不同损伤尺寸铝合金结构疲劳寿命分散性研究

飞机损伤结构疲劳寿命分散系数是分析损伤结构疲劳寿命分散程度的重要参数。针对飞机常用铝合金材料，开展预置损伤试验件疲劳测试。采用相关系数比较法，判断损伤结构剩余疲劳寿命分布类型；通过断口观察和数据统计处理，分析损伤与疲劳寿命关系及含损伤结构剩余疲劳寿命分散性规律。结果表明：含损伤结构剩余疲劳寿命更加符合威布尔分布；含预置损伤结构较未预置损伤结构疲劳寿命下降明显，随预置损伤尺寸增加，结构剩余疲劳寿命逐步降低，剩余疲劳寿命分散性增大，不同初始损伤结构疲劳寿命分散性差异较大。本文研究为建立飞机不同损伤尺寸铝合金结构疲劳寿命分散系数模型提供参考依据。     

基于临界距离理论的TC4合金缺口试样 低循环疲劳寿命预测

对TC4合金缺口试样的临界距离和低循环疲劳寿命分别进行了分析和预测.研究了缺口临界距离与疲劳寿命、载荷比、应力集中系数的相关关系及其对寿命预测结果的影响.研究结果表明:TC4合金缺口试样的临界距离不仅与疲劳寿命有关,还与载荷比和应力集中系数相关.载荷比相同时,临界距离与疲劳寿命之间可采用幂函数经验公式来描述.载荷比为-1和0.1时,TC4合金缺口试样的临界距离-疲劳寿命曲线基本重合,当载荷比增大为0.5时,临界距离明显增大.载荷比和疲劳寿命相同时,临界距离与应力集中系数近似成反比关系.寿命预测结果表明:采用临界距离理论预测TC4合金缺口疲劳寿命时,要获得更准确的疲劳寿命预测结果,应同时考虑临界距离与疲劳寿命、载荷比以及应力集中系数等因素的相关性.      

Crack monitoring method based on Cu coating sensor and electrical potential technique for metal structure

Advanced crack monitoring technique is the cornerstone of aircraft structural health monitoring.To achieve real-time crack monitoring of aircraft metal structures in the course of service,a new crack monitoring method is proposed based on Cu coating sensor and electrical potential difference principle.Firstly,insulation treatment process was used to prepare a dielectric layer on structural substrate,such as an anodizing layer on 2A12-T4 aluminum alloy substrate,and then a Cu coating crack monitoring sensor was deposited on the structure fatigue critical parts by pulsed bias arc ion plating technology.Secondly,the damage consistency of the Cu coating sensor and2A12-T4 aluminum alloy substrate was investigated by static tensile experiment and fatigue test.The results show that strain values of the coating sensor and the 2A12-T4 aluminum alloy substrate measured by strain gauges are highly coincident in static tensile experiment and the sensor has excellent fatigue damage consistency with the substrate.Thirdly,the fatigue performance discrepancy between samples with the coating sensor and original samples was investigated.The result shows that there is no obvious negative influence on the fatigue performance of the 2A12-T4 aluminum alloy after preparing the Cu coating sensor on its surface.Finally,crack monitoring experiment was carried out with the Cu coating sensor.The experimental results indicate that the sensor is sensitive to crack,and crack origination and propagation can be monitored effectively through analyzing the change of electrical potential values of the coating sensor.     

基于健康监测的飞机结构寿命预测技术

飞机结构健康监测技术在飞机的结构设计、飞行及维护过程中发挥着重要作用,该技术可用于结构健康状况预判、辅助维修与维护决策。本文首先介绍了当前结构健康监测的概念及其适用范围,讨论了结构健康监测相关规范要求,以F-35 和A400M 为例分析了国外飞机结构健康监测技术的典型工程案例,并给出了典型飞机单机跟踪和寿命控制、某老龄飞机载荷谱实测及寿命预测,讨论了基于裂纹的监测方法研究及限制其应用的主要因素。在此基础上,提出了飞机结构健康监测系统设计的主要思路,给出了寿命预计的基本流程,阐述了其中控制点选择、飞参筛选、载荷/应变方程构建、损伤计算及寿命评估、结果输出及方程验证等主要环节。最后,对航空领域未来开展结构健康监测智能化研究进行了展望。     

Simplification approaches for multi-level load spectra by using equivalent damage rule

Reasonable and effective fatigue load spectrum is key of aircraft structural fatigue test. Two kinds of load spectra simplification approaches based on statistical consistent fatigue damage model are proposed in the paper. One method is to simplify the original multi-level load spectra to spectral load with fewer level and was verified by the experimental data of five levels and seven levels load spectra. The equivalent damage here is not equivalent fatigue life, but equivalent number of spectral blocks. Moreover, it was proved that a section of low stress load cannot be converted into the highest stress load considering equivalent damage. The other is to convert the life distribution under multi-level load spectra into that of constant amplitude spectrum according to a certain principle, that is, equivalent damage is achieved through equivalent fatigue life, and two groups of three levels spectral data were used for experimental verification. The results show that equivalent damage simplification approach of multi-level load spectra is feasible, and it achieve that the damage of one loading block before and after the simplification is equal in probability statistics. The life distribution of load simplified as constant amplitude spectrum is consistent with test data. The simplification method presented in this paper can be generalized and is a predictive engineering method which does not depend on experimental data.     

