时效对0Crl5Ni5Cu2Ti钢微观组织与力学性能的影响

研究了960℃和1000℃固溶处理后,时效对马氏体沉淀硬化不锈钢0Cr15Ni5Cu2Ti微观组织与力学性能的影响。钢采用960℃和1000℃固溶处理,在455～460℃时效冲击值出现最低值,断口表现为准解理。强度和硬度在460℃时效出现峰值。主要与组织中细小富铜相共格析出有关。时效温度增加,富铜相长大,强度和硬度降低。     

热处理对高Co-Ni超高强度钢冲击断口的影响

研究了不同固溶及回火温度对高Co-Ni超高强度钢23Co 14Ni12Cr3Mo的Charpy V型缺口试样冲击功AKV和硬度HRC的影响,并用扫描电镜观察分析不同处理状态下的冲击断口形貌,用透射电镜对未溶碳化物进行了分析.结果表明,在850～930 ℃范围内固溶,随温度的提高,冲击功升高,硬度先升高后降低;在454～510 ℃范围内回火,随温度的提高,冲击功也增加,硬度降低.断口形貌观察结果表明,试验用钢冲击断口形貌均呈韧窝状,为韧性穿晶断裂,随固溶温度升高韧窝变大变深.韧窝中发现M23C6型碳化物颗粒,随固溶温度的升高而逐渐减少,提高固溶温度对改善试验用材料综合性能有利.     

固溶温度对C300钨极氩弧焊焊缝成分均匀化的影响

采用光学显微镜、扫描电镜和能谱分析对马氏体时效钢(C300级)钨极氩弧焊焊缝中偏析的合金元素在不同温度固溶时均匀化情况进行了初步的计算和分析。研究认为C300钨极氩弧焊焊缝中主要偏析合金元素是Ni,Mo,Ti;焊缝经1200℃/1h AC处理可以获得成分均匀的马氏体;成分均匀的焊缝进行480℃/4h AC时效处理将不再产生逆转变奥氏体。     

固溶对Al-Cu-Li-X合金组织和性能的影响

通过OM,SEM,TEM和力学性能测试等手段,研究了固溶处理对Al-Cu-Li-X合金组织和性能的影响.结果表明:2A97合金T6态(未拉伸态)在520℃固溶80min,淬火转移时间小于15s,水淬,获得了合适力学性能,抗拉强度为493MPa,屈服强度为415MPa,延伸率为7.3%.合金时效强化相以T1,θ′/θ″和δ′ 相为主.经510℃,520℃和530℃固溶水淬,再165℃时效18h,随固溶温度升高,强度和塑性趋于减小.在520℃固溶水淬,再165℃时效18h,随固溶时间延长,屈服强度趋于升高,延伸率先升后降低.随固溶温度升高和时间延长,可溶过剩相数量和体积分数减小.520℃固溶后时效,基体沉淀相T1,θ′/θ″和δ′ 相数量多,尺寸小,分布均匀.     

13Cr4Mo4Ni4VA钢复合硬化层的表征研究

对渗碳硬化13Cr4Mo4Ni4VA钢进行渗氮处理后形成复合硬化层,采用光学显微镜、扫描电镜、X射线衍射、透射电镜、高分辨电镜、电子探针及显微硬度测试等方法对复合硬化层进行表征。结果表明,复合硬化13Cr4Mo4Ni4VA钢渗层碳氮浓度呈梯度分布,从表面到心部组织性能也呈梯度变化,表现出异于传统硬化工艺的组织结构特性。复合硬化层为双层硬化结构,渗氮层组织优异,少无沿晶化合物,析出细小的片状的Mo2N、周期性层状分布的Mo2C以及Cr2(C,N)等合金碳(氮)化合物,在析出相沉淀硬化和碳氮原子固溶强化共同作用下,使复合硬化层表面硬度达到超硬化(70HRC),有效硬化层维持很大的层深,具有优异的硬度梯度及残余压应力场。     

固溶处理对一种2xxx/SiC_p铝基复合材料组织和性能的影响

采用快速凝固/粉末冶金工艺制备了一种2xxx/SiCp铝基复合材料,利用扫描电镜(SEM)、能谱(EDS)、室温拉伸和硬度等测试方法研究了不同热处理参数对材料微观组织和力学性能的影响。结果表明:当固溶温度为485℃时,仍有大量未溶解的可溶相θ(Al2Cu),S(Al2CuMg)和极少量不可溶相AlCuFe存在于基体中,随固溶温度的升高,未溶解的可溶相逐渐回溶,当固溶温度达到500℃,可溶相充分回溶,仅剩下含量极少的不可溶相残留在基体中,固溶温度在490~500℃时,复合材料能同时获得较高的强度和塑性;淬火介质(水)温度超过60℃时,复合材料强度开始明显降低;自然时效时间超过60min后,材料的布氏硬度迅速提升,时效强化效果趋于明显。     

