蠕变损伤DZ411合金恢复热处理组织演化

采用固溶+二级时效工艺对蠕变损伤DZ411合金进行常规恢复热处理,研究蠕变损伤合金组织恢复演化过程,并评价其力学性能。结果表明:蠕变损伤的DZ411合金中的一次γ′相发生明显球化和筏化,二次γ′相消失,未发现晶界蠕变孔洞;固溶处理对于回溶粗大形变γ′相,并重新析出细小均匀分布的γ′相至关重要,同时选择合适的固溶温度可避免初熔和再结晶;两级时效处理是优化γ′相尺寸、形态和配比的关键步骤;恢复后可获得大体积分数、双尺寸形态γ′相组织,二次和三次γ′相平均有效直径分别约为0.38μm和0.07μm,其体积分数分别约为47.5%和6.5%;恢复态合金室温强度与原始态合金相近,但在980℃/220 MPa下的持久寿命和伸长率分别达到121 h和13%,略低于原始态合金性能水平。     

Li 对 Al-Mg-Si 合金时效过程的影响

Ａｌ－０．６Ｍｇ－０．８Ｓｉ－０．２Ｃｒ合金中加入不同含量的Ｌｉ后，无针状Ｍｇ２Ｓｉ相析出，而形成近球形ＡｌＬｉＳｉ相，δ′成为主要时效析出相。Ｌｉ的加入量为１．７％时，δ′相体积分数和晶界析出相的线密度低，其时效硬化过程缓慢，峰值强度显著降低，但具有较好的延伸率；Ｌｉ的加入量为２．６时，δ′相体积分数高，其时效硬化速度与基体合金相近，但具有更高的峰值强度，大量δ′相的存在产生强烈的共面滑移倾向，合金的延伸率略有下降。     

Ni含量对钴基高温合金组织与性能的影响

采用非自耗真空熔炼炉制备钴基高温合金铸锭,利用扫描电子显微镜(SEM)和X射线衍射分析仪(XRD)研究Ni含量(0%,5%,10%,20%(原子分数))对钴基高温合金组织和晶格错配度的影响。通过对不同Ni含量的合金进行高温压缩实验,研究Ni含量对钴基高温合金性能的影响。结果表明:随着Ni含量的增加,γ′相的平均尺寸增加;当Ni含量从0%增加到15%时,合金中强化相的体积分数逐渐增加,当Ni含量增加到20%时,合金中强化相的体积分数稍有减少;Ni含量从0%增加到10%时,γ/γ′两相的晶格错配度降低,Ni含量从10%增加到15%时,γ/γ′两相的晶格错配度略有增加,当Ni含量增加到20%时,γ/γ′两相的晶格错配度又开始降低;Ni含量为5%的合金屈服强度最高。     

W含量及组织状态对镍基高温合金晶格常数及错配度的影响

通过对镍基合金的组织形貌观察和X射线衍射分析,研究元素W及组织状态对镍基合金晶格常数及错配度的影响。结果表明,7.5%W镍基合金经完全热处理后,立方γ′相以共格方式嵌镶并均匀分布在γ基体相中。随元素W含量增加,合金中γ′和γ两相的合成衍射峰值略有左移,使γ′和γ两相的晶格常数增加,其中γ′相晶格常数增加幅度较大的原因是元素W较大比例地分布在γ′相中,并由此使合金中两相的晶格错配度由负值转变为正值。经完全热处理后,合金中γ和γ′两相有较小的晶格错配度,在高温拉伸蠕变期间外加应力的作用下,γ基体相的晶格常数值增加幅度较大,致使合金中γ′和γ两相晶格错配度的绝对值增加。     

Re对定向凝固Ni基高温合金组织及性能的影响

采用真空感应熔炼和定向凝固重熔技术制备了不同Re含量的Ni基高温合金试样,分析了合金微观组织,测试了热处理后其室温拉伸和高温持久性能。结果表明:Re主要分布于γ基体中,在γ′强化相中分布很少。随着Re含量的增加,γ+γ′共晶体积分数略有增多,枝晶杆γ′细化明显。热处理后γ′立方化程度增加,共晶相含量明显减少。Re的加入显著提高了合金的室温拉伸屈服强度和高温持久寿命,但室温和高温塑性有所降低。Re主要通过固溶在γ基体中来阻碍γ′粗化,增大错配度,从而提高合金综合性能。     

镍基单晶合金初始细观结构及变形影响因素研究

通过对国内外大量镍基单晶合金的细观试验现象及结论进行分析,给出了单晶合金细观2相结构的主要变形特征,并研究得到影响单晶合金初始细观结构及其变形的3个因素分别为γ′初始尺寸、形状及γ/γ′初始错配度。结果表明：在高温、较高应力的条件下,γ′的初始尺寸为0.45 μｍ（γ′体积分数约为70％）,初始形状为立方块且不发生任何预筏化,初始错配度为负且绝对值较大时,合金的综合力学性能最佳     

