注胶法修复5228A/ CF3031 层压板力学性能研究

针对5228A/ CF3031 层压板生产过程中可能产生的缺陷,设计并制造了孔径超差、不圆孔、孔径
分层、孔边打磨过分、边缘分层等5 种常见缺陷,并采用注胶法对5 种缺陷进行修复。采用ASTM 标准对无缺
陷试样、缺陷试样、修复试样的拉伸、压缩、弯曲、纵横剪切和层间剪切强度进行了测试,并对试样进行了光学显
微镜观察。研究表明孔径超差对拉伸、压缩、弯曲强度影响较大,缺陷试样强度分别下降了11. 1%、13. 8%、
14.4%;孔边打磨过分对纵横剪切强度影响较大,缺陷试样纵横剪切强度下降了25. 6%;边缘分层对层间剪切
强度影响较大,缺陷试样层间剪切强度下降了27. 3%。采用注胶法修复后,5 种缺陷试样的力学性能均有一定
程度的提高。相比而言,修复后层压板抵抗拉伸、压缩、层间剪切等小形变破坏的效果显著;抵抗弯曲、纵横剪
切等大形变破坏的效果不理想。     

记忆合金箍环增强复合材料管件接头力学性能分析

复合材料管件在使用时需与接头粘接,粘接的强度常常决定了整个管件的承载能力。本文首先用有限元方法分析了记忆合金箍环对复合材料圆管接头承拉能力的影响,再通过两组轴拉静力试验测试了记忆合金箍环对复合材料圆管拉伸强度的影响程度。试验结果表明记忆合金箍环能提高复合材料圆管接头拉伸强度10.1%,能较好地提高连接性能,这与有限元分析结果相符,分析及试验结果对复合材料管件设计改进有指导作用。     

纤维曲线铺放的变刚度复合材料层合板的失效分析

介绍了一种纤维曲线铺放的变刚度复合材料层合板有限元建模方法。按照曲线铺放规律定义每

一个单元的实常数,并对这种纤维曲线铺放层合板进行建模。在此基础上讨论了在弯曲和压缩失效两种不同

边界条件下,采用Tsai-Wu 失效准则,对其进行失效分析,验证其面内受力情况,计算最大的Tsai-Wu 强度比

倒数1/ R。当1/ R =1 时,所施加的载荷为失效的临界载荷。对比两组纤维直线和纤维曲线的铺层算例,弯曲

失效条件下临界失效载荷提高16%和21%,压缩失效条件下临界失效载荷提高51% 和19%。纤维曲线铺放

层合板有效提高了失效性能。

     

国产中温固化热破胶膜性能

考察了一种适用于卫星太阳翼基板的国产中温固化胶膜的胶接性能和热破工艺性,并分别采用国产和进口胶膜,利用胶膜热破施胶方法制备了碳纤维网格面板/铝蜂窝芯夹层结构,对其弯曲性能进行评价。结果表明,国产胶膜的室温拉伸剪切强度（铝基材）为34.9 MPa,150 ℃时拉伸剪切强度降为10.2 MPa,-150 ℃时拉伸剪切强度降为30.4 MPa。碳纤维复合材料作为胶接基材时,室温拉伸剪切强度为17.5 MPa,破坏模式为基材分层破坏和胶黏剂内聚破坏的混合破坏模式。国产胶膜具有良好的热破工艺特性,在合适的工艺条件下,破孔率优于99.9%,90°板-芯剥离强度为15.4 N/cm;采用国产胶膜制备的蜂窝夹层结构的弯曲性能与采用进口Redux312UL的接近,弯曲刚度为1.94×10⁸ N·mm²,弯曲强度为35.7 MPa。     

复合材料帽型筋条脱粘的失效机理分析

复合材料加筋结构承受后屈曲载荷时,蒙皮局部屈曲会导致筋条承受面外弯曲载荷,极易引起蒙皮与筋条的界面脱粘,最终导致结构破坏.通过四点弯曲试验模拟加筋结构受后屈曲载荷时的蒙皮/筋条界面性能,建立渐进损伤模型,分别考虑筋条与蒙皮胶接界面以及复合材料层板的失效,并引入材料刚度退化模型,详细分析蒙皮/筋条界面的脱粘机理和失效过程.分析结果与试验结果一致,表明加载跨距对于结构的失效形式影响较大,90 mm加载时,胶层均首先失效于筋条与蒙皮内角处的胶接界面,且主要受Ⅱ型剪切模式影响;而150 mm加载情况下胶层均首先失效于翼缘自由端与蒙皮交界处.正向加载时胶层失效主要受Ⅰ型和Ⅱ型混合模式影响,反向加载胶层主要受Ⅱ型剪切模式影响.界面脱粘以后,随着载荷增加,筋条腹板与缘条转角外侧出现分层破坏,损伤模型预测结果与超声扫描检测结果一致.     

