微波烧结制备MoSi2 及SiC/ MoSi2 纳米复合陶瓷

采用微波烧结法制备了MoSi2和10vol%SiC/MoSi2纳米复合陶瓷。通过SiC预加热体的混合式加热法和合理的保温结构设计,实现了MoSi2低温阶段的快速升温,提高了温度均匀性。密度和力学性能测试结果表明,1 450℃保温60 min烧结工艺下,MoSi2试样的相对密度达到93.4%,断裂韧度4.5 MPa.m1/2,维氏硬度为10.53 GPa,弯曲强度为186 MPa。10vol%SiC/MoSi2试样尽管相对密度下降为90.3%,但各项力学性能均优于MoSi2试样。相比1 650℃热压烧结,微波烧结温度降低了200℃,MoSi2和SiC/MoSi2试样致密性有所下降,但力学性能有较大提高,尤其是MoSi2试样。断口扫描分析表明,微波烧结试样相对热压烧结试样基体晶粒更细,孔隙细小且分布均匀;SiC/MoSi2试样微波烧结的晶粒细化效果不如MoSi2明显。     

防止 C/C 复合材料氧化的 MoSi2/SiC 双相涂层系统的研究

 由固相扩散-浸渗处理制备了防止碳/碳复合材料氧化的MoSi2/SiC双相涂层。通过对涂层的结构、成份以及氧化机理的研究表明，MoSi2/SiC双相涂层由内层为β-SiC和外层为MoSi2/SiC双相层构成，具有优异的高温抗氧化性能。     

MoSi2基高温结构材料的研究进展

从合金化和复合化两个方面综述了MoSi2基高温结构材料的研究进展。通过合金化可改善MoSi2室温韧性和消除PEST现象，通过加入陶瓷第二相复合化可提高高温强度和室温韧性，并提出了合金化加纳米复合化的进一步研究方向。     

不同制备工艺对MoSi2涂层抗氧化性能的影响

为解决MoSi2和SiC线膨胀系数差异,在带有SiC外涂层的C/C复合材料表面采用等离子喷涂、电弧沉积和固渗等工艺制备MoSi2涂层。涂层表面形貌分析发现,等离子喷涂MoSi2涂层多孔不致密,电弧沉积MoSi2涂层易开裂剥落;而固渗MoSi2涂层致密均匀,且界面结合力好。氧化试验也表明,固渗MoSi2涂层性能较好。     

MoSi2 涂层高温抗氧化性能和微观组织

采用真空阴极电弧沉积工艺在铌钨合金喷管内、外表面和铌钨合金试样表面沉积了Mo层,采用真空包渗工艺使Mo层硅化生成MoSi2涂层。利用扫描电子显微镜、能谱、XRD、金相显微镜对Mo层和MoSi2涂层表面和断面微观形貌、结构进行了分析。分析表明:MoSi2涂层的相结构由外向内大致可分为外层(MoSi2)、中间层(NbSi2)和过渡层(Nb5Si3)。高温抗氧化试验结果表明:MoSi2涂层在大气环境下1 800℃的静态抗氧化性能达到了30 h,室温至1 700℃循环热震1 376次。考核热试车情况:发动机在温度1 450℃累计工作了415s,在1 610℃工作了100 s,涂层状况完好。     

Mo-Si材料相组成与热膨胀性能的研究

利用液相反应烧结制备不同配比的Mo-Si复合材料,用X射线分析相组成,扫描电镜观察微观组织形貌,热膨胀仪测不同块体材料的热膨胀系数(CTE).研究结果表明,不同配比烧结体相组成以MoSi2为主,当Si/Mo为2.2:1(at%)时MoSi2基体中仍含有极少量的Mo5Si3相,而Si/Mo为2.3:1时生成纯MoSi2.复合材料的CTE随Mo5Si3相含量的减少而增加,当Si/Mo达到2.3:1时,CTE为最大值(8.16×10-6K-1).     

