一种铝锂合金搅拌摩擦焊接头力学性能及微观组织研究

研究了C24S-T8铝锂合金搅拌摩擦焊接头力学性能及微观组织。通过焊接工艺参数的优化,获得了无孔洞缺陷、焊缝质量优异的接头,强度系数约82%。拉伸时塑性变形及断裂集中于焊缝处。基材晶粒呈薄饼状,沿轧制方向拉长;焊核区为细小等轴的再结晶晶粒,平均晶粒尺寸约2.3μm,大部分晶界是大于15°的大角度晶界;热机影响区的晶粒在焊接过程中发生了偏转和变形。C24S-T8铝锂合金基材强化相包括T1相(Al2CuLi)、θ’相(Al2Cu)和S’相(Al2CuMg);热机影响区及焊核区内强化相完全溶解,造成硬度下降。     

2219铝合金无倾角式搅拌摩擦焊接头组织性能

采用基于三轴联动系统的无倾角搅拌摩擦焊方法,研究了2mm厚2219铝合金焊接试验过程,重点分析了微观组织分布特点和接头力学性能。结果表明,采用内聚花纹锥形轴肩搅拌工具,实现了无倾角搅拌摩擦焊接过程,焊缝外观及内部质量良好,但搭接界面处存在Hook现象,在前进侧呈现先向上后向下弯曲,指向焊核区的纹路特征,而后退侧呈现了向上弯曲的Hook钩状纹路;2mm厚铝合金2219无倾角式搅拌摩擦焊搭接接头拉伸剪切抗力平均为5630N,与母材抗拉力的比值为75.7%;同时,通过试验证明了无倾角搅拌摩擦焊方法对曲线焊缝的适应性。     

SiCp/Al复合材料与2024铝合金搅拌摩擦焊搭接接头的组织与性能

采用搅拌摩擦焊对SiCp/A1复合材料和铝合金异种材料的搭接进行了研究,并用光学显微镜和电子万能试验机对焊缝组织及力学性能进行了分析测试.结果表明:在合适的工艺参数下,可以获得较好的焊缝成形和无缺陷的焊缝组织.焊核区形成了明显的洋葱环形貌,洋葱环下方是搭接区,其中SiC颗粒细小,分布均匀,由搭接区下部到上部SiC颗粒呈梯度过渡.随焊接速度增加,搭接区SiC颗粒尺寸有所增加,在焊接速度为80mm/min时有裂纹形成,而焊缝力学性能也有所下降.在焊接速度为10mm/min时,焊缝抗剪强度较高,达到81.8MPa.     

晶粒尺寸对钛合金TIG焊接接头组织及力学性能的影响

进行了2μm及8μm,19μm三种晶粒尺寸的细晶粒TC4钛合金常规TIG焊试验,分析了母材晶粒尺寸对钛合金焊接接头组织转变规律及力学性能的影响。结果表明,细晶粒TC4钛合金焊缝中心和热影响区组织相似,为α马氏体组织。相同焊接规范下,随着晶粒尺寸的减小,焊缝中心和热影响区组织由编织(网篮)状α组织向片状组织过渡;随着晶粒尺寸的减小,热影响区晶粒长大越来越明显,热影响区细晶区(FHAZ)明显变窄,热影响区粗晶区(CHAZ)明显变宽,焊缝—热影响区—母材的晶粒梯度增大,焊接接头三区域晶粒过渡越来越差;随着晶粒尺寸的减小,焊接接头拉伸强度和伸长率均有不同程度的提高。常温拉伸断口呈准解理断裂特征,随着母材晶粒度的增大,焊接接头解理断裂特征越明显。     

薄壁铝合金搅拌摩擦焊接头组织及性能

对2mm厚的LY12铝合金板进行了搅拌摩擦焊接,对接头的微观组织和力学性能进行了分析.结果表明:当搅拌头旋转速度1000r/min、焊接速度200r/min时,焊核区为细小均匀的等轴晶,晶粒大小在2～6μm之间;热机影响区晶粒沿流线方向被拉长,前进侧比后退侧晶粒变化明显.焊缝成形良好,接头抗拉强度为438.72MPa,...     

