钛合金薄板激光修饰焊残余应力研究

采用X射线法测量焊接残余应力,对比研究了TC4钛合金薄板激光焊和激光修饰焊的残余应力分布规律与特点。结果表明:激光修饰焊未改变TC4钛合金薄板激光焊接接头残余应力的分布特征;激光修饰焊可以显著降低焊接接头横向残余应力,X方向上的最大残余压应力由原来的409MPa降到345MPa,Y方向则从316MPa降至278MPa,在焊缝两侧8mm范围内,应力值波动很小,基本呈现均匀分布,对于焊接纵向残余应力激光修饰焊只是略微降低应力波动幅度;与激光焊的接头边缘处相比,由于边缘效应激光修饰焊接产生的残余应力释放幅度较低,从27%~42%降到10%~18%。     

AISI 304钢-铌异种金属激光焊温度场及残余应力研究

采用SYSWELD软件,对AISI 304钢–铌异种金属激光焊接过程进行动态模拟,在研究了AISI 304钢–铌异种金属激光焊接接头温度场的基础上,分析了焊后薄板的残余应力分布。结果表明:异种金属焊接温度场呈不对称分布,铌侧高温区域比不锈钢侧要宽;沿焊接方向上,无论是横向残余应力还是纵向残余应力,焊缝中部区域都存在最大残余拉应力;而垂直于焊缝方向上,横向残余应力和纵向残余应力在焊缝及焊缝附近区域应力梯度都比较大,分布形态都呈"M"状,纵向残余应力在焊缝区表现为残余拉应力,而横向残余应力在焊缝中心处出现了压应力。     

钛合金激光焊接研究现状

随着航空工业的发展,钛合金在航空结构中有着越来越广泛的应用。焊接作为重要的连接手段,其制造接头的力学性能决定了构件的使用性能。激光焊接具有高能束焊接方法热输入小、残余应力及变形小的特点,焊接质量高,并且能在开放环境中开展工作,已成为真空电子束焊接外另一种优秀的钛合金焊接方法,是近年研究的热点。总结了近期钛合金激光焊接的一些研究工作,重点介绍了关于激光焊接钛合金组织性能调控方面的成果,并讨论了钛合金激光焊所存在的问题,具体内容包括:激光类型和扫描方式对接头质量的影响、三种典型(α型、α+β型和β型)钛合金激光焊接头组织性能特点、焊后热处理对钛合金激光焊接头组织性能调控方法。为采用激光焊接方法制造高质量钛合金接头研究工作提供参考。     

激光喷丸对7075铝合金搅拌摩擦焊接头的影响

以7075铝合金试样的搅拌摩擦焊接头为对象,利用激光喷丸和常规喷丸工艺对其进行后续处理,通过试验对比分析了激光喷丸工艺对表面粗糙度、显微硬度、接头残余应力、裂纹扩展、疲劳寿命的影响。结果表明,经激光喷丸处理的搅拌摩擦焊接头的表面粗糙度远小于常规喷丸处理的接头表面,而对接头显微硬度的影响差异不大。激光喷丸可改变接头的残余应力分布,是增强搅拌摩擦焊接头抗疲劳性的有效方法,对其他焊接接头及构件的激光喷丸处理具有一定的参考价值。     

钛合金电子束焊接表面残余应力的测试和有限元分析

采用多束电子束流焊接Ti60钛合金,并利用小孔法和有限元分析方法分别测试和模拟焊后残余应力值.对焊前预热、焊后缓冷和焊前预热+焊后缓冷三种焊接工艺下的残余应力值进行比较,研究残余应力的分布规律.研究结果表明,在垂直焊缝截面上,纵向残余应力σx的模拟结果与测试结果在变化趋势上基本一致.在平行焊缝截面上,实测与模拟纵向残余应力σx的分布规律相似.证明了有限元模型的合理性和可靠性.采用预热+焊接的焊接工艺对残余应力影响不大,采用焊接+缓冷的焊接工艺可以改变残余应力的分布.     