固溶、时效对７００３铝合金组织与性能的影响

通过显微硬度测试、力学性能测试、SEM观察以及EDS分析等手段对不同热处理制度下的7003合金的组织与性能进行了系统的研究.结果表明:时效前,随着固溶温度的提高,合金的显微硬度和强度不断降低,而塑性则不断提高;随着固溶时间的延长,强度和硬度先降低后增大,塑性则先降低后提高.经过120℃/50 h人工时效和60 d自然时效后,合金的力学性能明显高于时效前,且470℃/70 min固溶的综合力学性能最好(σ0.2=302 MPa,σb=363 MPa,δ=12.5%).7003合金的优化固溶处理制度是470℃/70 min.     

热处理制度对1Cr16Ni2MoN钢组织和性能的影响

通过试验研究了不同热处理制度对1Cr16Ni2MoN钢的金相组织、室温拉伸、冲击性能、硬度的影响.随淬火温度的提高,晶粒长大,570℃回火后的强度、塑性、韧性均增加,但660℃回火后的强度、塑性均下降;脆性温度区间为500℃左右;随1040℃保温时间的延长,略提高570℃回火后的强度,略降低660℃回火后的强度.合金优化的热处理工艺为:(a) 1030～ 1040℃×1h油冷+ 550～570×1 h空冷;(b) 1030 ～ 1040℃×1h油冷+650～ 670×1 h空冷.     

一种1350MPa级低密度高强度钢的组织性能

开发了一种1350 MPa级低密度Fe-29Mn-10Al-1.0C钢。采用光学显微镜、X射线衍射、高分辨电镜等方法对不同热处理状态下低密度钢的力学性能和组织演变规律进行研究。结果表明:实验钢在固溶、时效过程中发生了调幅分解,形成了L′12结构有序相κ′碳化物;实验钢经950℃固溶处理后,尺寸为2~5 nm的κ′碳化物弥散分布在奥氏体基体上;随后的时效过程中,随着时效温度提高,κ′碳化物尺寸增大,趋向于沿100方向分布,长大粗化择优取向,最终形成规则的"方格阵"调制组织;在有序强化和调幅组织强化的共同作用下,实验钢具有良好的强塑性配合,抗拉强度高达1350 MPa,密度小于6.80 g/cm~3。     

铸造铝合金ZL114A 的热处理工艺

对铸造铝合金ZL114A开展热处理试验,研究了固溶温度、固溶时间、淬火水温、时效温度和时效时间等工艺参数对力学性能的影响,比较了铸态和固溶热处理后的组织变化,并优选出最佳的热处理工艺制度,540℃×14 h/水冷(55℃)+155℃×7.5 h/空冷,为后续的工业化生产提供了参考.     

Microstructure and mechanical properties of hybrid fabricated 1Cr12Ni2WMoVNb steel by laser melting deposition

 Laser melting deposition was carried out to deposit a 1Cr12Ni2WMoVNb steel bar on a wrought bar of same material. Room-temperature tensile properties of the hybrid fabricated 1Cr12Ni2WMoVNb steel sample were evaluated, and microstructure, fracture surface morphology, and hardness profile were analyzed by an optical microscope (OM), a scanning electron microscope (SEM), and a hardness tester. Results show that the hybrid fabricated 1Cr12Ni2WMoVNb steel sample consists of laser deposited zone, wrought substrate zone, and heat affected zone (HAZ) of the wrought substrate. The laser deposited zone has coarse columnar prior austenite grains and fine well-aligned dendritic structure, while the HAZ of the wrought substrate has equiaxed prior austenite grains which are notably finer than those in the wrought substrate zone. Besides, austenitic transformation mechanism of the HAZ of the wrought substrate is different from that of the laser deposited zone during the reheating period of the laser deposition, which determines the different prior austenite grain morphologies of the two zones. Microhardness values of both the laser deposited zone and the HAZ of the wrought substrate are higher than that of the wrought substrate zone. Tensile properties of the hybrid fabricated 1Cr12Ni2WMoVNb steel sample are comparable to those of the wrought bar, and fracture occurs in the wrought substrate zone during the tensile test.     

13Cr4Mo4Ni4VA钢复合化学热处理过程渗层组织性能演变

对13Cr4Mo4Ni4VA钢进行了表层复合化学热处理,即在渗碳硬化层的基础上再进行渗氮处理,形成复合硬化层.采用光学显微镜(OM)、扫描电镜(SEM)、X射线衍射(XRD)、电子探针(EMPA)及显微硬度梯度测试等方法对复合化学热处理过程组织性能的演变规律进行探索研究.结果表明,13Cr4Mo4Ni4VA钢在复合化学...     

