粉末渗铌探讨

本文通过团体粉末渗铌试验，分析了渗剂成分、渗入时间与温度对不同材料渗层的影响，研究与探讨了渗层的组织和性能。对４５钢、Ｔ１０钢、９ＣｒＳｉ钢和ＧＣｒ１５钢等材料采用铌铁粉末进行的渗铌处理，均可形成一定厚度的铌渗层，且表层硬度提高很多，摩擦力矩数值反映渗铌后摩擦系数减少。     

薄壁大尺寸铌钨合金喷管精密旋压成形工艺研究

通过对铌钨合金性能的研究,得到了铌钨合金一次旋压最大减薄率,采用变厚度平板旋压毛坯,合理分布两次剪切旋压变形量和各点壁厚变薄率,控制旋压过程,应用仿真软件对翻边成形进行仿真,掌握了薄壁大尺寸铌钨合金喷管精密旋压及翻边成形技术.     

Si和Ti对Nb-6Hf-4Zr-2B合金组织和室温力学性能的影响

 为了寻求Nb合金的强度和塑性的平衡,设计了以Nb基固溶体Nbss为主导相的Nb-xSi-6Hf-4Zr-2B-yTi(x=4,8;y=10,30;原子分数)合金,研究了Si和Ti对合金组织和室温力学性能的影响。结果表明,合金由Nbss、Nb3Si和Nb5Si3等3相组成。4Si-(10,30)Ti合金铸态组织是Nb枝晶和分布在枝晶间的硅化物(Nb3Si和Nb5Si3),8Si-(10,30)Ti合金Nb枝晶间分布的是Nb/硅化物(Nb5Si3)的共晶和Nb3Si,随着Si和Ti含量的增加,硅化物体积分数增加。1 600 ℃退火50 h可使部分Nb3Si共析分解,改变合金的组织形貌和各相的体积分数。随着Si和Ti含量的增加,合金的硬度和强度增加,但塑性和韧性降低。Nb枝晶的失效方式为解理断裂,而硅化物为脆性断裂。     

Plasma Niobium Surface Alloying of Pure Titanium and its Oxidation at 900 ℃

A niobium-modified layer on pure titanium surface was obtained by means of double glow plasma surface alloying technique. The modified layer was uniform, continuous, compact and well adhered to the substrate. The niobium composition in the modified layer decreased gradually from the surface to the substrate. The oxidation behavior of the niobium-modified layer was investigated and compared with the untreated surface at 900 ℃ for 100 h. Characterization of the layers was performed using X-ray diffraction and scanning electron microscope, respectively. The test results show that the oxidation behavior of pure titanium was improved by niobium alloying process. Niobium has a positive influence on the oxidation resistance.     

Plasma Niobium Surface Alloying of Pure Titanium and its Oxidation at 900℃

A niobium-modified layer on pure titanium surface was obtained by means of double glow plasma surface alloying technique. The modified layer was uniform, continuous, compact and well adhered to the substrate. The niobium composition in the modified layer decreased gradually from the surface to the substrate. The oxidation behavior of the niobium-modified layer was investigated and com- pared with the untreated surface at 900 ℃ for 100 h. Characterization of the layers was performed using X-ray diffraction and scanning electron microscope, respectively. The test results show that the oxidation behavior of pure titanium was improved by niobium alloying process. Niobium has a positive influence on the oxidation resistance.     

电子束区熔定向凝固Nb基高温合金的组织和性能

研究了Nb-Si-Ti-Hf-Cr-Al-B-Y合金在电子束区熔炉上的定向凝固组织、室温断裂韧性和高温瞬时拉伸性能.合金的组织主要由Nb基固溶体(Nbss)、α-(Nb)5Si3和(Nb)3Si相组成.定向凝固后,初生Nbss枝晶以及Nbss α-(Nb)5Si3/(Nb)3Si层片状或棒状共晶团均沿着试棒轴线定向排列.当电子枪移动速率R=2.4 mm/min时,定向效果最好.定向凝固使合金在1250℃的拉伸强度及室温断裂韧性均显著提高.R=2.4 mm/min试棒的抗拉强度最高,达85.0 MPa,同时其室温断裂韧性也达到19.4 MPa·m1/2.     

铁素体不锈钢TIG焊接头组织与性能研究

研究了焊接热输入和微合金元素铌对铁素体不锈钢TIG焊接头组织及性能的影响.实验结果表明,随着焊接热输入的增加,焊接热影响区的粗晶区和焊缝区中铁索体晶粒明显粗化,降低了焊接接头的强度和塑性.铁素体不锈钢中加入少量的铌元素,通过钉扎晶界和拖曳晶界移动的双重作用,阻碍了粗晶区和焊缝区中铁素体晶粒的长大,提高了焊接接头的强度和...     

复合包渗法制备铌合金表面硅化物涂层

采用复合包渗法在C103铌合金基体上制备硅化物涂层,进行1500℃静态氧化实验,室温～1500℃热震实验,利用X射线衍射(XRD)、扫描电镜(SEM)、能谱分析(EDS)等检测手段对涂层氧化前后的组织结构进行观察,分析涂层形成机理、硅化时间对涂层组织结构的影响以及涂层氧化前后组织形貌的变化.研究表明,复合包渗法制备硅化物涂层主要是通过扩散反应形成的;涂层是以MoSi2相为主体层的多相复合结构;在高温氧化环境下,涂层表面生成熔融态非晶玻璃膜,有效阻止了氧向内进一步扩散,涂层抗静态氧化及抗热震性能良好.     

低密度铌合金与铌铪合金电子束焊接性能分析北大核心CSCD

低密度铌合金与铌铪合金由于物理性能差异性较大,采用常规电子束方法焊接时,易产生焊接缺陷。为进一步探究低密度铌合金与铌铪合金焊接的可行性,通过数值模拟与工艺试验两种方法对其焊接接头的性能进行了系统研究。首先建立了异种材料有限元模型,对接头的温度场规律进行了分析;然后,采用真空电子束焊接的方法进行试验研究,从宏观形貌、力学性能、微观组织及元素分布等方面分析了接头性能。结果表明:采用电子束偏置铌铪侧焊接的方式,可获得无裂纹、无气孔,具有良好拉伸强度的低密度铌合金与铌铪合金接头。