FGH96/GH4169高温合金惯性摩擦焊微观组织及演变过程

对FGH96/GH4169异质高温合金惯性摩擦焊接头组织形貌及演变过程进行分析,测量了焊接过程的界面温度。结果表明,惯性摩擦焊近界面处最高温度超过1100℃,达到母材强化相固溶温度区间。摩擦初期GH4169侧率先产生磨损颗粒;摩擦过渡期磨损颗粒被细化,摩擦界面形成高温粘塑性金属,在顶锻压力作用下开始形成飞边,夹杂物随之被挤出;准平衡摩擦阶段界面处高温粘塑性金属被持续挤出,飞边增大。焊后于焊接界面处形成等轴细晶区,细晶区与母材间为热力影响区,产生明显的变形,形貌为拉长晶粒。     

挤压态喷射成形GH738合金热变形行为及组织研究

在温度950~1150℃、应变速率0.001~1 s–1及工程应变50%条件下,利用Gleeble-3500TM热模拟试验机对挤压态喷射成形GH738合金进行热压缩实验,研究合金的流变应力,建立合金热变形本构关系,利用EBSD分析合金组织演变。结果表明:合金流变应力随温度的升高和应变速率的减小而降低,在相同变形条件下,具有细晶组织特征的挤压态喷射成形GH738合金峰值流变应力低于粗晶组织的铸锻GH738合金;挤压态喷射成形GH738合金热变形激活能为651.08 kJ·mol–1,GH738合金的热变形激活能随着初始平均晶粒尺寸的减小而升高;形变温度的升高使挤压态喷射成形GH738合金初始被拉长的晶粒逐渐演变为等轴再结晶晶粒,在1000℃以上获得完全动态再结晶组织,再结晶组织随形变温度的进一步升高发生长大。     

环件惯性摩擦焊过程中轴向缩短量的数值模拟

建立了GH4169合金环形件惯性摩擦焊接过程的热力耦合有限元模型,计算了不同工艺条件下惯性摩擦焊工件的轴向缩短量,分析了初始转速、焊接压力和转动惯量对轴向缩短量的影响规律,计算了整个惯性摩擦焊接过程中摩擦副的轴向缩短量和轴向缩短速率,并做了相应的试验验证,计算结果和度验结果吻合较好.     

GH4169高温合金惯性摩擦焊接头温度场分布及变化规律

采用工控机实时检测系统,通过在焊接接头埋设热电偶的方法实时检测了GH4169高温合金惯性摩擦焊接过程中接头的温度变化历程,获得了接头轴向和径向的温度场分布,并结合摩擦机制分析了其变化规律。     

GH4169合金大型环形件惯性摩擦焊数值模拟

建立了GH4169合金大型环形件惯性摩擦焊的轴对称热力耦合分析模型:基于更新拉格朗日弹塑性有限元法分析了焊接过程的温度场和应力应变场:使用热电偶点焊到工件表面的方法对接头部分若干点的温度变化进行了实时测量,并与计算结果进行了对比.结果表明,计算结果与试验结果吻合良好.     

搅拌摩擦加工对Mg-2.67%Nd-0.5%Zn-0.5%Zr合金动态变形行为的影响

采用不同工艺对Mg-2.67%Nd-0.5%Zn-0.5%Zr合金进行了搅拌摩擦加工(FSP)处理,利用Hopkinson压杆对FSP处理前后的合金进行了冲击试验,探讨搅拌摩擦加工对该合金动态应力-应变行为及其应变率效应的影响。结果表明,FSP处理之后合金的显微组织因发生动态再结晶得到显著的细化,平均晶粒尺寸约由60μm减小至不足10μm。在高应变率冲击载荷下,合金母材的动态应力-应变行为表现出了明显的应变率强化效应,而FSP处理之后合金的动态应力-应变行为对应变率不敏感。这主要是由于经不同工艺FSP处理后,Mg-2.67%Nd-0.5%Zn-0.5%Zr合金产生的细晶强化及细小、弥散的沉淀相强化,大大提高了合金的变形抗力。     

