Deformation Behavior of Mg-8 wt%Li Alloy under High-speed Impact

Deformation behavior of the Mg-8 wt%Li alloy at high strain rate was studied by means of the Split Hopkinson Pressure Bar (with strain rate of 103 s-1). It is found that shear localization proves to be the main damage mode for the alloy during dynamic loading. Strain and strain rate are the two necessary parameters affecting the occurrence of deformation and shear bands. Deformation bands begin to form when the strain and strain rate reach 0.20 and 1 900 s-1 respectively and will develop gradually with the strain rate increasing. Be-sides, deformation bands will transform into shear bands when the strain and strain rate reach above 0.25 and 3 500 s-1 separately.     

钛合金的固态Cu致脆行为研究

分别采用慢应变速率拉伸、恒载荷拉伸加载方法研究了TC11钛合金在不同温度下的Cu脆行为,Cu与钛合金试样表面的接触分别采用离子束增强沉积和机械压合法实现.研究结果表明:在500℃慢速率拉伸条件下,钛合金呈现出较高的铜脆敏感性,而在300℃,400℃时,Cu脆敏感性不明显.在恒载荷试验条件下,500℃时,Cu对钛合金的力学性能影响较低;550℃时,Cu使TC11合金的断裂寿命和塑性指标显著降低.Cu脆的发生必须满足:Cu与钛合金紧密接触;合适的温度;试样应保持一定大小的形变速率.     

腰形柱壳的有限条元解

本文用考虑了曲率影响的两结线低阶有限板条元分析了腰形柱壳的力学性能这种条元位移参数少,能较好地体现壳体的几何特性。     

Y－TZP陶瓷超塑性拉伸变形试验

通过实验找出Ｙ－ＴＺＰ陶瓷超塑性变形的最佳温度、初始应变速率及最大的变形量，并求出应变速率敏感性指数ｍ值。利用得到的最佳工艺参数制造出陶瓷环形件样件。     

工程塑料应变测试误差的研究

本文采用了五种不同尺寸的应变片,在不同的测试电压下,利用四分之一桥电路和半桥电路,用system 4000应变仪测定了四种常见的工程塑料的静态表观应变。实验发现,这些工程塑料的表观应变具有明显的滞后特性,测试的表观应变值与测试电压成正比,与应变片的面积成反比。它还直接与测试时间、所测材料的传热能力、弹性模量以及它与应变片栅丝的热膨胀系数差值有较大关系。本文也比较了半桥测试法和四分之一桥测试法的结果,结果表明,四分之一桥测试法的测试误差远大于具有热补偿作用的半桥测试法,然而半桥测试法的热补偿作用仍然未令人满意。本文为此作出了一些解释,并提出了减小和消除测试误差的方法和途径。     

复合材料固化应力模型

本文建立了描述复合材料固化应力史的综合模型。在本模型中考虑了化学收缩对残余应力史的贡献,并考虑了以玻璃化转变区为应力释放区的应力松弛过程。整个模型由四部分组成:描述温度场的模型、物理力学参数的模型、描述细观纵向残余应力史的模型、描述层合固化应力史的模型。     

复合材料层合残余应力实验研究

取单向板90°试样用DMA法测出的玻璃化温度T_(?)为应力释放温度,用应变片包埋法测定了玻纤/648环氧复合材料单向试样与对称正交层板的热应变,用经典层板理论处理实验结果,实验值与理论值吻合;结果还表明,一般意义上的复合材料内的层合残余应力与制造过程中复合材料内的残余应力应作区别。     

缺口件疲劳寿命预测新方法

采用有限元方法针对缺口件多轴疲劳实验结果进行模拟。结果表明,相同路径条件下,随着缺口半径减小缺口根部附近的应力梯度显著增加。基于缺口根部应变值,采用等效应变法进行疲劳寿命预测,预测结果随缺口半径的减小而偏于保守。采用应力梯度法确定有效距离,相同路径下,随着缺口半径的减小有效距离减小;依据该有效距离处的等效应变进行疲劳寿命预测,总体预测结果较为分散且偏于不安全。基于实验及有限元模拟结果,提出了基于应变梯度的有效距离确定的新方法,大部分疲劳寿命预测结果位于2倍分散带内。     

Plastic deformation analysis and forming quality prediction of tube NC bending

Plane strain assumption and exponent hardening law are used to investigate the plastic deformation in tube bending. Some theoretical formulae including stress, curvature radius of neu-tral layer, angle of neutral layer deviation, bending moment, wall thickness variation and cross-section distortion, are developed to explain the phenomena in tube bending and their magnitudes are also determined. During unloading process, the springback angle is deduced using the virtual work principle, and springback radius is also given according to the length of the neutral layer which remains unchanged before and after springback. The theoretical formulae are validated by the experimental results or the validated simulation results in literature, which can be used to quickly predict the forming quality of tube numerical control (NC) bending.     

光纤环内部应力试验研究

光纤环是光纤陀螺的核心敏感部件,其内部应力值的大小和分布对光纤陀螺的整体性能有很大影响.光纤环的内部应力主要包含拉伸应力、弯曲应力和固化应力等,光纤环的绕制工艺和固化工艺等都会对光纤环的应力产生影响.通过测量不同绕制工艺下光纤环的应力分布和偏振串扰分布,得出光纤环绕制张力越小、光纤环直径越大、固化胶的收缩率越小,光纤环的应力也越小,相应的偏振串扰值也越小,为光纤环绕制技术的提高提供依据.