6082铝合金双轴肩搅拌摩擦焊试板温度场研究

采用热电偶测温技术系统测定了6mm6082铝合金双轴肩搅拌摩擦焊试板各特征点的温度变化曲线,分析了双轴肩搅拌摩擦焊过程中焊接试板不同区域的温度场分布特征。双轴肩搅拌摩擦焊搅拌头上、下轴肩同时产热,比传统搅拌摩擦焊产热量大,且热输入方式及试板接触散热条件也有很大不同,因此,其稳定焊接速度较大,从而导致双轴肩搅拌摩擦焊试板温度场分布特征与传统搅拌摩擦焊明显不同。双轴肩搅拌摩擦焊过程分为加速焊接和稳定焊接两个阶段,起始阶段,随着焊接速度的增加,靠近起始端测温点的温度逐渐升高,而远离起始端各测温点的温度升温则非常缓慢,当焊接速度达到较高的稳定焊接速度,搅拌头接近后续各测温点时,其温度值瞬间急剧升高,然后随着搅拌头的远离,温度值逐渐下降。不同区域测温点温度测试结果显示,靠近下轴肩试板测温点的温度高于靠近上轴肩试板、后退侧的温度明显高于前进侧;与单轴肩搅拌摩擦焊接试板相同,距离焊缝越近的位置温度上升和下降的越剧烈,峰值温度越高;焊接速度提高,各测温点的峰值温度依次降低,随着测温点远离焊缝中心,焊接速度对其温度分布的影响作用逐渐减弱。     

TC17钛合金焊接接头组织与力学性能分析

对TC17钛合金薄板采用氩弧焊和电子束焊两种焊接方法焊接,进行了拉伸试验,结合拉伸试验结果与断口形貌,对比分析了力学性能与焊接接头组织之间的联系。研究结果表明,TC17钛合金在经历TIG焊接热循环后,焊缝及靠近焊缝的热影响区晶粒粗化,电子束焊接头热影响区较窄且没有粗晶区形成;两种焊接试样抗拉强度均与母材等强;相对延伸率有所降低,主要是热影响区及焊缝的组织变化所致;氩弧焊焊缝组织较不均匀性更为显著。     

焊接及热处理对T250马氏体时效钢薄壁旋压圆筒性能的影响北大核心CSCD

采用脉冲TIG焊对T250马氏体时效钢薄壁旋压圆筒进行焊接,通过优化焊接工艺参数,得到了外观成形良好,内部缺陷达到QJ175—93 0级标准要求的焊缝。在焊前和焊后对T250马氏体时效钢薄壁旋压圆筒进行了热处理,研究了热处理对焊接接头金相组织、显微硬度、角变形和力学性能的影响。结果表明:时效处理后,焊缝金属枝晶晶界中存在逆转变奥氏体组织,显微硬度低于母材;熔合线附近焊接热影响区晶粒长大,最大处晶粒约为基材的6倍;焊前时效处理大幅度减小了焊接接头角变形;在焊后对试样进行500℃时效处理的情况下,焊前时效处理使焊接接头抗拉强度和弯曲角都有所提高;焊前对旋压圆筒进行500℃时效处理,焊后进行500℃时效处理,得到了最佳焊缝强韧性匹配。     

GH536镍基高温合金焊接组织演变

使用体视显微镜、光学显微镜、扫描电镜及其能谱仪对GH536焊接接头组织进行分析,结果表明:固溶态GH536由γ基体、大量M6C及少量M23C6组成;焊后,大量M6C在晶内弥散析出,在晶界和孪晶界上不连续析出,原有的碳化物长大。热影响区分为三个区域:靠近母材处,存在粗大"岛链状"碳化物;中部,部分碳化物重新固溶入基体,存在"网链状"碳化物;靠近熔合线,存在碳化物贫化区。焊缝处碳化物在晶界和枝晶间析出,从边缘到中心逐渐凝固:初始阶段,组织为非外延式生长的胞状晶,生长方向垂直于熔合线;中间阶段,组织转变为柱状树枝晶,且越靠近焊缝中心,晶粒尺寸越大;中心为粗大的等轴状树枝晶。焊接过程中,焊缝金属中各元素未损失。     

基于Tanaka-Mura模型的电子束焊接头疲劳裂纹萌生模拟

为揭示高温合金电子束焊接头的疲劳特性,对其开展了疲劳裂纹萌生数值模拟研究。考虑焊缝区微观组织特性,对Voronoi图法进行改进,建立了焊缝区包含柱状晶、细等轴晶及粗等轴晶的混合晶区微观组织模型;对ABAQUS进行二次开发,考虑晶粒随机取向,生成晶粒多滑移带模型。基于Tanaka-Mura位错滑移模型,编写了疲劳裂纹萌生算法,考虑晶界处裂纹的连接与合并,对算法进行了改进,并结合有限元计算建立了电子束焊接头疲劳裂纹萌生数值模拟方法。基于上述方法对GH4169电子束焊接头不同载荷大小的疲劳裂纹萌生进行数值模拟,分析了裂纹萌生过程及萌生寿命,并与试验结果进行对比验证;还探讨了不同热影响区晶粒尺寸对焊接接头疲劳裂纹萌生的影响规律。结果表明,电子束焊接头疲劳裂纹均萌生于热影响区,但随着载荷水平的提高,萌生位置向熔合区一侧靠近;当热影响区晶粒尺寸与母材区晶粒尺寸越接近时,接头疲劳寿命越长。     

