有序多孔磁性碳化硅陶瓷的制备

采用聚二甲基硅烷(PDMS)和二茂铁合成了聚铁碳硅烷(PFCS).以有序氧化硅凝胶小球为模板、PFCS作先驱体,经过先驱体的渗入、不熔化、陶瓷转化和除去模板,制得氮气吸附法(BET)比表面积为703.46 m2/g的有序多孔含铁碳化硅SiC(Fe) 性陶瓷.     

先驱体法制备连续Si-Fe-C-O吸波纤维的研究

用聚二甲基硅烷和二茂铁合成聚铁碳硅烷,经多孔熔融纺丝、预氧化、连续烧成,制得电阻率低至10-2Ω·cm,拉伸强度可达2.0GPa,长度大于500m的连续Si-Fe-C-O纤维,这种纤维在8～18GHz范围内具有较好的吸收雷达波性能.研究铁对Si-Fe-C-O纤维电阻率和β-SiC结晶的影响:铁含量的增加有利于β-SiC晶粒的增长和电阻率的降低.     

异型(三叶形)截面碳化硅纤维的异形度控制

以聚碳硅烷（ＰＣＳ）为原料,采用熔融纺丝制备三叶形ＰＣＳ纤维后,经不熔化和烧成制得异形度为０．６５～０．８５的三叶形碳化硅纤维。研究了纺丝温度、压力、收丝速度等对纤维异形度的影响,并对预氧化和烧成工艺进行了研究,研究表明,氏的纺丝温度、适当主的纺丝压力和较低的转率有效于提高纤维的异形度,聚碳硅烷原丝经预氧化和烧结后,纤维异形度基本保持不变。     

新型六角晶系铁氧体吸收剂的研制及应用

本文对(Zn_(1-x)Co_x)_2-W 型六角晶系铁氧体吸收剂在 X 波段的复数磁导率(?)_r=μ_r′-jμ_r″、复介电常数(?)_r=ε_r′-jε_r″进行了扫频测试。讨论了(?)_r,(?)_r 随频率 f、Co~(2 )含量 x、吸收剂的重量百分含量以及球磨时间长短(吸收剂粒度变化)变化的规律。在吸收剂:石蜡=5∶1(吸收剂重量百分含量83.3%)时,(?)_(rmax)(8.2GHz)=1.94∠-26.3°、(?)_r=5.78∠-1.3°其|μ_r|较大,具有较好的频率特性,同时|ε_r|合适,有利于获得宽带吸收,经航空航天部621所、703所应用得到了较好的结果,已通过机电部电科院鉴定。     

聚碳硅烷PC-P不熔化纤维的热解过程

聚碳硅烷PC—P是制备力学性能优异的低电阻率碳化硅纤维的先驱体。利用IR、TG、凝胶含量分析等手段研究了聚碳硅烷PC—P不熔化纤维的热解过程。研究表明，聚碳硅烷PC—P不熔化纤维高温热解过程与PCS不熔化纤维类似，但在300℃左右存在明显的自交联现象，使PC—P不熔化纤维的凝胶含量迅速增加，这是PC—P纤维在不熔化程度较低情况下能够通过高温烧成的原因。     

结构吸波材料SiC—C纤维的研究

本文用聚碳硅烷(PCS)与煤沥青(P)共混,制得PCS-P共混物,经纺丝、氧化、高温烧成,制得了SiC-C纤维,其电阻率随碳含量的增加而减小,强度和模量随碳含量的增高而降低,用该纤维与环氧树脂复合制得的层合板材,具有良好的吸收电磁波性能。     

C形、中空截面碳化硅纤维的成形工艺研究

以聚碳硅烷(PCS)为原料，经C形喷丝板熔融纺丝制备C形、中空截面PCS原丝后，再经不熔化和高温烧成后得到C形、中空截面SiC纤维。文中讨论了纺丝温度、N2压力和收丝速度对两种PCS纤维当量直径和异形度的影响，以及不熔化和烧成工艺对SiC纤维截面形状的影响。结果表明，纺丝温度对C形、中空PCS纤维当量直径和异形度影响较大；合适的纺丝工艺和不熔化及烧成条件下可以得到高异形度低当量直径的C形、中空截面SiC纤维。     

先驱体转化法制备改性SiC吸收剂研究

在聚碳硅烷先驱体中掺混Ｎｉ、Ｃｏ等纳米金属微粉,在Ｎ２气氛中裂解至１０００℃,得到改性碳化硅吸收剂,通过ＴＧ、ＩＲ等分析手段,研究了该裂解反应的过程,分析了裂解及热处理产物的相组成,讨论了原料中纳米金属含量、裂解（热处理）条件等地吸收剂的微波电磁参数的影响。     

Ni-Al—Ta／Mo合金的层错能及影响因素

采用置换原子的热力学模型,计算了Ni-Al-Ta/Mo合金的层错能.分析了Ni-Al-Ta/Mo合金中各元素浓度及温度对层错能的影响.结果表明:Ni-Al-Ta/Mo合金的层错能随Al含量的增加而明显降低,其中,随Al浓度提高,合金中原子偏聚自由能(ΔGγ→εs)降低,可促进γ′有序相的形成是使合金层错能降低的主要原因.随Mo/Ta含量的提高,可引起置换原子自由能(ΔGγ→εb)降低,原子偏聚自由能(ΔGγ→εb)升高;随温度提高,Ni-Al-Ta/Mo合金中的置换原子自由能(ΔGγ→εb)增加,表明合金中发生原子置换需要外部供给能量,而引起原子偏聚自由能(ΔGγ→εs)升高,表明高温不利于溶质原子的偏聚.     