GH4169合金超塑性及其复杂构件超塑成形

对GH4169高温合金板材超塑性及超塑成形进行了研究.研究结果表明:在典型的超塑成形应变速率范围(10-3～10-4)内,细晶GH4169合金在较宽的温度范围(920℃～980℃)内的延伸率都高于250%,最高延伸率可达513%,应变速率敏感性指数m值都大于0.3;合金在超塑过程中发生了晶粒动态长大,并且超塑变形后仍为等轴晶;利用超塑成形方法研制出了飞行器用GH4169合金燃气岐管,并通过了30MPa液压压力、保压10min的打压试验及20MPa、保压5min的气密试验.     

TC4-DT钛合金β锻动态再结晶元胞自动机模拟

通过对TC4-DT钛合金β单相区的等温恒应变速率压缩实验,分析合金的动态再结晶行为,并建立合金的动态再结晶的元胞自动机模型(CA模型)。在DEFORM-3D平台上,采用CA法模拟TC4-DT钛合金压缩过程中的显微组织演变。结果表明:随着应变量的增加动态再结晶的发生越来越充分;试样不同部位发生的动态再结晶程度有所不同,中心区域发生的动态再结晶更充分,很好地细化了原始组织;动态再结晶行为随着应变速率的增大而逐渐被抑制,但晶粒尺寸反而减小;模拟结果与实验结果相当吻合。     

δ相对GH4169合金热变形行为的影响

对GH4169合金进行四种不同工艺的热处理以得到不同的δ相析出状态,采用Gleeble-1500试验机在980℃下测试合金热变形特性.结果表明,GH4169合金经不同热处理后可获得不同初始状态的δ相含量及分布状态,合金中δ相的增加将降低合金变形抗力;δ相的存在促进变形合金再结晶形核和长大;晶界δ相的存在有利于热变形过程中的再结晶,而晶内δ相则阻碍形核过程;预先析出的δ相在变形过程中发生溶解.     

GH3044线性摩擦焊接头组织特征及其形成机制

进行了固溶强化型镍基高温合金GH3044线性摩擦焊接试验,光镜与扫描电镜组织观察、EDS成分分析及拉伸测试表明,接头中焊缝与热力影响区晶粒明显细化,碳化物分布发生改变使焊缝与热力影响区均可见明显流线,但未对接头拉伸强度造成影响,接头拉伸强度与母材相当。EBSD分析表明,接头主要发生了不连续动态再结晶,并伴随部分连续动态再结晶及静态再结晶,使焊缝与热力影响区中小角度晶界比例大幅增高,孪晶界大幅减少。热力影响区中小角度晶界比例更高,是因为该区形成较强织构而焊缝区再结晶更为充分。     

纯钛搅拌摩擦焊晶粒细化机制

通过搅拌摩擦焊实现了5 mm纯钛的可靠连接,并对焊接接头组织进行了细致研究。通过光学、扫描电子显微镜和透射电子显微镜对纯钛搅拌摩擦焊组织进行了精细表征,对焊接过程中的再结晶机制进行了研究。结果表明：采用搅拌摩擦焊可以得到成型良好,组织致密的焊缝;焊缝组织可以分为焊核区( NZ)、热机影响区( TMAZ)、热影响区( HAZ)和母材区( BM);根据各区组织形态和结构特点对纯钛搅拌摩擦焊动态再结晶过程进行了分析,揭示了纯钛搅拌摩擦焊焊缝细化机制;钛的层错能较大,搅拌摩擦产生的位错不能完全分解,遇到阻碍时,只能通过滑移和攀移继续运动,在多次搅拌摩擦作用下,位错缠结堆积,位错密度不断上升,产生新的晶界,从而形成细小晶粒,实现晶粒细化。     