铌合金MoSi2抗氧化涂层制备及组织性能分析

在铌合金棒试样上喷涂Mo粉高温烧结制得Mo层，然后在添加活化剂的Si粉中扩散渗制得Mo-Si2涂层。微观形貌分析表明涂层均匀致密，通过扩散与基材形成过渡层，结合力较好。抗氧化及抗热震试验验证了MoSi2涂层具有良好的综合性能。长时间氧化试验后涂层表面生成比较纯的玻璃质SiO2层，不仅隔绝氧气，也能填补涂层表面空隙。     

添加剂含量对二硅化钼发热体抗氧化性能的影响研究

研究了添加剂含量对MoSi2发热体性能的影响,使用SEM观察各种添加剂含量试样的微观组织,测定各种添加剂含量试样的氧化动力学曲线、致密度、烧损温度。     

激光合成金属间化合物基复合材料研究进展

对激光合成颗粒增强金属间化合物基复合材料进行了研究,包括Ni3Al/WC、NiAl/TiC、Ti3Al/TiC和MoSi2/SiC,用扫描电镜、能谱仪和X射线衍射仪对材料成分和组织特征进行了分析,提出并讨论了影响激光合成金属间化合物基复合材料的关键问题.激光合成具有多种强韧化方法协同、提高金属间化合物强度和塑性的特点,有利于金属间化合物性能的综合改善.     

包渗法制备Cf/SiC陶瓷基复合材料MoSi2-SiC-Si防氧化涂层

采用包渗法制备了Cf/SiC陶瓷基复合材料MoSi2-SiC-Si防氧化涂层,研究了渗层同埋粉关系,包渗时间对包渗结果的影响,并对涂层防氧化性能进行了分析,结果表明：包渗法制得的涂层致密,无裂纹,涂层起到了良好的防氧化作用,1400度在空气中氧化1h后试样的质量保留率为94．1％,保留强度为294．0MPa。     

焊缝及焊接材料中钼元素可见光谱快速分析方法

使用数字化技术对部分常用合金钢焊材和焊缝中钼(Mo)元素可见光谱进行了分析测定.研究了Mo438.16nm和Mo481.93nm分析谱线组的数字化处理和分析技术.探索了利用Mo元素可见光谱分析技术进行焊材和焊缝Mo元素含量分析及牌号鉴别的方法.结果可用于常用合金钢焊材和焊缝中Mo元素的定性、定量分析以及材料牌号鉴别.     

镍基合金钼元素可见光谱数字化分析技术研究

使用可见光谱数字化自动分析系统对镍基合金中Mo元素可见光谱进行了分析测定,研究了镍基合金中Mo元素的Mo550.65nm和M588.83nm分析谱线组的特征,探索了镍基合金中Mo元素的数字化分析技术.结果可用于镍基合金中Mo元素的定性、定量分析和牌号鉴别.     

高压燃气发射装置喉衬材料的烧蚀试验

介绍一种高压燃气发射装置喷管喉衬材料的烧蚀试验方法.提供了用炮钢、钨渗铜、钨渗银、钽10钨、钼合金及铌合金等材料的喷管试验结果,其中以钽10钨的抗烧蚀性最佳.     

不同电极材料下ADN基液体推进剂电点火特性的实验研究

目前二硝酰胺铵(ADN)基液体推进剂在工程应用中均采用催化点火燃烧方式,而电点火可以避开催化剂高温失活、冷启动等问题。为了研究ADN基液体推进剂的电点火特性,在密封装置中开展了不同电极材料下推进剂液滴电点火实验,并研究了180V～230V电压范围内液滴着火延迟时间、着火持续时间以及燃烧过程的变化规律。结果表明:ADN基液体推进剂能够通过电阻加热点火方式点燃。采用钨丝电极时,着火延迟时间、着火持续时间和反应总时间均随着电压增加逐渐减小,在230V电压时相对于180V时分别减小了25%,56%和38%。采用钼丝电极时,着火延迟时间在180V～200V范围随着电压增加逐渐降低,在200V～230V电压范围内基本不变;着火持续时间总体上随着电压的增加而呈现略微增加的趋势,但增加幅度较小;反应总时间在180V～230V电压范围内基本稳定在1.5s左右。     

