K418激光熔覆NiCrWMo组织及耐磨性研究

为研究修复某航空叶片,采用Nb：YAG激光在K418镍基高温合金表面熔覆NiCrWMo涂层。分析了熔覆层组织,测试了熔覆层硬度。结果表明：采用自配的镍基合金粉末,在工艺参数为电流160 A、脉宽8 ms、频率4 Hz时,用激光熔覆能够实现对K418镍基高温合金损伤结构的修复,获得了表面平整、连续,微观组织细密、均匀,与基体呈良好冶金结合,硬度高于基体,无缺陷的熔覆层。     

定向凝固镍基高温合金上激光熔覆Inconel 738的裂纹敏感性研究

针对定向凝固镍基高温合金叶片的强化与修复需求,研究了在定向凝固镍基高温合金基体上激光熔覆Inconel 738的裂纹敏感性问题.在定向凝固镍基高温合金基体上激光熔覆Inconel 738合金对裂纹非常敏感,所产生的裂纹为热裂纹,由定向凝固基体晶界处引发并穿过界面向熔覆层发展;多层熔覆过程中熔覆层间也会产生热裂纹,热裂纹沿晶界纵向扩展.定向凝固高温合金基体晶界处的低熔共晶成为主要的裂纹源.严格控制激光熔覆过程中的热输入量可以显著降低裂纹敏感性.选择适当的熔覆工艺方法和参数可以在定向凝固镍基合金基体上形成良好冶金结合且无裂纹的基本保持定向凝固特性的熔覆层组织.     

激光熔覆工艺的应用

激光熔覆具有广阔的发展前景,潜力很大,经济效益可观,引起国内外广泛的关注,并投入人才物力进行研究。 航空发动机钛合金和镍基合金摩擦副的接触磨损是发动机使用和维修中的一大难题,利用激光熔覆技术则可获得优良的涂层,为燃气涡轮发动机零件的修复开创了一个新途径。该工作研究了激光表面熔覆高温耐磨涂层的激光喷涂技术,在DZ4合金基体上,喷涂CoCrW合金粉末和WC粉末的机械混合物,厚度为0.3mm,提高了高温耐磨及抗腐蚀性能,对镍基合金制造的航空发动机涡轮叶片,利用激光熔覆技术熔覆钴基合金,提高了耐热耐磨性能,与热喷镀等方法相比,缩短了涂层制备的时间,质量稳定,且消除了由热影响可     

钨极氩弧焊与激光熔覆修复的K403镍基高温合金导向器叶片组织与性能

K403镍基高温合金具有优异的室温和高温综合性能,广泛用于航空发动机涡轮叶片及导向器的制造。针对涡轮叶片长期服役于复杂工况产生的裂纹缺陷等问题,本工作先对钨极氩弧（tungsten inert gas,TIG）焊和激光熔覆两种工艺修复后的组织与拉伸性能展开对比分析,而后使用激光熔覆工艺修复叶片,并进行无损检测。利用OM、SEM观察微观组织、断口形貌,利用EDS进行相的成分分析。结果表明：TIG焊修复工艺在修复界面区附近易产生微裂纹缺陷,主要碳化物相和低熔点共晶组织引起;激光熔覆工艺修复区域的晶粒与组织更加均匀,微裂纹缺陷更易得到控制;激光熔覆工艺修复的试样综合力学性能明显高于TIG焊修复工艺的试样,且激光熔覆工艺具有较好的工艺稳定性,TIG焊修复工艺的室温拉伸强度为K403母材强度的69.22%,激光熔覆修复工艺室温抗拉强度达到了母材的87.44%,断口形貌显示修复区域的室温拉伸断口呈现出混合断裂特征,高温拉伸断口呈现出沿晶断裂的特征。修复区域的微裂纹、局部液相不足缺陷和碳化物是拉伸断裂的主要原因。激光熔覆修复工艺具有热源集中、热影响区小的优势,能够有效抑制修复区缺陷并细化微观组织,在...     

TiB2／Cu激光熔覆工艺研究

激光熔覆技术中,激光的工艺参数是获得高质量熔覆层的关键因素.文章采用激光熔覆原位合成技术,通过化学分析确定预覆合金粉末的成分和配比,从分析激光与材料的相互作用入手,通过计算和试验确定了激光工艺参数,在纯铜表面原位合成Cu-TiB2复合材料.试验表明,球形TiB2 颗粒细小均匀,熔覆层与基体呈良好的冶金结合.     

