为了改善高体积比铝基SiC复合材料的可加工性,提高加工效率,本文对高体积比铝基SiC复合材料进行了平面铣磨加工试验研究.试验结果表明,高体积比铝基SiC复合材料在铣磨加工中主要表现为脆性材料的特性,电镀金刚石砂轮在磨削过程中不会出现磨屑粘附现象.SiC颗粒的破损程度是影响表面粗糙度的主要因素,并且在相同磨削参数和条件的情况下随着颗粒的破损程度、砂轮粒度的增大和进给速度vf的降低,磨削表面的粗糙度值会逐渐减小.在给定其他试验参数的情况下,120#的φ8mm电镀砂轮适合进行粗磨,并且磨削的材料去除率能够达到2400mm3/min,同时进给抗力Fz小于25N,磨宽抗力Fx和磨深抗力Fy小于15N.使用230#的φ8mm电镀砂轮进行精磨能够保证表面形成率达到6400mm2/min,并使表面粗糙度优于Ra0.4μm.     

SiC晶须增强铝复合材料的超精切削

本文阐明了ＳｉＣｗ／Ａｌ超精密切削加工时，刀具材料、金刚石粒度、切削路径及晶须方向对加工表面粗糙度的影响规律。     

《航空精密制造技术》2002年总目录

综述大规模定制概述（１）超精密加工技术的现状和展望（３）２１世纪的切削刀具…………………………………………（５）大规模定制下质量保证的研究……………………………（６）精密加工SiC晶须增强铝基复合材料超精密切削试验研究………（１）金刚石薄膜图形化技术的研究……………………………（１）超声振动切削金属基复合材料的刀具磨损………………（２）ELID精密镜面磨削技术的开发应用………………………（２）超精密车床主轴回转精度动态测试机构的研制…………（２）超光滑表面杂质微粒的识别与统计技术…………………（３）…     

磨料电化学射流加工SiCp/Al复合材料仿真和试验

碳化硅颗粒增强铝基复合材料(SiC_p/Al)具有优异的物理及力学性能,但是其二次加工极为困难。仿真和试验研究了SiC_p/Al复材的磨料电化学射流加工。结果表明,随着铝基体的去除,SiC增强体与铝基材之间的结合界面不断减小,界面的疲劳寿命随界面面积减小而呈现若干数量级式降低。当结合界面面积下降到较低水平时,SiC增强相会从基体材料上脱落,同时在加工表面留下微坑。加工表面的粗糙度与这些微坑的数量和尺寸高度相关。SiC增强相尺度越大或含量越高,则加工表面越粗糙。     

微量液相与铝基复合材料的高应变速率超塑性

对展现高应变速率超塑性变形行为的β－ＳｉＣ晶须增强ＬＹ１２铝基复合材料、β－ＳｉＣ晶须增强Ｌ４纯铝基复合材料进行了差示扫描量热（ＤＳＣ）分析,探讨微量液相在铝基复合材料高应变速率超塑性变形过程中的作用。研究表明：适当的微量液相是铝基复合材料获得好的高应变速率超塑性的必要条件。     

C-SiC陶瓷基复合材料磨削参数优化研究

通过C-SiC陶瓷基复合材料的正交磨削试验进行磨削参数优化研究,探讨磨削参数对内锥体表面粗糙度的影响规律,提出了磨削参数的优化原则,获得了优化的磨削参数,提高了陶瓷基复合材料内锥体精密磨削的表面加工质量。     

PCD刀具车削不同颗粒含量SiCp/Al复合材料试验研究

碳化硅铝基复合材料具有优良的导热性、较高的比强度和比刚度,在航空航天领域具有广泛的应用前景。由于此复合材料中含有增强相,导致材料的切削加工性能变差。通过试验分析了不同颗粒体积分数(纳米级5%、微米级25%)SiCp/Al复合材料和切削参数(切削速度、背吃刀量、进给量)对刀具磨损和工件表面质量的影响,并对刀具磨损机理进行了研究。试验结果表明,车削微米级25%SiCp/Al材料时聚晶金刚石PCD(Polycrystalline Diamond)刀具磨损更严重,且工件表面质量更差。随着进给量和背吃刀量的增大,工件表面粗糙度值增大,刀片前刀面磨损严重;随着切削速度的增大,工件表面粗糙度值减小,刀片前刀面磨损量增大。选取本文切削参数进行SiCp/Al复合材料的切削加工时,发现刀具磨粒磨损、微崩刃是PCD刀具后刀面磨损的主要成因,且刀具前刀面也会产生积屑瘤。研究结果可为SiCp/Al复合材料PCD车削工艺的优化提供理论基础。     