蜂窝结构板后埋件拉脱力的影响因素

介绍了蜂窝结构板上M5 后埋直通连接件的拉脱力测试条件及结果,分析了后埋件胶接施工过

程、胶接固化规范对后埋件拉脱力和胶接质量的影响。结果表明,沿开孔轴向竖直灌胶后再安装埋件,胶液填

充效果最好,气孔最少,有利于提高拉脱力;对于EA934NA 后埋胶,于室温≥22℃下完成固化,更有利于提高拉

脱力。所得结果可为产品试验设计和拟定工艺参数提供

     

纤维铺层方式对CFRP?铝合金单搭接胶接接头拉伸性能影响

为了分析异质材料胶接接头内部典型应力分布规律与刚度退化特点,探究不同铺层方式对异质材料单搭接胶接接头内部应力分布状态影响规律,开展试验和仿真相关研究。首先,制备不同铺层方式的CFRP（carbon fiber reinforce plastic）?铝合金单搭接胶接接头试验件,使用拉伸试验机进行拉伸试验,获得基本试验数据。其次,利用连续损伤模型、3D Hashin失效判据和Cohesive Zone Model研究异质材料胶接接头不同部位典型破坏特点。结果表明,随着复合材料板中0°铺层比例增加,胶接接头极限载荷呈现增加趋势,与之相反接头拉伸位移逐渐缩短。接头铺层方式与载荷方向共同影响胶接接头力学性能,当复合材料板内部各个方向纤维铺层较为均匀时,可以有效降低接头应力集中,载荷方向与铺层纤维方向一致时,可有效提高接头连接强度。复合材料板中0°铺层占比对接头的极限载荷和刚度退化（scalar stiffness degradation,SDEG）影响较大,0°占比越小接头承载能力越弱,接头刚度退化越复杂。      

蜂窝夹层结构及其埋件的力学性能研究

对蜂窝夹层结构及其侧向和板内M5埋件力学性能进行了研究,分析了蒙皮厚度、胶黏剂面密度和胶接强度对力学性能的影响。结果表明,适当增加蒙皮厚度,有利于提高蜂窝夹层结构及其埋件的力学性能;在同等胶接强度下,胶黏剂面密度对力学性能的影响可以忽略,可选用面密度较低的胶黏剂来降低结构质量;埋件系统承受面内剪切载荷的能力明显优于其承受垂直于蒙皮的面外拉拔载荷能力;承受面内剪切载荷时,埋件系统的失效模式以埋件区域蒙皮局部破坏为主;承受面外拉拔载荷时,埋件周围蜂窝芯先失稳破坏,并最终导致埋件带动蒙皮变形、局部发生破坏。所得结果可为结构设计优化提供参考。     

湿热环境下K-cor夹层复合材料的力学性能

K-cor夹层结构是应用Z-pin技术增强的一种新型高性能夹层结构,本文研究了Z-pin不同植入密度对K-cor夹层结构试样吸湿特性的影响规律,在此基础上对不同Z-pin植入参数对试样湿热前后三点弯曲性能和压缩性能的影响规律进行了深入研究。研究结果表明：夹层结构中Z-pin的植入能提高试样的尺寸稳定性,且不会对其吸湿率造成明显影响;Z-pin植入密度的增加能明显提高湿热前后试样三点弯曲强度和压缩强度,且具有较高的强度保持率,Z-pin密度为12 mm×12 mm的K-cor夹层结构湿热处理试样的三点弯曲强度比未湿热处理空白试样的要高11.1%,8 mm×8 mm湿热处理K-cor试样的芯部压缩强度比未湿热处理空白夹层结构试样要高17.5%,体现出K-cor夹层结构优异的抗湿热性能;而Z-pin植入角度的减小能明显提高试样湿热处理前后的压缩强度,0°植入K-cor试样湿热处理后的芯部压缩强度与40°植入K-cor试样未湿热处理的基本相同,但植入角度对三点弯曲强度影响较小。     

