Effects of Shot Peening Process on Thermal Cycling Lifetime of TBCs Prepared by EB-PVD

Conventional two-layered thermal barrier coatings (TBCs) are prepared by electron beam physical vapor deposition (EB-PVD) with ZrO2-8 wt% Y2O3 (8YSZ) as top coat and CoCrAlY as bond coat on disk-shaped Ni based super-alloy. In this paper, three kinds of shot peening process with different lengths of operating time were adopted for bond coating. As a result, changes took place in its sur- face roughness and the surface micro-hardness. A thermal cycling test at 1 273 K×55 min and another at room temperature for 5 min were performed to study the effects of shot peening process on the thermal cycling lifetime of TBCs. It is found that a moderate shot peening process will be able to prolong the life time. The oxidation dynamic of the as-processed TBCs basically accords with the para- bolic rule, and the oxidation test also attests to the spallation between YSZ and thermal growth oxide (TGO) responsible mainly for the failure of TBCs.     

热障涂层表面裂纹水浸超声检测

为有效检测热障涂层(TBCs)表面裂纹,进行了热障涂层表面裂纹水浸超声检测技术的应用研究。以常用的大气等离子喷涂(APS)热障涂层作为试验材料,采用水浸超声检测回波声程差和C扫描图像对不同深度、宽度和长度的热障涂层表面裂纹进行了表征。结果表明:热障涂层基体材料对热障涂层表面裂纹的检测效果无明显影响;通过优化检测参数和合理选用仪器探头,利用水浸超声方法可实现对热障涂层表面深度为0.1 mm、长度为2 mm裂纹的有效检测;水浸超声检测技术可以获得裂纹的长度、深度参数,是解决热障涂层表面裂纹检测问题的有效方法。      

APS热障涂层氧化动力方程适用性实验

使用实验的方法研究了大气等离子喷涂(APS)热障涂层在4种不同高温环境下的氧化层生长规律, 并且使用目前常见的两种氧化层生长动力学曲线方程拟合了涂层氧化的实验数据, 分别得到了相应的方程特征参数值.研究结果表明:APS热障涂层在所研究的4种温度下的动力学曲线形式上是一致的;抛物线形式的动力学方程只能描述较高温度下的氧化层生长规律, 而幂函数形式的动力学方程对氧化温度的适应能力比较强, 能很好的描述在所研究的4种温度下APS热障涂层的生长规律.      

航空发动机涡轮叶片热障涂层应用的关键技术和问题

热障涂层是提高涡轮叶片可靠性和服役寿命的关键技术。从热障涂层的粘结层与涡轮叶片高温合金基体的匹配性、CMAS(一种基于CaO、MgO、Al2O3和Si O2等多种氧化物构成的环境沉积物)形成及其对热障涂层的损伤和相应的防护、叶片热障涂层厚度分布的过程控制、热障涂层制备过程中气膜孔缩孔、热障涂层的在线无损检测及涂层返修以满足涡轮叶片全寿命周期需求等方面论述了航空发动机涡轮叶片热障涂层工程应用技术和需要解决的实际问题。     

热障涂层的激光表面改性参数优化和结构设计

热障涂层是航空发动机涡轮叶片关键核心技术之一,但在服役条件下常受环境沉积物、熔盐等的腐蚀而过早失效。激光表面改性是一种提高涂层抗腐蚀性能的有效办法,但改性涂层的激光工艺优化和结构设计亟待研究。本文采用脉冲Nd：YAG激光系统对Y₂O₃部分稳定ZrO₂（YSZ）热障涂层进行表面改性,研究了激光功率、扫描速度以及光束长度对改性层厚度、微观结构的影响。结果表明,激光改性层呈致密的柱状晶结构,并有纵向裂纹贯穿其中。改性层的厚度与激光功率成正比,受扫描速度影响不大,与光束长度成反比。激光功率过高,则改性层裂纹增加明显;光束长度过大,则改性层与下方涂层的界面缺陷增多,不利于界面结合。优化的激光改性参数为：激光的功率为75~80 W,扫描速度8 mm/s,光束长度为160 mm。设计了双层激光改性层,每层中的纵向裂纹不连续,使得整个改性层中无贯穿的纵向裂纹,有助于抑制高温腐蚀熔体的内渗。     