含硅镍基铸造高温合金的相成份和热稳定性

利用物理—化学相分析和差热分析法研究了硅对Ni-Cr-Co-W-Al-Ti-Nb-Hf-C系合金结晶时的相成份变化及相变过程的影响,合金中硅含量由0.05％增加至0.4％,引起不等轴共晶γ-γ′析出分量的增加,并从熔融合金中补充析出以HfC为基的Me_C和MeC型碳化物。在高温等温持久及蠕变条件下,硅引起碳化物转变,加剧了γ′-相的凝聚,这样就降低了合金的寿命和瞬时塑性。     

单晶镍基合金拉伸蠕变期间γ‘相定向粗化的特征及影响因素

对[001]取向单晶镍基合金恒载拉伸蠕变的组织形貌进行SEM观察和EDAX成分分析,研究了γ′相定向粗化特征及影响因素.结果表明,由于应力场和温度场的差别,蠕变样品不同位置处筏状γ′相粗化尺寸及特征不同,近断口处筏状γ′相扭曲且粗化加剧,随离断口距离增加,γ′相粗化程度减弱;在γ′相定向粗化的扩散场中,分配比值较小且相对稳定的元素W可成为其他元素的扩散障碍,使合金2中γ′相的形筏时间明显延长.     

单晶镍基合金拉伸蠕变期间γ′相定向粗化的特征及影响因素

对[001]取向单晶镍基合金恒载拉伸蠕变的组织形貌进行SEM观察和EDAX成分分析,研究了γ′相定向粗化特征及影响因素.结果表明,由于应力场和温度场的差别,蠕变样品不同位置处筏状γ′相粗化尺寸及特征不同,近断口处筏状γ′相扭曲且粗化加剧,随离断口距离增加,γ′相粗化程度减弱;在γ′相定向粗化的扩散场中,分配比值较小且相对稳定的元素W可成为其他元素的扩散障碍,使合金2中γ′相的形筏时间明显延长.     

Cr,Al含量对铸造TiAl基合金显微组织的影响

为寻找细晶组织的铸造ＴｉＡｌ基合金，在Ｔｉ－４４Ａｌ（ａｔ－％）和Ｔｉ－４８Ａｌ（ａｔ－％）两种Ａｌ含量的二元合金中添加了３Ｃｒ和６Ｃｒ（ａｔ－％）。结果表明，Ｃｒ对铸态α＿２＋γ合金的晶粒大小无明显的影响，但通过热处理可显著细化晶粒。对Ｔｉ－４４Ａｌ－３Ｃｒ和Ｔｉ－４８Ａｌ－３Ｃｒ合金分别采用１１５０℃、１６８ｈ和１２００℃、２４ｈ处理可取得最佳的细化晶粒效果，而且４８Ａｌ合金热处理后可更容易获得细晶组织。Ｃｒ促进有序富Ｃｒ相β＿２的形成，该相或者与片状α＿２相共生，或者分布于γ相的晶界，阻碍γ相长大。Ｃｒ在β＿２、γ＿２和γ相中的溶解度依次减少，它主要取代γ和α＿２相中的Ｔｉ，因而随着合金中Ｃｒ量增加，γ和α＿２相中的Ａｌ／Ｔｉ比增加。Ｃｒ还促使γ相内形成孪晶。     

基于飞机油箱模型形状特征油量测量切片步长选择方法研究

 在分析飞机数字式油量测量过程中目前广泛使用的切片法油量测量原理的基础上,针对现有的定步长切片法无法得到准确、可靠的燃油质量特性数据库的缺陷,结合对飞机油箱模型形状特征的分析,提出了基于飞机油箱模型形状特征的油量测量切片步长选择方法。此方法包括切片步长整体和局部选择两个过程,整体选择以实现相邻两切片平面所夹油箱模型体积近似相等为目的来确定切片步长,以体现油箱模型截面整体变化规律;局部选择以设计切片平面与截面突变平面重合或尽可能接近的方式,突出油箱截面的局部变化特征。实验结果表明：该切片步长选择方法较定步长方法能够建立更为合理、可靠的燃油质量特性数据库,从而提高了油量测量精度。     

二维翼段颤振的μ控制

 采用超声电机作为作动器来实现含控制面的翼段颤振鲁棒抑制。针对作者设计的二维翼段颤振主动抑制系统，通过理论与实验相结合的方法，建立了考虑沉浮方向阻尼和作动器模型参数不确定性的控制系统模型，设计了μ控制器，并对控制器做了降阶处理。数值仿真和风洞试验表明，μ控制器可有效地抑制颤振的发生，将颤振临界速度提高23.4%。相对于H_∞控制器，μ控制器的控制效果和鲁棒性更好。     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

