ZA27Ce合金组织形态对阻尼性能的影响

对铸态ZA2 7Ce合金进行固溶处理 ,获得单一均匀的固溶体后 ,分别进行 96℃ ,180℃和 2 5 0℃人工时效。采用悬挂弯曲共振法测量阻尼性能Q-1值 (阻尼本领 ) ,结果是 ,96℃人工时效后阻尼性能好于 180℃以及 2 5 0℃人工时效后的阻尼性能。利用SEM研究时效后微观组织 ,结果发现 ,96℃人工时效获得粒状组织 ,180℃以及2 5 0℃人工时效获得层片状组织。利用等轴晶界面滑动内耗机理分析认为 ,ZA2 7Ce合金粒状组织的阻尼性能好于层片状组织的阻尼性能     

Calculation of quasisynchronous orbits of a spacecraft around Phobos for solving the problem of landing on its surface

The problem of selecting quasi-synchronous orbits of a spacecraft around Phobos is considered. These quasi-synchronous orbits are far (with respect to the Hill’s sphere) quasi-satellite orbits with retrograde rotation in the restricted three body problem. The orbit should pass through a given point at a specified time instant. It should also possess a property of minimum distance from the Phobos surface at every passage above the region of planned landing. The equations of dynamics are represented in the form describing the orbit as a combination of motions in two drifting ellipses, inner and outer ellipses. The center of the outer ellipse is located on the inner ellipse. A formula is derived that relates averaged values of half-axes of the inner and outer ellipses. It is used for construction of the first approximation of numerically designed orbit, which makes it possible to simplify and speed up the computing process. The tables of initial conditions obtained as a result of calculations are presented.     

LaBr3(Ce)元件破损在线监测关键核素确定及效率校准

常用的元件破损在线监测方法受外在因素影响较大，以γ能谱中关键裂变产物核素比活度进行在线定量分析是一种可靠的元件破损监测方法。针对新型LaBr₃(Ce)元件破损监测仪，设计了元件破损模拟实验，对逸出的裂变产物采用HPGe和LaBr₃(Ce)探测器进行了对比测量。通过不同冷却时间γ能谱的核素分析，确定了¹³⁵Xe，⁸⁸Kr，¹³⁸Xe，⁸⁸Rb，¹³⁸Cs等可作为LaBr₃(Ce)元件破损γ能谱监测的关键核素。同时，制备了覆盖能量范围(250～2 400)keV，含⁶⁰Co，¹³⁷Cs，¹³³Ba；²⁴¹Am，¹⁵²Eu；¹⁰⁹Cd，⁸⁸Y，⁵⁷Co及²⁴Na的4组放射性标准溶液，在建立的效率校准系统上，校准了LaBr₃(Ce)在线监测仪的效率。在反应堆一次异常情况分析中，已校准的LaBr₃(Ce)元件破损监测仪对关键核素的现场分析结果与HPGe的取样分析结果一致，表明效率校准结果准确，校准方法可靠。     

Ce在钛合金阳极化中作用的研究

 研究了 Ce元素在钛合金阳极氧化中的作用。通过对普通工艺和稀土工艺之间氧化膜微观形貌的对比,讨论了 Ce元素对氧化膜完整性的影响。利用能谱分析,说明了 Ce元素加入可以使钛合金表面氧化较为充分,并且 Ce元素参与了氧化膜的组成。采用局部成分分析法确定了膜层的横向分布范围。对氧化膜截面的SEM图进行分析,讨论了 Ce元素对钛合金阳极氧化膜厚度的影响。利用动电位扫描,对普通氧化膜和稀土氧化膜的耐点蚀性进行了比较,表明 Ce盐的加入可以提高钛合金氧化膜抗点蚀的能力。     

用Ce~(3+):YVO_4晶体荧光粉与蓝光LED制造自然白光LED

本文报导了通过结合自行制备的掺铈钒酸钇晶体(Ce3 :YVO4)荧光粉与InGaN／GaN蓝光发光二极管(LED)结合而得的白光发光二极管(W-LED)。在室温、正向电压3.5V、正向电流20mA时W-LED的CIE色坐标为(0．32,0．37),接近纯白色(0．33,0．33)。     

Quasi-synchronous orbits and their employment for the approach of a spacecraft to Phobos

The problem of construction of quasi-synchronous orbits which pass through a prescribed point over the surface of Phobos at a prescribed instant of time is considered. The orbits should pass as close as possible to the surface of Phobos at each passage above the planned region of landing.     

Some new applications of the generalized problem of two fixed centers

A generalized problem of two fixed centers and its limiting version is considered. New possible applications of this problem are obtained. Using a symmetric version of the problem, the external field of gravitation is approximated. The limiting version approximates the inner field.     

Ce元素含量和铸造方法对AZ91-2Ca合金微观组织与力学性能的影响

在AZ91-2Ca合金中分别添加0.5%,1.0%和1.5%的Ce元素,采用重力铸造制备合金并结合组织性能分析,优化出最佳Ce含量。对最佳成分合金进行不同浇铸温度的压力铸造,对比研究Ce含量和铸造方法对AZ91-2Ca合金微观组织和力学性能的影响。研究表明:在重力铸造条件下,随Ce含量提高,合金组织明显细化,强化相Al_4Ce含量逐渐增加,进而改善了力学性能。当Ce含量为1.5%时,强度和延伸率均达到最大值。在压力铸造条件下,随浇铸温度由640℃提高到700℃,压铸AZ91-2Ca-1.5Ce合金微观组织不断细化,Al_4Ce相分布均匀,700℃压铸合金综合性能最高,抗拉强度、屈服强度和延伸率分别为191 MPa,157 MPa和1.7%。相比于重力铸造,压力铸造可进一步提高该合金的强度,从而为解决高Ca阻燃镁合金阻燃效果和力学性能之间的矛盾提供了新思路,促进了该合金在航空航天和汽车领域的应用。     

热处理工艺对复合熔体处理A356合金组织和性能的影响

利用熔体超声处理、Sr/Ce复合变质及热处理相结合的方法提高铝合金的强韧性,通过金相组织分析及力学性能测试研究了固溶处理对A356合金组织和性能的影响。研究结果表明,熔体处理有利于改善α-Al枝晶和共晶硅相,铸态合金的抗拉强度和伸长率分别达到215 MPa和9.5%;T6热处理后,共晶硅的形态由纤维状转变成独立分布的颗粒状,而除了伸长率之外,合金的力学性能都显著提高;随着固溶时间的延长,共晶硅的等效直径呈现先减小后增大的趋势,而长径比逐渐减小,合金的拉伸性能和硬度均呈现先增大后减小的趋势;当固溶时间为4 h时,合金的综合力学性能达到最佳,其抗拉强度、屈服强度、伸长率和显微硬度分别达到300、240 MPa、8.0%和110HV。