纤维表面PIP-SiC涂层对2D-SiC_f/SiC复合材料力学性能影响

采用低浓度先驱体溶液利用先驱体浸渍裂解(PIP)工艺在SiC纤维表面制备了SiC涂层,研究了浸渍裂解次数对纤维涂层形貌的影响.研究表明,采用10%的PCS先驱体溶液经3次浸渍裂解后可在纤维表面制得连续致密的SiC涂层.采用经涂层处理的SiC纤维布经热模压成型-先驱体浸渍裂解工艺制备了2D-SiCf/SiC复合材料,其弯曲强度随制备涂层浸渍裂解次数的增加先增后降,经3次浸渍裂解制备涂层的复合材料强度最高,由未经涂层处理的163.5MPa增大到245.9MPa,强度提高近50%.研究证明,SiC纤维表面SiC涂层使纤维在材料致密化过程所受的损伤减小,同时改善了界面,使复合材料强度明显提高.     

浸渍工艺对先驱体转化制备Cf/SiC复合材料结构与性能的影响

以聚碳硅烷(PCS)/二乙烯基苯(DVB)为先驱体制备了3D-B Cf/SiC复合材料,研究了不同浸渍工艺对材料力学性能的影响.结果表明采用加热加压浸渍可以大大提高先驱体的浸渍效率,提高所制备材料的密度,从而明显提高Cf/SiC复合材料的力学性能.选用加热加压浸渍条件所制备的材料密度达到1.944g/cm3,室温弯曲强度达到662MPa,在1650℃(真空)和1800℃(真空)下测试,材料的弯曲强度分别为647MPa和609MPa.     

热压辅助先驱体裂解制备的三维Cf／Si—O—C复合材料的微观结构与力学性能

采用聚硅氧烷(PSO)先驱体浸渍裂解工艺制备出碳纤维三维编织物增强Si—O—C复合材料(3D-B C_(?)/Si—O—C)。研究发现,第一周期采用热压辅助裂解可以显著提高材料的力学性能与致密度。第一周期经1600℃、10MPa的条件热压裂解处理5min后,材料的弯曲强度和断裂韧性从未处理前的246.2MPa和9.4MPa·m~(1/2)提高到502MPa和23.7MPa·m~(1/2)。该材料的弯曲强度在真空中可以保持到1400℃。探讨了工艺参数对材料结构与力学性能的影响。高温裂解弱化界面结合同时提高纤维就位强度以及加压提高材料致密度是热压辅助裂解能提高材料力学性能的主要原因。     

以一种新型先驱体制备SiC/SiC复合材料高温弯曲性能研究

以新型先驱体LPVCS(含乙烯基液态聚碳硅烷)为原料,以经CVD裂解碳(PyC)界面改性的KD-1型SiC纤维作为增强相,采用先驱体浸渍裂解工艺(PIP)制备三维编织SiC/SiC复合材料,并对其室温及1300℃弯曲性能测试表征。试验结果表明,采用LPVCS为先驱体制备SiC/SiC复合材料,降低了材料制备周期,且9个周期后材料密度达到2.14g/cm3,开孔率为10.8%。在1300℃空气环境中,SiC/SiC复合材料弯曲强度达到470.2MPa,断裂韧性达到20.7MPa·m1/2。采用扫描电镜对SiC/SiC复合材料1300℃下断口形貌进行观察,SiC纤维存在一定拔出;断口表面存在较为严重的氧化现象,这是导致材料弯曲强度降低的主要原因。     

PIP 工艺对2D C/ SiC-ZrB2 复合材料结构和力学性能的影响

采用CVI结合SI及PIP工艺制备2D C/SiC-ZrB2复合材料.研究了PIP工艺中循环浸渍次数及热处理对复合材料结构和力学性能的影响.比较了多孔C/SiC浸渍浆料后用PIP结合CVI致密化和仅用CVI致密化的效果.结果表明:浸渍裂解后,热处理温度相同,热处理次数对复合材料的开孔率和弯曲强度影响不大.2D C/SiC-ZrB2复合材料的弯曲强度不随PIP次数的增多而增加,PIP处理二次后,复合材料的强度逐渐增加,PIP处理五次,强度达到最大值,制备的复合材料开孔率为8.0%、弯曲强度为423 MPa.SI后用PIP结合CVI致密化比仅用CVI致密化效果好.     