SiCw／Al复合材料的拉伸性能与变形行为

本文对SiCw/6061Al复合材料进行了拉伸试验和断口分析。结果表明,该材料具有与基体合金大致相同的比例极限,但却具有高的加工硬化率,其抗拉强度远高于基体合金。复合材料低的比例极限可由晶须端部应力集中所导致的低应力局部塑性变形来解释。高的加工硬化率则与变形过程中复合材料基体中的位错大量增殖及晶须裂纹扩展的阻碍作用有关。由细小韧窝组成的复合材料断口表征了塑性变形的局部性。     

超精密加工技术的发展

以单点金刚石车削和超精密金刚石磨削为基础的超精密加工能够经济地制造光学、机械和电子部件,或生产在微米和毫微米范围内的成形精度和表面粗糙度的产品。辅助成形精度和表面粗糙度测量技术在评估超精密加工表面质量中也起着重要作用。在香港建立了超精密加工中心,用各种设备和技术服务帮助当地企业对高质量超精密产品进行快速研制和试验超精密加工技术的发展     

TiAl合金精密振动电解加工表面质量的研究

电解加工技术是解决Ti Al合金难切削的有效工艺方法,而精密振动电解加工技术可实现高精度及良好的表面质量。开展了精密振动电解加工Ti Al合金试验,研究了不同工艺参数下Ti Al合金的精密振动电解加工表面质量。结果表明:随着电流密度的增加,工件表面粗糙度减小;随着脉冲频率的提高,工件表面粗糙度先减小后基本保持不变。优化参数后采用精密振动电解加工的试件表面在光学显微镜下均未见到晶间腐蚀。     

旋转条件下切割SiC 单晶片实验研究

通过旋转条件下切割SiC单晶片,分析了切片表面微观形貌特点,研究了线锯速度、工件进给速度和工件转速对切片表面粗糙度与切向锯切力的影响规律。结果表明:增加工件旋转,切片表面平整光滑,沿线锯运动方向没有明显沟槽及凸起,质量明显得到改善;当转速由0增加到12 r/min时,切片表面粗糙度由1.532μm降到0.513μm;线锯速度和工件旋转速度增大、工件进给速度减小,切向锯切力减小,表面粗糙度减小。当线锯速度和工件旋转速度过大,切向锯切力和表面粗糙度反而会有所增加。     

TC4钛合金侧铣加工表面形貌分析及工艺参数优化

TC4钛合金是 1种典型的不易加工材料,其切削加工表面质量很难控制。为实现面向侧铣加工表面形貌的切削工艺参数优选,开展了 TC4钛合金侧铣加工实验研究。首先,探究了加工表面微观缺陷特征及其形成机制;然后,采用粗糙度参数 Ra和 Sa对铣削表面形貌进行定量表征,并分析了切削速度、进给量和切削深度对表面粗糙度参数的影响;最后,基于遗传算法(Genetic Algorithm,GA)对铣削工艺参数进行了优化。研究发现,加工表面微观缺陷主要有进给刀痕等固有缺陷和黏附颗粒等随机缺陷。铣削表面粗糙度随主轴转速的增大先减小后增大;随径向切深的增大先增大后减小;随进给量先增大后减小。在主轴转速 n = 1 093 r/min、径向切深 ae = 0.2 mm、每转进给量 f = 0.06 mm/r的条件下可以获得较小的表面粗糙度。     

加工工艺对7075 铝合金紧固孔表面质量的影响

为确定最佳制孔工艺、获得理想表面特性,从表面完整性和疲劳寿命角度对7075铝合金飞机紧固孔表面质量进行了实验性和数值仿真研究.通过比较常规多步制孔和钻扩铰一步复合工艺(Winslow),发现钻扩铰多步慢进给工艺(DBM)和Winslow所产生的表面具有较小的Ra值,较少的加工缺陷、较大的残余压应力及较高的疲劳强度,而后者的Ra值低于前者60％,疲劳寿命高于前者23％;基于实验数据,建立了切削参数对表面粗糙度和残余应力影响的经验公式;应用数值仿真分析了加工过程中应变和切削温度的变化规律;探讨了Winslow工艺的强化机理;指出适当减少进给量、增加切削速度能够提高紧固孔的表面质量.     

次摆线走刀在高速铣削窄槽结构中的应用

在阐述次摆线参数方程的基础上,基于CAM/HSM技术,将次摆线走刀方式应用于窄槽结构的高速铣削试验中,研究了次摆线走刀的铣削力变化规律、窄槽结构的表面粗糙度及其局部形貌,并建立了次摆线走刀高速铣削窄槽结构的铣削力模型。研究表明:次摆线走刀高速铣削窄槽结构有效可行,加工出了高质量的窄槽型腔表面(Ra=0.142μm);次摆线走刀的铣削力呈周期变化,在走刀平面内,次摆线切削宽度方向上的铣削力是进刀宽度方向上的4倍;采用次摆线走刀加环切走刀策略加工窄槽结构,既改善了窄槽的铣削加工条件,又满足了高速铣削粗精加工的要求和原则。     