激光熔覆沉积成形NbMoTaTi难熔高熵合金的组织与强度研究

通过激光熔覆沉积技术制备应用于航空航天工业的Nb Mo Ta Ti难熔高熵合金材料,通过X射线衍射判断出成形的合金晶体结构为体心立方的单相固溶体结构。高熵合金晶粒尺寸大多在2~12μm之间;平均显微硬度为397.6HV,室温抗压强度为1301.83MPa,1000℃高温抗压强度只达到347.28MPa,其原因可能与激光熔覆沉积成形Nb Mo Ta Ti高熵合金的过程中产生的气孔、未熔化/不完全熔化的Ta粉末粒子和裂纹有关,需进一步研究。     

铝青铜表面激光熔覆层组织与性能研究

采用激光熔覆技术在QAl9-4铝青铜表面熔覆了一层Ni基合金层,以提高QAl9-4铝青铜的耐磨性.为了提高QAl9-4铝青铜对激光的吸收率,实验采用少量自制的粘结剂并配合压力机将合金粉末预置在QAl9-4铝青铜表面,然后激光重熔.通过对QAl9-4铝青铜表面熔覆层组织研究分析表明:熔覆层与基体形成了良好的冶金结合,无裂纹缺陷的存在;熔覆层组织受凝固速度的影响较大,其表面组织为胞状晶,中部为发达的树枝晶,结合区上部由于基体的激冷作用而呈细晶区,细晶区以下又以树枝晶和胞状晶为主.激光熔覆层的平均硬度是QAl9-4铝青铜基体硬度的3倍多.     

300M钢激光熔覆耐磨防腐自润滑涂层温度场数值模拟研究

为了提高飞机起落架减震支柱300M超高强钢的抗磨性能,突破由于温度梯度过大诱发的激光熔覆耐磨防腐自润滑涂层裂纹等技术瓶颈,基于ANSYS软件的生死单元法编制热循环程序,考虑自润滑相和耐磨相材料热物性参数随温度的变化、相变潜热、激光熔覆过程中与外界的换热、激光熔覆功率、激光熔覆扫描速率等因素对激光熔覆过程温度场、熔池、温度梯度的影响,建立300M超高强钢激光熔覆耐磨防腐自润滑涂层温度仿真模型。结果表明:基体的熔化需要激光、熔化的粉末等综合作用使传导到该区域的有效能量达到熔化的临界值,熔化高度增加率随激光功率的增加先降低后增加,熔化高度减少率随激光扫描速率的增加先变小后变大;由于激光熔覆的不同区域温度、冷却速率差异等综合因素影响,熔覆层熔池的纵截面为勺状熔池;伴随激光功率的增加,由于熔覆层不同区域对能量输入产生的温度响应速率差异导致Z方向温度梯度值增加,且最大冷却速率增加;伴随激光扫描速率的增加,激光输入能量降低,降低了高温区域温度及激光的快速局部加热等综合影响,Z方向温度梯度值降低。通过调控激光参数,在保持熔覆层结合强度的条件下,基体熔凝区能被控制到最小,并能够降低温度梯度。     

激光熔覆成型用Ni-Cu-Sn合金粉末的制备及其成形特性

研制了适合激光熔覆成型的Ni-Cu-Sn合金粉末,通过工艺试验,分析了激光熔覆成型件的微观组织特征及微观缺陷的形成原因,并提出了预防缺陷形成的方法。     

金属材料激光表面改性与高性能金属零件激光快速成形技术研究进展

 简要报道本实验室目前在先进航空金属材料激光表面改性及高性能金属零件激光快速成形技术研究与应用的新进展。主要内容包括 :(1 )钛合金耐磨阻燃激光表面合金化与激光熔覆表面改性技术;(2 )刷式密封及指尖密封跑道高温自润滑耐磨涂层新材料及其激光熔覆制备新技术;(3 )难熔金属硅化物复合材料高温耐磨耐蚀多功能涂层新材料及激光熔覆涂层技术;(4 )高性能 /梯度性能钛合金及高温合金结构件激光快速成形技术。     

基于飞机油箱模型形状特征油量测量切片步长选择方法研究

 在分析飞机数字式油量测量过程中目前广泛使用的切片法油量测量原理的基础上,针对现有的定步长切片法无法得到准确、可靠的燃油质量特性数据库的缺陷,结合对飞机油箱模型形状特征的分析,提出了基于飞机油箱模型形状特征的油量测量切片步长选择方法。此方法包括切片步长整体和局部选择两个过程,整体选择以实现相邻两切片平面所夹油箱模型体积近似相等为目的来确定切片步长,以体现油箱模型截面整体变化规律;局部选择以设计切片平面与截面突变平面重合或尽可能接近的方式,突出油箱截面的局部变化特征。实验结果表明：该切片步长选择方法较定步长方法能够建立更为合理、可靠的燃油质量特性数据库,从而提高了油量测量精度。     