TiAl金属间化合物与42CrMo"三体"摩擦焊接头的热机械处理

在对"三体"摩擦焊热机械处理(TMP)的作用原理进行理论分析的基础上,研究了接头的组织变化和动态再结晶规律,从而形成了以摩擦焊热力耦合与焊后热处理制度复合的TMP模式。     

Role of the inter-pass cooling rate in recrystallization behaviors of Ni-based superalloy during interrupted hot compression

The microstructural evolution of a Ni-based superalloy under interrupted hot compressive deformation with different cooling rates in the inter-pass stage is investigated. It is found that metadynamic recrystallization(MDRX) in the inter-pass stage is more sensitive to the accumulated strain than the deformation temperature which is above the recrystallization temperature. The variations of both the grain distribution and the texture intensity caused by MDRX during the interpass stage result in variations of the yield stress(YS) and the work hardening(WH) rate in each stage. Results also show that the MDRX process in the inter-pass stage has a considerable influence on the final microstructure of three-pass compression. The final grain distribution is more uniform,and the compression texture gradually transforms into recrystallization texture with an increasing degree of MDRX. In order to predict the MDRX fraction in the inter-pass cooling stage, a modified kinetic equation is established, which can reasonably predict the MDRX behavior under multi-pass compression with different conditions in the inter-pass stage. Meanwhile, the influence of the interpass cooling stage on the mechanism of dynamic recrystallization(DRX) is studied. It is universally acknowledged that the discontinuous dynamic recrystallization(DDRX) process is the major deformation mechanism for the Ni-based superalloy. However, the continuous dynamic recrystallization(CDRX) process is promoted in the compression stage with a decrease of the cooling rate in each inter-pass stage.     

Al-Li-Cu-Mg-Zr合金的超塑性研究

Al-1.91Li-1.25Cu-0.46Mg-0.21Zr合金超塑性变形结果表明,最佳的时效工艺是400℃8h;冷轧工艺得到了比温轧(550％)更高的超塑性延伸率(630％);最佳超塑性变形工艺是T=500℃,(?)_i=3.33×10~(-3)s~(-1)(起始拉伸速度)。研究指出,Al-1.91Li-1.25Cu-0.46Mg-0.21Zr合金的超塑性预处理的时效工艺和轧制工艺影响了合金超塑变形初期的应变诱发再结晶,从而影响超塑性性能。超塑变形中的动态回变和动态再结晶是晶界滑动的重要协调机制之一。     

应变对PH13-8Mo 钢在1 050 ~1 150时变形组织的影响

采用Gleeble热模拟试验机,对PH13-8Mo钢进行热变形模拟实验,研究了应变对PH13-8Mo钢在应变速率为10/s,变形温度为1050 ～1150℃时变形组织的影响.结果表明,PH13-8Mo钢在1 050℃、应变达到0.69时仍未发生完全再结晶,但在1100和1150℃、应变分别达到0.29和0.24后,发生了明显的完全再结晶.再结晶体积分数随应变增加和变形温度升高而逐渐增大,直至发生完全再结晶.当应变＜0.29时,再结晶晶粒尺寸和试样的平均晶粒尺寸随应变增加较快地减小；当应变＞0.29后,再结晶晶粒尺寸和试样的平均晶粒尺寸随应变增加缓慢地减小.再结晶晶粒尺寸和试样的平均晶粒尺寸均随变形温度的升高而增大.     

