铝合金在模拟SO2污染大气环境中的腐蚀行为

采用扫描电镜(SEM/EDX)、增重法、傅立叶变换红外光谱(FTIR)和X射线衍射研究铝合金1060、铝合金2A12和7A04分别在表面沉积与未沉积70μg/cm2氯化钠条件下在含50×10-6SO2(50ppm)污染大气环境中的腐蚀行为和规律,并测试三种材料力学性能的变化。研究结果表明,随试验时间的延长,铝合金表面腐蚀产物不断增多,腐蚀增重符合指数衰减规律Δm/A=B Dexp(-t/k),抗拉强度和延伸率呈下降趋势;表面腐蚀产物形貌呈团状或圆团状,并不断向外扩展延伸,呈现不均匀的凹凸形貌;铝合金在50ppm SO2污染大气环境中腐蚀产物少,腐蚀增重较少,表面腐蚀产物主要为氧化铝和硫酸铝;而表面沉积70μg/cm2NaC l的铝合金在模拟50ppm SO2污染大气环境中腐蚀产物明显增多,腐蚀增重大,力学性能下降幅度大,二氧化硫和氯化钠的协同作用明显促进铝合金的腐蚀,腐蚀产物主要为氧化铝、铝的硫酸盐和铝的氯化物。     

纯镁和镁锂合金在中性3.5%NaCl溶液中的腐蚀行为

采用电化学方法研究了纯Mg和Mg-Li合金在中性3.5%NaCl溶液中的腐蚀行为,采用扫描电镜观察了腐蚀后的表面形貌,利用XRD测试了腐蚀前后纯Mg和Mg-Li合金表面的组成成分,并用失重法测试了腐蚀速率。结果表明:腐蚀初期,纯Mg的腐蚀电流小于Mg-Li合金,纯Mg的腐蚀电位高于Mg-Li合金,纯Mg的电化学反应电阻大于Mg-Li合金。经过24h腐蚀后,纯Mg的腐蚀速率大于Mg-Li合金,且两者腐蚀形貌不同,纯Mg的腐蚀坑大而深,蚀坑数量少;Mg-Li合金的腐蚀坑小而浅,蚀坑数量多并且表面变黑。纯Mg的腐蚀产物主要为Mg(OH)2,Mg-Li合金的腐蚀产物主要为Mg(OH)2,LiOH,MgLi,Mg3Li7,Al2O3。     

局部包铝层对铝合金疲劳板材盐雾环境中点腐蚀的影响

研究了在3.5%NaCl水溶液(质量分数,下同)中性盐雾环境中,带有局部包铝层的2024和7B04高强铝合金轴向疲劳板材光滑试样的腐蚀.发现疲劳试样表面的局部包铝层不仅保护其覆盖区域不被腐蚀,同时也间接减轻了其未覆盖区域的腐蚀程度.这主要是由于局部包铝层的存在减小了其未覆盖区域的腐蚀面积,而铝合金腐蚀面积的减小会造成腐蚀程度降低.腐蚀面积的变化对2024铝合金影响较小,造成腐蚀深度的减小;对7B04铝合金影响较大,可以使其不发生点腐蚀.     

前处理工艺对航空铝锂合金硫酸阳极氧化膜层性能影响

针对一种新研制的航空用Al-Li-Cu-Zn-Mg系铝锂合金,采用了光学显微镜、电子显微镜和能谱分析技术,分析碱腐蚀和三酸脱氧两种不同前处理工艺对铝锂合金硫酸阳极氧化膜层的外观、耐蚀性和疲劳性能的影响规律。结果表明:相比三酸脱氧工艺,碱腐蚀工艺对铝锂合金表面的腐蚀程度较深,晶界处的耐腐蚀能力较差,硫酸阳极氧化膜层表面形成了网状晶界形貌;采用碱腐蚀处理的试样疲劳寿命较三酸脱氧处理试样更低,而不同前处理后经过硫酸阳极氧化的试样疲劳寿命相差不大。不同前处理对铝锂合金的硫酸阳极氧化膜层的耐蚀性的影响不大。     