新型超高强度钢应力腐蚀断裂行为研究

采用恒载荷拉伸应力腐蚀实验研究了23Co14Ni12Cr3及40CrNi2Si2MoVA两种超高强度钢在质量分数为3.5％的NaCl溶液中的应力腐蚀开裂行为,为两种超高强度钢在结构件中的安全使用提供数据依据.通过金相显微镜和扫描电镜(SEM)对两种超高强度钢的显微组织以及断口形貌进行了分析.恒载荷拉伸应力腐蚀实验结果表...     

二次硬化16Co14Ni10Cr2Mo钢低倍“亮点”的研究

用光学金相、显微硬度、扫描电镜、电子探针对二次硬化１６Ｃｏ１４Ｎｉ１０Ｃｒ２Ｍｏ钢低倍“亮点”进行了深入研究。结果表明：低倍“亮点”是一种偏析性质的点缺陷，亮点区主要是由于Ｎｉ的正偏析造成的。讨论了点状偏析对合金工艺性能和力学性能的影响。     

热处理对9 Cr13 Mo3 Co3 Nb2 V组织与硬度的影响

采用金相分析、硬度测试等技术手段,研究热处理对马氏体不锈钢9Cr13Mo3Co3Nb2V组织和硬度的影响。结果表明：9Cr13Mo3Co3Nb2V经淬火、冰冷处理及多次回火后,残余奥氏体充分转变为回火马氏体,并产生较强的二次硬化效果,进而获得稳定的组织和高的硬度;在350℃以上回火时,由于组织中二次碳化物的析出,开始出现二次硬化倾向,至480~520℃时,回火硬度达到了最大值。     

30CrMnSiNi2A超高强度钢真空电子束焊接工艺应用研究

针对锁底对接形式的30CrMnSiNi2A超高强度钢进行了真空电子束焊接工艺分析与讨论,借助金相分析、显微硬度、扫描电镜等测试方法对焊缝形貌、组织和性能进行了研究,并分析了常见缺陷的种类和防止措施。试验结果表明,在合适的电子束焊接参数下可以获得较为理想的30CrMnSiNi2A超高强度钢焊缝形貌,且具有较好的综合力学性能,焊缝经目视检查、X射线探伤和磁粉探伤,达到I级焊缝要求,并将此焊接工艺成功地应用于飞机机体产品的焊接。     

SiO2 改性ZrO2 气凝胶高温稳定性

以ZrOCl2·8H2O 为锆源,以环氧丙烷( PO) 为凝胶促进剂制备ZrO2 凝胶,将ZrO2 凝胶置于正硅
酸乙酯乙醇溶液中老化,再结合高温超临界干燥工艺制备了SiO2 改性ZrO2 气凝胶。通过对比ZrO2 气凝胶和
SiO2 改性ZrO2 气凝胶高温结构转变讨论了SiO2 改性对ZrO2 气凝胶高温结构的影响。采用FT-IR、XRD、SEM
和TEM 等分析手段对样品进行高温结构表征。结果表明:采用正硅酸乙酯乙醇溶液老化ZrO2 凝胶后,在ZrO2
凝胶粒子表面形成了一层SiO2 包裹层,这层SiO2 包裹层显著抑制了ZrO2 的扩散、成核和生长过程,高温稳定
性得以显著提高。     

正交设计在沉淀硬化不锈钢热处理研究中的应用

用正交设计法研究固溶温度、固溶时间、调整处理温度和调整处理时间对0Cr17Ni5Mo3沉淀硬化不锈钢力学性能的影响.研究结果表明,在沉淀硬化不锈钢热处理研究中采用正交设计法安排试验,可以用很少的试验量获得主要热处理工艺参数对力学性能影响的规律.     

原位合成TiB_2/6351复合材料热压缩变形特性

采用Gleeble-1500D热模拟试验机对原位合成TiB2(质量分数,8%)/6351复合材料在不同变形温度和不同应变速率条件下的热变形特性进行了研究,利用透射电镜(TEM)和光学显微镜分析了压缩后试样的微观组织.结果表明, 材料的流变应力随变形温度的升高而降低,随应变速率的提高而增大;材料的流变行为主要表现为加工硬化、动态回复和动态再结晶;相应的显微组织特征为:位错网络、混乱的位错团和胞状结构,亚晶及等轴晶.在应变速率和变形温度均较低时,增强体颗粒周围的基体中形成高密度位错区,但随变形温度的升高而减少;在应变速率较高时,增强体颗粒和基体的界面处开裂甚至增强体颗粒本身发生破碎.     

GC-4超高强钢焊接冷裂倾向的评价

GC-4钢是我国自行研制的一种无Ni低Cr超高强钢,主要用它取代30CrMnSiNi2A钢制造飞机起落架等受力构件。但由于该钢种含碳量高,合金元素多,冷裂倾向较大,使其应用受到限制,因此探明该钢种的冷裂倾向。制定一套合理的焊接工艺,防止冷裂纹的产生。