应变对PH13-8Mo 钢在1 050 ~1 150时变形组织的影响

采用Gleeble热模拟试验机,对PH13-8Mo钢进行热变形模拟实验,研究了应变对PH13-8Mo钢在应变速率为10/s,变形温度为1050 ～1150℃时变形组织的影响.结果表明,PH13-8Mo钢在1 050℃、应变达到0.69时仍未发生完全再结晶,但在1100和1150℃、应变分别达到0.29和0.24后,发生了明显的完全再结晶.再结晶体积分数随应变增加和变形温度升高而逐渐增大,直至发生完全再结晶.当应变＜0.29时,再结晶晶粒尺寸和试样的平均晶粒尺寸随应变增加较快地减小；当应变＞0.29后,再结晶晶粒尺寸和试样的平均晶粒尺寸随应变增加缓慢地减小.再结晶晶粒尺寸和试样的平均晶粒尺寸均随变形温度的升高而增大.     

等径角挤扭变形过程中纯铝粉末材料的显微组织与力学性能

采用EBSD和TEM研究了200℃下,纯铝粉末材料经不同道次ECAPT变形后的微观组织,并进行了显微硬度和相对密度测试。结果表明,1道次ECAPT变形后,材料显著细化但变形不均匀,晶粒基本沿剪切方向呈条带状分布,平均晶粒尺寸约为5.20μm,但多为小角度晶界结构。随着变形道次的增加,亚晶在不断被细化的同时晶粒间的取向差不断增大,形状更加趋于等轴,该过程可认为发生了连续动态再结晶。4道次变形后,材料内部形成了均匀、细小且呈大角度晶界分布的等轴再结晶组织,最小晶粒尺寸可达0.5μm。ECAPT变形过程中,晶粒细化机制为机械剪切、应变累积和动态再结晶三者的综合作用,粉末材料力学性能的提高与组织致密、细晶强化和位错强化等因素有关。     

热变形工艺对FGH96高温合金PPB析出相及组织的影响

以AA粉制备的HIP态FGH96高温合金为研究对象,研究不同热变形工艺前后FGH96高温合金PPB析出物及组织状态的变化。结果表明:HIP态FGH96高温合金可见呈圆形分布的PPB析出物,粗大的长条状γ′相呈圆形链状分布是PPB的主要特征之一;经热变形后,FGH96高温合金PPB变形、破碎,再结晶晶粒细化、扭转,晶粒取向差变小;随着热变形温度升高、变形量增大、变形速率减小,PPB析出物变形和破碎程度越显著,粗大的初生γ′相和二次γ′相残留越少、尺寸越小;热变形温度升高、变形量增大以及变形速率减小有利于PPB的减轻甚至消除。     

高温变形参数对TC6钛合金微观组织的影响研究

在热模拟实验和金相实验的基础上,研究了变形参数(变形温度、应变速率、变形程度)对TC6钛合金微观组织的影响。研究结果表明:变形温度对TC6钛合金的变形组织有着显著影响。在两相区,随着变形温度的升高,组织中初生相的含量在减少,而相晶粒的尺寸有先增大后减小的趋势。应变速率对TC6钛合金变形组织中初生相的形态和尺寸有较大影响。较大的应变速率能促进变形时的动态再结晶,有利于晶粒的细化。变形程度存在着一临界值,当超过这一临界值后,变形程度的增加有利于晶粒的细化。     

退火处理对Ti-55531 钛合金组织与性能的影响

对退火处理后的Ti-55531钛合金α片层宽度、β晶粒尺寸、晶界仅相不连续度和针状α相比例等特征进行了定量表征和统计分析,探讨了随着退火温度的升高,Ti-55531钛合金显微组织及其力学性能的相关性。结果表明,在β相区退火处理,退火温度的升高将引起晶内α片粗化长大,平均β晶粒尺寸从86μm增大到210μm,晶界不连续度降低,针状仪相的相比例先降低后升高。β晶粒尺寸与延伸率、静韧度、裂纹形成功负相关,与裂纹扩展功正相关;晶界不连续度与静韧度正相关;针状α相比例与屈服强度正相关。     