LY12CZ 合金相电化学腐蚀行为的研究

分别研究了LY12CZ合金中的纯铝（Al）、晶间化合物θ（CuAl2）、S（Al2CuMg）和MnAl6在含Cl-离子的中性溶液中的电化学腐蚀行为。结果表明,各合金相作为独立相在含Cl-离子的中性介质中均有点蚀敏感性,其中S相耐蚀性最差,L1相耐蚀性最好。各相点蚀主要是由于Al或Mg的阳极溶解所致,腐蚀产物主要是铝的不溶性氢氧化物、可溶性氯化物及镁的可溶性盐类。     

工艺参数对搅拌摩擦焊7022铝合金残余应力及耐磨耐蚀性能的影响

采用不同的焊接参数对10mm厚7022铝合金进行搅拌摩擦焊研究.利用X射线应力分析仪检测焊接试样的残余应力分布;利用摩擦磨损试验机对焊缝试样进行磨损性能研究,并通过三维形貌仪观察其磨损形貌;利用pH=5的Na2SO4溶液对焊接试样进行腐蚀试验,并通过SEM观察其表面腐蚀形貌.结果表明:各参数下焊接试样的残余应力均较小,...     

中性盐雾预腐蚀对AF1410高强钢疲劳寿命的影响

采用失重法和XRD法研究了AF1410钢在中性盐雾环境中的耐蚀性能,并对中性盐雾预腐蚀不同时间后的试样进行疲劳性能测试,研究了不同预腐蚀时间对材料疲劳寿命的影响。结果表明:AF1410钢发生了严重的全面腐蚀,腐蚀产物主要由FeO(OH)和Fe3O4组成,并得到其腐蚀失重曲线;疲劳断口形貌分析表明,随预腐蚀时间的延长,腐蚀损伤程度增加,在疲劳加载过程中易形成较多的疲劳裂纹扩展源而导致疲劳断裂失效;最终获得中性盐雾预腐蚀AF1410钢结构疲劳寿命特性以及预腐蚀对疲劳寿命的影响系数C(t)曲线。     

基于三维格子Boltzmann铝点蚀动态数值模拟

铝作为目前最经济且应用最为广泛的材料之一，具有重量轻、耐腐蚀、导热性好、导电性好等优点。然而，金属铝在氯离子环境中容易发生点蚀。根据中性溶液中铝表面点蚀反应机理，结合液体流动和相变特性，建立了三维格子Boltzmann铝点蚀模型，研究了中性溶液中铝表面的点蚀现象，弥补了传统实验方法的不足。采用建立的腐蚀模型对整个铝点蚀过程进行了模拟，得到了不同组分的浓度分布以及不同参数与腐蚀程度的关系。结果表明：铝的腐蚀程度随接触时间的增加而增加。随着初始氯离子浓度的增加和腐蚀反应速率的增大，铝被腐蚀得更严重。三维格子Boltzmann铝点蚀模型为金属腐蚀数值研究提供了新的思路。     

AL—Li合金2091应力腐蚀开裂的研究

一般认为阳极溶解(AD)和氢脆(HE)是铝合金应力腐蚀开裂(SCC)的主要机制。为了区分应力腐蚀敏感的铝锂合金2091 T8x 板材的这些过程,我们研究了它在不同腐蚀性介质中全浸或交浸以及在潮湿空气中的行为。结果表明:在2091合金的 SCC 中,AD 和 HE 两者均起作用;在一些特殊的腐蚀性条件下,它们的作用可以被区分开。     

分光光度法测定TRIP钢在3.5% NaCl溶液中的腐蚀行为

用全浸实验方法研究了四种不同成分TRIP钢在3.5%NaCl溶液中的腐蚀行为,采用分光光度法测定了其腐蚀速率,利用扫描电镜对腐蚀后试样进行表面形貌观察。结果表明：溶液中微量Fe的含量与溶液的吸光度呈良好的线性关系;不含合金元素的A钢腐蚀速率最大,加入合金元素较多的B、D钢腐蚀速率较小,含合金元素的C钢腐蚀速率适中。随着腐蚀时间的增加,四种钢的腐蚀速率明显降低。合金元素在锈层中富集使锈层更致密,提高了试样的耐腐蚀性能。     