超高温陶瓷改性C/SiC复合材料的制备及其性能

以碳纤维为增强体,聚碳硅烷和聚烷基铪为前驱体,采用前驱体浸渍裂解(PIP)工艺制备C/Si C-HfC复合材料,将其与同种工艺所得C/SiC复合材料进行对比评价分析。发现C/SiC-HfC复合材料具有较低密度和较好的高温力学性能,且在1 650℃静态氧化实验中,含有HfC的基体对纤维具有更佳保护效果。C/SiC-HfC密度约为1.92 g/cm~3,常温弯曲强度为345 MPa,1 800℃高温无氧环境弯曲强度可达424 MPa。C/SiC-HfC复合材料表现出更加优异高温力学性能是由于HfC组分的添加抑制了SiC晶粒的生长,降低了基体内部较大裂纹产生的概率。在1 650℃空气环境下,含有HfC的基体对纤维具有更佳保护作用,主要是由于HfC组分的添加使材料表面的SiC及时氧化成SiO_2,SiO_2在纤维和基体表面形成包覆层,防止了材料内部的进一步氧化。     

PIP工艺制备SiC晶须增强SiCf/SiC复合材料的性能

以不同界面层厚度的SiC纤维为增强相,采用先驱体浸渍裂解工艺(PIP)制备SiC_f(PyC)/SiC复合材料,并在复合材料基体中引入SiC晶须,对其性能进行研究。结果表明:热解碳(PyC)界面层厚度约为230 nm时,SiC纤维拔出明显,SiC_f/SiC复合材料拉伸强度、弯曲强度和断裂韧度分别达到192.3 MPa、446.9 MPa和11.4 MPa?m^1/2;在SiC_f/SiC复合材料基体中引入SiC晶须后,晶须的拔出、桥连及裂纹偏转等增韧机制增加了裂纹在基体中传递时的能量消耗,使复合材料的断裂韧度和弯曲强度分别提高了22.9%和9.1%。     

C/ C-PAA 与C/ C-FA 弯曲性能对比

通过PIP工艺制备了C/C-PAA、C/C-FA复合材料,对PAA、FA裂解碳的XRD、浸渍效果以及C/C-PAA和C/C-FA的弯曲强度进行了分析.结果表明:PAA裂解碳的炭质量、浸渍效果较好,C/C-PAA弯曲强度比C/C-FA弯曲强度高34.9％,弯曲模量对比不明显.     

PIP 法制备SiBN 纤维增强氮化物陶瓷基复合材料Ⅰ———纤维和先驱体性能分析

利用先驱体聚合物浸渍-裂解(PIP)技术制备SiBN纤维增强氮化物陶瓷基复合材料,对SiBN纤维、聚硅硼氮烷有机先驱体裂解以及SiBN纤维增强氮化物陶瓷基复合材料性能进行了分析。研究表明:聚硅硼氮烷先驱体在氨气气氛下裂解得到的陶瓷产物碳含量较低,其裂解产物介电常数在3.0左右,介电损耗小于0.01;SiBN纤维中C和O元素含量均较高,碳的存在对材料介电性能影响明显;制备的氮化物陶瓷基复合材料弯曲强度为88.52 MPa,弹性模量为20.03 GPa。     