钛/铝异质金属搅拌摩擦焊技术研究进展

钛合金和铝合金均具有质轻、比强度高和抗腐蚀性能好等优点,已广泛应用于航空航天、军事工业和公共交通等领域,钛/铝异种金属复合结构的连接逐渐成为研究热点。然而,由于物理和化学性能差异明显,钛/铝焊接难度大,存在成形困难、接头性能较差等问题。搅拌摩擦焊作为一种固相焊接方法,对克服异种材料性能差异带来的焊接困难具有极大的优势。本文综述了钛/铝异质金属搅拌摩擦焊的研究现状,主要涉及焊缝成形、焊接参数、力学特征、冶金结合和连接机制等,以及衍生的搅拌摩擦焊新技术,为钛/铝异质金属结构的轻量化设计提供新思路,并对其未来发展进行了展望。     

2219薄板铝合金浮动式双轴肩搅拌摩擦焊接及组织性能分析

以运载火箭助推器贮箱广泛应用的4 mm厚2219薄板铝合金为焊接对象,研制了浮动式双轴肩搅拌头,分析了内部塑性金属流动模式及特点,并推测出需匹配较低焊接热输入才能获得优质焊缝。工艺探索及优化试验结果直接验证了焊缝内部塑性金属流动模式及推测。接头宏观组织形貌分析结果显示:不同焊接速度下的焊缝横截面宏观形貌都可以观察洋葱环特征,且随着焊接速度提高,洋葱环特征越发增多,并从靠近前进侧的焊核区逐渐向后退侧孕育发展,这也有效验证了薄板铝合金双轴肩搅拌头的设计思路。薄板铝合金双轴肩搅拌摩擦焊接头横截面显微硬度分布均呈"U"型,接头显微硬度最低点位于焊核区与后退侧热机影响区的交界处。接头力学性能测试结果显示:随着焊接速度逐渐升高,接头抗拉强度逐渐升高,且当焊接速度达到350 mm/min时,接头抗拉强度达到最高值。铝合金浮动式双轴肩搅拌摩擦焊接头延伸率整体较高,焊接速度对其影响不大。铝合金双轴肩搅拌摩擦焊接头正、背弯均可以达到180°无裂纹。基于立式纵缝搅拌摩擦焊系统成功实现了2 m长试片的浮动式双轴肩搅拌摩擦焊,累计焊接长度达到60 m,且双轴肩搅拌头完整,未发现裂纹、扭曲或其他损伤。     

Hot-cracking susceptibility and shear fracture behavior of dissimilar Ti6Al4V/AA6060 alloys in pulsed Nd:YAG laser welding

Laser welding of dissimilar titanium/aluminum alloys has been employed at an increasing rate, particularly in the aerospace industry, owing to its advantages in terms of current design flexibility and fuel/cost savings. The major problem with dissimilar Ti/Al welds arises from the difference in the thermal expansion and contraction of the two metals, which leads to hot-cracking susceptibility and the mitigation of the mechanical property after welding. In the present study, pulsed Nd:YAG laser welding of Ti6Al4V and AA6060 has been addressed. Hot-cracking susceptibility in the heat affected zone and the shear fracture behavior of the lap joints were investigated through microstructural characterization and mechanical tests. The results indicate that the hot cracking tendency can be reduced by increasing the pulse peak power (7.5–8.5 kW) and the laser point diameter (0.8–1.0 mm) with specific pulse duration and overlap. An alternative control strategy for less hot cracks in the Ti/Al lap joint can be to increase the weld width and decrease the cooling rate during solidification. The shear fracture of the Ti/Al lap joint is likely to occur along the lower side path of the weld interface with decreasing weld surface collapsed amount and increasing aluminum base metal melt depth.     

00Ni18%马氏体时效钢的氩弧焊工艺试验研究

近期对00Ni18%高强度马氏体沉淀硬化时效钢的焊接性能进行了试验研究,探索出了适用于该钢薄壁旋压筒体自动钨极氩弧焊的焊接工艺规范,同时对比、分析了不同的热处理工艺对该钢氩弧焊接头力学性能和显微组织的影响.结果表明:在相同的焊接规范参数下,固溶+焊接+固溶+时效后焊缝及热影响区已有了一定的细晶粒,组织中含有大量的金属间化合物沉淀强化质点,焊接接头及母材都呈现出了高强度和高韧性相搭配的优异性能.     

