考虑刀具偏心的微铣削加工表面粗糙度预测模型研究

基于微铣削刀具轨迹建立了考虑刀具偏心、最小切削厚度的塑性材料微铣削底面粗糙度的预测模型,预测结果表明粗糙度表面形貌呈锯齿状,刀具偏心会影响表面粗糙度的形貌周期和高度,并进行微铣削加工实验,对粗糙度预测模型进行了验证。采用回归统计方法,建立了脆性材料微铣削加工表面粗糙度预测模型,对加工表面形貌进行观察,利用响应曲面法得到了各铣削用量对表面粗糙度的影响规律。     

孔挤压强化对2124铝合金疲劳寿命及微观组织的影响

采用疲劳试验、透射电镜、扫描电镜及X射线衍射仪等方法研究了2124-T851铝合金厚板不同参数孔挤压强化后疲劳寿命与显微组织的变化。结果表明：孔挤压强化后试样的疲劳寿命先随挤压量的增大而升高，随后又迅速降低，挤压量为0.4 mm时疲劳寿命达到峰值，较未强化增加12.66倍；组织观察结果表明孔挤压强化后，在孔壁强化层内形成了位错胞状结构和残余压应力，并且随挤压量增大先迅速增加然后趋于平缓，强化层的形成可以有效延缓疲劳裂纹的扩展速率；同时，适当的孔挤压强化可改善表面粗糙度，降低裂纹萌生几率，从而提高材料的疲劳寿命。     

A100钢外螺纹椭圆超声滚压强化试验研究

A100钢有较高的疲劳抗力和显著的减重效果.在航空工业中,飞机起落架主要承力件正逐步采用A100钢,且主要承力件多采用螺纹联接.为了提高螺纹疲劳寿命,提出了超声振动滚压强化工艺方法,设计了外螺纹超声滚压强化装置,进行了螺纹超声滚压强化前后性能对比试验.利用X射线分析仪、维式硬度计、粗糙度仪和疲劳试验机,分别测量了螺纹超声滚压强化前后的残余应力、维氏硬度、表面粗糙度以及疲劳寿命.结果表明,超声滚压强化后牙底残余应力提高了70％,显微硬度提高了14％,粗糙度降低了51％,600MPa应力条件下寿命提高了5倍.     

原位自生TiB2/Al复合材料车削参数多目标优化方法

原位自生TiB2/Al复合材料具有密度小、比强度高、高耐磨等特点,在航空航天领域具有广泛的应用前景.主要针对TiB2/Al复合材料车削参数对表面粗糙度的影响进行探索性研究.首先,以车削速度、进给速度、车削深度为对象,基于单因素试验研究了车削参数控制域.进一步在控制域内设计正交试验,并基于试验结果研究了表面粗糙度与车削参数的映射关系,推导了材料去除率模型.最后,以表面粗糙度和材料去除率为优化目标,提出并研究了基于GA-Pareto的车削参数多目标优化方法,并通过试验验证了该方法的可行性和有效性.     

热等静压工艺制备的Ti-6Al-4V薄壁筒的切削加工

为了能够提高钛合金薄壁筒的加工效率,利用热等静压工艺制备了两个具有不同结构的Ti-6Al-4V薄壁筒,研究了夹具、填充泥浆和筒结构对Ti-6Al-4V薄壁筒的外圆表面粗糙度和精度的影响。结果显示,Ti-6Al-4V热等静压薄壁筒经过切削加工能够达到精度要求,填充泥浆降低了弹性回弹,提高了薄壁筒外圆精度;筒结构的内圆环和粗大端能够提高刚度,有效降低了外圆表面粗糙度值;夹具尺寸误差对圆度和同轴度影响较大,较大的尺寸误差显著降低了筒的外圆精度。     

风力机组叶片的先进翼型族设计

大型风力机组叶片设计需要专用的翼型族,以满足风力机组运行的环境要求。高升阻比、低粗糙度影响是该翼型族的气动性能特点。为了发展我国具有自主知识产权的风力机专用翼型族,在科技部863项目的支持下,北京航空航天大学联合国内气动研究单位,通过理论分析、数值模拟和风洞试验等技术途径,开发了两个适用于大型风力机组叶片的先进翼型族。理论分析和风洞试验表明,设计结果基本达到了预先设定的气动性能指标。     

Specific grinding energy and surface roughness of nanoparticle jet minimum quantity lubrication in grinding

Nanoparticles with the anti-wear and friction reducing features were applied as cooling lubricant in the grinding fluid. Dry grinding, flood grinding, minimal quantity of lubrication（MQL）, and nanoparticle jet MQL were used in the grinding experiments. The specific grinding energy of dry grinding, flood grinding and MQL were 84, 29.8, 45.5 J/mm³, respectively. The specific grinding energy significantly decreased to 32.7 J/mm³ in nanoparticle MQL. Compared with dry grinding, the surface roughness values of flood grinding, MQL, and nanoparticle jet MQL were significantly reduced with the surface topography profile values reduced by 11%, 2.5%, and 10%,respectively, and the ten point height of microcosmic unflatness values reduced by 1.5%, 0.5%,and 1.3%, respectively. These results verified the satisfactory lubrication effects of nanoparticle MQL. MoS₂, carbon nanotube（CNT）, and ZrO₂ nanoparticles were also added in the grinding fluid of nanoparticle jet MQL to analyze their grinding surface lubrication effects. The specific grinding energy of MoS₂ nanoparticle was only 32.7 J/mm³, which was 8.22% and 10.39% lower than those of the other two nanoparticles. Moreover, the surface roughness of workpiece was also smaller with MoS₂ nanoparticle, which indicated its remarkable lubrication effects. Furthermore,the role of MoS₂ particles in the grinding surface lubrication at different nanoparticle volume concentrations was analyzed. MoS₂ volume concentrations of 1%, 2%, and 3% were used.Experimental results revealed that the specific grinding energy and the workpiece surface roughness initially increased and then decreased as MoS₂ nanoparticle volume concentration increased.Satisfactory grinding surface lubrication effects were obtained with 2% MoS₂ nanoparticle volume concentration.     

大长径比圆截面隔离段流场的数值研究

对2 Ma均匀来流条件下大长径比L/D=17.5的等直圆截面隔离段内流场进行了数值模拟.研究了在不同背压和不同壁面粗糙度的条件下,隔离段内激波串形态、静压分布、总压恢复.结果表明:激波串位置与背压呈非线性关系,激波串中形成数道“X”形的激波,总压恢复系数随背压增加先减小后增大;壁面粗糙度增加会使激波串前的壁面压力有所增加,使激波串向上游移动,激波串的第一道激波强度增大,之后的激波强度迅速衰减.     

推广使用REM37BY电嘴

在我院使用的活塞发动机飞机中,点火系统故障率居高不下,其中又以电嘴积铅带来的发动机抖动故障居多。本文通过对比分析,以及实际监控使用的具体情况,证明了REM37BY电嘴能使这一故障大大减少,并且能节约成本,缩短工时,具有较大的推广价值。     

核翼比法进行表面粗糙度的标定及测量

介绍了一种表面粗糙度标定及测量的新方法。通过标定一组标准样块的核翼比，可以实现该标定范围内待检样块的粗糙度测量，该方法稳定可靠，试验装置简单，数据处理方便，为表面粗糙度的非接触测量提供了较好的方案。