表面涂层破损对7 B04铝合金点蚀的影响及仿真研究

模拟7B04铝合金表面涂层破损,采用电化学试验研究7B04铝合金在不同环境条件下的自腐蚀与点蚀行为,基于电偶腐蚀数学模型,通过有限元法分析7B04铝合金与TA15钛合金接触后发生点蚀的条件。结果表明：7B04铝合金点蚀电位受Cl-浓度和pH值的影响,在NaCl质量分数>10%的中性溶液及NaCl质量分数为3.5%的酸性溶液中,自腐蚀状态下7B04铝合金即可发生点蚀;7B04铝合金与TA15钛合金接触后,电位升高,增加了发生点蚀的可能性,在NaCl质量分数为3.5%的中性溶液中,当阴阳极面积比≥40时,7B04铝合金发生点蚀的萌生并进一步扩展;7B04铝合金电位随阴阳极距离的增大而下降,但幅度有限,在10 m的距离内下降不超过2 mV。     

Effect of temperature on corrosion behavior of 3003 aluminum alloy in ethylene glycol–water solution

The effect of temperature on the corrosion behavior of 3003 aluminum alloy in ethylene glycol–water solution was investigated by potentiodynamic polarization and electrochemical impedance spectroscopy(EIS) techniques. The surface characterization was observed and determined by scanning electron microscopy(SEM), atomic force microscopy(AFM) and energy dispersive spectrometer(EDS). The results demonstrate that the anodic aluminum dissolution and the cathodic oxygen reduction were accelerated by the increased temperature. However, as temperature was over60 °C, the solubility and concentration of oxygen decreased, resulting in the inhibition of cathodic reaction. The cathodic reaction rate of 3003 aluminum alloy rose to the maximum at 60 °C. The Warburg impedance in Nyquist diagram diminished and then was replaced by a negative capacitance caused by the absorption of intermediate corrosion product on electrode. On the other hand,after potentiodynamic measurements, 3003 aluminum alloy suffered pitting corrosion. The dissolution of aluminum alloy around secondary phase particles expanded both horizontally and vertically.     

2024-T3铝合金DFR退化规律及疲劳断口分析

通过对2024-T3铝合金进行不同时长条件下的预腐蚀疲劳试验,拟合得出了2024-T3铝合金DFR(Detail Fatigue Rating)随腐蚀时长的变化曲线,并通过对2024-T3铝合金预腐蚀后的疲劳断口分析,得到了2024-T3铝合金疲劳性能退化过程的一些基本特点和规律。对于掌握2024-T3铝合金的DFR退化规律,做好飞机结构的腐蚀防护有重要的参考和借鉴作用。     

SiCp含量及缓蚀剂对SiCp／Al金属基复合材料腐蚀行为的影响

研究了ZL101A铝合金及以其为基体含5vol%,10vol%,15vol%和20voll%SiCP的SiCP/Al金属基复合材料在3.5%NaCl溶液中的腐蚀行为,通过添加钼酸钠、硅酸钠等缓蚀剂在3.5%NaCl溶液中,将SiCP/Al金属基复合材料在室温下浸泡一定的周期,采用失重法和SEM技术分别计算腐蚀速率和分析腐蚀后的微观组织形貌.试验结果表明SiCP颗粒增强物的加入对SiCP/Al金属基复合材料腐蚀速率影响不大,甚至略有降低,SiCP改变了铝合金基体表面腐蚀的形核和发展,点蚀数量增加、深度变浅.添加缓蚀剂后,抑制了SiCP/Al金属基复合材料表面点蚀的形成,与钼酸钠缓蚀剂相比,硅酸钠具有良好的缓蚀作用,当SiCP颗粒增强物的含量达到15vol%和20vol%时,缓蚀剂的缓蚀效果明显下降.     

Cu含量对2219铝合金锻件及其焊接接头组织与性能的影响

采用力学拉伸实验、焊接实验、电化学阻抗谱(EIS)、循环阳极极化曲线(Tafel)以及金相和扫描电镜(SEM)等分析测试方法,研究Cu含量对2219铝合金锻件组织与性能的影响。结果表明:降低Cu含量,有利于减少2219铝合金基体内的残余结晶相,并有效抑制在合金焊接过程中粗大Al_2Cu相的析出,使基材和焊件的伸长率显著提高,强度略有下降;Cu在铝基体中形成Al_2Cu相诱导合金发生局部腐蚀,使材料的耐腐蚀性能变差,降低Cu含量能够减小合金的腐蚀倾向,改善合金的耐腐蚀性能。     