Research on Ultrasonic Vibration Grinding of the Hard and Brittle Materials

It is well known that grinding techniques are main methods to machine hard and brittle materials such as engineering ceramics. But the conventional grinding has many shortcomings such as poorer surface finish,quicker wear and tear of grinding tools,lower effi-ciency and so on. Ultrasonic vibration grinding (UVG) which combines ultrasonic machining and grinding emerged as a developing and promising technique in recent years. In this paper,experimental studies on UVG were conducted on several kinds of hard and brittle material by altering processing parameters such as vibration frequency and its amplitude,diamond abrasive grit size,cutting depth,feeding speed and rotary speed of tools. The experimental results show that alteration in any of above mentioned parameters will bring effects on the processed surface finish of these materials. Of them,the diamond abrasive grit size has the greatest. Moreover,conven-tional grinding experiments were also carried out on these materials. By comparison,it was found that the UVG is superior to the con-ventional method in terms of the ground surface quality,the working efficiency and the wear rate of tools.     

Elliptical vibration cutting of large-size thin-walled curved surface parts of pure iron by using diamond tool with active cutting edge shift

Large-size thin-walled curved surface parts of pure iron are crucial in aerospace, national defense, energy and precision physical experiments. However, the high machining accuracy and surface quality are difficult to achieve due to the serious tool wear and deformation when machining the parts with conventional cutting tools. In this paper, an elliptical vibration cutting (EVC) with active cutting edge shift (ACES) based on a long arbor vibration device is proposed for ultra-precision machining the pure iron parts by using diamond tool. Compared with cutting at a fixed cutting edge, the influence of ACES on the EVC was analyzed. Experiments in EVC of pure iron with ACES were conducted. The evolutions of the surface roughness, surface topography, and chip morphology with tool wear in EVC with ACES are revealed. The reasonable parameters of ultra-precision machining the pure iron parts by EVC with ACES were determined. It shows that the ACES has a slight influence on the machined surface roughness and surface topography. The diamond tool life can be significantly prolonged in EVC of pure iron with ACES than that with a fixed cutting edge, so that high profile accuracy and surface quality could be obtained even at higher nominal cutting speed. A typical thin-walled curved surface pure iron part with diameter ∅240 mm, height 122 mm, and wall thickness 2 mm was fabricated by the presented method, and its profile error and surface roughness achieved PV 2.2 μm and Ra less than 50 nm, respectively.     

慢刀伺服加工自由曲面的表面形貌预测

本文通过建立自由曲面车削加工的仿真预测模型,在加工前进行参数优选.该模型考虑了刀具几何形状、切削用量及刀具轨迹点和插补方法对加工后自由曲面的表面形貌的影响.对渐进式近视镜片光学元件进行了加工实验,实测粗糙度R_a=31nm,仿真得到粗糙度R_a=23nm.实验验证了仿真模型的有效性.     

TC9钛合金拉削加工性与表面完整性的试验研究

 本文介绍了用P18、M2Al、M42等三种高速钢拉刀低速拉削TC9钛合金时的刀具磨损、拉削表面完整性同拉削工艺条件的关系,同时也探讨了用H19硬质合金拉刀高速拉削TC9钛合金的可能性;并比较了两种拉削条件下的刀具磨损和表面完整性状况;分析了为提高钛合金拉削的表面完整性所应采取的措施。     

不锈钢镜面的游离磨粒精密加工

利用游离磨粒加工方法对马氏体平面不锈钢SUS440C试件进行精密加工.通过田口实验方法对研磨阶段的工艺参数进行了优化,涉及的工艺参数包括研磨盘转速、加工载荷和加工时间.利用优化的研磨工艺加工后试件表面粗糙度达Ra72nm.抛光过程中使用聚氨酯抛光垫和二氧化硅磨粒,经抛光后试件表面粗糙度达Ra8nm、表面呈镜面.     

闭式整体叶盘通道五坐标分行定轴加工刀轴矢量规划方法

闭式整体叶盘是新一代航空发动机实现减重增效的关键零件,其通道结构属于典型多约束复杂通道结构。针对闭式整体叶盘通道精加工,提出了一种基于五坐标分行定轴加工的刀轴矢量规划方法。从加工原理上给出了分行定轴加工方法的基本概念,并分析了闭式整体叶盘通道五坐标加工的特征;在刀具预定义和建立检查面球体包围盒层次树结构的基础上,给出了刀轴矢量无干涉区域的计算方法;基于刀位点最短刀长的计算与分析,进行了叶盘通道加工区域划分,建立了分行定轴加工刀轴矢量规划方法。实验验证表明:分行定轴相对五轴联动加工方法不仅可明显提高加工过程中的稳定性和叶片加工表面质量,还可提高叶片精加工效率。