DSM11镍基高温合金表面三种涂层高温性能

DSM11镍基高温合金表面制备Al-Si、Al和Co-Al三种涂层,研究三种涂层在900℃下的涂盐（质量分数为5% NaCl+95% Na₂SO₄）热腐蚀性能和800℃下的疲劳性能。实验结果表明:在900℃热腐蚀200h后,Al-Si涂层和Co-Al涂层表面腐蚀区均形成了以Al₂O₃为主的连续且致密的氧化层,抑制热腐蚀反应的进行,具有一定的抗热腐蚀性能;Al涂层表面腐蚀区形成了混合型氧化层,热腐蚀反应会持续进行,抗热腐蚀性能较差。在800℃的疲劳实验后,Al-Si涂层表面生成大量的微裂纹,涂层容易发生开裂,进而引起合金试样快速断裂;Co-Al涂层和Al涂层的合金试样表现较好的抗高温疲劳性能。在高温合金的防护涂层使用中,要充分考虑到涂层的服役环境,对相关性能进行综合评价,选出最适合的防护涂层。      

Oxidation Properties in CO2 of Inconel Alloy 600 Coated by Simultaneous Aluminizing-Chromizing Process

IN 600 alloy was coated with two different types of coatings, Cr-modified aluminide coating this is called aluminizing-chromizing and Y-doped chromium modified aluminide coating this is called aluminizing-chromizing-yttriumizing. Diffusion coating was carried at 1 050 ℃ for 8 h under Ar atmosphere by simultaneous aluminizing-chromizing process and by simultaneous aluminizing-chromizing- yttriumizing. Cyclic oxidation tests were conducted on the uncoated and on the coated Inconel 600 alloy in the temperature range 800- 1 000 ℃ in CO2 for 100 h at 10 h cycle.The results showed that the oxidation kinetics for uncoated Inconel 600 alloy in CO2 is parabolic and the phases present are NiO, (Fe, Cr)2O3 , NiFe2O4 and NiCrO4. The oxidation kinetics for both coated systems in CO2 was found to be parabolic and the value of kP for both coated systems were found to be lower than that for uncoated Inconel 600 alloy. Oxide phases that formed on coated systems are Al2O3 and NiCrO4. The role of yttrium can be attributed to its ability to improve the adherence of the oxide scale.     

铝-硅涂层中Si的分布及作用

 本文研究了Al-Si涂层中Si的分布和存在形式,揭示了含Si的铝化物涂层中形成的富Si的M₆C隔层,它阻碍铝化物涂层中Al和Si向内扩散,从而提高涂层的抗高温氧化能力。利用预处理法可使Al-Si涂层预制成富Si的M₆C隔层,进一步提高它的防护能力。     

复合包渗法制备铌合金表面硅化物涂层

采用复合包渗法在C103铌合金基体上制备硅化物涂层,进行1500℃静态氧化实验,室温～1500℃热震实验,利用X射线衍射(XRD)、扫描电镜(SEM)、能谱分析(EDS)等检测手段对涂层氧化前后的组织结构进行观察,分析涂层形成机理、硅化时间对涂层组织结构的影响以及涂层氧化前后组织形貌的变化.研究表明,复合包渗法制备硅化物涂层主要是通过扩散反应形成的;涂层是以MoSi2相为主体层的多相复合结构;在高温氧化环境下,涂层表面生成熔融态非晶玻璃膜,有效阻止了氧向内进一步扩散,涂层抗静态氧化及抗热震性能良好.     

TiAl合金高温循环氧化行为及其表面改性研究

研究了TiAl金属间化合物及表面涂层在空气中的高温循环氧化行为。结果表明:在800℃时TiAl合金具有较好的抗高温氧化行为,但当温度高于800℃时,TiAl合金表面未能形成单一的Al2O3保护层,而是形成外3层为疏松的TiO2层,内层为TiO2+Al2O3的混合氧化物层,因而使得TiAl合金的抗高温循环氧化性能严重蜕化。TiAl合金经过Cr改性铝化处理后,表面形成了具有立方Ll2结构的Al67Ti26Cr7层,立方Ll2结构的Al67Ti26Cr7不仅具有较高的铝含量,而且具有优良的韧性,因而使得处理后的TiAl合金具有良好的抗高温循环氧化性能。铝化物涂层尽管有很高的铝含量,但由于铝化得到的TiAl3相具有四方形结构,涂层非常脆,故该涂层抗高温循环氧化性能有待进一步提高。     