挤压态喷射成形GH738合金热变形行为及组织研究

在温度950~1150℃、应变速率0.001~1 s–1及工程应变50%条件下,利用Gleeble-3500TM热模拟试验机对挤压态喷射成形GH738合金进行热压缩实验,研究合金的流变应力,建立合金热变形本构关系,利用EBSD分析合金组织演变。结果表明:合金流变应力随温度的升高和应变速率的减小而降低,在相同变形条件下,具有细晶组织特征的挤压态喷射成形GH738合金峰值流变应力低于粗晶组织的铸锻GH738合金;挤压态喷射成形GH738合金热变形激活能为651.08 kJ·mol–1,GH738合金的热变形激活能随着初始平均晶粒尺寸的减小而升高;形变温度的升高使挤压态喷射成形GH738合金初始被拉长的晶粒逐渐演变为等轴再结晶晶粒,在1000℃以上获得完全动态再结晶组织,再结晶组织随形变温度的进一步升高发生长大。     

7050-T7651铝合金厚板显微组织及力学性能不均匀性

采用金相显微镜、扫描电镜、透射电镜和力学拉伸试验机，研究160 mm 7050-T7651铝合金特厚板不同厚度位置的金相组织、晶粒取向、织构类型、时效纳米析出相分布以及力学性能的差异。结果表明：从板材表层到心部，组织中的第二相粒子含量降低，但尺寸增加；板材表层以小角度晶界亚结构组织为主，小角度晶界比例在79%～85%之间，而板材心部小角度晶界的比例为58%左右，相比于板材表层小角度晶界比例降低了26.6%～31.8%；板材表层以{001}<110>剪切织构为主，占比为3.64%，并随厚度增加，变形织构组分含量逐渐增多；板材厚度方向力学性能呈现出沿厚度表层-心部-表层方向先降低后升高的趋势，且力学性能最优位置均为板材表层位置。     

变形参数对挤压成型镍基粉末高温合金 固溶热处理晶粒组织的影响

进行双锥体试样热模拟压缩实验,研究变形温度、应变速率及应变状态对一种挤压成型镍基粉末高温合金固溶热处理晶粒组织的影响,获得在变形温度1060～1120℃,应变速率0.003～0.3 s–1范围内,变形温度、应变速率与热处理晶粒组织的对应关系。结果表明:在相同应变量下,温度一定,应变速率越大,流变应力越大;应变速率一定,温度越高,流变应力越小;在相同应变速率下,较低变形温度的试样晶粒组织出现不均匀的现象;在相同的变形温度下,三种应变速率下的试样平均晶粒尺寸为18～20μm,但较大应变速率的试样明显出现不均匀晶粒组织。为获得均匀的晶粒组织,更适合的热变形参数为:变形温度1120℃,应变速率0.003 s–1。在相同的变形温度和应变速率下,随局部应变的减小,平均晶粒尺寸呈逐渐增大的趋势。     

轧制变形对TiNiFe形状记忆合金组织结构及力学性能的影响

对不同变形量轧制和不同温度热处理的Ti₅₀Ni₄₇Fe₃合金的组织结构、力学性能进行了研究。X射线衍射结果表明,随着轧制变形量的增加,Ti₅₀Ni₄₇Fe₃合金在轧制方向上出现了择优取向;Ti₅₀Ni₄₇Fe₃合金的晶粒尺寸随着轧制变形量的增加而减小,随着热处理温度的升高而增大;Ti₅₀Ni₄₇Fe₃合金的抗拉强度和屈服强度随着轧制变形量的增加而增大,随热处理温度的升高而降低。     