7075-T6铝合金厚板FSW焊缝沿厚度方向上的显微组织演变规律

采用金相显微镜（OM）、扫描电镜（SEM）和背散射电子衍射（EBSD）技术表征7075铝合金厚板搅拌摩擦焊（FSW）焊核中心区的微观结构，研究沿焊缝厚度方向上的显微组织演变规律。结果表明，焊核中心区发生了明显的动态再结晶，由原始粗大的板条状组织转变成了细小的等轴晶；随着距焊缝上表面距离的增加，中心区等轴晶晶粒尺寸呈现逐渐增大的趋势。其中，中心区上部4 mm处的晶粒尺寸最小，仅为7.8 μm；底部19 mm处的晶粒尺寸最大，达18.6 μm。中心区动态再结晶分数随距离的增大而逐渐减小，从中心区顶部1 mm处最大值90.4%减小至底部19 mm处最小值57.5%。受动态再结晶影响，焊核中心区主要以大角度晶界（HAGB）分布为主，且中心区大角度晶界随距离的增加呈逐渐降低的趋势；但每一个典型位置处的大角度晶界分布呈现先增大后减小的趋势，且在45°左右时达到最大值；此外，中心区并没有强取向组织产生。同时，焊核中心区主要以细小、弥散的二次析出强化相η相为主，且二次析出强化相颗粒尺寸随距离的增加而呈逐渐增大的趋势，但二次析出强化相颗粒总体数量却呈相反的趋势变化。     

2219铝合金变截面结构搅拌摩擦焊接工艺及组织特性

针对变截面结构产品,提出了一种变截面搭接结构搅拌摩擦焊接方法,通过加装辅助板将整条焊缝焊接方向上补偿为等厚度。焊接采用一次定位焊接+二次定位焊接+正式焊接的工艺方式,一次定位焊为预定位,二次定位焊保证辅助板与试片主体结构之间形成有效连接,正式焊保证形成完整的焊缝。焊缝表面成形良好,超声相控阵检测无超标缺陷。通过对力学性能的分析,变截面搭接结构处焊缝与非搭接处焊缝和常规对接焊缝的力学性能基本相同,平均抗拉强度均达到母材的70%以上,平均延伸率均在5.8%以上。变截面搭接焊缝焊核处晶粒形态为细小的等轴晶,靠近轴肩影响区部分的晶粒尺寸大于靠近焊缝根部的晶粒尺寸,受再结晶影响,焊缝两侧热机影响区处辅助板搭接界面消失。     

铝合金盘型件等温辗压过程中晶粒尺寸演化的数值模拟与实验验证

 为了揭示盘型件双面辗压成形过程中微观组织的演化特征,应用数值模拟方法研究了这一成形过程中所发生的动态再结晶和晶粒长大规律.所研究的盘型件材料为铝合金6061,辗压成形温度为350~500 ℃.晶粒尺寸演化规律的数值模拟结果与实验结果基本符合.与整体锻造不同,双面辗压成形没有变形死区,并且越靠近盘型件表面晶粒细化效果越好;辗压头通过对盘型件厚度方向压缩和表面环向剪切两种方式驱动盘型件变形.计算结果表明,即使压下量零增量辗压也会在沟槽附近产生显著变形和晶粒细化,这说明盘型件变形和组织演化主要源于辗压头对盘型件表面的环向剪切;多遍次辗压过程中,第1遍次辗压对晶粒细化的贡献最大,后续辗压的贡献较小;提高成形温度可能会出现动态晶粒长大区,在这种情况下,盘型件上的点将交替发生动态再结晶和动态晶粒长大,最终晶粒尺寸会有一定程度增加.     

TC11与TC17异质钛合金线性摩擦焊连接机理研究

为了探明TC11与TC17异质钛合金线性摩擦焊接头连接机理,采用扫描电镜来研究接头不同位置的微观形貌。结果表明,在振幅为3mm、频率为40Hz、摩擦压力为66.7MPa、摩擦时间为2s的条件下,在接头表面表现为"摩擦磨损"特征。在距接头表面2.5mm处,接头具有"粘着剪切"特征,且原始摩擦界面上有微孔存在,TC11钛合金发生了动态再结晶,而TC17未发生动态再结晶。在距接头表面5mm处,界面上有微孔存在,且在TC17焊缝与热机械影响区(TMAZ)交界处产生裂纹。在距接头表面7.5mm处,原始摩擦界面无微孔存在,在TC17焊缝与TMAZ交界处有裂纹存在。在距接头表面10mm处,接头内无缺陷存在。接头内不同位置的形貌在一定程度上反映了接头的形成过程。