Inconel625合金摩擦焊接工艺研究

研究与评定了Inconel625镍基高温合金的摩擦焊接性能,在本文所优化的摩擦焊接工艺条件下,Inconel625合金均可获得焊区100%焊合、焊态组织结构良好、焊合区强度系数满足要求、焊件同轴度精度较高的摩擦焊接头。     

TC11/TC17线性摩擦焊飞边及焊缝微区特征分析

对TC11/TC17异种钛合金线性摩擦焊飞边和接头的组织进行了分析。研究结果表明,焊接飞边组织不是2种钛合金的混合组织而是由TC11钛合金、过渡区和TC17钛合金组成。而线性摩擦焊接头由TC11母材、TC11侧热力影响区、焊合区、TC17侧热力影响区、TC17母材组成,两侧热力影响区组织沿着飞边挤出方向被拉长,而两侧焊合均发生动态再结晶,并在焊合线处形成了共生晶粒。     

镍基高温合金摩擦焊接研究现状

镍基高温合金是航空发动机、燃气轮机等高温部件的重要制造材料,与之相关的摩擦焊工艺正因工程需求的增长而日渐受到重视。主要介绍了目前应用最为广泛的3种摩擦焊接方法(线性摩擦焊、惯性摩擦焊与搅拌摩擦焊)在高温合金焊接上的应用,涵盖了高温合金接头显微组织、力学性能、工艺探索、数值模拟等方面,较为全面地总结了镍基高温合金摩擦焊接的研究现状,并提出了今后在相关研究中应考虑的关键问题。     

G105钻杆摩擦焊接头的断裂韧度和组织性能

G105钻杆的工具接头和管体采用摩擦方式进行焊接,对摩擦焊接头进行了适当热处理.对钻杆工具接头、管体、焊合区三点弯曲试样的断裂韧度进行了测试,分析了弯曲试样的微观组织和断裂形貌以及接头焊合区韧性损伤的原因.     

顶锻速度Vd对摩擦焊合区金属组织的影响

从顶锻速度Vd对摩擦焊合区金属塑性成形的影响入手,系统研究了Vd与摩擦焊合区金属组织的关系。考量了LC9超硬铝摩擦焊时的顶锻速度范围,为精细结构摩擦焊成形与控制提供了实验研究基础。     

2195铝锂合金搅拌摩擦焊接头组织及性能

为了研究搅拌摩擦焊(FSW)对2195铝锂合金组织及性能的影响,对5mm薄板进行了不同工艺参数的搅拌摩擦焊接。显微组织分析及力学测试结果表明:合金经FSW后,接头组织由焊核区、热机影响区、热影响区三个明显不同的区域组成。当焊速不变,搅拌头转速ω在700~1300r/min之间变化时,接头抗拉强度随转速ω增大而降低;搅拌头转速不变,焊速υ在60~140mm.min-1之间变化时,接头抗拉强度随焊速υ增大而提高。当υ=140mm.min-1,ω=1000r/min时,焊接接头强度系数达到73%。焊后接头显微硬度发生了较大程度的软化。     

TA12改进型钛合金电子束焊接头性能分析

采用真空电子束焊对TA12合金进行了焊接,试样表面成型性良好。通过光学显微镜、拉伸和疲劳试验等方法,对获得焊接接头的组织和机械性能进行了研究。结果表明:真空电子束焊焊接TA12改进型合金,焊缝区以马氏体为主,焊接接头有很好的机械性能,达到作为焊接结构件的要求。     

先进的焊接技术─—摩擦搅动焊

摩擦搅动焊是新近发明的一种先进焊接技术,它采用非熔化固态焊接,利用局部产生的摩擦热生成连续的固相焊缝,用它可以焊接传统上认为“不能焊接”的合金和实现不同类金属的焊接。本文简要介绍摩擦搅动焊的焊接工艺、焊缝性能、设备及应用。     

先进的焊接技术——摩擦搅动焊

摩擦搅动焊是新近发明的一种先进焊接技术,它采用非熔化固态焊接,利用局部产生的摩擦热生成连续的固相焊适宜和它可以焊接传统上认为“不能焊接”的合金和实现不同类金属的焊接,本文简要介绍摩擦搅动焊的焊接工艺,焊缝性能,设备及应用。     

FGH96/GH4169高温合金惯性摩擦焊微观组织及演变过程

对FGH96/GH4169异质高温合金惯性摩擦焊接头组织形貌及演变过程进行分析,测量了焊接过程的界面温度。结果表明,惯性摩擦焊近界面处最高温度超过1100℃,达到母材强化相固溶温度区间。摩擦初期GH4169侧率先产生磨损颗粒;摩擦过渡期磨损颗粒被细化,摩擦界面形成高温粘塑性金属,在顶锻压力作用下开始形成飞边,夹杂物随之被挤出;准平衡摩擦阶段界面处高温粘塑性金属被持续挤出,飞边增大。焊后于焊接界面处形成等轴细晶区,细晶区与母材间为热力影响区,产生明显的变形,形貌为拉长晶粒。     

