铝合金激光冲击表面强化试验研究

 激光冲击是一种新型的材料表面强化技术。将激光冲击技术用于铝合金的强化处理，探讨了激光冲击处理的技术关键，研究了激光冲击处理对铝合金疲劳寿命的影响。研究结果表明：在优选激光参数的条件下，激光冲击处理能显著地提高铝合金的疲劳寿命。     

激光冲击强化7075铝合金熔焊接头的疲劳性能

激光冲击强化（LSP）技术具有残余压应力场深、冷作硬化程度低和强化区域可控等优点,在焊接结构表面改性方面应用前景广阔。对2 mm厚度的7075-T6铝合金激光-电弧复合焊接接头实施了激光冲击强化处理,对比分析了强化前后接头的硬度、残余应力、疲劳寿命以及疲劳裂纹形核机制。结果表明,焊缝中心的最高硬度由强化前的152 HV提高到强化后的175 HV,有效强化层深度约为100 μm;经激光冲击强化后,焊缝区呈现残余压缩应力,最大残余压应力为-200 MPa;9组焊接接头试样的平均疲劳寿命为675 937周,约为强化前疲劳寿命（262 297周）的2.6倍;疲劳裂纹萌生位置从具有高度应力集中的表面缺陷转移至强化层以下的亚表面,进而有效地提高了疲劳裂纹的形核寿命。     

Laser Shock Peening of Aluminum Alloy 7050 for Fatigue Life Improvement

The effects of laser shock peening (LSP) on improving fatigue life of aluminum alloy 7050 are investigated.Surface hardness is increased corresponding to a high dislocation density induced by LSP.The X-ray diffraction stress measurement shows that LSP results in prominent increase of surface compressive stress,quasi-symmetrically distributed in the laser peened region.The fatigue life of the alloy 7050 in rivet fastener hole structure is notably improved owing to LSP.The sequence of LSP and fastener hole preparation also influence the fatigue cycle life of the alloy.     

激光冲击处理对铝合金疲劳扩展速率影响的研究

研究了激光冲击处理对2024-T62铝合金疲劳裂纹扩展速率的影响,并探讨了将其作为止裂工艺的可行性。疲劳裂纹扩展试验结果表明：激光冲击处理可以显着地降低疲劳裂纹扩展速率,作为止裂工艺是可行的。     

激光喷丸强化TC6钛合金的振动疲劳寿命及断口形貌分析

为了研究TC6钛合金激光喷丸强化(Laser Shocking Peening,LSP)处理后对振动疲劳寿命的影响,采用不同喷丸次数的方法对TC6钛合金进行LSP处理,采用振动疲劳测试系统对振动试样进行振动疲劳测试,用X射线衍射仪和显微硬度计测试LSP前后试样的残余应力和硬度,研究LSP对TC6钛合金振动疲劳性能的影响...     

激光冲击强化提高压气机叶片疲劳性能研究

根据1Cr11Ni2W2MoV不锈钢材料性能,确定了激光冲击强化参数;并通过标准试片疲劳试验,验证了该参数条件下激光冲击强化提高不锈钢材料振动疲劳寿命的有效性.设计了不锈钢叶片振动疲劳试验,确定了叶片冲击强化部位和方式,对强化叶片进行了型面检查、一阶弯曲振动疲劳试验和强化机理研究.结果表明:激光冲击强化后的叶片各个截面尺寸在设计范围之内,强化后叶片的应力-循环次数(S-N)曲线往上移动,提高了叶片的疲劳强度,在660MPa应力水平下,叶片的振动中值疲劳寿命提高70%;激光冲击强化引起的残余应力和表层微观组织变化是疲劳强度提高的主要原因.      

Influence of laser shock peening on surface integrity and tensile property of high strength low alloy steel

Laser Shock Peening (LSP) is a well-established surface treatment commonly used to improve mechanical properties of material's surfaces. To further understand the relationship between tensile property and fatigue life improvement of high strength low alloy steel in the LSP process, LSP treatment of 32CrNi high strength low alloy steel was carried out by YAG laser with pulse energy of 15 J, and tensile property was tested by electronic universal material testing machine. Surface morphology, residual stress and tensile fracture of the specimens before and after LSP were observed by white light interferometer (WLI), X-ray measuring apparatus and scanning electron microscope (SEM). Result shows that LSP did not change tensile strength of 32CrNi steel but cause yield characteristic transform from obvious yield point to no yield phenomenon which is the only factor benefiting fatigue life, indicating that the increment of fatigue life was probably related to the disappearance of yield phenomenon. Formation mechanisms of tensile fractures and yield phenomenon induced by LSP at room temperature were also discussed and completely revealed. Deeper compressive residual stress and flat grains contributed to the transition of yield characteristic and lower elongation rate of 32CrNi steel subjected to LSP.     

