单侧面板裂纹损伤对钛合金蜂窝夹层结构弯曲性能影响 |
| |
引用本文: | 岳喜山,闫群,赵伟,谢宗蕻. 单侧面板裂纹损伤对钛合金蜂窝夹层结构弯曲性能影响[J]. 北京航空航天大学学报, 2020, 46(11): 2018-2025. DOI: 10.13700/j.bh.1001-5965.2019.0587 |
| |
作者姓名: | 岳喜山 闫群 赵伟 谢宗蕻 |
| |
作者单位: | 1.西北工业大学 航天学院, 西安 710072 |
| |
摘 要: | 钛合金蜂窝夹层结构在制备或使用过程中可能会产生面板裂纹损伤。采用试验和有限元结合的方法研究了单侧面板裂纹损伤对钛合金蜂窝夹层结构弯曲性能的影响。结果显示:单侧面板裂纹损伤会明显降低钛合金蜂窝夹层结构面板弯曲强度,弯曲强度近似随裂纹长度的增加而线性降低;有限元模型能够准确预测结构的破坏模式和破坏强度,预测得到的面板弯曲强度与试验结果最大偏差仅为6%。采用的有限元方法可用于含面板裂纹损伤的钛合金蜂窝壁板结构弯曲性能的工程预估。
|
关 键 词: | 钛合金蜂窝夹层结构 面板裂纹 三点弯曲试验 弯曲强度 有限元 |
收稿时间: | 2019-11-14 |
Influence of one side facesheet crack damage on flexural properties of titanium honeycomb sandwich structures |
| |
Affiliation: | 1.School of Astronautics, Northwestern Polytechnical University, Xi'an 710072, China2.Aeronautical Key Laboratory for Welding and Joining Technologies, AVIC Manufacturing Technology Institute, Beijing 100024, China3.Structure Department, Shenyang Aircraft Design and Research Institute, Shenyang 110035, China4.School of Aeronautics and Astronautics, Sun Yat-Sen University, Guangzhou 510275, China |
| |
Abstract: | During the manufacturing process and service period, the crack damage may occur in the facesheet of titanium honeycomb sandwich structure. The influence of one side facesheet crack damage on flexural properties of titanium honeycomb sandwich structures was studied experimentally and numerically. The research results show that the flexural strength of titanium honeycomb sandwich structure with one side facesheet crack damage is obviously lower than that of the structure without crack damage, and the flexural strength decreases linearly with the increase of the crack length; the finite element models can accurately predict the failure mode and fracture strength of the structures, and the maximum deviation between the predicted results and the test result is only 6%. The finite element analysis method can be used to predict the flexural strength of titanium honeycomb sandwich structure with facesheet crack damage in the engineering estimate. |
| |