A progressive approach to predict shot peening process parameters for forming integral panel of Al7050-T7451

In this paper, a progressive approach to predict the multiple shot peening process parameters for complex integral panel is proposed. Firstly, the invariable parameters in the forming process including shot size, mass flow, peening distance and peening angle are determined according to the empirical and machine type. Then, the optimal value of air pressure for the whole shot peening is selected by the experimental data. Finally, the feeding speed for every shot peening path is predicted by regression equation. The integral panel part with thickness from 2 mm to 5 mm and curvature radius from 3200 mm to 16000 mm is taken as a research object, and four experiments are conducted. In order to design specimens for acquiring the forming data, one experiment is conducted to compare the curvature radius of the plate and stringer-structural specimens, which were peened along the middle of the two stringers. The most striking finding of this experiment is that the outer shape error range is below 3.9%, so the plate specimens can be used in predicting feeding speed of the integral panel. The second experiment is performed and results show that when the coverage reaches the limit of 80%, the minimum feeding speed is 50 mm/s. By this feeding speed, the forming curvature radius of the specimens with different thickness from the third experiment is measured and compared with the research object, and the optimal air pressure is 0.15 MPa. Then, the plate specimens with thickness from 2 mm to 5 mm are peened in the fourth experiment, and the measured curvature radius data are used to calculate the feeding speed of different shot peening path by regressive analysis method. The algorithm is validated by forming a test part and the average deviation is 0.496 mm. It is shown that the approach can realize the forming of the integral panel precisely.     

钛合金近β锻造研究

 提出钛合金塑性变形中一种新的热加工方法——钛合金近β锻造。试验和生产实践表明,它能在不影响合金塑性、不降低热稳定性的条件下,显著地提高合金的高温性能、低周疲劳性能和断裂韧性、使钛锻件具有最好的塑性、热强性和断裂韧性的综合。新工艺适用于（α+β）型合金,可应用于α型和近α型合金。     

喷射沉积制备Al-Zn-Mg-Cu合金大型坯组织性能的研究

利用Ospray公司的喷射沉积设备制备了Al11.3Zn2.4Mg1.1Cu合金,合金挤压成棒材后,经过固溶和时效处理,用万能材料实验机对其进行了力学性能测试,合金的抗拉强度为849 MPa、屈服强度为796 MPa,延伸率为3.3%.透射电镜和扫描电镜对拉伸试样微观组织的研究结果表明,合金微观组织中包括微米级晶粒和纳米级晶粒,合金的强化方式为纳米晶强化、固溶强化以及沉淀强化,拉伸试样的断口分析表明,合金的断裂方式主要为沿晶断裂.     

TC4钛合金紧固件孔E-I强化研究

 介绍TC4(Ti-6Al-4V)钛合金螺栓孔无衬套冷胀孔干涉配合综合强化的研究结果。实验证明,在给定的条件下,冷胀孔强化的TC4板状空孔试件的疲劳寿命增益系数(LIF)为13,干涉配合螺栓连接的LIF=3,而E-l强化件的疲劳寿命比单纯干涉配合又有成倍提高。电镜断口分析表明TC4合金强化件的疲劳裂纹的形成和扩展与LY12CZ及30CrMnSiA相似,它们不表现为典型的角裂纹,即沿板平面和厚向扩展速率有明显差异。对于TC4合金,在改善疲劳品质上,带衬套冷胀孔强化比无衬套冷胀孔强化好得多。     

40CrNi2Si2MoVA钢喷丸强化层微观结构

喷丸强化在金属材料表面形成强化层,可以有效提高构件的疲劳寿命,是金属构件表面完整性制造的重要方法.喷丸强化已有效应用于40CrNi2Si2MoVA钢制构件,为了探明喷丸强化对该钢种的强化机理,本工作采用高分辨电子显微电镜(HREM)对40CrNi2Si2MoVA钢喷丸强化层微观组织结构进行了系统分析研究.结果表明:喷丸强化使40CrNi2Si2 MoVA钢组织细化,呈明显的马氏体“有效晶粒”现象,“有效晶粒”尺寸为几个纳米到几十个纳米;“有效晶粒”界面呈明显的倾转现象,相邻“有效晶粒”间转动角度为几度到几十度,最大达到30°.     