工艺参数对钛合金激光T型接头焊缝成形及剪切力的影响

文摘采用连续激光焊工艺焊接TC4/TA15激光T型接头,运用体式显微镜及拉伸试验机对接头进行测试分析,研究工艺参数对激光T型接头焊缝成形及剪切性能的影响。结果表明:在其他参数保持不变的情况下,随着激光功率在一定范围内的提高,焊接速度在一定范围内的降低,骨架熔宽及骨架熔深增加;骨架熔宽是影响激光T型接头剪切性能的决定性参数,匹配激光功率超过4.1 kW、焊接速度低于80 mm/s、离焦量为-5~+10 mm,可使骨架熔宽超过0.51 mm,接头剪切力达到14 kN以上水平。     

钛合金激光焊接残余应力试验与数值模拟

采用小孔释放法对钛合金薄板激光焊接残余应力进行了试验研究,并基于ANSYS分析软件,针对钛合金薄板的焊接残余应力进行了数值模拟,分析了不同焊接工艺参数对激光焊接残余应力分布的影响.     

浅析搅拌摩擦焊残余应力

讨论了搅拌摩擦焊残余应力的产生原因,在已有的试验结果的基础上对残余应力的分布和规律进行了概述。并且以钨极氩弧焊(TIG)为例,将搅拌摩擦焊与传统熔焊的残余应力分布进行了对比,进一步肯定了搅拌摩擦焊在铝合金焊接时的优越性。同时还介绍了对搅拌摩擦焊残余应力的控制方法及其效果,最后对有关搅拌摩擦焊的残余应力的研究工作做出了展望。     

铝合金焊接结构的应力松弛及控制

针对生产现场大尺寸5A06-H112铝合金板箱形件拼焊制造过程中存在应力松弛的问题,对多种焊接工艺方法进行了研究.通过对不同焊接接头的力学性能试验、残余应力测试、焊接金相和硬度测量结果对比显示,铝合金焊接结构的应力变化存在先升后降的变化趋势,而TIG焊由于采用较小的线能量和多层焊,较MIG焊其应力松弛的程度存在差异.结果表明,增加焊后时效时间8～10d,并采用TIG焊技术将有效减小铝合金焊接结构的应力松弛,使端头下沉减少50％左右,满足了设计图纸的要求.     

钛合金T-型结构单面焊背面双侧成形焊接接头组织与性能

应用TIG焊、激光-TIG电弧复合焊工艺,采用单面焊背面双侧成形焊接技术对钛合金T-型结构进行焊接.对两种工艺进行金相组织、拉伸、弯曲、疲劳性能对比试验.研究结果表明,激光-TIG电弧复合焊工艺焊接钛合金T-型结构,近缝区及热影响区晶粒长大倾向明显要小于TIG焊接头,激光-TIG电弧复合焊工艺的明显高于TIG焊工艺,复合焊接的疲劳强度相比TIG焊提高约50％.因此,激光-TIG电弧复合焊工艺焊接钛合金T-型结构综合力学性能优于TIG焊接头.     

轻合金T型结构双激光束双侧同步焊接技术研究进展

轻合金双激光束双侧同步焊接(Double Laser-Beam Bilateral Synchronous Welding,DLBSW)技术是一项极具应用前景与发展潜力的先进技术,对实现航空航天壁板结构的轻量化与高效率制造具有重要意义。然而,由于轻合金本身的材料特性与DLBSW技术的特殊性,轻合金T型结构DLBSW技术仍然存在诸多细节问题有待深入探索。分析了轻合金T型结构DLBSW技术的焊接冶金特点与稳定性,重点研究了DLBSW接头中焊接缺陷的形成机理与抑制措施,考察了T型接头的力学性能与断裂机理。此外,探讨了轻合金T型结构DLBSW过程数值模拟研究的重要意义。     

基于形状改变比能和材料属性离散的焊接残余应力估算

为了提高焊接残余应力测量精度,在2219-T87铝合金TIG焊接接头残余应力测定试验基础上,通过离散接头材料属性并利用形状改变比能对焊接残余应力进行塑性修正,分别研究孔边塑性变形和接头强度不匹配对焊接残余应力估算的影响。结果表明：同时考虑孔边塑性变形和接头强度不匹配因素的焊接残余应力估算方法,比线弹性残余应力计算方法能最大减小39.8%的误差;当测量点距焊缝距离小于8mm时,在考虑孔边塑性变形的情况下,同时考虑接头不匹配的影响相比不考虑其影响可最大减小40.6%的误差;当测量点距焊缝距离大于8mm时,可忽略接头强度不匹配对焊接残余应力估算的影响。     