Abnormal Shape Mould Winding

为解决网格化芯模的缠绕问题,本文提出了复合材料面片缠绕机理;接着详细分析了面片缠绕过程中的芯模凹曲面上纤维滑线和架空现象,应用微分几何曲面理论和空间几何理论,提出判据及其解决方案;最后,针对飞机发动机进气道的缠绕成型,编制缠绕控制程序并进行相应的实验,验证了面片缠绕方法的可行性。     

基于H∞性能指标的质量矩拦截弹鲁棒控制

 以所建立的质量矩拦截弹数学模型为基础，利用微分几何的反馈线性化理论，得到一个解耦线性系统，考虑到拦截弹的鲁棒性要求和3个滑块的协调控制问题，提出采用双回路的设计方法，内回路采用线性二次调节器（LQR），外回路采用考虑混合灵敏度问题的H_∞控制设计。仿真结果证明了该方法动态性能满足设计要求，同时对系统参数的不确定性具有较强的鲁棒性。     

航天器返回地球的气动特性综述

航天器返回地球的飞行过程中,气动特性是实现将宇宙飞行速度减到落地前速度、保证再入飞行得到有效控制以及再入防热安全可靠的关键因素。针对简单旋成体气动外形、半弹道式再入控制、烧蚀防热类返回航天器,综述了返回地球过程中变化的空气流域特性、航天器周围的气体绕流环境、空气与航天器作用产生的动力学与热效应等。系统地给出了该类航天器的再入气动特性参数与飞行性能的共性规律,包括:气动阻力与再入减速、气动升力与再入轨迹控制、配平攻角与飞行稳定性、气动加热与防热,以及再入过程中不同气动特性航天器、气象条件变化等对再入飞行性能的影响规律。为航天器开展返回飞行过程的跨流域气动性能工程研制提供设计参考。     

基于马赫数分布可控曲面外/内锥形基准流场的前体/进气道一体化设计

提出了一种高超声速飞行器乘波前体的外锥形基准流场设计方法,在锥面马赫数分布规律给定的条件下,通过有旋特征线法实现反设计,提高了基准流场设计的灵活性。该基准流场通过锥形"下凹"弯曲激波和波后等熵压缩波系压缩气流,可以在较短的长度内完成高效压缩。基于反正切马赫数分布外锥形基准流场设计的乘波前体具有较高的容积率,乘波特性良好且出口均匀,设计点时有黏升阻比为1.89。另外,基于该乘波前体和马赫数分布可控的内收缩进气道给出了一种双乘波的前体与进气道一体化设计方案,实现了内外流分别独立乘波,充分发挥了乘波前体和内收缩进气道的各自优势。     

Potentials of manufacture and repair of nickel base turbine components used in aero engines and power plants by laser metal deposition and laser drilling

IntroductionExpensive turbine parts like HPT(HighPressure Turine)blades or vanes are replaced bynew parts in case of damage.For example theburn through of the inner side of a blade or vane(Figure 1)is a frequently appearing damage,which cannot be repaired…     

Enhancing the efectiveness of film cooling

Advanced gas turbine stages are designed to operate at increasingly higher inlet temperatures to increase thermal efficiency and specific power output.To maintain durability and reasonable life,film cooling is needed in addition to internal cooling,especially for the first stage.Film cooling lowers material temperature by forced convection inside film-cooling holes and by forming a layer of coolant about component surfaces to insulate them from the hot gases.Unfortunately,each cooling jet forms a pair of counter-rotating vortices that entrains hot gas and causes the film-cooling jet to lift off from the surface that it is intended to protect.This paper gives an overview of efforts to enhance the effectiveness of film-cooling.This paper also describes two new design concepts.One design concept seeks to minimize the entrainment of hot gases underneath of film-cooling jets by using flow-aligned blockers.The other design concept shifts the interaction between the approaching hot gas and the cooling jet to occur further above the surface by using an upstream ramp.For both design concepts,computational fluid dynamics results are presented to examine their usefulness in enhancing film-cooling effectiveness.      

Guide for Authors

<正>About Journal Chinese Journal of Aeronautics(CJA)is a comprehensive academic journal dealing with the fields of aeronautics and astronautics.It reports researches concerning the two fields in China and abroad to promote the academic exchange.Founded in 1988 and sponsored by the Chinese Society of Aeronautics and Astronautics and Beihang University,CJA publishes papers bimonthly,with issues released in February,April,June,August,October and December.