水溶液中LC4铝合金的微生物腐蚀缓蚀杀菌剂

通过电化学极化、表面分析等方法,研究了 LC4铝合金在无菌培养液和培养液加硫酸盐还原菌( sulfate-reducing bacteria,简称 SRB)的厌氧体系中加入缓蚀杀菌剂的腐蚀行为。实验结果表明 :SRB能加速LC4铝合金的腐蚀破坏,其腐蚀破坏行为属于点蚀腐蚀机理;加入缓蚀杀菌剂能够影响 SRB的生长规律,抑制 SRB和 Cl-离子对 LC4铝合金的腐蚀破坏。在所研究的 4种缓蚀杀菌剂中,BHA-2缓蚀杀菌剂具有最好的缓蚀和杀菌双重功效,且明显优于市场上广泛使用的 1 2 2 7。     

7085-T651铝合金特厚板组织性能的不均匀性

采用拉伸实验、剥落腐蚀实验、显微组织、化学成分、扫描电镜以及透射电镜和差示扫描量热法分析等手段,研究7085-T651铝合金特厚板组织性能的不均匀性。结果表明：110 mm厚7085-T651特厚板不同厚度层显微组织、力学性能和剥落腐蚀性能存在明显的不均匀性;1/4厚度层抗拉强度最低,为540 MPa,抗剥落腐蚀性能最差,腐蚀等级为EB级;心层抗拉强度最高,为580 MPa;表层抗剥落腐蚀性能最好,腐蚀等级为EA级;1/4层再结晶分数最多,约为47.7%,尺寸较大,约为105μm,晶界及晶内均有平衡相析出,时效析出相尺寸较小,因而力学性能及抗剥落腐蚀性能均最差;中心层再结晶分数最少,约为14.8%,存在大量亚晶,残余的 Al7 Cu2 Fe 相最多,约为1.43%,晶界平衡相尺寸、时效析出相尺寸及PFZ宽度均较大,因而力学性能较好而抗剥落腐蚀性能较差。     

LC4铝合金服役环境下点蚀形貌特征及其演变规律

为获取飞机LC4铝合金在服役环境下典型点蚀形貌特征,采用模拟服役环境的加速腐蚀实验环境谱对材料试件进行加速腐蚀实验,定义3个参数蚀坑深度H、蚀坑表面长度L、蚀坑表面宽度W为表征蚀坑形貌特征参量,跟踪测量典型蚀坑不同腐蚀年限下此3个特征参量数值,获取典型蚀坑形貌特征参量数据检测结果。在此基础上,对检测结果分别采用统计分析和分形理论方法进行数据分析,获取LC4铝合金同一腐蚀年限下和不同腐蚀年限下典型点蚀蚀坑的形貌特征及其演变规律。结果表明:同一腐蚀年限下,点蚀蚀坑形貌特征参量符合对数正态分布;随着腐蚀年限的增加,点蚀蚀坑形貌特征参量逐渐体现出明显的分形特征,蚀坑形貌逐渐趋向坑深度较浅、坑表面长度较长、坑表面宽适中的特征。     

不同环境下LY12-CZ铝合金表面腐蚀损伤演化规律研究

 本文对不同腐蚀温度、不同腐蚀时间作用下铝合金的表面腐蚀损伤形态进行了试验研究。腐蚀损伤在实验室中由人工产生。在光学显微镜下测量得到不同腐蚀环境下试验件的表面腐蚀损伤度数值，并对这些数值进行了详细的统计分析。研究结果表明，腐蚀损伤度随腐蚀时间和温度的增加而增大很快，腐蚀损伤度的概率分布符合逻辑分布。     

新型Al-Zn-Mg-Cu合金的应力腐蚀行为研究

采用周期浸泡试验,研究了不同热处理制度下的新型A l-Zn-Mg-Cu合金应力腐蚀行为。对比了国产A l-Zn-Mg-Cu合金与进口合金的腐蚀行为差异。探讨了合金应力腐蚀开裂的宏观特征及裂纹的微观特征。采用A1热处理制度生产的国产合金对应力腐蚀具有敏感性,而采用A2和A3两种热处理制度生产的国产合金均达到了与进口合金相当的抗应力腐蚀性能。