Basaltic glasses (hyaloclastite) are a widespread habitat for life in volcanic environments, yet their interior physical conditions are poorly characterized. We investigated the characteristics of exposed weathered basaltic glass from a surface outcrop in Iceland, using microprobes capable of continuous sensing, to determine whether the physical conditions in the rock interior are hospitable to microbial life. The material provided thermal protection from freeze-thaw and rapid temperature fluctuations, similar to data reported for other rock types. Water activity experiments showed that at moisture contents less than 13% wet weight, the glass and its weathering product, palagonite, had a water activity below levels suitable for bacterial growth. In pore spaces, however, these higher moisture conditions might be maintained for many days after a precipitation event. Gas exchange between the rock interior and exterior was rapid (< 10 min) when the rocks were dry, but when saturated with water, equilibration took many hours. During this period, we demonstrated the potential for low oxygen conditions within the rock caused by respiratory stimulation of the heterotrophic community within. These conditions might exist within subglacial environments during the formation of the rocks or in micro-environments in the interior of exposed rocks. The experiments showed that microbial communities at the site studied here could potentially be active for 39% of the year, if the depth of the community within the outcrop maintains a balance between access to liquid water and adequate protection from freezing. In the absence of precipitation, the interior of weathered basaltic glass is an extreme and life-limiting environment for microorganisms on Earth and other planets.     

等离子喷涂Al_2O_3涂层的电击穿机理

采用大气等离子喷涂技术在铜基体上沉积了Al2O3涂层。采用XRD和SEM对涂层微观结构进行了表征。通过探讨孔隙率和吸潮行为对绝缘性能的影响,分析了等离子喷涂Al2O3涂层结构与电绝缘失效机理的关系。结果表明:等离子喷涂Al2O3涂层较致密,界面结合较好。随涂层厚度不同其孔隙率在5%~7%范围变化。等离子喷涂Al2O3涂层结构中的孔洞是电绝缘失效的主要部位且呈典型电晕击穿形貌。电晕击穿诱发的裂纹沿击穿方向扩展形成击穿隧道。击穿方向与电极极性无关而由击穿孔洞位置决定。涂层厚度与涂层击穿强度呈现倒数关系。吸潮会诱发导电通路形成降低Al2O3涂层抗击穿能力。