喷丸处理对铝锂合金激光焊接结构性能的影响

为解决铝锂合金焊后性能弱化问题,推进双激光束双侧同步焊接工艺在国产民用飞机壁板制造中的应用,研究了焊后喷丸、固溶时效热处理+喷丸处理两种共3组焊后强化工艺,通过静力拉伸、疲劳及表面应力状态测试分析,评估强化效果,探讨强化机制。结果显示:纯喷丸强化可显著提高疲劳性能,其中0.20mmN喷丸后细节额定疲劳强度截止值DFR_(cutoff)较焊态提高27.8%,但静力拉伸性能与焊态相差不大; 0.36mmN喷丸后DFR_(cutoff)提高了118.5%,但抗拉性能明显下降;热处理+喷丸的组合强化工艺对静力拉伸及疲劳性能均有明显提升,抗拉强度较焊态提高32%,DFR_(cutoff)较焊态提高21.9%,综合性能较好。     

喷丸强化对TC17钛合金表面残余应力的影响

利用ANSYS Work Bench动态分析模块模拟喷丸强化过程,建立简化喷丸强化数值模型,通过模拟喷丸工艺参数改变对强化效果的影响,考察喷丸在不同表面形态时对表面残余应力的影响,便于进一步估测这一典型表面加工工艺对疲劳性能的影响。     

消除应力打击片的原理及在航空领域的应用

飞机经过长时间的飞行和使用后,机上很多部件会存在耐疲劳强度降低和应力腐蚀。对于应力的消除和增强金属部件的表面强度,波音在标准工艺规范SOPM20-10-03和BAC5730里面专门详细介绍了一种常见的标准工艺规范——喷丸工艺。喷丸工艺是一种能够提高金属部件表面强度和去除残余应力的工艺。它是通过在被喷丸部件的表面施加挤压应力来提高金属部件的疲劳强度和抵抗应力腐蚀裂纹的能力。目前,在飞机维护中,为采用喷丸工艺完成消除应力,需要对飞机部件进行拆卸及重新组装,所耗时间与人力成本较大。3M推出了一种新型应力消除工艺,即采用3M TM…     

喷丸对TC9钛合金表面层质量的影响

喷丸强化工艺是保证钛合金零件获得良好表面层质量的一种重要手段。由于这种工艺的适应性强、使用方便、方法可靠、强化效果佳,并且成本低廉,所以,目前在工业生产中得到了越来越多的应用。 试验是在TC9钛合金的拉削表面上进行喷丸。采用液压湿喷,弹丸为直径d=0.5～0.8mm的生铁丸,然后对喷丸及未喷丸的试件做冷作硬化、残余应力及疲劳强度的对比性试验,最终评价喷丸对钛合金表面层质量的影响。     

采用喷丸硬化和强力刷光的表面复合处理

经喷丸硬化和强力刷光复合处理后,机械零件的疲劳强度与单项处理时相比有更大的提高。在改善疲劳强度方面,强力刷光的作用与喷丸硬化的作用相似。作者们采用 Schenck 型试样进行了平面弯曲疲劳试验,澄清了复合处理的作用。复合处理后,疲劳强度最大提高了79%。同时,也检查了沿深度方向的残余应力分布,另一方面,如果用化学方法去除喷丸硬化表层,去除的深度达应力峰值存在的部位,则疲劳强度进一步提高达98.3%,但是在单独强力刷光时没有明显的提高。     

