基于3D技术的燃气舵烧蚀率测量方法研究CSCD

针对目前采用的燃气舵烧蚀率测量方法存在误差较大问题,提出了一种基于3D扫描技术的新型测量方法,可以有效提高燃气舵烧蚀率测量准确度,为后续武器型号精确设计奠定基础。     

国产T700级碳纤维增强双马树脂基复合材料的力学性能

采用扫描电子显微镜(SEM)、反气相色谱(IGC)和X射线光电子能谱仪(XPS)对国产T700级碳纤维和东丽T700S碳纤维的表面形貌、表面能和表面化学特性进行表征,测试两种碳纤维增强双马树脂基复合材料的力学性能,考察国产碳纤维复合材料的界面黏结性能、韧性和湿热性能。结果表明:碳纤维表面特性(表面形貌、表面能和表面化学组成等)对复合材料界面黏结性能具有显著影响;国产T700级碳纤维/QY9611复合材料在室温下的界面黏结性能优于T700S/QY9611复合材料;国产T700级碳纤维/QY9611复合材料的韧性优异,冲击后压缩强度达到了国外先进复合材料IM7/5250-4的水平;经湿热处理后的层间剪切强度仍与T700S/QY9611复合材料相当,说明国产T700级碳纤维/QY9611复合材料具备良好的湿热性能。     

Microstructure,porosity and mechanical properties of selective laser melted AlSi10Mg

Finite element modeling (FEM), microscopy, X-ray computed tomography (CT) and mechanical property tests were used to study the microstructure, porosity and mechanical properties of an AlSi10Mg alloy produced by selective laser melting (SLM). The simulation of the melt pool and thermal history under different energy densities produced an optimized result with an energy density of 44.5 J·mm⁻³. The high cooling rate during the SLM process significantly refined the previous α-Al dendrites. The growth direction of the network-like Al-Si eutectic structure at different orientations confirmed the anisotropic nature of the microstructure. Furthermore, the microhardness, tensile testing and fracture analysis results proved that there were no obvious distinctions in the strength between the transverse and longitudinal directions, and that the ductility was anisotropic, possibly due to the shape and distribution of the pores. The pores measured by X-ray CT at different energy densities confirmed that the sphericity of the pores was inversely related to pores volumes. With optimized processing conditions, the porosity of the selective laser melted sample decreased leading to the improved fabricated fuel system component via SLM.     

Ultrasound assisted solidification process of ternary Cu–Sn–Sb alloy

It is well-known that the application of ultrasound during liquid to solid transitions for alloys can refine the solidification microstructure and thus improves the mechanical properties. How-ever, most published work focuses on single phase dendritic growth, whereas little has been con-ducted on the multiphase alloys with complicated phase transformations during solidification. In this work, the solidification process of ternary Cu40Sn45Sb15 alloy was realized within intensive ultra-sonic field with a resonant frequency of 20 kHz and ultrasound power from 0 W to 1000 W. The ultrasound refines the size of the primary e(Cu3Sn) intermetallic compound by two orders of mag-nitudes. If the ultrasound power increases to 1000 W, g(Cu6Sn5) phase nucleates and grows directly from parent liquid phase without the occurrence of peri-eutectic reaction on the top of the alloy sam-ple where the ultrasound intensity is sufficiently high. These microstructural variations lead to the enhancement of compressive strength and elasticity modulus of ternary Cu40Sn45Sb15 alloy.     

丁腈橡胶增韧环氧树脂基烧蚀防热材料性能

以丁腈橡胶(CTBN)为增韧剂对环氧树脂(F51)进行增韧改性,通过FTIR、TG以及力学性能测试研究了丁腈橡胶对环氧树脂固化反应、热稳定性能和力学性能的影响,并分析了其增韧机理;分别采用燃气流剪切烧蚀试验和电弧风动烧蚀实验考核了低密度烧蚀材料的烧蚀性能。结果表明:经CTBN改性后,两者的分子链产生了一定程度的交联;树脂基体的拉伸、弯曲性能有所下降,但韧性得到了增强;热稳定性大大提高,增韧后的F51树脂在800℃时的残重率由增韧前的23%提高到了54%;低密度烧蚀材料的抗剪切、抗剥蚀能力得到了增强,且碳层的尺寸稳定性也得到了改善,烧蚀性能提高。     