焊接顺序对TA15钛合金壁板焊接变形的影响

建立了TA15钛合金壁板焊接有限元模型,利用热弹塑性有限元法分析了焊接顺序对壁板变形的影响。通过对比焊缝截面宏观形貌和残余应力,建立了TIG穿透焊焊接工艺的双椭球热源模型,进而模拟了5种焊接顺序下壁板变形情况。结果表明:按从一侧开始的顺序进行焊接时,下壁板中部边缘凸起,最大变形量为3.9mm;采用对称施焊,可有效地控制壁板变形量。     

Microstructural formation and mechanical performance of friction stir double-riveting welded Al-Cu joints

A novel friction stir double-riveting welding (FSDRW) technology was proposed in order to realize the high-quality joining of upper aluminum (Al) and lower copper (Cu) plates, and this technology employed a Cu column as a rivet and a specially designed welding tool with a large concave-angle shoulder. The formations, interfacial characteristics, mechanical properties and fracture features of Al/Cu FSDRW joints under different rotational velocities and dwell times were investigated. The results showed that the well-formed FSDRW joint was successfully obtained. The cylindrical Cu column was transformed into a double riveting heads structure with a Cu anchor at the top and an Al anchor at the bottom, thereby providing an excellent mechanical interlocking. The defect-free Cu/Cu interface was formed at the lap interface due to the sufficient metallurgical bonding between the Cu column and the Cu plate, thereby effectively inhibiting the propagation of crack from the intermetallic compound layer at the lap interface between the Al and Cu plates. The tensile shear load of joint was increased first and then decreased when the rotational velocity and dwell time of welding tool increased, and the maximum value was 5.52 kN. The FSDRW joint presented a mixed mode of ductile and brittle fractures.     

铝合金ZL114A的激光焊接工艺

主要研究了铝合金ZL114A的激光焊接工艺特性.首先对其可焊性进行了摸索,然后探讨了激光焊接工艺参数对焊缝熔深、焊缝宽度以及接头组织和力学性能的影响.结果表明,选择适当的激光焊接工艺参数,如：激光功率、焊接速度、离焦量、保护气体流量等,可以获得高质量的焊缝.组织观察发现,焊缝组织致密、晶粒细小,接头强度可以满足使用要求.     

板宽对胶焊接头应力分布影响的数值分析

采用三维弹塑性有限元方法,研究了酚醛树脂和丙烯酸树脂两种胶粘剂的胶焊接头中,板宽对应力分布的影响。结果表明,酚醛树脂胶粘剂胶焊接头中,搭接区边缘应力值高于焊点边缘应力值,导致接头从搭接区边缘起裂,板宽增大时,焊点边缘处和搭接区边缘的峰应力都减小,对于提高胶焊接头的强度有利,但不会改变接头的断裂形式;丙烯酸树脂胶粘剂的胶焊接头,焊点边缘应力远高于搭接区边缘应力,因此接头从焊点边缘起裂,板宽增大时,焊点边缘应力基本不变。因此增加板宽对提高接头强度无明显作用,接头断裂形式也不发生改变。     

2219铝合金双轴肩搅拌摩擦焊与熔焊交叉接头的组织及性能

文摘对2219C10S铝合金进行双轴肩搅拌摩擦焊接,之后沿垂直于双轴肩搅拌摩擦焊方向进行变极性TIG焊接制备交叉接头,并对比分析了交叉接头与单一TIG接头的组织和力学性能。交叉接头与单一TIG接头的组织特征既有相同之处也存在差异。相同之处为焊缝区均由直流氦弧焊作用下的柱状区和交流脉冲氩弧焊作用下的碗状区组成;不同之处在于两者的母材区分别为细小等轴晶和轧制板条晶粒,而热影响区都是在母材晶粒上发生粗化长大。显微硬度测试结果表明,两类接头的横截面显微硬度分布均呈"W"型,单一TIG接头的的显微硬度分布梯度大于交叉接头,但交叉接头的软化区宽度更窄。拉伸测试结果得出,两类接头均断裂于接头的热影响区。沿SR-FSW焊缝方向的交叉接头的抗拉强度系数为66.14%,略低于单一TIG接头,但接头延伸率比单一TIG接头高约30%。断口形貌研究表明,交叉接头的断口形貌为典型的韧性断裂,而单一TIG接头还可观察到部分脆性断裂特征。