高温合金纳米晶涂层的发展

高温合金纳米晶涂层是一种新的高温合金防护涂层体系.与目前通常采用的涂层不同,其成分与基体合金基本相同,有良好的抗氧化性能,且避免了传统涂层高温使用后在涂层与基体间因互扩散形成的脆性有害相.高温合金纳米晶涂层是在研究晶粒度对合金抗氧化性能影响的基础上发展起来的.本文综述了国内外对晶粒细化影响铁基合金、金属间化合物、高温合金等氧化性能的研究概况,重点介绍了高温合金溅射纳米晶涂层的研究结果.     

电弧离子镀Al扩散障结构及抗高温氧化性能研究

采用电弧离子镀技术(AIP)在HY3(NiCrAlYSi)涂层与镍基高温合金(K5合金)之间沉积一层Al薄膜经过马弗炉870℃加热1h形成Al2O3作为扩散障层,研究了Al2O3对HY3(NiCrAlYSi)涂层与基体的元素互扩散的阻碍作用和对涂层氧化动力曲线的影响。对于添加扩散障层前后的试样,进行循环抗氧化试验来评价其抗高温氧化性能,并用扫描电镜(SEM)分析氧化前后试样微观形貌和成分,用X-射线衍射仪分析涂层的相结构。试验结果表明:Al2O3有效阻止基体与涂层之间的元素互扩散,提高了HY3(NiCrAlYSi)涂层和K5合金的抗高温氧化性能。     

姿/ 轨控液体火箭发动机推力室高温抗氧化涂层

概述了国内外姿/轨控液体火箭发动机高温抗氧化涂层的研究和应用进展,研制过程涉及多种材料体系,但仅有几类广泛应用于型号,包括Nb基材表面硅化物材料体系、Pt-Rh合金、Re基材表面Ir涂层。随着对发动机性能要求的提高,Re/Ir材料体系成为目前主要的研究方向。     

氧化时间对MB8镁合金微弧氧化膜的影响

研究氧化时间对MB8镁合金氧化膜致密度、厚度和耐蚀性的影响,分析不同氧化时间膜层表面微观形貌、成分和结构的变化.结果表明,随微弧氧化时间的延长,氧化膜变厚变粗糙,氧化时间为10min时,膜层腐蚀速率最低.微弧氧化初期膜层主要由立方结构的MgO构成,随氧化时间的延长,斜方晶体结构的Mg2(SiO4)和单斜晶体结构的Mg(PO3)2在膜层中的含量逐渐增加.     

Dy对EB-PVDβ-NiAl涂层高温瞬态氧化行为的影响(英文)

β-NiAl是一种有前景的应用于1150°C以上的抗氧化涂层材料。本文利用电子束物理气相沉积(EB-PVD)方法制备了0~0.5at%Dy含量的β-NiAl涂层,研究了涂层的瞬态氧化行为。1200°C时,在0.05at%Dy掺杂的涂层中只观察到了稳态α-Al2O3相,而在0.5at%Dy掺杂的涂层中,1h氧化过程中,发生了θ-Al2O3到α-Al2O3的相变。1100°C时,在最初的15min所有涂层均发生了θ-α相变。0.05at%Dy掺杂的涂层在45min的时候相变已经完成,这比0.5at%Dy掺杂涂层要早得多。过量Dy的掺杂能够延缓θ-α相变。未掺杂和过量掺杂涂层在20h氧化之后仍存在针状相θ-Al2O3,而0.05at%Dy掺杂的涂层中则为经典的颗粒状α-Al2O3形貌。     

Corrosion mechanism investigation of TiN/Ti coating and TC4 alloy for aircraft compressor application

It is imperative to develop multifunctional erosion and corrosion resistant coatings for compressor blades of aircraft engines in harsh environment. PVD (Physical Vapor Deposition) technology has the advances in processing erosion-resistant coatings; however, the performance of PVD coatings to combat corrosion depends on various coating defects. Determining and comparing the corrosion performances of PVD TiN/Ti coating and uncoated TC4 alloy was the main objective of present work. The 960 h salt spray corrosion and 116 h hot corrosion tests were conducted to simulate the grounding and working environments of the aircraft compressors. The corrosion mechanisms due to the coating defects such as pinhole, columnar boundary and large grain were analyzed based on the OM, Confocal microscope, electrochemical measurements, SEM, XRD and EDS results. Owing to the disordered state associated with the columnar boundary and the coating defect, nitrogen could be easily replaced by oxygen in the hot corrosion process, these structures were channels for fast diffusion of oxygen. Moreover, the Gibbs energy changes of Ti oxidation and TiN oxidation were thermodynamically calculated according to the working condition of aircraft compressors, and considerable research effort was focused on mapping out the phase diagram of Ti, TiN and high pressure gases. The findings of this research can provide insights into developing multifunctional coatings for future aircraft engines.     