喷丸强化对TC17钛合金表面完整性及疲劳寿命的影响

研究了喷丸强化对TC17钛合金表面完整性及疲劳寿命的影响。采用表面粗糙度仪、扫描电子显微镜、X射线残余应力测试仪、显微硬度计等分析了弹丸种类和喷丸强度对表面粗糙度、残余应力场、显微硬度场和微观组织的影响;在旋转弯曲疲劳试验机上测试了喷丸强化后的疲劳寿命,探讨了表面完整性与疲劳寿命的内在联系及作用机制。结果表明:喷丸强化后TC17钛合金表面粗糙度为0.5~1.0μm,残余压应力层为100μm左右,最大残余压应力位于表面下30μm处,表面出现加工硬化,晶粒发生了压缩变形;与未喷丸试样相比,玻璃丸对疲劳寿命的提升幅度最大,陶瓷丸次之,铸钢丸最小。喷丸强化提高疲劳寿命的机制归结于引入较深的残余应力层、较高的表面硬化程度和表层晶粒的细化。     

飞机机加框激光喷丸轨迹生成及数值分析

在飞机服役过程中,部分金属零件因承载应力及环境因素,疲劳及腐蚀问题突出,常用表面强化在零件表层引入残余压应力进行改善。激光喷丸强化利用短脉冲激光束作为介质对材料表面改性达到强化效果,文中利用基于CATIA软件开发的激光喷丸强化工艺轨迹规划平台,实现喷丸区域CAD几何特征提取与喷丸轨迹的规划、生成、可视化及输出功能的一体化,对某机型货舱门框的机加框零件进行激光喷丸强化轨迹路径的规划和输出。利用ABAQUS软件子程序分析机加框激光喷丸强化后的变形行为,包括喷丸区应力、应变及变形位移量分布特点。结果表明:在给定工艺参数情况下,机加框喷丸区最大压应力位于表面1.0 mm左右,最大等效应变0.03～0.04,喷丸区域表面平均变形位移50μm,数值模拟验证了轨迹平台用于规划生成轨迹的适用性。     

LY12CZ铝合金微动损伤及防护技术

分析了LY12CZ铝合金及其铆接／螺接件微动损伤的微观特征以及4种工艺措施对疲劳强度的影响。试验结果表明：LY12CZ铝合金对微动作用十分敏感,容易引起严重的表面损伤。微动作用使铝合金的疲劳强度急剧下降。铝合金经喷丸强化处理后。可将常规疲劳强度提高。并使材料的疲劳性能不受微动作用的影响。涂层—胶粘—干涉组合是防止铆接件产生微动损伤的有效措施;喷丸—涂层—胶粘—干涉组合是防止螺接件产生微动损伤的有效措施。     

喷丸强化7475-T7351铝合金的小裂纹行为和寿命预测

对7475-T7351铝合金进行了喷丸强化和未喷丸(机械加工后抛光)单边缺口拉伸(SENT)试样的小裂纹扩展行为试验研究,利用权函数法(WFM)和叠加原理分析计算了三维表面小裂纹在外加载荷和残余应力场联合作用下的应力强度因子(SIF),并将其加入到基于裂纹闭合的小裂纹扩展分析程序FASTRAN3.9中,采用该程序预测了均布外载荷σmax=160MPa、R=0.06下,喷丸强化和未喷丸SENT试样自然萌生裂纹扩展的a-N曲线。研究发现喷丸强化残余压应力对疲劳小裂纹扩展速率的降低是疲劳寿命延长最主要的原因,采用基于裂纹闭合的小裂纹扩展分析方法能够较好地定量描述喷丸强化的疲劳延寿作用。     

40CrNi2Si2MoVA钢机械加工与喷丸试样旋转弯曲疲劳寿命的预测方法

为了预测机械加工及喷丸强化后40CrNi2Si2MoVA钢试样在室温下的旋转弯曲疲劳寿命,结合商用有限元软件ABAQUS和疲劳寿命分析软件FE-SAFE对不同数值计算方法的适用性及准确性进行比较,提出了喷丸强化40CrNi2Si2MoVA钢的寿命预测经验公式。结果表明:对于机械加工试样,选择"Brown-Miller"算法和表面残余应力用于计算可获得比较准确的预测结果;对于喷丸强化试样,高应力水平下也可选用"Brown-Miller"算法及表面残余应力,而低应力水平下则应改用"Stress-based Brown Miller"算法及最大残余应力。基于上述两种方法提出的经验公式:σmax=–64.378·lgN+1449.268,可改善40CrNi2Si2MoVA钢喷丸强化试样疲劳寿命预测的准确性。     