TB-13钛合金动态再结晶行为研究

研究TB-13钛合金在β单相区热轧变形过程中不同变形量对组织演变规律的影响.进行了32％,50％,59％和75％变形量的热轧后,利用光学显微镜和透射电子显微镜观察了该合金热轧变形后的组织变化.结果表 明,TB-13钛合金在热轧变形过程中的动态再结晶发生机制是连续动态再结晶.当变形量为32％时,沿着轧制方向存在拉长的扁平状原始β晶粒,晶界平直,晶粒内部存在大量无规则位错和胞状结构位错.随着变形量的增加,晶界处形成亚晶,大量位错在亚晶界处聚集,使亚晶界角度不断增大,最终由小角度晶界转为大角度晶界,从而形成细小的动态再结晶晶粒.     

Role of the inter-pass cooling rate in recrystallization behaviors of Ni-based superalloy during interrupted hot compression

The microstructural evolution of a Ni-based superalloy under interrupted hot compressive deformation with different cooling rates in the inter-pass stage is investigated. It is found that metadynamic recrystallization(MDRX) in the inter-pass stage is more sensitive to the accumulated strain than the deformation temperature which is above the recrystallization temperature. The variations of both the grain distribution and the texture intensity caused by MDRX during the interpass stage result in variations of the yield stress(YS) and the work hardening(WH) rate in each stage. Results also show that the MDRX process in the inter-pass stage has a considerable influence on the final microstructure of three-pass compression. The final grain distribution is more uniform,and the compression texture gradually transforms into recrystallization texture with an increasing degree of MDRX. In order to predict the MDRX fraction in the inter-pass cooling stage, a modified kinetic equation is established, which can reasonably predict the MDRX behavior under multi-pass compression with different conditions in the inter-pass stage. Meanwhile, the influence of the interpass cooling stage on the mechanism of dynamic recrystallization(DRX) is studied. It is universally acknowledged that the discontinuous dynamic recrystallization(DDRX) process is the major deformation mechanism for the Ni-based superalloy. However, the continuous dynamic recrystallization(CDRX) process is promoted in the compression stage with a decrease of the cooling rate in each inter-pass stage.     

细晶AZ31镁合金高温压缩变形行为研究

通过Gleeble-1500试验机对坯料预先经过晶粒细化处理的AZ31镁合金圆柱体试样进行单向热压缩试验,压缩温度为300～450℃,应变速率.ε为0.01s-1,0.1s-1,1.0s-1,根据试样结果分析计算了本构方程中的各参数,获得了完整的镁合金高温本构方程,进一步分析了压缩试样的显微组织。结果表明:在本试验条件下,AZ31镁合金的热变形应力指数n为6.24,热变形激活能为177.2kJ/mol。压缩试样心部组织变形程度明显高于边缘;随着温度的升高,心部压缩组织发生明显的再结晶,新晶粒在晶界处形核并长大。     

细晶态FGH96热成型时的流动行为研究

 通过热模拟试验,对细晶态FGH96 合金的高温流动特性进行了研究,分别从宏观和微观上对影响FGH96 流动特性的因素(变形温度、变形速率和变形程度以及Z 因子和动态再结晶晶粒尺寸等) 作了系统分析。结果表明:变形温度、变形速率和变形程度对流动应力和再结晶晶粒尺寸均有不同程度的影响。在此基础上,建立了细晶态FGH96 合金热成型时的本构模型,该模型充分考虑了变形温度、变形速率和变形程度对流动应力的影响,这对FGH96 合金热成型过程的数值模拟和热力参数的合理制订具有重要意义。     

Al-Li-Cu-Mg-Zr合金的超塑性研究

Al-1.91Li-1.25Cu-0.46Mg-0.21Zr合金超塑性变形结果表明,最佳的时效工艺是400℃8h;冷轧工艺得到了比温轧(550％)更高的超塑性延伸率(630％);最佳超塑性变形工艺是T=500℃,(?)_i=3.33×10~(-3)s~(-1)(起始拉伸速度)。研究指出,Al-1.91Li-1.25Cu-0.46Mg-0.21Zr合金的超塑性预处理的时效工艺和轧制工艺影响了合金超塑变形初期的应变诱发再结晶,从而影响超塑性性能。超塑变形中的动态回变和动态再结晶是晶界滑动的重要协调机制之一。     