基体曲率对热障涂层结合强度影响的无损检测研究

 针对复杂型面航空发动机涡轮叶片表面热障涂层(TBCs)的失效问题,采用交流阻抗谱(IS)法和洛氏硬度(RH)压痕法对比研究了制备在平板基体和曲率基体上,热障涂层在热循环过程中微观结构和界面结合强度的演变规律。交流阻抗谱法的结果表明:两种涂层试样的热生长氧化(TGO)层厚度及陶瓷层内裂纹数量均随着热循环时间增加而增长,但曲率试样的微观结构恶化速度更快;洛氏硬度压痕法的结果验证了经热循环后,曲率基体上热障涂层界面结合强度低于平板样品。     

热障涂层杨氏模量和泊松比的测试

为了降低航空发动机热端部件的温度,空气等离子喷涂已被广泛地应用。为确定热障涂层的残余应力、结合力、断裂韧性、疲劳裂纹扩展速率等性能和特性,需要知道其杨氏模量和泊松比。因为涂层厚度非常薄且使用时是结合在基体上的,所以需要一个能够在原处测量涂层的杨氏模量和泊松比的方法。采用等离子喷涂工艺在GH150高温合金上喷涂了MCrAIY和陶瓷层,利用一种改进的悬臂梁方法测量了热障涂层的杨氏模量和泊松比。这种无损测试方法为测定其他薄膜材料的杨氏模量和泊松比提供了借鉴。     

涡轮叶片热障涂层在CMAS 环境下的失效分析

对于多台份某型发动机在试车后出现的带热障涂层涡轮叶片表面附着较多环境沉积物CMAS进而导致热障涂层脱落 失效的故障,通过宏观形貌观察、化学成分分析、微观结构分析等方法对CMAS分布规律、成分特征和失效模式进行了分析。结果 表明：CMAS沉积物在叶盆面较厚、叶背面较薄,靠近缘板处较厚、叶身中部位置较薄,进气边较厚、排气边较薄;厚度较薄处的附 着物颗粒细小、分布均匀,较厚处的附着物结构较疏松,大多呈块状不均匀分布;涡轮叶片热障涂层表面沉积物及气膜孔堵塞物的 成分以CMAS为主,同时还有中低温部件碰摩磨屑生成的Fe2O3、TiO2和NiO;由CMAS腐蚀引发的热障涂层失效模式主要有气膜孔 堵塞引发周围涂层烧结失效、涂层表面和内部应力失配、陶瓷层柱状晶被冲击撞断以及8YSZ热障涂层被溶解。     

电子束物理气相沉积热障涂层寿命预测模型

为了准确预测热障涂层（TBCs）的剥落寿命，把涂层使用过程中所存在的潜在危险减到最低，建立精确的热障涂层寿命预测模型具有十分重要意义。本文介绍了一种电子束物理气相沉积（EB-PVD）技术制备的热障涂层的寿命预测模型。该模型是通过对EB-PVD热障涂层陶瓷的物理和力学性能、结合强度的测定，热生长氧化层（TGO）生长动力学的研究以及热循环剥落寿命数据的定量研究而建立的一个TBCs系统的非线性寿命预测模型。从涂层实际寿命与模型预测寿命对比发现，该模型预测的涂层寿命与涂层的实际寿命相吻合。     

交流阻抗谱法评价热障涂层的热腐蚀行为(英文)

本文利用交流阻抗这种无损检测的方法研究了热障涂层在质量分数为25%NaCl+75%Na2SO4混合盐体系中的热腐蚀行为。实验结果显示,热腐蚀条件下,在陶瓷层和粘结层界面处形成TGO层为混合氧化物层,成分为Cr2O3、(Ni,Co)(Cr,Al)2O4和NiO,其厚度增长符合抛物线规律。热障涂层在110个循环腐蚀之前时,TGO层的电阻值随其厚度的增加而增加;110个循环后,虽然TGO层的厚度还是在增加,但由于TGO层孔隙的增多而导致其电阻值有所下降。陶瓷层的电阻值随着陶瓷层中裂纹的萌生和扩展而不断增大。等效电路中得到的参数可以用来表征热障涂层的失效行为。     

高熵热障涂层陶瓷材料研究进展

随着军事和科技的发展,热障涂层应用技术已成为现代国防尖端技术中最重要的技术之一.而高熵热障涂层陶瓷材料具有高温相稳定性、超低热导率、耐腐蚀性强、热膨胀系数和断裂韧性较高等优点,可为高温合金基底提供良好的热防护,在航空航天、航海和核能等领域有重要的应用前景.对国内外已报道的高熵热障涂层陶瓷候选材料进行系统性分类总结,重点...     

