钛合金表面抗激光涂层损伤特性及热效应影响研究

实验研究了钛合金和高反射型陶瓷涂层材料抗连续型激光烧蚀的损伤及温度分布特性，并从热效应影响角度对比分析了二者在抗激光损伤效果方面的差异性。研究结果表明：相比于钛合金，高反射型陶瓷涂层材料能有效增强钛合金基底抗激光损伤的能力；在同等激光功率密度辐照下，陶瓷涂层材料能有效提升钛合金基底耐受激光辐照的时间长度。实验结果表明该陶瓷涂层材料的激光损伤阈值比钛合金高约5.8倍。实验发现陶瓷涂层温升速率高于钛合金，但由于陶瓷材料具有较高的反射特性，以及良好的热吸收和热传导特性，因此能使由激光辐照产生的热量在其表面较快地扩散，而降低向基底方向传导的程度，最终提升陶瓷涂层的抗激光损伤阈值。     

不同密度弹丸对水冰的超高速撞击成坑实验

为了研究冰冻天体表面撞击坑的形成与演化，开展了水冰的超高速撞击成坑实验。使用二级轻气炮发射1.0 mm直径的球形弹丸，以3 km/s、5 km/s和7 km/s速度对圆柱状冰块进行撞击。弹丸材料包括聚碳酸酯和不锈钢两种，冰块温度为253 K。实验观察到了不同弹丸和不同速度条件下，冰块中撞击坑的形貌特征。对撞击坑直径、深度和剖面形状进行了测量，并与文献中铝弹丸对水冰的撞击坑进行了比较分析。获得了水冰撞击坑特征随撞击参数的变化规律，结果表明：撞击坑直径和深度的主导机制不同，坑深主要由弹丸侵彻作用形成，而坑径主要由冰块的剥落所致；坑深比坑径具有更强的对于弹丸密度的依赖性，高密度弹丸撞击坑直径具有比低密度弹丸更强的对于撞击速度的依赖性；撞击坑体积与撞击能量成正比，高密度弹丸形成的撞击坑直径表现出“能量缩比”行为，而低密度弹丸形成的撞击坑直径表现出“动量缩比”行为。     

Review and propositions for the sliding/impact wear behavior in a contact interface

A thermal-solid-liquid complex operational environment induces structural interface developing a typical coupling sliding/impact wear behavior. It results in contact damage until systems fail, which may cause significant economic losses and catastrophic consequences. The key point of solving this problem is to reveal the coupling damage mechanism of the sliding/impact behavior in typical systems and life characterization under a complicate evolving environment. This has been a hot topic in the area of mechanical reliability. The main work in this paper can be concluded as follows. Firstly, the main industries in which the “sliding/impact behavior” takes place have been introduced. Then, existing studies on the wear mechanism and degree analysis are presented, which includes surface morphology analysis, wear debris analysis, and wear degree measurement. Meanwhile, existing problems in theoretical modeling and experiments in current research are summarized, so as to point out a bright direction for future research on wear prediction. They include interface contact modeling, mathematic coupling mechanism modeling, wear equation establishment, and wear life characterization, which can provide some new ideas for improving the existing studies on the sliding/impact wear behavior.     

等质量异形粒子超高速撞击侵蚀

用数值方法模拟双锥，圆柱，椭球、圆锥和倒圆锥五类等质量异形铝粒子五种高宽比共２５种粒子对半无限铝靶的超高速撞击侵蚀，撞击速度为４ｋｍ／ｓ，给出了坑深、坑径、坑形参数和坑体积随粒子形状及高宽比的变化曲线。结果与非圆球异形粒子超高速撞击侵蚀计算有重要参考价值。     