芯材高度对三维中空夹芯复合材料低速冲击性能的影响

选取芯材高度分别为5、6、7 mm 的三维中空夹芯复合材料为研究对象,采用落锤式低速冲击试

验装置分别对上述材料进行8 J 能量的低速冲击测试,研究材料的低速冲击性能;利用Instron 3385H 型万能材

料试验机分别测试上述材料受到低速冲击载荷前后的压缩强度,研究材料受到低速冲击载荷后的压缩损伤容

限。结果表明:三维中空夹芯复合材料对低速冲击载荷比较敏感;随着芯材高度的增加,材料抗低速冲击性能

有所增加;低速冲击载荷使材料的剩余压缩强度大幅下降。

     

激光增材制造钛合金构件的化学抛光工艺研究

采用HNO3-HF抛光液对激光选区熔化钛合金制件进行化学抛光,以试样表面粗糙度、减薄及失重变化为指标探究了抛光过程中不同温度和时间对钛合金增材制件抛光效果的影响。通过电化学测量、拉伸试验、残余应力测试等方法对比分析了化学抛光前后钛合金试样的电化学和力学性能。结果表明在温度30℃、反应时间10min下抛光钛合金可以取得较理想的抛光效果,试样表面粗糙度减小、耐腐蚀性能提高。化学抛光后钛合金的强度出现小幅下降,内部原有的残余应力由拉应力转变为压应力。     

一种交织铺层结构层合板性能

结合复合材料自动纤维铺放(AFP)技术,提出了一种交织铺层结构层合板成型方法,制备了非交织、交织正交层合板、非交织、两向交织和四向交织准各向同性层合板复合材料,并对交织铺层结构复合材料的层间结构和性能进行了分析研究。结果表明:交织正交层合板的拉伸、压缩、弯曲性能较非交织板性能均有所下降,但其层间剪切性能有明显提高,提高幅度约为16%;随着交织铺层组厚度的增加,交织层合板的拉伸性能呈下降趋势;交织层合板的开孔后拉伸、开孔后压缩和冲击后压缩强度保持率均高于非交织板,且冲击后分层损伤面积明显低于非交织板。交织铺层结构层合板相对于普通非交织层合板具有更好的损伤容限能力。     

固体自润滑材料极端温度环境适应能力研究

模拟月球表面极端高低温环境,对空间飞行器机构活动部件常用固体自润滑材料进行极端温度环境存贮实验.通过拉伸强度、压缩强度、弯曲强度、冲击强度、摩擦磨损等性能研究,评价固体自润滑材料在月面极端高低温环境下的生存适应能力.结果表明,两种典型空间用固体自润滑材料模拟三个月球日经历极端温度环境存储实验后,各项性能都未发生明显变化.     

Dynamic tensile behavior of AZ31B magnesium alloy at ultra-high strain rates

The samples having {0001} parallel to extruding direction(ED) present a typical true stress–true strain curve with concave-down shape under tension at low strain rate. Ultra-rapid tensile tests were conducted at room temperature on a textured AZ31 B magnesium alloy. The dynamic tensile behavior was investigated. The results show that at ultra-high strain rates of 1.93 · 102 s 1and 1.70 · 103 s 1, the alloy behaves with a linear stress–strain response in most strain range and exhibits a brittle fracture. In this case, {10-12} 10-11 extension twinning is basic deformation mode. The brittleness is due to the macroscopic viscosity at ultra-high strain rate, for which the external critical shear stress rapidly gets high to result in a cleavage fracture before large amounts of dislocations are activated. Because {10-12} tension twinning, {10-11} compressive twinning,basal a slip, prismatic a slip and pyramidal c + a slip have different critical shear stresses(CRSS), their contributions to the degree of deformation are very differential. In addition,Schmid factor plays an important role in the activity of various deformation modes and it is the key factor for the samples with different strain rates exhibit various mechanical behavior under dynamic tensile loading.     

Tensile properties analysis of CFRP-titanium plate multi-bolt hybrid joints

Hybrid joints have better tensile properties than pure bonded and bolted bolts, and are increasingly used in the aerospace field. Tensile tests are carried out for the Hybrid Bonded/Bolted(HBB) joints of Carbon Fiber Reinforced Polymer(CFRP) laminate and titanium alloy plate under different bolt numbers, and the corresponding load–displacement curves are obtained. At the same time, based on Continuum Damage Mechanics(CDM) theory, which is derived from 3D Hashin failure criteria, and a Cohesive Z...     