航空发动机热障涂层材料体系的研究

介绍了热障涂层的结构、陶瓷表层材料和中间粘结层的材料发展趋势。热障涂层的结构已由经典的双层结构向成分、结构连续变化的梯度结构发展,涂层的寿命有明显的提高。制备方法中电子束物理气相沉积技术具有明显优势。热障涂层表层材料的最佳成分是(质量百分数6%～8%)Y2O3部分稳定的ZrO2陶瓷材料。粘结层体系发展的一个重要趋势是能同时保证力学性能和抗氧化性能的低Al含量NiCoCrAlY。     

热暴露对带热障涂层DD6单晶高温合金组织的影响

采用0.3 MPa压力对DD6单晶高温合金进行水吹砂,然后用电子束物理气相沉积的方法在DD6合金基体上制备了热障涂层,将带热障涂层试样置于1100℃空气气氛中分别进行50 h和100 h热暴露,在1100℃/130 MPa条件下测试持久性能。研究了水吹砂及高温热暴露对带热障涂层DD6合金组织的影响。结果表明：0.3 MPa压力水吹砂制备热障涂层并高温热暴露后没有发现再结晶组织;热暴露过程中,基体和涂层之间的元素会发生不同程度的互扩散;表面残余应力和元素互扩散导致了γ′相粗化方向的变化;性能测试后试样断口附近的涂层与基体界面下方局部区域形成了二次反应区。     

Hot Corrosion Behavior of Double-ceramic-layer LaTi2 Al9O19/YSZ Thermal Barrier Coatings

LaTi 2 Al 9 O 19 (LTA) exhibits promising potential as a new kind of thermal barrier coating (TBC) material, due to its excellent high-temperature capability and low thermal conductivity. In this paper, LTA/yttria stabilized zirconia (YSZ) TBCs are produced by atmospheric plasma spraying. Hot corrosion behavior and the related failure mechanism of the coating are investigated. Decomposition of LTA does not occur even after 1 458 hot corrosion cycles at 1 373 K, revealing good chemical stability in molten salt of Na 2 SO 4 and NaCl. However, the molten salt infiltrates to the bond coat, causing dissolving of the thermally grown oxide (TGO) in the molten salt and hot corrosion of the bond coat. As a result, cracking of the TBC occurs within the oxide layer. In conclusion, the ceramic materials LTA and YSZ reveal good chemical stability in molten salts of Na 2 SO 4 and NaCl, and the bond coat plays a significant role in providing protection for the component against hot corrosion in the LTA/YSZ TBCs. LTA exhibits very promising potential as a novel TBC material.     

交流阻抗谱法在热障涂层失效研究中的应用

介绍了交流阻抗谱法作为无损检测方法在热障涂层失效分析中的应用。通过对热循环、静态氧化过程中热障涂层体系的阻抗谱分析,利用交流阻抗谱对热障涂层进行拟合,得到了服役过程中D_M以及TGO电阻R拟合的结果与氧化时间呈抛物线关系;并根据阻抗的变化确定了粘结层的氧化过程中氧化物成分从Al₂O₃变化到混合氧化物的过程;对陶瓷层电阻的拟合结果表明,陶瓷层在热循环250~350次之间的电阻变化与陶瓷层内微观结构以及应力的变化有关。     