激光冲击强化提高外物打伤钛合金模拟叶片高周疲劳性能

为指导钛合金叶片抗外物打伤激光冲击强化工艺设计,根据真实叶片叶型特征设计了刃口型模拟叶片,采用两种激光冲击强化工艺对模拟叶片进行预处理,并采用空气炮系统进行外物打伤模拟试验,最后通过疲劳试验和应力场预测进行疲劳性能影响规律及机理分析。试验结果表明:模拟叶片外物打伤后疲劳强度由51845 MPa降为29072 MPa,而激光能量为5 J和7 J强化工艺下疲劳强度分别提升至34449、37493 MPa。激光冲击引入高数值残余压应力场,大大改善了外物打伤区域的局部应力场分布,在显著提高外物打伤模拟叶片疲劳强度的同时,可承受更大的应力集中,也增大了疲劳缺口系数偏差。两种强化工艺中激光能量越大,产生的残余压应力场数值和深度越大,更加有效地降低裂纹扩展过程中的等效应力强度因子幅值,外物打伤模拟叶片疲劳强度和疲劳缺口系数偏差提高程度越大。      

某些因素对30CrMnSiNi2A钢门槛值影响的研究

 本文研究了30CrMnSiNi2A超高强钢的降载方式,应力比、试样厚度及裂纹长度对门槛值及低速疲劳裂纹扩展行为的影响。氧化物诱发的闭合效应与氢脆机制的相互作用导致了高强钢的门槛值与应力比的弱相关性。证实了试样厚度及裂纹长度在所观察的范围内对门槛值及低速扩展无明显的影响。     

Investigation on surface roughness,residual stress and fatigue property of milling in-situ TiB2/7050Al metal matrix composites

For higher efficiency and precision manufacturing, more and more attentions are focused on the surface roughness and residual stress of machined parts to obtain a good fatigue life. At present, the in-situ TiB₂/7050Al metal matrix composites are widely researched due to its attractive properties such as low density, good wear resistance and improved strength. It is of great significance to investigate the machined surface roughness, residual stress and fatigue life for higher efficiency and precision manufacturing of this new kind material. In this study, the surface roughness including two-dimensional and three-dimensional roughness, residual stress and fatigue life of milling in-situ TiB₂/7050Al metal matrix composites were analyzed. It was found from comparative investigation that the three-dimensional surface roughness would be more appropriate to represent the machined surface profile of milling particle reinforced metal matrix composites. The cutting temperature played a great role on the residual stress. However, the effect of increasing cutting force could slow down the transformation from compressive stress to tensile stress under 270 °C. An exponential relationship between three-dimensional roughness and fatigue life was established and the main fracture mechanism was brittle fracture with observation of obvious shellfish veins, river pattern veins and wave shaped veins in fracture surface.     

ARALL层压板结构疲劳性能分析

目前在航空领域发展非常迅速的ARALL层压板结构和芳纶预浸料的制造工艺,预浸料在具有高的抗疲劳特性和拉伸特性的ARALL层压板结构中起到非常重要的承力和抗疲劳作用。本结构所采用的制造方法是纤维拉伸法,是一种能使ARALL结构的铝板层具有残余压应力,使纤维层具有残余拉应力的方法,从而改善了材料本体的抗疲劳性能。     

Surface integrity and fatigue behavior when turning γ-TiAl alloy with optimized PVD-coated carbide inserts