Review on residual stress and its effects on manufacturing of aluminium alloy structural panels with typical multi-processes

In the aerospace industry, integrated aluminium alloy plates and stiffened panels with high accuracy and performance attract significant interest. To manufacture these panels as integrity with high accuracy, multiple processes need to be utilised, such as machining, welding and forming. During the whole manufacturing chain, residual stresses can be generated and redistributed in the components among different processes. The residual stress would significantly affect the shapes and properties of the final products. Currently, these great effects are not well considered in the design and manufacturing processes. This paper aims to draw a general understanding of the residual stress generated in the pre-manufacturing processes and its effects on subsequent manufacturing processes. The mechanisms and distributions of residual stresses generated in typical pre-manufacturing processes of structural panels, including machining, welding and additive manufacturing (AM), are firstly summarised. The detailed effects of generated residual stresses on distortion and application properties in subsequent manufacturing processes are then concluded. In addition, current methods developed for the investigation of residual stress effect in multi-processes manufacturing are critically reviewed, including experimental, analytical, finite element (FE) and machine learning methods. Furthermore, the future development trend of methods for residual stress consideration and control in the design of manufacturing processes is summarised, providing comprehensive guidance to achieve the high accurate manufacturing of aluminium alloy structural components.     

Hail impact responses and residual tensile properties of CFRP T-joints

Hail impact is a major challenge encountered by aircraft in flight, and thus is a key concern in the design of damage-tolerant composite T-joints in aviation. The study uses the Z-pinning technique(the pre-hole insertion technology) in combination with fillets of two radiuses to manufacture four types of Carbon Fiber Reinforced Polymers(CFRP) T-joints. The T-joints are then subjected to hail impact tests at two energy levels, as well as post-impact quasi-static tensile tests.The results show tha...     

钛合金平板电子束焊接残余应力数值分析

本文建立了钛合金平板移动电子束热源的焊接温度场和应力场的数值分析模型,针对6mm厚的TC11钛合金平板试件,计算分析3种不同工艺参数的电子束焊接温度场及残余应力分布规律,结果表明对于平板电子束焊接接头,在焊缝及近缝区的很窄的区域内,存在数值接近材料屈服极限的纵向残余应力,焊接工艺不同将会影响残余应力的数值,采用正面焊透加背面修饰的焊接工艺可在一定程度上降低纵向残余应力的数值。      

金属壳体支座角焊缝应力场数值模拟

文摘针对某固体发动机金属壳体支座焊接过程及热处理过程,利用通用ANSYS有限元分析软件对不同尺寸支座角焊缝应力场进行模拟计算。结果表明:支座焊后的应力主要集中在角焊缝热影响区处,应力水平较高,且随着支座尺寸的增加,残余应力显著增加;壳体经过退火和调质热处理后,角焊缝残余应力得到重新分布,整体残余应力较小。     

工艺参数对搅拌摩擦焊7022铝合金残余应力及耐磨耐蚀性能的影响

采用不同的焊接参数对10mm厚7022铝合金进行搅拌摩擦焊研究.利用X射线应力分析仪检测焊接试样的残余应力分布;利用摩擦磨损试验机对焊缝试样进行磨损性能研究,并通过三维形貌仪观察其磨损形貌;利用pH=5的Na2SO4溶液对焊接试样进行腐蚀试验,并通过SEM观察其表面腐蚀形貌.结果表明:各参数下焊接试样的残余应力均较小,...     

2324铝合金厚板内部残余应力分布特征及其影响

 采用了新改进的宏观应力释放法测定 2 32 4铝合金厚板内部残余应力,比较了 T39和淬火状态厚板残余应力分布特点,分析其成因,探讨了 T39状态特殊残余应力分布的成因及对加工性能的影响。结果表明 :T39状态残余应力分布特点为中心受压,与淬火态相反,且应力水平比淬火态低一个数量级,这导致了切削加工中特别的变形