激光冲击强化铝合金小孔构件的疲劳寿命研究

研究了激光冲击强化对7050-T7451铝合金小孔件疲劳寿命和断口形貌的影响。采用ABAQUS对峰值压力2.7GPa下小孔构件孔壁与表面上的应力分布进行了研究,并基于仿真结果对试样进行激光冲击强化试验和疲劳拉伸试验。结果显示,激光双面冲击强化在板料两侧形成一定深度的残余压应力影响层,而在中心形成一定范围的残余拉应力层,这也是导致疲劳源由孔角向孔壁中心转移的主要原因;在应力水平165.8MPa、195.0MPa和275.4MPa下,试样的疲劳寿命分别平均可增大451%、216%、116%;经激光冲击强化后,试样的疲劳源位置由孔角转移至孔壁内部,且疲劳裂纹扩展区面积明显增大。研究表明,激光冲击强化能明显改善铝合金小孔构件的疲劳性能,但强化效果随外加载荷的增加逐渐减小。     

Investigation of Surface Integrity on TC17 Titanium Alloy Treated by Square-spot Laser Shock Peening

Laser shock peening(LSP) is an innovative surface treatment method,which has been shown to greatly improve the fatigue life of many metallic components.This work investigates surface integrity of TC17 titanium alloy treated by LSP with innovative square laser spot.Nd:glass laser with duration of 30 ns and spot size of 4 mm×4 mm is applied.The surface morphology and surface residual stress of the TC17 titanium alloy,treated with varying peening parameters such as laser power density and overlapping ratio,have been studied in detail.The results show that laser pulse energy greatly influences surface morphology and surface residual stress around single-spot treated areas,and compressive residual stresses are saturated as laser pulse energy is over 55 J.There are significantly different surface morphologies and residual stress distributions at the overlapped areas with different overlapping ratios.A relative smooth surface is produced with uniform compressive residual stress distribution at an overlapping ratio of 8 %.The experiment of residual stress relaxation is implemented by measuring residual stress at the center of four overlapped spots and by four point bending fatigue test at the frequency of 105 Hz.The compressive residual stresses induced by LSP are found to relax quite slowly under cyclic fatigue loading.     

激光冲击强化对加力燃烧室火焰探测器焊缝的影响

为了研究激光冲击强化(LSP)后加力燃烧室火焰探测器焊缝位置异常开裂原因,采用X射线衍射方法和金相方法对激光冲击强化效果进行分析,并利用扫描电子显微镜对断口进行了观察。在Abaqus有限元分析软件中建立了与观察到的焊缝缺陷相似的有限元模型,对焊缝缺陷的LSP处理及冲击波传播过程进行了模拟分析。试验结果表明:具有较好材料完整性的区域经LSP处理后,表面会预置较大残余压应力,同时表面金属晶粒得到细化,疲劳裂纹会在焊缝缺陷位置萌生和扩展。有限元分析结果表明:存在分层缺陷的焊缝经LSP强化后,冲击波会在分层缺陷处产生反射,造成分层位置发生开裂,形成裂纹源造成疲劳开裂。根据试验和仿真分析结果,为提升火焰探测器焊缝激光冲击抗疲劳效果,建议优化焊接工艺,提高焊接质量。     

激光冲击对TC11钛合金组织和力学性能的影响

对TC11钛合金进行激光冲击强化处理,通过透射电子显微镜观察不同参数下TC11钛合金的微观组织变化,用显微硬度计和X射线应力测试仪分别测试材料表层硬度和残余应力,并通过TC11钛合金标准疲劳试片高周振动疲劳试验验证激光冲击对其疲劳性能的影响.试验结果表明:激光冲击波作用后表面组织结构发生明显变化,当冲击次数增加,先后出现了高密度位错、位错胞和纳米级晶粒等微观组织特征.冲击10次后,表面残余应力最高达到-632.5MPa,相应的塑性变形层深度达到1500μm左右;同时表面硬度在冲击1次即可提高19%,硬度影响深度为700μm,随着次数增加而提高,但幅度不大.经3次冲击处理的TC11钛合金标准疲劳试片的疲劳极限由原始483MPa提高到593MPa.      

7050凹槽铝板激光冲击强化残余应力分布与疲劳寿命

激光冲击强化（LSP）是改善结构疲劳性能的重要手段，传统数值模拟方法很难模拟复杂结构的多点冲击强化过程。本文利用一种连续动态冲击方法对7050凹槽铝板进行激光冲击强化数值模拟，得到了冲击后稳定的残余应力场，并与试验测量的残余应力相对比，验证了该方法的精度与较高效率。运用4种基于临界平面法的应变模型，最大正应变模型、最大剪应变模型、BM模型和SWT模型分别对未强化件和强化件进行疲劳寿命预测。完成了激光冲击强化件和未强化件的疲劳试验，得到其疲劳寿命。结果表明：寿命预测值与试验结果吻合较好；对未强化件进行平均应力修正后，前3种模型误差分别为31.2%、22.6%和40.7%，而SWT模型的计算结果过于保守；对强化件进行最大正应力修正后，前3种模型误差分别为1.84%、24.0%和46.4%，而SWT模型的计算结果过于危险。     