二维翼段颤振的μ控制

 采用超声电机作为作动器来实现含控制面的翼段颤振鲁棒抑制。针对作者设计的二维翼段颤振主动抑制系统，通过理论与实验相结合的方法，建立了考虑沉浮方向阻尼和作动器模型参数不确定性的控制系统模型，设计了μ控制器，并对控制器做了降阶处理。数值仿真和风洞试验表明，μ控制器可有效地抑制颤振的发生，将颤振临界速度提高23.4%。相对于H_∞控制器，μ控制器的控制效果和鲁棒性更好。     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

Abnormal Shape Mould Winding

为解决网格化芯模的缠绕问题,本文提出了复合材料面片缠绕机理;接着详细分析了面片缠绕过程中的芯模凹曲面上纤维滑线和架空现象,应用微分几何曲面理论和空间几何理论,提出判据及其解决方案;最后,针对飞机发动机进气道的缠绕成型,编制缠绕控制程序并进行相应的实验,验证了面片缠绕方法的可行性。     

基于H∞性能指标的质量矩拦截弹鲁棒控制

 以所建立的质量矩拦截弹数学模型为基础，利用微分几何的反馈线性化理论，得到一个解耦线性系统，考虑到拦截弹的鲁棒性要求和3个滑块的协调控制问题，提出采用双回路的设计方法，内回路采用线性二次调节器（LQR），外回路采用考虑混合灵敏度问题的H_∞控制设计。仿真结果证明了该方法动态性能满足设计要求，同时对系统参数的不确定性具有较强的鲁棒性。     

航天器返回地球的气动特性综述

航天器返回地球的飞行过程中,气动特性是实现将宇宙飞行速度减到落地前速度、保证再入飞行得到有效控制以及再入防热安全可靠的关键因素。针对简单旋成体气动外形、半弹道式再入控制、烧蚀防热类返回航天器,综述了返回地球过程中变化的空气流域特性、航天器周围的气体绕流环境、空气与航天器作用产生的动力学与热效应等。系统地给出了该类航天器的再入气动特性参数与飞行性能的共性规律,包括:气动阻力与再入减速、气动升力与再入轨迹控制、配平攻角与飞行稳定性、气动加热与防热,以及再入过程中不同气动特性航天器、气象条件变化等对再入飞行性能的影响规律。为航天器开展返回飞行过程的跨流域气动性能工程研制提供设计参考。     

基于马赫数分布可控曲面外/内锥形基准流场的前体/进气道一体化设计

提出了一种高超声速飞行器乘波前体的外锥形基准流场设计方法,在锥面马赫数分布规律给定的条件下,通过有旋特征线法实现反设计,提高了基准流场设计的灵活性。该基准流场通过锥形"下凹"弯曲激波和波后等熵压缩波系压缩气流,可以在较短的长度内完成高效压缩。基于反正切马赫数分布外锥形基准流场设计的乘波前体具有较高的容积率,乘波特性良好且出口均匀,设计点时有黏升阻比为1.89。另外,基于该乘波前体和马赫数分布可控的内收缩进气道给出了一种双乘波的前体与进气道一体化设计方案,实现了内外流分别独立乘波,充分发挥了乘波前体和内收缩进气道的各自优势。     

Potentials of manufacture and repair of nickel base turbine components used in aero engines and power plants by laser metal deposition and laser drilling

IntroductionExpensive turbine parts like HPT(HighPressure Turine)blades or vanes are replaced bynew parts in case of damage.For example theburn through of the inner side of a blade or vane(Figure 1)is a frequently appearing damage,which cannot be repaired…     

Enhancing the efectiveness of film cooling

Advanced gas turbine stages are designed to operate at increasingly higher inlet temperatures to increase thermal efficiency and specific power output.To maintain durability and reasonable life,film cooling is needed in addition to internal cooling,especially for the first stage.Film cooling lowers material temperature by forced convection inside film-cooling holes and by forming a layer of coolant about component surfaces to insulate them from the hot gases.Unfortunately,each cooling jet forms a pair of counter-rotating vortices that entrains hot gas and causes the film-cooling jet to lift off from the surface that it is intended to protect.This paper gives an overview of efforts to enhance the effectiveness of film-cooling.This paper also describes two new design concepts.One design concept seeks to minimize the entrainment of hot gases underneath of film-cooling jets by using flow-aligned blockers.The other design concept shifts the interaction between the approaching hot gas and the cooling jet to occur further above the surface by using an upstream ramp.For both design concepts,computational fluid dynamics results are presented to examine their usefulness in enhancing film-cooling effectiveness.      

Guide for Authors

<正>About Journal Chinese Journal of Aeronautics(CJA)is a comprehensive academic journal dealing with the fields of aeronautics and astronautics.It reports researches concerning the two fields in China and abroad to promote the academic exchange.Founded in 1988 and sponsored by the Chinese Society of Aeronautics and Astronautics and Beihang University,CJA publishes papers bimonthly,with issues released in February,April,June,August,October and December.