低电阻率Si—C—O纤维制备

采用将聚二甲基硅烷与聚氯乙烯共裂解合成制备了Si－C－O纤维先驱体聚合物，并对其进行了表征。表明反应体系中聚氯乙烯含量较高时，生成的先驱体聚合物既有聚碳硅烷的结构特征，又具有－CH＝CH－共轭结构特征的－（SiCH3H-CH2)n（CH＝CH）m－共聚物。先驱体聚合物经熔融纺丝及NO2不熔化处理，高温烧成制得低电阻率Si－C－O（电阻率小于10^0Ω.cm），而通过聚碳硅烷制得的SiC纤维电阻率为10^6Ω.cm。结果表明能够从聚二甲基硅烷与聚氯乙烯共裂解出发制备低电阻率Si－C－O纤维。     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

ν-gap度量及其在飞行控制律评估中的应用

 传统控制律评估方法主要用于单输入单输出（SISO）系统，且对模型参数摄动考虑不够全面,针对这些不足，研究了ν-gap度量方法。在介绍系统广义稳定裕度相关概念的基础上，给出了ν-gap度量的定义、特点和性质以及近似摄动模型的计算，提出ν-gap度量评估控制律的步骤。实例结果表明，该方法不仅克服了上述传统评估方法的缺陷，而且还有根据所求的各摄动影响情况忽略影响小的元素，以减少计算量及可以找到最坏情况下的参数摄动组合等优点。     

基于飞机油箱模型形状特征油量测量切片步长选择方法研究

 在分析飞机数字式油量测量过程中目前广泛使用的切片法油量测量原理的基础上,针对现有的定步长切片法无法得到准确、可靠的燃油质量特性数据库的缺陷,结合对飞机油箱模型形状特征的分析,提出了基于飞机油箱模型形状特征的油量测量切片步长选择方法。此方法包括切片步长整体和局部选择两个过程,整体选择以实现相邻两切片平面所夹油箱模型体积近似相等为目的来确定切片步长,以体现油箱模型截面整体变化规律;局部选择以设计切片平面与截面突变平面重合或尽可能接近的方式,突出油箱截面的局部变化特征。实验结果表明：该切片步长选择方法较定步长方法能够建立更为合理、可靠的燃油质量特性数据库,从而提高了油量测量精度。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

Integrated Entry Guidance for Reusable Launch Vehicle

A method for the implementation of integrated three-degree-of-freedom constrained entry guidance for reusable launch vehicle is presented. Given any feasible entry conditions, terminal area energy management interface conditions, and the reference trajectory generated onboard then, the method can generate a longitudinal guidance profile rapidly, featuring linear quadratic regular method and a proportional-integral-derivative tracking law with time-varying gains, which satisfies all the entry corridor constraints and meets the requirements with high precision. Afterwards, by utilizing special features of crossrange parameter, establishing bank-reversal corridor, and determining bank-reversals according to dynamically adjusted method, the algorithm enables the lateral entry guidance system to fly a wide range of missions and provides reliable and good performance in the presence of significant aerodynamic modeling uncertainty. Fast trajectory guidance profiles and simulations with a reusable launch vehicle model for various missions and aerodynamic uncertain-ties are presented to demonstrate the capacity and reliability of this method.     

二维翼段颤振的μ控制

 采用超声电机作为作动器来实现含控制面的翼段颤振鲁棒抑制。针对作者设计的二维翼段颤振主动抑制系统，通过理论与实验相结合的方法，建立了考虑沉浮方向阻尼和作动器模型参数不确定性的控制系统模型，设计了μ控制器，并对控制器做了降阶处理。数值仿真和风洞试验表明，μ控制器可有效地抑制颤振的发生，将颤振临界速度提高23.4%。相对于H_∞控制器，μ控制器的控制效果和鲁棒性更好。     

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

Abnormal Shape Mould Winding

为解决网格化芯模的缠绕问题,本文提出了复合材料面片缠绕机理;接着详细分析了面片缠绕过程中的芯模凹曲面上纤维滑线和架空现象,应用微分几何曲面理论和空间几何理论,提出判据及其解决方案;最后,针对飞机发动机进气道的缠绕成型,编制缠绕控制程序并进行相应的实验,验证了面片缠绕方法的可行性。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。