两种MCrAlY涂层/DD6合金的循环氧化和互扩散行为

在DD6单晶高温合金基体上,利用电子束物理气相沉积(EB-PVD)技术制备Ni Co Cr Al Y涂层,采用低压等离子喷涂(LPPS)技术制备Ni Co Cr Al YHf Si涂层,通过扫描电镜(SEM)、X射线能谱(EDS)、X射线衍射(XRD)、电子探针显微分析(EPMA)等手段研究了在1100℃下的热循环氧化和互扩散行为。结果表明,涂层显著提高了DD6基体的抗氧化能力,经100h的循环氧化后,涂层表面氧化层主要成分仍为α-Al2O3,依然发挥着较好的抗氧化保护作用。这两种涂层与基体之间形成了互扩散区(IDZ)和二次反应区(SRZ),IDZ和SRZ的厚度均随着循环氧化时间延长而增大;SRZ中析出的棒状与颗粒状的拓扑密堆相(TCP)含有W、Re、Mo等高熔点元素,其质量分数分别高达37.51%、14.22%和10.61%,TCP含量随着氧化时间而增多。活性元素Si、Hf对涂层中富Cr相和TGO的增长速率均有一定的抑制作用。     

GH907合金防护涂层耐腐蚀性能研究

通过盐雾-热暴露循环腐蚀试验对3种GH907合金防护涂层分别进行了耐腐蚀性能研究,利用扫描电镜、能谱分析等方法对其腐蚀形貌和产物进行了详细地对比分析,并探究了其腐蚀速率变化规律。研究结果表明：在该试验条件下,3种涂层均发生了不同程度的破坏,基体也发生氧化腐蚀。TW-7水基耐高温涂层（底层＋面层）的耐腐蚀性能优于SKNC-65纳米自修复涂层和TW-7水基耐高温涂层（底层）的。3种涂层的腐蚀破坏机理均不相同。     

基于甲基三甲氧基硅烷/正硅酸乙酯的聚碳酸酯耐磨涂层

以甲基三甲氧基硅烷(MTMS)水解聚合产物作为主要成膜物质,引入正硅酸乙酯(TEOS)水解产物硅溶胶作为无机增强物,采用溶胶凝胶法在聚碳酸酯(PC)表面形成耐磨涂层。结果表明:PC表面形成了Si—O—Si的交联网络结构。通过测试耐磨实验前后光学性能的变化研究表面涂覆涂层的聚碳酸酯的耐磨性能与涂层组分之间的关系。当涂层原料MTMS和TEOS的摩尔比为2∶1时,聚碳酸酯的耐磨性能达到最优,500次摩擦后雾度为13.22%,为纯PC的56.21%。     

两种不同成分NiAl涂层性能的对比研究

采用双丝电弧喷涂在6061-T6铝合金基底上制备NiAl-95/05和NiAl-80/20涂层,利用标准测试方法测量涂层的机械性能,并提出了NiAl涂层摩擦磨损机理的新理论。结果表明：NiAl-80/20涂层具有较高的结合强度和显微硬度。随磨损进行,NiAl-80/20涂层的静摩擦系数随磨损的继续一直单调下降,直至最后进入稳态阶段;NiAl-95/05涂层的静摩擦系数先缓慢下降,200个循环之后由于磨损形貌的进一步恶化,静摩擦系数呈缓慢上升的趋势。NiAl-95/05涂层的磨损机制主要为磨粒磨损,并且在磨损过程中伴随有犁削效应;NiAl-80/20涂层主要为粘着磨损机制,并且具有更好的耐磨性。     

