保温时间对K452高温合金钎焊接头组织与性能的影响

采用钴基钎料及镍基合金粉料,分别在1170℃保温10min、60min和120min的钎焊工艺下,对K452镍基铸造高温合金进行真空钎焊实验,通过扫描电镜和能谱分析仪进行了接头显微组织观察与物相分析,并测试钎焊接头的高温力学性能。结果表明:在保温60min的工艺规范下,界面实现较好的结合,钎缝内部孔洞缺陷较少,钎缝组织均匀,有利于钎焊接头性能的提高;在更长的保温时间120min下,钎缝内部又有蚀孔缺陷形成,且较多的白色块状化合物在合金粉颗粒间聚集长大,但界面结合良好,钎焊接头性能较高,900℃抗拉强度达到400MPa,900℃/100MPa持久寿命为141h55min。     

MGH956合金钎焊接头力学性能分析

以MGH956合金钎焊接头高温抗拉强度为考察对象进行了正交试验设计。结果表明,考察的3个因素对接头性能影响的主次顺序为:钎料成分﹥保温方式﹥焊缝间隙;对应较优工艺参数为:钎料为KCo3,保温方式为:1240℃/10min加1000℃/30min;焊缝间隙为0.02mm。在所进行试验中,1000℃拉伸试验结果最好的焊缝强度接近了母材水平。     

K403合金高性能钎焊技术研究

用新型镍基钎料3P1对K403合金进行真空钎焊试验,分析钎焊接头的微观组织和连接机制,测试接头高温力学性能.结果表明:采用3P1钎料,在1230℃/10min 1160℃/4h条件下进行K403合金钎焊,可以获得无缺陷的,与基体组织相似的钎焊接头,其1000℃下高温拉伸强度可以达到基体强度的90%,高温持久强度可以达到基体强度的70%以上.     

K403与DZ4高温合金的大间隙钎焊

采用两种含钨钎料N171,N300和Rene'95高温合金粉末对K403与DZ4高温合金的大间隙钎焊工艺进行了研究。试验结果表明,在钎焊接头间隙中预填合适粒度的Rene'95高温合金粉末,可实现K403+DZ4的大间隙钎焊。焊后在较高温度进行较长时间的扩散处理,可明显改善大间隙钎焊接头组织,并防止其焊后固溶处理时发生严重重熔,但为避免高温合金粉被钎料过分溶解,在高温扩散处理前,应先在较低温度进行一定时间的热处理。采用N300钎料、预填Rene'95粉钎焊的K403+DZ4大间隙接头经焊后扩散处理,具有良好的高温力学性能,接头900℃的拉伸强度达铸态K403母材的92%,980℃/126MPa条件下持久寿命为135h;再经固溶处理后,接头900℃的拉伸强度超过铸态K403母材水平(677MPa),持久寿命也略有提高。     

多钎缝喷注器真空钎焊工艺

针对不同部位多条钎焊缝一次钎焊成型,开展采用BNi-2钎料进行喷注器真空钎焊工艺方法的实验研究。分析了表面洁净度、钎焊温度及钎缝间隙对喷注器密封性的影响。结果表明:钎缝间隙对由高温合金与不锈钢两种材料组成喷注体钎焊接头的密封性有显著影响。合理的钎缝装配间隙为10～15μm,此间隙使钎缝中的钎着率90%,并得到了内外部质量、密封性优良的接头。     

Ti_2AlNb合金的钎焊试验研究

采用箔带状Ti-15Cu-15Ni钎料合金对Ti2Al Nb合金开展钎焊试验研究。随着钎焊温度的升高,钎料合金在基体材料上的润湿角逐渐减小,直至965℃完全润湿基体材料。当钎焊工艺为975℃/10min时,钎焊接头室温抗拉强度可达855MPa,达到基体强度的80%。钎焊界面为冶金结合界面,未见焊接缺陷,界面中心存在10μm宽的钎料元素富集区。该工艺条件下,Ti2Al Nb合金的室温拉伸断口为脆性解理断口,钎料元素富集区处产生了大量的二次裂纹。研究结果为Ti2Al Nb合金钎焊构件的制造技术提供了理论基础。     