综合考虑载荷谱和结构特性分散的概率断裂力学方法

在飞机结构的设计定型阶段,要综合考虑载荷谱和结构特性的分散评估机群的可靠寿命。为此,进行了某型飞机结构细节的TA15M钛合金模拟试件在3个单机谱下的耐久性试验,断口判读得到主裂纹扩展(a,t)数据,反推得到了当量初始缺陷尺寸(EIFS)。对比分析表明,载荷谱分散对EIFS分布参数无影响,估计得到了通用EIFS分布参数。建立了考虑载荷谱分散的裂纹扩展对数正态随机变量模型及参数估计方法,由此确定裂纹超越概率并进行损伤度评估,建立了综合考虑载荷谱和结构特性分散的概率断裂力学方法(PFMA)。     

基于飞行科目统计分析的严重谱编制方法

我国飞机的疲劳试验绝大多数采用均值谱,具有疲劳周期较长的缺陷,若采用载荷严重谱则可以大大缩短试验时间。为满足全机试验疲劳寿命评估的需要,响应国内外飞机强度规范的要求,以国内某教练机的起落数据为基础,将任务分析法与统计思想相结合,建立基于飞行科目统计分析的严重谱编制方法,整理和完善编谱流程,编制得到各飞行科目包含加权中值载荷谱,一倍标准差谱,两倍标准差谱,90%存活概率95%置信度的严重谱,以及所有科目的总严重谱。通过K-S检验方法验证了载荷损伤分布的合理性,并根据当量损伤计算的统计结果给出严重谱代表起落的选取方法。结果表明:此严重谱编制方法合理有效,得到的编谱结果符合严重谱特征,选出的代表起落能够代表各飞行科目不同严重程度的使用情况。     

航空发动机典型材料超高周疲劳试验技术研究综述

航空发动机作为飞行器最关键、最核心的部位，长期服役于高温、高载等极端环境，疲劳失效是导致发动机结构破坏的主要原因之一。随着工业的发展，发动机材料的超高周疲劳问题日益凸显。本文总结了发动机典型材料超高周疲劳关注领域的研究现状，对当前超高周疲劳试验技术的应用情况进行了阐述，包括超高周轴向振动疲劳、弯曲振动疲劳、扭转振动疲劳、复合振动疲劳等试验加载技术以及温度控制技术、损伤监测技术，并对我国航空发动机典型材料超高周疲劳试验技术的发展做出展望。     

求飞机结构真实腐蚀容限的原理和方法

本文通过静强度、疲劳强度和腐蚀3个学科的综合研究,分别给出飞机结构（下称机件）在静载荷作用下的应力与腐蚀损伤D的分布曲线和机件在疲劳载荷作用下的寿命与腐蚀损伤D的分布曲线。根据这两条曲线和机件使用的容限应力值及总疲劳寿命值,便可分别求出机件在静载荷作用下的腐蚀损伤容限值和机件在疲劳载荷作用下的腐蚀损伤容限值以及同一机件同时受静载荷和疲劳载荷作用的腐蚀损伤容限值。此外,本文提出了用一个腐蚀损伤容限值保证同一机件的总疲劳寿命和总日历寿命皆安全的方法,以及总疲劳寿命和总日历寿命的匹配设计和匹配使用等问题。研究结论适用于大气、海洋、土壤等环境的腐蚀机件,解决了国际机械和腐蚀领域一直未解决的一些难题。     

安—24飞机延寿疲劳试验中裂纹临界长度和扩展寿命的计算

在飞机结构疲劳试验中,正确地给出裂纹的临界长度和扩展寿命是圆满完成疲劳试验,并保证损伤后的飞机能够通过剩余强度试验的关键环节。本文采用能量释放率法计算了安-24飞机延寿疲劳试验中主要裂纹的应力强度因子.并确定了临界长度和扩展寿命。这为适时结束安-24飞机疲劳试验,进行l审j余强度试验提供了理论分析依据,这里所给出的确定裂纹临界长度和扩展寿命的分析方法,对飞机结构疲劳试验和剩余强度试验有较高的参考价值;同时,这种分析方法对服役飞机出现裂纹后正确确定检测周期也具有一定参考价值。