GH4169高温合金惯性摩擦焊接头动态再结晶过程

当温度、应变、应变速率达到一定条件时 ,GH4 16 9镍基高温合金在惯性摩擦焊接过程中易发生动态再结晶。本文研究结果表明 ,由于GH4 16 9合金惯性摩擦焊接时间很短 ,动态再结晶进行得相当充分 ,而动态回复不足 ,在动态再结晶的过程中还可以看到有些结晶过程还处于形核阶段 ,这是惯性摩擦焊接头产生细晶乃至超细晶的根本原因     

工进和顶锻速度对摩擦焊接面形变织构的影响

针对异种高强材料摩擦焊接成形与控制问题,系统研究了工进速度和顶锻速度对摩擦焊接面的作用行为,发现了摩擦焊接面形变织构的变化及其影响接头性能的规律。     

A review of friction stir joining of SiCp/Al composites

SiCp/Al composites have excellent comprehensive properties and have been widely used in aerospace, automotive industry and other fields. Due to the huge difference in performance between SiC particles and matrix alloys, traditional fusion welding methods are difficult to meet the join requirements of SiCp/Al composites. Friction stir joining (friction stir welding), as a solid phase joining process, has been proved to be a new technology with fine prospect in joining SiCp/Al composites compared with fusion welding process. Although some progress has been made in recent years, there are still full of challenges. In this paper, the research status of friction stir joining of SiCp/Al composites in recent years is expatiated, including the weldability of SiCp/Al composites, the macrostructure and the microstructure of joints, mechanical properties of joints, and tool wear and monitoring. Furthermore, the existing challenges of friction stir joining of SiCp/Al composites are summarized and the future development directions are prospected.     

航天用铝合金/ 焊丝焊接性研究

针对2A14、2219、2195、2A97、1460铝合金,通过焊接热模拟试验、焊接裂纹敏感性试验和拉伸试验,建立了材料脆性温度区间大小和焊接性的关系及焊丝主成分和焊接性的关系。结果表明,试验合金焊接性从好到差的排列顺序为2219、2A14、1460、2195、2A97。其中2A14、2219铝合金现用焊丝可以满足推进剂贮箱用铝合金焊接性要求。脆性温度区间较小时,焊接性良好,随脆性温度区间增加,焊接性变差;采用满足主成分含量之和为6%的焊丝焊接时,若抗裂性满足要求,则接头延伸率满足要求。     

粉末高温合金FGH96惯性摩擦焊接头室温CTOD测试与分析

FGH96是采用损伤容限设计思想研制的新型粉末高温合金,是满足高推比、高燃效发动机使用要求的涡轮盘、环形件和其他热端部件的理想材料。FGH96惯性摩擦焊接头的CTOD值小于母材,其断口的韧窝小于母材。母材和接头断裂路径均为穿晶断裂。     

00Ni18%马氏体时效钢的氩弧焊工艺试验研究

近期对00Ni18%高强度马氏体沉淀硬化时效钢的焊接性能进行了试验研究,探索出了适用于该钢薄壁旋压筒体自动钨极氩弧焊的焊接工艺规范,同时对比、分析了不同的热处理工艺对该钢氩弧焊接头力学性能和显微组织的影响.结果表明:在相同的焊接规范参数下,固溶+焊接+固溶+时效后焊缝及热影响区已有了一定的细晶粒,组织中含有大量的金属间化合物沉淀强化质点,焊接接头及母材都呈现出了高强度和高韧性相搭配的优异性能.     

改善铸造热强镍基合金可焊性的研究

针对铸造热强镍基合金有限可焊性的问题,介绍了俄罗斯学者经多方试验研究找出了改善其可焊性的有效途径,从而确保了它们在航空发动机零组件制造上的安全应用。     

钛铝基金属间化合物熔焊工艺性的研究进展

综述了钛铝基金属间化合物(主要是Ti3Al，TiAl)熔焊连接技术的研究现状，主要涉及电子束焊、激光焊和氩弧焊等方法，指出钛铝基金属间化合物的焊接性不存在本质上不可焊的问题。无论采用何种熔焊方法连接此类合金，焊态下焊接接头的组织和性能一般不理想，焊缝和热影响区很容易脆化。控制冷速是成功连接此类材料的关键，同时受该类材料的物理冶金学特点限制，其组织转变动力机制、氢脆、间隙元素的引入对其焊接性的影响尚未引起注意。