Precipitation behavior and properties of extruded 7136 aluminum alloy under different aging treatments

In this work, the mechanical properties and electrical conductivity of the extruded 7136 aluminum alloy treated by single-stage aging treatment (T6), retrogression and re-aging treatment (RRA), and multiple retrogression and re-aging treatment have been investigated by means of hardness measurements, electrical conductivity tests and tensile tests. The results have shown that the properties of the 7136 alloy such as hardness, tensile strength and electrical conductivity were sensitive to retrogression time (within 90 min). With prolonging the retrogression time, the tensile strength was enhanced first and then decreased, yet the electrical conductivity was continuously increased. The 60 min-treated alloy performed the highest tensile strength (716 MPa), whereas the 90 min-treated alloy possessed the highest electrical conductivity (33.95%IACS). Compared with the T6-treated alloy, the tensile strength and electrical conductivity were improved by 3.3% and 18.9%, respectively. The electrical conductivity showed an obvious increase with repetitious times of the RRA treatment. After 3RRA60 treatment, a good combination of tensile strength (705 MPa) and electrical conductivity (33.20%IACS) can be obtained. Compared with the T6 condition, the tensile strength and electrical conductivity were improved by 1.7% and 16.3%, respectively. The mechanism of microstructure evolution under different aging treatments has been discussed in detail.     

EB-PVD热障涂层对IC10合金力学性能的影响

采用电弧离子镀技术在IC20合金基体上制备NiCrAlYSi粘结层,利用电子束物理气相沉积（EB—PVD）技术在粘结层上制备YSZ陶瓷面层。研究了YSZ热障涂层对IC10合金拉伸、持久、疲劳性能的影响。结果表明：IC10合金沉积YSZ热障涂层后,980℃／200MPa高温持久寿命与IC10合金相当;900℃高温抗拉强度σb、屈服强度σ0.2、伸长率占和断面收缩率砂与基体相比,基本保持不变;室温抗拉强度σb。屈服强度σ0.2：与基体相比稍有下降;800℃／447MPa疲劳寿命与基体合金相当。因此,IC10合金沉积TBCs涂层后,对IC10合金力学性能无明显影响,不影响合金的实际使用。     

刚性隔热材料的力学性能

采用纤维烧结法制备了刚性隔热材料,研究了材料密度、纤维取向、测试温度、与气凝胶复合等因素对材料力学强度的影响规律.结果表明:隔热材料力学强度随着密度的提高而增加;隔热材料平面方向拉伸和压缩强度均达到厚度方向的4倍以上;800和1 000℃下,材料的压缩强度保持率分别达到90%和50%;与气凝胶复合后隔热材料在拉伸强度维持不变的情况下,压缩强度增加35%以上.     

固化温度对苎麻纤维增强复合材料性能的影响

研究了固化温度对苎麻纤维增强复合材料力学性能的影响,同时对比研究了平纹苎麻织物、单向苎麻纤维和单向玻璃纤维增强复合材料的力学性能.结果表明:环氧树脂3233分别在120℃,140℃和l80℃固化2h后,其拉伸性能和弯曲性能没有明显的变化;而基于环氧树脂3233的苎麻纤维增强复合材料在120℃和l40℃固化2h后力学性能相当,但是在180℃固化2h后,强度明显减小,模量变化不大;单向苎麻纤维增强复合材料的力学性能要远远大于平纹苎麻织物增强复合材料的力学性能,如单向苎麻复合材料uRamie-3233-120的压缩强度和压缩模量分别为154.0 MPa和35.6 GPa,而苎麻织物增强复合材料fRamie-3233-120分别为95.0 MPa和9.2 GPa;玻璃纤维增强复合材料的强度也会高明显高于苎麻纤维增强复合材料的强度.     

制备工艺对NiAl-30Fe-Y合金组织与性能的影响

研究了铸态、挤压态、热轧态和定向凝固结晶４种不同制备工艺对ＮｉＡｌ－３０Ｆｅ－Ｙ合金组织与性能的影响。结果表明,热轧和定向凝固结晶工艺明显改善了合金性能,特别是提高了合金室温塑性。在室温下不同制备工艺其拉伸断口特征明显不同。不同制备工艺仅对微观组织形态产生影响,其合金组织皆是由先共晶Ｂ２结构β和β与（γ＋γ'）共晶相组成,定向凝固合金成长方向为＜２１１＞β‖＜１００＞（γ＋γ'）。