元素分布相对均匀。此外,稀土氧化物CeO₂主要分布于TiC_x与CrTi₄相界以及CrTi₄晶粒边界处。与基材相比,尽管TiC_x增强钛基复合涂层具有较高的摩擦系数,但其耐磨性显著增加（提高近52%）。熔覆层和基材磨损机制均为黏着磨损和磨粒磨损的复合磨损模式,但熔覆层的磨损程度较轻。     

弱界面粘结对复合材料有效性能的影响

采用非线性弹簧元模拟界面,用细观力学有限元法计算分析了不同界面特性下弱界面粘结的纤维增强金属基复合材料的宏细观性能。并考虑了3种不同的界面模型。结果表明弱界面粘结的存在使复合材料宏观性能下降。在常响应界面情况下,复合材料横向拉伸应力-应变曲线存在明显的转折点,对应于界面分离的起始点,转折点的位置取决于界面粘结强度。当存在渐进适应界面时,复合材料横向拉伸应力-应变曲线存在3个阶段。      

硝胺推进剂界面键合的表征研究

从红外光谱分析，表面（界面）自由能测定、光电子能谱分析等方面，研究了键合剂，包覆固体填料颗粒对界面增强的效果，并与静态力学性能的数据进行了对比，结果表明；取代酰胺类键合剂对ＨＭＸ间的作用力为氢键。效果倨于醇胺，多元胺类化合物，其中一种键合剂对ＨＭＸ的浸润可以在热力学和动力学两方面达到较好的统一，键合效果并不仅仅取决于包覆度的大小，还与键合剂附着在ＨＭＸ表面上形成的界面层或预包覆层的性质有关。     

水悬浮法制备GF／PVC复合材料的界面形态和形成机理

应用扫描电镜、红外光谱、电子探针等方法研究了水悬浮法制备GF/PVC复合材料的界面形态和形成机理 ,研究结果表明 :由含有I,II,III ,V号悬浮液制备的复合材料 ,其纤维与机体的界面粘结和界面相互作用主要是纤维表面与这些高分子添加剂之间的物理作用 ,由Ⅳ号悬浮液制备的复合材料 ,其两相间的界面粘接很好 ,界面相互作用以化学相互作用为主。纤维经KH5 5 0或KH5 6 0及LCB或LCM复合涂层处理 ,材料纤维与基体间的界面相互作用主要归结为偶联剂的活性基团与聚合物涂层及PVC的化学作用     

激光快速制备Tix Aly-TiN复合涂层

采用激光气体氮化与同步送粉相结合的工艺方法,在Ti-6Al-4V合金表面原位合成了Tix Aly-TiN复合涂层。通过XRD,SEM,OM,EDS,显微硬度测试等手段研究了该复合涂层的物相组成、显微组织、元素分布及显微硬度。结果表明：涂层主要由TiN和Tix Aly 金属间化合物组成;沿激光熔深方向TiN含量下降;Tix Aly 金属间化合物含量上升;涂层无裂纹和孔隙,厚度较均匀,涂层与基体间形成良好的冶金结合;沿激光熔深方向N、Al元素的分布均匀;涂层显微硬度得到显著提高,且从涂层到基体逐渐降低。     

发动机高温结构隔热涂层的力学特性

介绍了发动机涡轮导向叶片隔热层的力学特性;涂层材料的物理性能以及基体材料在各种温度条件下与涂层的匹配;涂层在抗热震性方面的能力;涂层与基体材料组合结构的寿命失效模型,试验结果证明,隔热涂层对叶片具有良好的保护作用,对提高叶片工作温度和使用寿命很有好处。