含氢 WC/ C 复合涂层在不同润滑油环境的摩擦性能

利用非平衡磁控溅射技术,通过同时离化乙炔气体和共溅射石墨靶与碳化钨靶,在304不锈钢和单晶硅基底上沉积具有Cr过渡层和WC过渡层的含氢WC/C复合涂层。采用扫描电镜、Raman光谱仪、X射线衍射仪、纳米压痕仪等对涂层的微观结构、力学性能进行分析。利用Rtec摩擦磨损试验机对WC/C复合涂层与304不锈钢基底在PAO基础润滑油环境、发动机润滑油环境以及腐蚀性发动机润滑油环境进行摩擦性能测试。结果表明:涂层内含有较多类石墨sp2键,WC1-x相镶嵌在非晶碳基质中构成多相复合结构;涂层的硬度和弹性模量明显高于304不锈钢基底,且其H/E值远高于基底;与304不锈钢基底相比,在三种润滑油环境下涂层均具有较低的摩擦因数和磨损率。     

PBT弹性体力学性能及低温脆性研究

采用一步法制备了热固性3,3-双(叠氮甲基)环氧丁烷-四氢呋喃共聚醚(PBT)弹性体,并对其氢键结构、应力-应变关系和动态力学性能及低温脆性进行了研究。结果表明,合成的PBT弹性体拉伸强度和断裂伸长率在DEG羟基含量为35%、R=0.97时,可达2.51 MPa和1 274%,玻璃化温度为-34.5℃。高DEG含量的PBT弹性体脆化参数较低,与常温力学性能变化规律相反。因此,引入低温脆化参数,对PBT弹性体的性能优化具有积极意义。     

C/C素坯密度对GSIC/C-SiC复合材料摩擦磨损性能的影响

采用气相渗硅工艺(GSI)制备C/C-Si C复合材料,研究了C/C素坯密度对GSI C/C-Si C复合材料物相组成与摩擦磨损性能的影响,分析了C/C-Si C复合材料的制动过程,并归纳了其摩擦磨损机理。结果表明,随着C/C素坯密度的增大,GSI C/C-Si C复合材料的密度呈递减趋势,且C含量和开气孔率逐渐增加,而Si C含量和残余Si含量逐渐减少;自对偶条件下,复合材料的平均摩擦系数、磨损率均呈现先增大后减小的趋势,当C/C素坯密度为1.25g/cm3时有最大值,而制动稳定系数则不断增大。GSI C/C-Si C复合材料的制动过程是犁沟效应和粘着效应共同作用的结果,制动初始阶段和刹停阶段以犁沟效应为主,中间阶段以粘着效应为主。     

热变形对TC4氩弧拼焊板拉伸与疲劳性能的影响

在700℃下,对TC4氩弧拼焊板进行了3个变形量(主应变0.5％、1.6％、2.7％)的等双向拉伸成形,研究了热变形对TC4氩弧拼焊板单向拉伸性能和疲劳寿命的影响.结果表明:等双拉变形前后,TC4氩弧拼焊板拉伸试样均断裂在焊接热影响区,热影响区的强度低于母材和焊缝.随着等双拉热变形量增加,TC4拼焊板试样疲劳寿命有所增加,这是因为一定变形量的热成形释放了焊接残余应力.     

冷坩埚定向凝固TiAl基合金高温持久性能研究

采用电磁冷坩埚定向凝固技术制备了成分为Ti-47A1-2Cr-2Nb的合金铸锭,定向凝固后的显微组织为α2+γ全片层结构.在0.4～1.2mm/min的抽拉速率范围内,随着抽拉速率的增加,片层间距减小,柱状晶与生长方向的夹角增大.随着温度升高,合金的拉伸强度有所下降,但由于细化片层界面对切变应力变形的阻碍作用,合金的高温拉伸强度会随着抽拉速率的增加而提高.通过对抽拉速率为1.0mm/min试样的拉伸强度与温度的拟合,得到了拉伸强度和温度之间的函数关系.随着抽拉速率的增加,Ti-47A1-2Cr-2Nb合金的持久寿命明显升高,对于抽拉速率为1.2mm/min试样的持久性能测试表明,其持久寿命最长,达到了48h.持久试样的断口形貌表明,其断裂的主要方式是伴随着少量延性断裂的脆性解理断裂.最后根据时间-温度模型,分别采用Larson-Miller和Manson-Haferd参数法建立了定向凝固Ti-47Al-2Cr-2Nb合金的持久强度预测函数模型,预测的理论值与试验结果吻合度较高.