Formability enhancement in hot spinning of titanium alloy thin-walled tube via prediction and control of ductile fracture

The damage and fracture in hot spinning of titanium alloy is a very complex process under the combined effects of microstructure evolution and stress state. In this study, their dependences on processing parameters were investigated by an integrated FE model considering microstructure and damage evolution, and revealing the effects of microstructure and stress states on damage evolution. The results show that the inner surface of workpiece with the largest voids volume fraction is the place with...     

AZ31B镁合金双道次热变形过程流变应力特征模拟研究

建立了一类镁合金双道次热变形过程的二维元胞自动机模型。考虑到镁合金具有六重对称的密排六方晶体结构,模型采用了六边形元胞网格。另外,通过计算位错密度演变和设定晶粒形核长大规则,模型将热变形过程中动态再结晶、静态回复、静态再结晶、亚动态再结晶和晶粒长大等单个物理过程耦合到一起。为了验证模型,将其应用到AZ31B镁合金单道次和双道次热压缩过程。探讨了不同变形温度、应变速率、道次间隔和预应变对应力-应变曲线的影响。将计算结果和实验结果进行了对比,吻合较好。     

7075-T6铝合金厚板FSW焊缝沿厚度方向上的显微组织演变规律

采用金相显微镜（OM）、扫描电镜（SEM）和背散射电子衍射（EBSD）技术表征7075铝合金厚板搅拌摩擦焊（FSW）焊核中心区的微观结构，研究沿焊缝厚度方向上的显微组织演变规律。结果表明，焊核中心区发生了明显的动态再结晶，由原始粗大的板条状组织转变成了细小的等轴晶；随着距焊缝上表面距离的增加，中心区等轴晶晶粒尺寸呈现逐渐增大的趋势。其中，中心区上部4 mm处的晶粒尺寸最小，仅为7.8 μm；底部19 mm处的晶粒尺寸最大，达18.6 μm。中心区动态再结晶分数随距离的增大而逐渐减小，从中心区顶部1 mm处最大值90.4%减小至底部19 mm处最小值57.5%。受动态再结晶影响，焊核中心区主要以大角度晶界（HAGB）分布为主，且中心区大角度晶界随距离的增加呈逐渐降低的趋势；但每一个典型位置处的大角度晶界分布呈现先增大后减小的趋势，且在45°左右时达到最大值；此外，中心区并没有强取向组织产生。同时，焊核中心区主要以细小、弥散的二次析出强化相η相为主，且二次析出强化相颗粒尺寸随距离的增加而呈逐渐增大的趋势，但二次析出强化相颗粒总体数量却呈相反的趋势变化。     

GH4169合金晶粒尺寸与持久性能的关联性

以GH4169合金大规格棒材为研究对象,结合棒材的加工过程,利用OM、FE-SEM、EBSD和TEM等手段分析了该合金不同晶粒尺寸试样的持久性能。结果表明:在长时高温应力作用下,不同晶粒尺寸试样呈现不同的持久性能和不同的晶粒取向演变规律。发生变形至断裂的位置,晶粒尺寸较小时,部分〈101〉取向明显转向〈001〉或〈111〉取向,加上宏观变形协调性较好,促使应力集中得到有效释放,表现出较好的塑性;但细晶试样中更多晶界带来的扩散蠕变对高温强度不利,裂纹也容易在与〈111〉硬取向晶粒接邻的晶界处形核并扩展,降低持久寿命;此外,细晶试样的变形程度较大,应变主要集中于晶界处,且大角度取向差的含量较多,这些位置容易萌生裂纹而使寿命降低。