EB-PVD热障涂层对IC10合金力学性能的影响

采用电弧离子镀技术在IC20合金基体上制备NiCrAlYSi粘结层,利用电子束物理气相沉积（EB—PVD）技术在粘结层上制备YSZ陶瓷面层。研究了YSZ热障涂层对IC10合金拉伸、持久、疲劳性能的影响。结果表明：IC10合金沉积YSZ热障涂层后,980℃／200MPa高温持久寿命与IC10合金相当;900℃高温抗拉强度σb、屈服强度σ0.2、伸长率占和断面收缩率砂与基体相比,基本保持不变;室温抗拉强度σb。屈服强度σ0.2：与基体相比稍有下降;800℃／447MPa疲劳寿命与基体合金相当。因此,IC10合金沉积TBCs涂层后,对IC10合金力学性能无明显影响,不影响合金的实际使用。     

钛合金表面镍基喷焊涂层的组织和耐磨行为

采用火焰喷焊技术对钛合金表面进行耐磨改性,可以较好地解决实施工艺过程中的工程适应性问题,但对于任何一种表面耐磨处理技术,耐磨性能的改善和提高都是其最终目的。考察了钛合金表面上3种不同成分的镍基火焰喷焊涂层的组织和耐磨行为。研究发现,3种成分的镍基涂层都具有韧基体+硬质相的耐磨组织,其基体均为强韧性很好的镍基固溶体,但硬质相的差别较大。在相同试验条件下,100%的F102涂层、含4%La2O3的稀土复合涂层和含25%WC的N i-WC复合涂层的磨损失重仅为未处理钛合金的1/6,1/8和1/10。试验结果表明,采用火焰喷焊技术对钛合金表面进行耐磨处理,可以有效地改善表面的耐磨性。     

High-temperature oxidation behavior and analysis of impedance spectroscopy of 7YSZ thermal barrier coating prepared by plasma spray-physical vapor deposition

Quasi-columnar structure 7YSZ(yttria stabilized zirconia) thermal barrier coatings(TBCs) are prepared by plasma spray-physical vapor deposition(PS-PVD) onto pretreated and un-pretreated bond coating, respectively. An isothermal oxidation experiment of 7YSZ TBCs is carried out in the atmosphere of 950 °C in order to simulate the high-temperature oxidation process of engine blades. The isothermal oxidation process of 7YSZ thermal barrier coatings is investigated systematically by impedance spectroscopy. The electrochemical physical model and equivalent circuit of columnar 7YSZ coatings are established. Results show that the isothermal oxidation kinetic curve of columnar 7YSZ thermal barrier coatings appears to follow the parabolic law. A pretreatment of bond coating can reduce the growth rate of the thermally grown oxide(TGO) layer, restraining the initiation and propagation of microcracks between YSZ and TGO layers. The oxidation rate constants of 7YSZ coatings with pretreated and un-pretreated bond coating are 0.101×10~(-12) cm~2·s~(-1) and 0.115 × 10~(-13) cm~2 ·s~(-1), respectively. Impedance analysis shows that the content of oxygen vacancies decreases and the density increases after the TGO layer is oxidized for 150 h. In addition, shrinkage microcracks formed by sintering during the oxidation process is the main reason for an increase of the capacitance and a decrease of the resistance in the grain boundary of YSZ.     

常温腐蚀对Al-Si涂层氧化行为的影响

研究了未经 /经常温腐蚀的 DZ1 2 5镍基合金表面 Al-Si涂层的高温氧化行为。结果表明 ,经腐蚀的涂层等温氧化行为发生变化。在初始阶段 ,经腐蚀的试样增重大于未经腐蚀的试样 ,而且经腐蚀的试样的耐高温性能明显下降。氧化皮中主要是 Al2 O3及少量的 Ti O2 .     

脉冲频率对7050高强铝合金微弧氧化膜层的影响

在脉冲频率为50、250、500、750、1 000 Hz的条件下，应用微弧氧化（MAO）技术在7050高强铝合金表面制备了陶瓷膜层，并采用扫描电镜（SEM）、X射线衍射仪（XRD）、电化学工作站、摩擦磨损试验机等手段分别对陶瓷膜的表面形貌、相组成、耐腐蚀性、耐磨性等进行分析。结果表明，当脉冲频率过低时，MAO陶瓷膜层表面粗糙，影响膜层致密性；而当脉冲频率过高时，则不利于MAO陶瓷膜层生长，所得的膜层耐蚀性和耐磨性较差。当脉冲频率为250 Hz时，所制备的膜层具有最佳的耐磨性及耐蚀性。