等离子喷涂工艺参数对GdPO4热障涂层组织结构和结合强度的影响

随着航空发动机涡轮进口温度提升,目前最广泛使用的Y₂O₃部分稳定ZrO₂(YSZ)热障涂层(TBCs)已难以满足需求,亟须发展新一代超高温TBCs。GdPO₄是一种极具应用前景的TBCs材料。本工作采用等离子喷涂方法制备GdPO₄/YSZ双陶瓷层结构TBCs,研究喷涂工艺参数特别是喷涂功率对GdPO₄陶瓷涂层相组成、表面形貌、微观结构以及结合强度的影响。结果表明:等离子喷涂GdPO₄过程中会有元素P损耗,得到的涂层除了GdPO₄外,还有一些Gd₃PO₇相;随着喷涂功率降低,Gd₃PO₇相含量减少;GdPO₄陶瓷涂层的主体结构由充分熔融的喷涂粒子堆垛构成,其中镶嵌有未熔化粒子构成的微区;随着喷涂功率降低,未熔化微区增多,涂层厚度降低;GdPO₄/YSZ TBCs的结合强度随喷涂功率降低而减小,主要是由于未熔化微区增多降低了涂层的内聚力;因此,低喷涂功率不利于涂层的结合强度。     

Impermeability of Y3Al5O12 ceramic against molten glassy calcium-magnesium-alumina-silicate

Degradation of thermal barrier coatings (TBCs) caused by calcium-magnesium-alumina-silica (CMAS) glassy penetration is becoming an urgent issue for TBCs industrial applications. In this work, yttrium aluminum garnet (Y₃Al₅O₁₂, YAG) nano-powders were synthesized through a chemical co-precipitation route. The resistance of YAG ceramic to glassy CMAS infiltration at 1250?°C was evaluated. YAG ceramic bulk sintered at 1700?°C for 10?h was comprised of a single garnet-type Y₃Al₅O₁₂ phase. The molten CMAS glass was suppressed on the surface of the YAG ceramic at 1250?°C. A chemical reaction between YAG and the molten CMAS glass did not occur at 1250?°C for 24?h, suggesting that YAG could act as an impermeable material against glassy CMAS deposits in the TBC field.     

直升机旋翼桨叶动态RCS特性研究

从时域和频域两方面,对直升机动态旋翼的RCS特征进行了较全面研究,即不仅考虑旋翼的旋转运动,而且还考虑桨叶的变距、挥舞和桨盘倾斜等引起RCS的动态效应。以NACA0012为翼型的直平翼作为直升机旋翼桨叶,建立旋翼桨叶的几何模型,采用物理光学和等效电磁流法,计算各种运动情况下旋翼RCS的时域曲线,然后,用准静态法计算一个周期内的平均多普勒频谱,最后,对连续的瞬时频谱进行时间-频谱分析,得到一些重要研究结果。     

大气等离子喷涂热障涂层高温氧化行为研究

采用等离子喷涂工艺在GH4099合金基体上制备了热障涂层,并进行了1050℃恒温氧化试验,综合利用X射线衍射仪、扫描电子显微镜、能谱分析仪等检测手段,分析了涂层的显微结构及高温氧化行为。结果表明：等离子喷涂（APS）热障涂层在高温氧化过程中,黏结层被氧化生成热生长氧化物（TGO）。但长时间氧化后,在与TGO毗邻的金属黏结层中产生了范围较窄但浓度变化较大的贫Al带,TGO层出现保护性Al2O3向非保护性混合氧化物转变的现象,导致致密Al2O3层的连续性被破坏,TGO厚度快速增加。     

一种单晶涡轮叶片热机械疲劳寿命评估方法

针对单晶涡轮叶片热机械疲劳(TMF)问题,围绕单晶涡轮叶片TMF试验,结合单晶变形、损伤理论及数值模拟,建立了一套单晶涡轮叶片TMF寿命评估方法.利用空心气冷涡轮叶片TMF试验系统,对单晶涡轮片考核截面在服役条件下所产生的交变应力场和交变温度场进行模拟,确定了裂纹萌生部位及其TMF寿命.考虑单晶涡轮叶片变形和损伤行为的特征,分别建立了基于滑移系的Walker黏塑性本构模型和基于临界平面的循环损伤累积(CDA)模型.利用上述本构和寿命模型,完成了单晶涡轮叶片TMF试验的数值模拟.结果表明:叶片理论危险点与试验结果一致,且计算寿命基本落在试验寿命的3倍分散带内.