在复合材料表层铺设压电元件，利用压电元件能够实现力学量和电学量之间相互转化的独特性能，可将其用作传感器和驱动器，赋予材料和结构传感及动作的能力。本研究的压电材料采用锆钛酸铅压电陶瓷，基体材料采用玻璃纤维－环氧树脂复合材料，与外部信号采集和控制系统结合，构成了智能结构实验系统。本文对这一系统的损伤诊断和损伤主动控制功能进行了实验研究。该结构一方面可对冲击、过载等可能造成损伤的原因进行监测，并诊断裂缝、连接松动等损伤的产生和位置，另一方面还可自适应地驱动结构中的压电驱动器，改善结构应力状态，防止损伤的扩展。     

Interaction of oblique wave beam with ionospheric layer F2

Interaction of a powerful obliquely incident wave beam of decameter radio waves with the ionospheric F2 layer is analyzed. Much like the linear case, propagation through the natural anti-waveguide layer F2 splits the initial beam. Some part of its energy leaks through the ionospheric layer, the other part goes back along a downward trajectory. However, nonlinearity leads to further stratification of the ionospheric layer. A new feature, in comparison with the linear case, is appearing a narrow waveguide beneath the F2 layer maximum which traps a small part of the beam energy. We study the relationship between these parts of the wave field in a simplified model of parabolic F2 layer, with nonlinearity caused by thermal plasma expulsion from the high field intensity region. Analytical results are supplemented with numerical estimates of the effects.     

主减速器后撑杆失效分析

本文采用化学成分分析、力学性能、金相检验、断口分析和能谱分析等方法,对失效的后撑杆进行分析,结果表明,在三件失效件中,1号为正常的疲劳断裂,2号、3号件属于微动磨损引起的疲劳断裂。     

On uncertainties in carbon flux modelling and remotely sensed data assimilation: The Brasschaat pixel case

Uncertainty on carbon fluxes is determined by the uncertainties of ecosystem model structure, data and model parameter uncertainties and the temporal and spatial inaccuracy of the input data retrieval. The objective of this paper is to understand the error propagation and uncertainty of evaporative fraction (EF), soil moisture content (SMC) and water limited net ecosystem productivity (NEP). In this respect, C-Fix and spaceborne remote sensing are used for the ‘Brasschaat’ pixel. A simple model based on error theory and a Monte-Carlo approach are used. Different error scenarios are implemented to assess input uncertainty on EF, SMC and NEP as estimated with C-Fix.     

Influence of Low Load Truncation Level on Crack Growth for Al 2324-T39 and Al 7050-T7451

Tests with middle-crack tension (M(T)) specimens made of Al 2324-T39 and Al 7050-T7451 are conducted to investigate the influence of low load truncation level on fatigue crack growth. The six different truncated spectra are obtained by removing the small cycles of which amplitudes are less than the specified percentages of the maximum amplitude in the basic flight-by-flight loading spectrum and the remainder of the spectrum is untouched. The tests indicate that the mean level of fatigue crack growth life (FCGL) increases as the load truncation level is enhanced. Considering both the time saving and the influence on FCGL, there is an applicable choice (i.e. spectrum S2 or spectrum S3 in this investigation) for full scale fatigue test. The scatter of FCGL becomes much larger than that under the basic spectrum when the load truncation level is increased to a specified high level, mainly due to the occurrence of crack slanting and branching under the high level truncated loading spectra.     

某刹车装置的活塞组件衬套裂纹机理探究

某刹车装置耐久性试验中,活塞组件的衬套出现疲劳裂纹,经分析是由于汽缸座和刹车壳体外翘,活塞在与刹车盘间的摩擦力作用下对衬套外端产生交变挤压所致,试验验证结果成立,证明产品刚性影响构件的疲劳寿命。     

基于多传感器的裂纹扩展监测研究

疲劳裂纹扩展是结构健康监测的主要问题之一，为了保证金属结构的可靠和安全运行，实时监测结构的疲劳裂纹扩展过程十分必要。针对结构裂纹扩展的问题，采用压电传感器（PZT）和电阻应变片两种传感器，提出结合能够连续监测结构损伤的被动监测方法以及对微小损伤敏感的主动监测方法对裂纹扩展进行综合监测，以提高裂纹扩展的监测水平。采用随机森林算法对裂纹长度进行识别，并使用D-S证据理论对两种传感器的识别结果进行数据融合，得到比单一传感器更准确、可靠的裂纹扩展识别结果。进行了基于应变和主动Lamb波的裂纹扩展监测实验研究，验证了该方法对提高裂纹扩展监测识别准确率的有效性和实用性。     

直升机金属结构的全范围安全S-N曲线确定方法

本文介绍了直升机结构安全S-N曲线的确定方法.在常用的三参数S-N曲线公式Stromeyer方程的基础上,根据直升机载荷的特点,介绍了一种适合直升机疲劳评定的全范围S-N曲线公式,并提供一套根据中值S-N曲线获得安全S-N曲线的方法.     

某型飞机主起落架机轮半轴断裂原因分析

基于某型飞机主起落架机轮半轴的疲劳断裂事故,本文分析了半轴高强度结构钢的材料属性,测量了故障件相关部位的尺寸和油气式减震器的充填参数,阐明了导致该事故的原因———高应力低周疲劳断裂,并提出避免类似事故的解决措施。     

MSD薄板疲劳寿命预测

结合工程中应用最为广泛的Paris公式对多裂纹板的疲劳寿命进行了预计,计算结果与现有试验结果比较吻合,表明了该方法的可行性。由于力学响应的计算采用有限元方法,所以该方法适用于裂纹任意分布的多部位损伤板,可直接用于工程实际结构。