Emergence of a Habitable Planet

We address the first several hundred million years of Earth’s history. The Moon-forming impact left Earth enveloped in a hot silicate atmosphere that cooled and condensed over ∼1,000 yrs. As it cooled the Earth degassed its volatiles into the atmosphere. It took another ∼2 Myrs for the magma ocean to freeze at the surface. The cooling rate was determined by atmospheric thermal blanketing. Tidal heating by the new Moon was a major energy source to the magma ocean. After the mantle solidified geothermal heat became climatologically insignificant, which allowed the steam atmosphere to condense, and left behind a ∼100 bar, ∼500 K CO₂ atmosphere. Thereafter cooling was governed by how quickly CO₂ was removed from the atmosphere. If subduction were efficient this could have taken as little as 10 million years. In this case the faint young Sun suggests that a lifeless Earth should have been cold and its oceans white with ice. But if carbonate subduction were inefficient the CO₂ would have mostly stayed in the atmosphere, which would have kept the surface near ∼500 K for many tens of millions of years. Hydrous minerals are harder to subduct than carbonates and there is a good chance that the Hadean mantle was dry. Hadean heat flow was locally high enough to ensure that any ice cover would have been thin (<5 m) in places. Moreover hundreds or thousands of asteroid impacts would have been big enough to melt the ice triggering brief impact summers. We suggest that plate tectonics as it works now was inadequate to handle typical Hadean heat flows of 0.2–0.5 W/m². In its place we hypothesize a convecting mantle capped by a ∼100 km deep basaltic mush that was relatively permeable to heat flow. Recycling and distillation of hydrous basalts produced granitic rocks very early, which is consistent with preserved >4 Ga detrital zircons. If carbonates in oceanic crust subducted as quickly as they formed, Earth could have been habitable as early as 10–20 Myrs after the Moon-forming impact.     

Modelling of Ejecta as a Space Debris Source

When a micro-debris or a micrometeoroid impacts a spacecraft surface, a large number of secondary particles, called ejecta, are produced. These particles can contribute to a modification of the debris environment: either locally by the occurrence of secondary impacts on the components of complex and large space structures, or at great distance by the formation of a population of small orbital debris. This paper describes firstly, the ejecta overall production, and secondly, the lifetime and the orbital evolution of the particles. Finally the repartition of ejecta in LEO is computed. Some results describing the population as a function of size and altitude are presented.     

抗空间碎片碰撞穿透的航天器加强防护板设计

文章描述了以整体薄护罩和等效重量波纹薄护罩制作的双层板结构系统穿孔阻力的研究结果。指出如果以等效重量波纹缓冲器代替整体缓冲器可以显著地增加穿孔防护能力。针对在倾斜超高速碰撞事件中跳飞碎片的产生,波纹薄护罩的波纹参数可以用减少势的方法优化。     

利用遥测数据预报导弹落点的方法

给出利用遥测数据对导弹进行落点预报的方法。根据遥测数据传输多遍的特点，对解码后的ＰＣＭ 数据进行处理，得到误码率很小的数据。然后对头体分离时刻前导弹飞行的状况和遥测数据进行分析，从而对发动机后效误差进行修正，得到较精确的导弹运动参数，最后利用弹道方程预报导弹落点     

基于损伤力学的概率疲劳曲线获取方法

文章基于损伤力学方法获得满足疲劳试验的损伤演化方程,推导出一般条件下的理论疲劳曲线以及相对应的理论中值疲劳曲线与理论理想疲劳曲线；然后根据试验数据即可确定理论疲劳曲线中的参量,从而获取疲劳曲线计算公式。通过此计算公式,可以方便地得到一组以初始损伤为参数的疲劳曲线族,继而得到以失效概率为参数的疲劳曲线族,大大降低了所需试验的数量,并为结构抗疲劳设计和寿命估算提供了依据。     

克服地球轨道空间碎片的航天器防护结构几何规划设计

文章描述了一个用于航天器防护结构综合优化的独特方法——几何规划优化技术,以减小暴露于流星体和空间碎片超高速碰撞环境下的航天器防护结构系统的重量。空间碎片和流星体环境由广义加权目标函数的公式来定义。通过Wilkinson,Burch和Nysmith超高速碰撞预示模型说明几何规划的性能。表明遵循几何规划形式的超高速碰撞模型,可以进行综合非线性设计优化。