Ion engine grids: Function,main parameters,issues, configurations,geometries, materials and fabrication methods

Ion optics are crucial components of ion thrusters and the study of the different ion extraction solutions used since the beginning of the electric propulsion era is essential to understand the evolution of ion engines. This work describes ion engine grids' main functions, parameters and issues related to thermal expansion and sputter erosion, and then introduces a review of ion optics used for significant launched and tested ion thrusters since 1970. Configurations, geometries, materials and fabrication methods are analyzed to understand when typical ion thrusters use two or three grids, what are the thicknesses and aperture sizes of the screen, accelerator and decelerator grids, why molybdenum and carbon-based materials such as pyrolytic graphite and carbon–carbon are the best available options for ion optics and what is the manufacturing method for each material.     

Temperature Cycling Effects on Solar Panels

Temperature cycling for more than 300 cycles and for temperatures down to - 175°C performed on soldered silicon cell assemblies with copper, Kovar, and molybdenum interconnectors showed a wide range in failures depending both upon the materials used and on interconnector thickness and substrate material. The solder fatigue failure rate is strongly dependent on stress level in agreement with analytical predictions.     

Oriented molybdenum disulfide-silica/hydrogenated nitrile butadiene rubber composites: Effects of nanosheets on mechanical and dielectric properties

A series of non-covalently functionalized molybdenum disulfide-silica (f-MoS₂-SiO₂) nanocomposites was prepared by an in-situ assembled method and used to fabricate the oriented molybdenum disulfide-SiO₂/Hydrogenated Nitrile Butadiene Rubber (f-MoS₂-SiO₂/HNBR) composites. The characterization results show the synergistic dispersion between the functionalized molybdenum disulfide (f-MoS₂) nanosheets and SiO₂ nanoparticles. The addition of f-MoS₂ nanosheets can improve the dispersion of fillers in the rubber matrix and weaken the filler network. The non-covalently functionalization improves the interface interaction between f-MoS₂ nanosheets and the rubber matrix. Furthermore, the tensile strength of f-MoS₂-SiO₂/HNBR is 65.9% higher than that of SiO₂/HNBR by adding 1.0wt% of f-MoS₂. At the same time, the dielectric constant of f-MoS₂-SiO₂/HNBR is increased by 23.7% compared to SiO₂/HNBR due to the micro-capacitor structure of parallel f-MoS₂ nanosheets in the rubber matrix. Our work provides new ideas for the development of high-performance elastomer materials.     

合金化及热处理对Fe_3Al合金组织和性能影响

研究了不同的热处理条件及添加Mn,Mo,Nb,Cr,V,RE（La-Ce）等合金元素对Fe3Al合金组织和性能的影响。结果表明,Fe3Al合金在B2相区间保温淬火后的硬度值较小,在DO3相区短时间回火硬度值大幅增加,随回火时间延长硬度值呈降低趋势,在本实验的最长回火时间内（50h）硬度稍有提高;TEM分析表明,这与回火过程中DO3畴的尺寸变化有关;合金化后Cr和V的加入降低合金硬度,其它几种元素都提高了合金的硬度;SEM分析表明合金元素的作用机理不同：Cr软化了合金,Mo主要产生固溶强化,Mn、V、Nb加入后有第二相析出,RE元素主要偏析在晶界,细晶强化。     

Multi-channel discharge characteristics cutting by ultra-fine wire-EDM

Compared with a copper wire electrode, molybdenum wire with a poor conductor is usually used as the electrode in high speed wire-cut electrical discharge machining(HSWEDM), so the resistance of an ultra-fine wire cannot be ignored. To study the differences of discharge characteristics between the ultra-fine wire and the conventional diameter wire, the continuous discharge waveform of two kinds of wire electrodes was compared. It was found that there was a multichannel discharge phenomenon in the...