界面层对SiC_f/SiC复合材料力学性能及氧化行为的影响

为研究界面层对SiC_f/SiC复合材料力学性能及氧化行为的影响,采用先驱体浸渍裂解工艺制备了3种不同界面层体系的SiC_f/SiC复合材料。3种界面层分别为热解碳(PyC)、PyC+BN-Ⅰ和PyC+BN-Ⅱ(其中BN-Ⅰ表示B质量分数大约2%,BN-Ⅱ表示B质量分数大约20%)。研究表明,具有PyC界面层的SiC_f/SiC复合材料常温力学性能最高,其常温弯曲强度达到380MPa,而双界面层体系中,SiC_f/SiC复合材料常温弯曲强度分别为282MPa(PyC+BN-Ⅰ)和259MPa(PyC+BN-Ⅱ)。1200℃氧化试验表明,具有PyC+BN-Ⅱ界面层的SiC_f/SiC复合材料弯曲强度保留率最高,为54%。3种不同界面层体系的SiC_f/SiC复合材料在氧化后均表现为脆性断裂。微观结构显示,界面和纤维被氧化是导致材料最终失效的原因;能谱分析表明,具有PyC+BN-Ⅰ和PyC+BN-Ⅱ界面层的SiC_f/SiC复合材料纤维内部未检测到O原子存在,证实BN有保护纤维的作用。     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

ν-gap度量及其在飞行控制律评估中的应用

 传统控制律评估方法主要用于单输入单输出（SISO）系统，且对模型参数摄动考虑不够全面,针对这些不足，研究了ν-gap度量方法。在介绍系统广义稳定裕度相关概念的基础上，给出了ν-gap度量的定义、特点和性质以及近似摄动模型的计算，提出ν-gap度量评估控制律的步骤。实例结果表明，该方法不仅克服了上述传统评估方法的缺陷，而且还有根据所求的各摄动影响情况忽略影响小的元素，以减少计算量及可以找到最坏情况下的参数摄动组合等优点。     

基于飞机油箱模型形状特征油量测量切片步长选择方法研究

 在分析飞机数字式油量测量过程中目前广泛使用的切片法油量测量原理的基础上,针对现有的定步长切片法无法得到准确、可靠的燃油质量特性数据库的缺陷,结合对飞机油箱模型形状特征的分析,提出了基于飞机油箱模型形状特征的油量测量切片步长选择方法。此方法包括切片步长整体和局部选择两个过程,整体选择以实现相邻两切片平面所夹油箱模型体积近似相等为目的来确定切片步长,以体现油箱模型截面整体变化规律;局部选择以设计切片平面与截面突变平面重合或尽可能接近的方式,突出油箱截面的局部变化特征。实验结果表明：该切片步长选择方法较定步长方法能够建立更为合理、可靠的燃油质量特性数据库,从而提高了油量测量精度。     

Integrated Entry Guidance for Reusable Launch Vehicle

A method for the implementation of integrated three-degree-of-freedom constrained entry guidance for reusable launch vehicle is presented. Given any feasible entry conditions, terminal area energy management interface conditions, and the reference trajectory generated onboard then, the method can generate a longitudinal guidance profile rapidly, featuring linear quadratic regular method and a proportional-integral-derivative tracking law with time-varying gains, which satisfies all the entry corridor constraints and meets the requirements with high precision. Afterwards, by utilizing special features of crossrange parameter, establishing bank-reversal corridor, and determining bank-reversals according to dynamically adjusted method, the algorithm enables the lateral entry guidance system to fly a wide range of missions and provides reliable and good performance in the presence of significant aerodynamic modeling uncertainty. Fast trajectory guidance profiles and simulations with a reusable launch vehicle model for various missions and aerodynamic uncertain-ties are presented to demonstrate the capacity and reliability of this method.     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

二维翼段颤振的μ控制

 采用超声电机作为作动器来实现含控制面的翼段颤振鲁棒抑制。针对作者设计的二维翼段颤振主动抑制系统，通过理论与实验相结合的方法，建立了考虑沉浮方向阻尼和作动器模型参数不确定性的控制系统模型，设计了μ控制器，并对控制器做了降阶处理。数值仿真和风洞试验表明，μ控制器可有效地抑制颤振的发生，将颤振临界速度提高23.4%。相对于H_∞控制器，μ控制器的控制效果和鲁棒性更好。     

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

Abnormal Shape Mould Winding

为解决网格化芯模的缠绕问题,本文提出了复合材料面片缠绕机理;接着详细分析了面片缠绕过程中的芯模凹曲面上纤维滑线和架空现象,应用微分几何曲面理论和空间几何理论,提出判据及其解决方案;最后,针对飞机发动机进气道的缠绕成型,编制缠绕控制程序并进行相应的实验,验证了面片缠绕方法的可行性。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。