Nb对富钛TiNiAl金属间化合物强化机制的影响

 采用力学压缩试验、扫描电镜和X射线衍射方法研究了Nb元素对于Ti₅₀Ni₄₂Al₈合金的力学性能和微观组织结构的影响。结果表明，Nb能够显著提高合金从室温到700 ℃之间的强度。在600 ℃时，Ti₅₀Ni₄₀Al₈Nb₂合金的压缩屈服强度和比强度分别为1 237 MPa和216 MPa/(g·cm^-3)，超过Rene95高温合金。微观组织观察及成分分析表明，Nb元素在基体和强化相Ti₂Ni（Al）中固溶，促进强化相的弥散析出和细化，并导致高强富Nb相的析出，从而提高了合金的强度。     

反舰导弹末端机动对近程反导舰炮的突防模型研究

分析了近程反导舰炮武器的工作原理以及武器系统的射击误差,依据反舰导弹突防“密集阵”系统的对抗过程建立突防模型,并对比分析了速度突防和机动弹道突防的优劣,指出了反舰导弹末端机动对于提高突防概率的必要性。     

TB6钛合金激光喷丸与机械喷丸残余应力场有限元模拟

利用有限元软件建立了TB6钛合金激光喷丸以及机械喷丸的三维数值分析模型,研究了不同工艺参数对残余应力场的影响;对比了两种喷丸工艺所形成的应力波和各自的衰减规律;研究了两种喷丸工艺的复合强化工艺对残余应力场的影响。结果表明:激光喷丸形成的平面波造成较深的应力影响层,深度可达1.5mm;机械喷丸形成的球面波产生较大的残余应力,最大残余压应力可以达到屈服强度的1.1倍。塑性应变越大残余应力越大,塑性应变层与残余应力影响层深度相近;在两者复合强化工艺中,残余应力影响层深度与激光喷丸的相近,最大残余压应力可达屈服强度的1.2倍。     

喷丸强化对AISI420不锈钢固体粒子冲蚀行为的影响

研究了喷丸强化(SP)对AISI 420马氏体不锈钢抗同体粒子冲蚀(SPE)行为的影响.探讨了喷丸引起的表面残余压应力,表面粗糙度增大和表面加工硬化等三因素对SPE抗力的作用机制.结果表明:SP处理对AISI 420不锈钢在30°攻角下的SPE抗力无明显影响,但却降低了该钢在90°攻角下的SPE抗力.SP处理后进行表面抛光,则使该钢在两种攻角下的SPE抗力均得以提高.SP三因素对SPE抗力的作用机制主要有:表面粗糙化增大了试样表面对冲蚀粒子的有效暴露面积,因而降低了不锈钢在两种攻角下的SPE抗力;表面残余压应力能够有效抑制疲劳裂纹萌生和早期扩展,因而能有效提高AISI 420不锈钢的SPE抗力,特别是对90°垂直冲击条件下SPE抗力的提高作用更为明显;表面加工硬化提高了材料表面的微犁削抗力,因而对提高AISI 420钢在30°攻角下的SPE抗力有贡献,但是表面加工硬化层的抗多冲疲劳性能差,却不利于AISI 420钢在90°攻角下抗SPE性能的改善.     

多重纳米结构轻质高强铝基复合材料的制备和组织性能

为了研究多重纳米结构对块体材料强化和变形能力的影响机制,采用粉末冶金法制备了多重纳米结构的B4C颗粒增强铝基复合材料,并对复合材料的强化和形变破坏机制进行了定量和定性的讨论。由100%球磨复合粉末制备的块体复合材料的室温压缩强度为670MPa;当加入10vol%气雾化态的Al2024粉末后,复合材料的室温压缩强度升高到1.115GPa;之后随着气雾化态Al2024粉末含量的增加,复合材料的强度逐渐下降,但是没有产生明显的塑性变形;当气雾化态Al2024粉末的含量增加到50vol%时,复合材料的压缩强度下降到580MPa,断裂前变形率达到了10%。扫描电镜(SEM)和透射电镜(TEM)的分析结果显示,亚微米级的B4C颗粒、位错以及纳米晶基体分别通过Orowan强化、位错强化和细晶强化机制对复合材料进行强化;粗晶Al2024区域与复合结构区域的比例显著影响复合材料的形变及破坏机制。