This paper presents a comprehensive investigation on the effects of tool and turning parameters on surface integrity and fatigue behavior in turning c-Ti Al alloy. The wear of inserts surface, cutting forces, and surface roughness were studied to optimize PVD-coated carbide inserts.Surface topography, residual stresses, microhardness, and microstructure were analyzed to characterize the surfaces layer under different turning parameters. Surface integrity and fatigue life tests of c-Ti Al alloy were conducted under turning and turning-polishing processes. The results show that compared to CNMG120412-MF4, CNMG120408-SM is more suitable because it obtained low cutting force, surface roughness, and tool wear. With increasing the cutting speed and depth, the depths of the compressive residual stress layer, hardening layer, and plastic deformation layer increased. For turning and turning-polishing specimens, the compressive residual stress was relaxed by less than 20%–30% after 10~7 cycles. The fatigue life of a turning-polishing specimen with R_a= 0.15 mm has increased 3 times from that of a turning specimen with R_a= 0.43 mm.     

激光冲击强化对钛合金高温微动疲劳寿命的影响

为了解高温工作环境下激光冲击强化工艺(LSP)对钛合金材料微动疲劳寿命的影响,开展了强化前后TC11钛合金在室温、300°C和500°C下的微动疲劳试验并测试了试验件表层的残余应力及硬度。结果表明:随着温度的升高,激光冲击强化对TC11钛合金微动疲劳寿命的提高倍数逐渐减小。在轴向载荷为400MPa,法向载荷为65.5MPa时,经激光冲击强化后TC11钛合金试验件在室温、300°C和500°C下的微动疲劳寿命分别为强化前的5.5倍、3.5倍和1.7倍;强化后试验件表层的残余应力会在高温下发生松弛,且松弛程度会随温度的升高而增大,这是激光冲击强化效果随温度升高而逐渐弱化的主要原因。     

滚压强化表面状态特征的疲劳演化及抗疲劳机制研究进展

作为机械表面强化技术之一,滚压强化工艺能够有效提高材料的疲劳性能、耐磨损性能、耐腐蚀性能以及损伤容限性能,现已被应用于航空发动机叶片等的表面改性处理。首先,对滚压强化的基本原理及优点进行了介绍。其次,鉴于表面状态特征演化对疲劳性能的重要影响及越来越多的学者对此问题的重视与研究,分别综述了滚压强化工艺的表面状态特征（残余应力、显微硬度和微观组织）的疲劳演化、抗疲劳机制以及疲劳寿命预测方面的研究进展。然后,并与其他工艺的研究进展进行横向对比分析,总结了滚压强化工艺当前研究存在的不足。最后,对滚压强化工艺今后的研究内容与发展方向进行了展望。     

喷丸强化的综合效应理论

 对几种钢材进行了喷丸强化,疲劳试验,测定了残余应力场和表面粗糙度。提出了表面粗糙度应力集中系数的计算模型和公式,以及疲劳源萌生于表面时表达疲劳极限规律的修正Goodman方程。根据断口分析和应力计算,提出了材料的内部疲劳极限概念及相应的强化机制。在上述研究基础上,建立了喷丸强化的综合效应理论。     

激光冲击强化7075铝合金熔焊接头的疲劳性能

激光冲击强化（LSP）技术具有残余压应力场深、冷作硬化程度低和强化区域可控等优点,在焊接结构表面改性方面应用前景广阔。对2 mm厚度的7075-T6铝合金激光-电弧复合焊接接头实施了激光冲击强化处理,对比分析了强化前后接头的硬度、残余应力、疲劳寿命以及疲劳裂纹形核机制。结果表明,焊缝中心的最高硬度由强化前的152 HV提高到强化后的175 HV,有效强化层深度约为100 μm;经激光冲击强化后,焊缝区呈现残余压缩应力,最大残余压应力为-200 MPa;9组焊接接头试样的平均疲劳寿命为675 937周,约为强化前疲劳寿命（262 297周）的2.6倍;疲劳裂纹萌生位置从具有高度应力集中的表面缺陷转移至强化层以下的亚表面,进而有效地提高了疲劳裂纹的形核寿命。