| 摘 要： | Based on probabilistic fracture mechanics approach, a new concept of material initial fatigue quality (MIFQ) is developed. Then, the relation between S-N curve and crack propagation curve is studied. From the study, a new durability analysis method is presented. In this method, S-N curve is used to determine crack growth rate under constant amplitude loading and evaluate the effects of different factors on durability and then the structural durability is analyzed. The tests and analyses indicate that this method has lower dependence on testing, and higher accuracy, reliability and generality and is convenient for application.
|
Analysis Approach to Durability Based on Material Initial Fatigue Quality and S-N Curve |
| |
| Yang Moucun a,*,Nie Hong b a College of Energy and Power Engineering,Nanjing University of Aeronautics and Astronautics,Nanjing ,China b College of Aerospace Engineering,Nanjing University of Aeronautics and Astronautics,Nanjing ,China.Analysis Approach to Durability Based on Material Initial Fatigue Quality and S-N Curve[J].Chinese Journal of Aeronautics,2007,20(6):518-523. |
| |
| Authors: | Yang Moucun Nie Hong |
| |
| Abstract: | Based on probabilistic fracture mechanics approach, a new concept of material initial fatigue quality (MIFQ) is developed. Then,the relation between S-N curve and crack propagation curve is studied. From the study, a new durability analysis method is presented. In this method, S-N curve is used to determine crack growth rate under constant amplitude.loading and evaluate the effects of different factors on durability and then the structural durability is analyzed. The tests and analyses indicate that this method has lower dependence on testing, and higher accuracy, reliability and generality and is convenient for application. |
| |
| Keywords: | probabilistic fracture mechanics approach durability S-N curve crack propagation rate initial fatigue quality Curve Quality Fatigue Initial Material Based Durability Approach reliability convenient application accuracy analyses lower dependence testing loading evaluate effects different |
| 本文献已被 CNKI 万方数据 等数据库收录！ |