随机载荷作用下锥形螺栓干涉配合的疲劳寿命增益

介绍了以7475 T761铝合金为基材的锥形螺栓干涉配合和普通螺栓非干涉配合连接的犬骨形试件,在随机疲劳载荷谱作用下的疲劳试验。结果表明:锥形螺栓干涉配合与普通螺栓连接比较,疲劳寿命增益明显;应力水平降低,寿命增益倍数增加。锥形螺栓干涉提高疲劳寿命的主要原因是:(1)干涉使孔附近区域形成拉伸预应力,它可以降低外加疲劳载荷引起的交变应力幅;(2)锥形螺栓干涉使螺栓与孔之间的接触更均匀、更紧密,当有载荷传递时,其分布趋于均匀;(3)锥形螺栓干涉改善了孔壁的初始疲劳质量。     

密布多孔构件的低周疲劳寿命予测和试验研究

一、多孔构件应力场有限元分析　　为了计算多孔的涡轮叶片和燃烧室等构件的应力应变 ,我们编制和开发了壳体弹塑性有限元分析程序。用退化方法从三维单元推导出的曲壳单元。这种单元直接离散连续介质力学的三维方程 ,避免了由一般壳理论带来的复杂。曲面等参元具有独立的转角自由度和平移自由度 ,三维应力应变就退化为壳体情形。本文编制的这种退化壳单元程序还可进行各向异性材料的应力应变分析[1 ] 。涡轮叶片因开有很多孔而使结构强度大大降低 ,由于孔间的相互影响 ,应力场相当复杂。我们用下列三种简化模型作计算分析。三种平板尺寸为 …     

挤压强化对LY12CZ板材疲劳裂纹起始寿命的影响

 <正> 以往研究者着重研究了挤压强化对疲劳裂纹扩展速率和总寿命的影响,而最近研究分析表明,挤压强化对改善裂纹起始寿命(N_i)也具有很大作用,但是,关于挤压强化后,疲劳裂纹起始寿命的定量表达式还未见报道。     

2524-T3铝合金铆钉填充锪窝孔疲劳特性研究

2524-T3铝合金被认为是目前综合性能最好的飞机蒙皮用铝合金,研究其在疲劳载荷状态下的力学性能对材料的安全使用具有重要的意义。通过疲劳试验研究2524-T3铝合金铆钉填充锪窝孔试样在一种典型应力比、不同载荷水平下的疲劳性能,得到铆钉填充锪窝孔试样疲劳裂纹寿命的p-S-N曲线,同时借助扫描电镜观察疲劳裂纹的萌生和扩展行为。研究结果表明：2524-T3铝合金铆钉填充锪窝孔试样具有良好的抗疲劳损伤性能;在指定疲劳寿命条件为3×106周次下,试样在室温轴向疲劳加载条件下的条件疲劳极限为108MPa;疲劳断口由疲劳源区、裂纹扩展区及瞬断区组成。     

关于铆钉对止裂孔填充作用的研究

通过试件的疲劳寿命试验与计算，研完了空止裂孔与铆钉填充止裂孔对构件裂纹的止裂作用。试件疲劳寿命试验结果表明，疲劳裂纹尖端止裂孔铆上铆钉后的试件疲劳寿命是空止裂孔试件疲劳寿命的2．9～7．8倍。同时，通过对试验和计算结果的对比分析，确定用于计算带止裂孔构件疲劳寿命的铆钉填充作用系数为0．87。     

多孔多裂纹平板的疲劳裂纹扩展试验与分析方法

飞机结构广布疲劳损伤是目前大型客机损伤容限设计与分析的难点。通过试验研究了典型多孔多裂纹2024-T3铝合金平板的裂纹扩展行为。试验结果表明：相邻孔边裂纹之间的相互干扰明显降低了共线多裂纹平板的疲劳裂纹扩展寿命。就本文研究的典型多孔板,所有孔边都出现了等长裂纹这一极端情况,其裂纹扩展寿命是单孔平板孔边裂纹扩展寿命的10%左右。本文采用Eshelby夹杂理论和权函数法给出了典型多孔多裂纹问题的应力强度因子近似解析解,并结合Paris裂纹扩展公式预测疲劳裂纹扩展寿命。与采用有限元法获得应力强度因子并预测多孔多裂纹板的疲劳裂纹扩展寿命进行对比,对比结果表明：采用解析解和有限元解获得的应力强度因子预测的疲劳裂纹扩展寿命与试验结果吻合良好;相比于有限元法,本文的应力强度因子解法简单、高效,将有助于飞机结构多位置损伤（MSD）的疲劳裂纹扩展寿命预测分析。     

一种紧固孔细节原始疲劳质量评定方法

 给出了一种由等幅载荷试验的断口金相数据反推得到的当量初始裂纹尺寸额定值（EIFSR）表征的紧固孔原始疲劳质量评定方法。并据此建立了原始疲劳质量符合性检查的EIF-SR判据和寿命判据。最后用上述判据对紧固孔细节进行了原始疲劳质量评定和符合性检查。     

孔的挤胀销棒应力压印工艺

本文主要分析孔的挤胀销棒应力压印工艺特点，挤压孔的受力机理分析，并通过疲劳试验观察不同条件下的寿命。