C/ C 复合材料与高温合金钎焊接头微观组织与性能分析

采用BNi68Cr WB粉末作为连接材料,利用真空钎焊工艺成功制备了C/C复合材料与镍基高温合金(GH600)的连接试样。并借助扫描电子显微镜和材料万能试验机,研究钎焊接头微观组织结构和室温及高温(700℃)下的抗剪切性能。结果表明,使用BNi68Cr WB粉末可以实现C/C与GH600的钎焊连接,接头的断裂位置为C/C复合材料母材;与室温条件相比,钎焊接头在700℃下的抗剪强度较低。     

镍基高温合金电子束钎焊润湿性及界面产物

采用两种钎料对镍基高温合金进行了真空电子束钎焊润湿性试验,探讨了真空电子束钎焊主要工艺参数对钎料铺展润湿性的影响.在确定优选钎料的基础上,进行了电子束钎焊搭接试验,研究了界面结构,确定了界面反应产物及其形态分布.     

扩散处理对K403铸造高温合金大间隙钎焊接头组织和力学性能的影响

研究采用自制钎料加入FGH95高温合金粉末的K403铸造高温合金大间隙钎焊后扩散处理参数对接头组织和持久性能的影响.结果表明,钎焊后进行温度1180℃,32h的扩散处理,钎缝化学成分及组织均匀,钎缝基体组织为γ固溶体,占体积50%～53%的γ′相均匀分布.骨架状硼化物化合物消除,少量小块和粒状碳化物和硼化物分布在晶界上.钎焊接头975℃的持久强度较高.     

Ni-Cu-Mn-Co钎料及其高温变形机制

研究了低镍高温钎料。在试验温度高于钎料熔点0.5倍的高温条件下,对钎料的温度效应和应变速率进行了试验;分析了钎料高温性能与应变速率、钴的变质剂作用等因素之间的理论规律。     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

基于飞机油箱模型形状特征油量测量切片步长选择方法研究

 在分析飞机数字式油量测量过程中目前广泛使用的切片法油量测量原理的基础上,针对现有的定步长切片法无法得到准确、可靠的燃油质量特性数据库的缺陷,结合对飞机油箱模型形状特征的分析,提出了基于飞机油箱模型形状特征的油量测量切片步长选择方法。此方法包括切片步长整体和局部选择两个过程,整体选择以实现相邻两切片平面所夹油箱模型体积近似相等为目的来确定切片步长,以体现油箱模型截面整体变化规律;局部选择以设计切片平面与截面突变平面重合或尽可能接近的方式,突出油箱截面的局部变化特征。实验结果表明：该切片步长选择方法较定步长方法能够建立更为合理、可靠的燃油质量特性数据库,从而提高了油量测量精度。     

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

二维翼段颤振的μ控制

 采用超声电机作为作动器来实现含控制面的翼段颤振鲁棒抑制。针对作者设计的二维翼段颤振主动抑制系统，通过理论与实验相结合的方法，建立了考虑沉浮方向阻尼和作动器模型参数不确定性的控制系统模型，设计了μ控制器，并对控制器做了降阶处理。数值仿真和风洞试验表明，μ控制器可有效地抑制颤振的发生，将颤振临界速度提高23.4%。相对于H_∞控制器，μ控制器的控制效果和鲁棒性更好。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

Abnormal Shape Mould Winding

为解决网格化芯模的缠绕问题,本文提出了复合材料面片缠绕机理;接着详细分析了面片缠绕过程中的芯模凹曲面上纤维滑线和架空现象,应用微分几何曲面理论和空间几何理论,提出判据及其解决方案;最后,针对飞机发动机进气道的缠绕成型,编制缠绕控制程序并进行相应的实验,验证了面片缠绕方法的可行性。